CN105254982A - Anti-tear polyethylene film - Google Patents
Anti-tear polyethylene film Download PDFInfo
- Publication number
- CN105254982A CN105254982A CN201510811027.3A CN201510811027A CN105254982A CN 105254982 A CN105254982 A CN 105254982A CN 201510811027 A CN201510811027 A CN 201510811027A CN 105254982 A CN105254982 A CN 105254982A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyethylene film
- polyethylene
- styrene
- following components
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-tear polyethylene film. The anti-tear polyethylene film comprises the following components in parts by weight: 3-4 parts of chloridized distearyl dimethyl ammonium, 1-2 parts of a styrene-acrylonitrile copolymer, 4-5 parts of epoxy acrylate, 1-2 parts of polyethylene glycol acrylate, 3-4 parts of oxidized polyethlene wax, 30 parts of polyethylene micropowder, 2-3 parts of triguaiacyl phosphite, 3-4 parts of vinyl trimethoxy silane and 1-2 parts of viscose. The anti-tear polyethylene film is good in transparency, heat resistance and tensile strength and is unlikely to crinkle.
Description
Technical field
The present invention relates to anti tear polyethylene film.
Background technology
Existing anti tear polyethylene film, its transparency, thermotolerance, tensile strength all have much room for improvement, and easily send out wrinkle.
Summary of the invention
The object of the present invention is to provide a kind of anti tear polyethylene film, its transparency, thermotolerance, tensile strength are good, not easily send out wrinkle.
For achieving the above object, technical scheme of the present invention is a kind of anti tear polyethylene film of design, composed of the following components by weight:
3 ~ 4 parts of Varisoft TA 100s,
1 ~ 2 part of styrene-acrylonitrile copolymer,
4 ~ 5 parts of epoxy acrylates,
1 ~ 2 part of polyethyleneglycol diacrylate,
3 ~ 4 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
2 ~ 3 parts of GW-540s,
3 ~ 4 parts of vinyltrimethoxy silanes,
1 ~ 2 part of viscose fiber.
Preferably, anti tear polyethylene film, composed of the following components by weight:
3 parts of Varisoft TA 100s,
1 part of styrene-acrylonitrile copolymer,
4 parts of epoxy acrylates,
1 part of polyethyleneglycol diacrylate,
3 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
2 parts of GW-540s,
3 parts of vinyltrimethoxy silanes,
1 part of viscose fiber.
Preferably, anti tear polyethylene film, composed of the following components by weight:
4 parts of Varisoft TA 100s,
2 parts of styrene-acrylonitrile copolymers,
5 parts of epoxy acrylates,
2 parts of polyethyleneglycol diacrylates,
4 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
3 parts of GW-540s,
4 parts of vinyltrimethoxy silanes,
2 parts of viscose fibers.
Preferably, anti tear polyethylene film, composed of the following components by weight:
3.4 parts of Varisoft TA 100s,
1.2 parts of styrene-acrylonitrile copolymers,
4.5 parts of epoxy acrylates,
1.2 parts of polyethyleneglycol diacrylates,
3.4 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
2.3 parts of GW-540s,
3.4 parts of vinyltrimethoxy silanes,
1.2 parts of viscose fibers.
Advantage of the present invention and beneficial effect are: provide a kind of anti tear polyethylene film, its transparency, thermotolerance, tensile strength are good, not easily send out wrinkle.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Anti tear polyethylene film, composed of the following components by weight:
3 parts of Varisoft TA 100s,
1 part of styrene-acrylonitrile copolymer,
4 parts of epoxy acrylates,
1 part of polyethyleneglycol diacrylate,
3 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
2 parts of GW-540s,
3 parts of vinyltrimethoxy silanes,
1 part of viscose fiber.
Embodiment 2
Anti tear polyethylene film, composed of the following components by weight:
4 parts of Varisoft TA 100s,
2 parts of styrene-acrylonitrile copolymers,
5 parts of epoxy acrylates,
2 parts of polyethyleneglycol diacrylates,
4 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
3 parts of GW-540s,
4 parts of vinyltrimethoxy silanes,
2 parts of viscose fibers.
Embodiment 3
Anti tear polyethylene film, composed of the following components by weight:
3.4 parts of Varisoft TA 100s,
1.2 parts of styrene-acrylonitrile copolymers,
4.5 parts of epoxy acrylates,
1.2 parts of polyethyleneglycol diacrylates,
3.4 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
2.3 parts of GW-540s,
3.4 parts of vinyltrimethoxy silanes,
1.2 parts of viscose fibers.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. anti tear polyethylene film, is characterized in that, composed of the following components by weight:
3 ~ 4 parts of Varisoft TA 100s,
1 ~ 2 part of styrene-acrylonitrile copolymer,
4 ~ 5 parts of epoxy acrylates,
1 ~ 2 part of polyethyleneglycol diacrylate,
3 ~ 4 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
2 ~ 3 parts of GW-540s,
3 ~ 4 parts of vinyltrimethoxy silanes,
1 ~ 2 part of viscose fiber.
2. anti tear polyethylene film according to claim 1, is characterized in that, composed of the following components by weight:
3 parts of Varisoft TA 100s,
1 part of styrene-acrylonitrile copolymer,
4 parts of epoxy acrylates,
1 part of polyethyleneglycol diacrylate,
3 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
2 parts of GW-540s,
3 parts of vinyltrimethoxy silanes,
1 part of viscose fiber.
3. anti tear polyethylene film according to claim 1, is characterized in that, composed of the following components by weight:
4 parts of Varisoft TA 100s,
2 parts of styrene-acrylonitrile copolymers,
5 parts of epoxy acrylates,
2 parts of polyethyleneglycol diacrylates,
4 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
3 parts of GW-540s,
4 parts of vinyltrimethoxy silanes,
2 parts of viscose fibers.
4. anti tear polyethylene film according to claim 1, is characterized in that, composed of the following components by weight:
3.4 parts of Varisoft TA 100s,
1.2 parts of styrene-acrylonitrile copolymers,
4.5 parts of epoxy acrylates,
1.2 parts of polyethyleneglycol diacrylates,
3.4 parts of oxidized polyethlene wax,
30 parts of polyethylene micropowders,
2.3 parts of GW-540s,
3.4 parts of vinyltrimethoxy silanes,
1.2 parts of viscose fibers.