CN105247418B - Developer supply roller and its manufacturing method - Google Patents
Developer supply roller and its manufacturing method Download PDFInfo
- Publication number
- CN105247418B CN105247418B CN201480029515.2A CN201480029515A CN105247418B CN 105247418 B CN105247418 B CN 105247418B CN 201480029515 A CN201480029515 A CN 201480029515A CN 105247418 B CN105247418 B CN 105247418B
- Authority
- CN
- China
- Prior art keywords
- supply roller
- developer supply
- developer
- high molecular
- foam material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of developer supply roller is provided, can easily remove undeveloped developer, and an adequate amount of developer can promptly be supplied with good responsiveness;Also provide the manufacturing method of the developer supply roller.For image forming apparatus and its surface be high molecular foam material the developer supply roller be characterized by having surface roughness be 60 μm more than and less than 140 μm, the wherein surface roughness is defined as: when measurement length is 40mm, measurement interval is 1mm and there are when 40 measurement points, the standard deviation of the displacement of whole measurement points and baseline.
Description
Technical field
The present invention relates to a kind of developer supply rollers, are used for image forming apparatus, particularly, the figure of electrofax processing
As forming device;With its manufacturing method.
Background technique
In the image forming apparatus that the electrofax of such as duplicator and printer etc. is handled, has existed in Fig. 1 and show
Method out is as image forming method, wherein supplying monocomponent toner to the image with the electrostatic latent image carried thereon
Body, such as photoreceptor are formed, and the sub-image visualizes and adhering to developer thereon.
Specifically, it shows as shown in figure 1, the configuration of developer roll 2 is in developer supply roller 3 and the sense for carrying electrostatic latent image thereon
Between body of light 1, and photoreceptor 1 is contacted via transfer materials 8 with transfer roll 5.Transfer materials 8 without when, transfer roll 5 with
Photoreceptor 1 directly contacts.Developer supply roller 3, developer roll 2 and photoreceptor 1 are rotated with the direction shown in arrow, therefore will development
Agent is supplied from developer supply roller 3 to the surface of developer roll 2, and is being adjusted to uniform thin layer using layer adjusting scraper plate 4
Later, the electrostatic latent image being attached on photoreceptor 1, therefore visualize the sub-image.Electric field is formed in photoreceptor 1 and transfer roll
Between 5, therefore by the developer image on photoreceptor 1 to transfer materials 8.Number 6 indicates clearer, and will turn
Remaining developer is removed using clearer 6 on the surface of photoreceptor 1 after print.Number 7 indicates charging roller.
The developer supply roller of image forming apparatus as the non-magnetic single component developer handled for electrofax
3, use the roller of the steel shaft comprising being covered by high molecular foam material.The hardness that developer supply roller needs to have low, does not pollute
Developer roll, and do not melt and have developer.
The example for constituting the material of high molecular foam material includes: blown rubber, wherein will such as silicon rubber, epichlorohydrin rubber
The solid rubber of glue and acrylonitrile-butadiene rubber etc. is foamed using chemical foaming agent and is solidified by vulcanization;With it is poly-
Urethane Foamex is obtained by following: the curing reaction of the liquid charging stock such as polyalcohol and isocyanates, is led to simultaneously
It crosses mechanical stirring and foams to mix bubble or add the foaming agent such as water.
The component of the image forming apparatus formed by previous materials can need in some cases it is conductive, and can
There is defined electricity by mixing conductive material such as carbon black and metal oxide or addition electrolyte to adjust
Resistance value.Wherein, as material, since what the material can be used in conductive material and electrolyte any assigns electric conductivity and electricity
Solution matter can by be dissolved in its liquid charging stock come using the advantage that, use polyalcohol and polyisocyanates as mainly
Raw material and the polyurethane resin that is formed are suitable for the foaming polymer material of developer supply roller (referring to PTL 1).
There are three functions for developer supply roller tool, that is, removes the remaining undeveloped developer on developer roll, new is aobvious
Shadow agent is supplied to developer roll, and the charge volume of control developer.It removes undeveloped developer and supplies new developer by aobvious
The influence of the stomatal number of the hardness and high molecular foam material of shadow agent supply roller, and in the case where carrying out electric control, also by
The influence of the resistance of developer supply roller.
Existing technical literature
Patent document
PTL 1:JP-A-2001-42630
Summary of the invention
Problems to be solved by the invention
The increase of number that with the high speed of image forming apparatus in recent years and does not exchange developing apparatus and can print,
Such developer supply roller needs the ability with the increased undeveloped developer of removal and can also supply substantial amount
Developer be suitable for flying print simultaneously.Effectively to it, increase the hardness of developer supply roller, but developer supplies wherein
To roller hardness it is too big in the case where, when after printing a large amount of paper without exchanging developing apparatus, developer can be undergone instead
Normal charged state causes image bad, such as fuzzy and striped.In addition, the stomatal number in high molecular foam material increases
And in the case that hole diameter reduces, the removal ability of undeveloped developer also be will increase, but the new development that can be supplied
The amount of agent can reduce.Under the stomatal number reduction of high molecular foam material and the increased situation of hole diameter, it can supply
The amount of new reagent can increase, but the ability for removing undeveloped developer can reduce.
In this case, the object of the present invention is to provide a kind of developer supply rollers, undeveloped with high removal
The ability of developer and an adequate amount of developer can be supplied while being suitable for flying print;With its manufacturing method.
The solution to the problem
As the result conscientiously studied made by the present inventor in order to realize the purpose, it has been found that new
Developer can effectively supply, while so that the surface roughness on the surface of high molecular foam material is thick greater than defined
Such mode of rugosity, removes effectively undeveloped developer.
Present invention accordingly provides:
[1] a kind of developer supply roller for image forming apparatus includes high molecular foam material on the surface thereof,
Wherein, the surface roughness defined below of the high molecular foam material is 60 μm more than and less than 140 μm, and
And
The surface roughness is defined as in measurement length being 40mm, and 1mm is divided between measurement and measures points as 40
In the case of, the standard deviation of the displacement for whole measurement points that the slave baseline measured is started.
[2] a kind of manufacturing method of the developer supply roller according to item [1] comprising: by high molecular foam material
Surface ground with grinding stone to polish;The grinding stone used is RF grinding stone, and the grinding is in the RF grinding stone
Revolution be 800rpm or more and 2,000rpm it is below under the conditions of carry out.
The effect of invention
According to the present invention it is possible to a kind of developer supply roller is provided, the energy with the high undeveloped developer of removal
Power and an adequate amount of developer can be supplied while being suitable for flying print;With its manufacturing method.
Detailed description of the invention
[Fig. 1] Fig. 1 is the explanatory diagram for showing an example of image forming apparatus for electrofax processing.
[Fig. 2] Fig. 2 is the schematic diagram for showing the measurement method of surface roughness.
[Fig. 3] Fig. 3 is the photo for showing the surface state of RF grinding stone.
[Fig. 4] Fig. 4 is the photo for showing the surface state of NX grinding stone.
Specific embodiment
Developer supply roller of the invention can be the developer supply roller for image forming apparatus comprising have height
Molecule foamed material covers the metallic roll on its surface, and wherein the surface roughness on the surface of high molecular foam material is 60 μm or more
And less than 140 μm.
The surface roughness on the surface of material is usually defined by JIS B0601 etc., but developer supply roller is by its table
Has leachy high molecular foam material on face to be formed, therefore surface roughness cannot be measured with probe.Therefore, in this hair
In bright, surface roughness is defined as in measurement length be to be divided into 1mm between 40mm measurement and measure in the case that points are 40,
The standard deviation of the displacement for whole measurement points that the slave baseline measured is started.
Surface roughness described in detail below.To developer supply roller of the invention it is important that control rough surface
The quality of degree, but cannot be used for measuring using the surface finish measurement equipment of probe, this is because the probe is hindered by stomata.
Therefore, in the present invention, surface roughness is evaluated using laser dimension measuring apparatus by measuring the displacement apart from baseline.
In the evaluation, necessarily explore such condition: the image such as fuzzy and striped is bad to be shown and passes through
The good relationship and measured value of the measured value of evaluation method are stablized.Knot as the conscientious research made by the present inventor
Fruit, it has been found that the distance between measurement point is important to the good relationship provided between image quality and measured value
's;And it is necessary that the distance between measurement point (being hereinafter properly termed as measurement interval) is 0.5 to 3mm, and measurement point
Number is 20 or more, and more preferable 30 or more.When measurement interval is more than 3mm, will not obtain and the undesirable relationship of image;And
When measurement interval is less than 0.5mm, the fluctuation of measurement becomes larger that the reproducibility of measurement cannot be provided.
In the present invention, by being 40mm in measurement length, it is divided into 1mm between measurement and measures the case where points are 40
Under, the standard deviation of the displacement for whole measurement points that the slave baseline that measures is started evaluates surface roughness.Baseline can pass through
The least square method of whole measurement points measures to draw straight line.
More specifically, being used in the measurement such as Fig. 2 of evaluation show to carry out.The upper part of Fig. 2 is developer of the invention
The schematic diagram of supply roller, and its underpart is the schematic diagram for showing measurement method.Measurement line 13 shows laser, and will have
The interval of 1mm sequentially include 40 points from L1, L2 and L3 to L40 by with the direction shown in arrow using linear laser come
It scans and measures.Therefore, the measurement length of total is 40mm.It is used herein as the laser of Mitsutoyo Corporation production
Dimension measuring apparatus.
Then, baseline is provided by the least square method as shown in the dotted line in Fig. 2, and by baseline and measurement point it
Between difference, that is, calculate the standard deviation of the displacement for whole measurement points that the slave baseline that measures is started and be defined as rough surface
Degree.
Measurement method needs about 30 seconds durations of each developer supply roller.The quality of roller can pass through JIS
AQL (acceptable quality horizontal) inspection by sampling that Z9015 is recorded ensures.Thus it is speculated that using a grinder in a life
It produces the developer supply roller produced in the period and is defined as a batch, select the sample of the conventional detection standard I of the subordinate list A1 of JIS Z9015
Product text measures standard by the way that the table sampling of conventional detection to be measured to sample number, and according to the batch of conventional detection to survey
The qualified distribution of the fixed batch.In the case, acceptable quality level can be 0.1 or more and 1.0 hereinafter, and preferably 0.4,
Therefore the occurrence frequency of detection working hour and substandard product is within the acceptable range.In the case where unqualified batch occurs,
Detection is necessarily converted into strict inspection, and if detection is continued with the sampling frequency of conventional detection, substandard product
Occurrence frequency can become unacceptable.In the case that continuing three batches in strict inspection does not have unqualified batch, work as detection
When recovery to conventional detection, the occurrence frequency of substandard product can be within the acceptable range.Continue three in conventional detection
In the case where batch not having unqualified batch, when detection is converted into loose detection, the occurrence frequency of substandard product can be with
Within the acceptable range.In the case that in loose detection, unqualified batch occurs, detection necessarily restores to conventional detection,
And if loose detection continues, the occurrence frequency of substandard product can become unacceptable.In addition, it is thick to calculate three batches of surfaces
The process capability index of rugosity, and when process capability index is 1.33 or more, special detection level S-1 can be used, and
And the occurrence frequency of substandard product can be within the acceptable range.
The surface roughness as defined above of developer supply roller of the invention is 60 μm more than and less than 140 μm.When
When surface roughness is less than 60 μm, an adequate amount of developer will not be supplied, can cause to obscure in flying print.Another party
Face, when surface roughness is 140 μm or more, the ability for removing undeveloped developer can be insufficient, can inhibit not hand over
The number that developing apparatus can print is changed to increase.
In view of the viewpoint, preferably 70 μm of surface roughness more than and less than 120 μm.Particularly, good image can lead to
Crossing makes target reach 80 μm of surface roughness more than and less than 120 μm to retain.
The example of the manufacturing method of developer supply roller including the high molecular foam material with aforementioned surfaces roughness
Include:
(1) by high molecular foam material in the mold with defined surface roughness cured method;
(2) by with slightly large-sized cured high molecular foam material in the mold with defined surface roughness
The method of thermal deformation (figuration);With
(3) surface roughness of cured high molecular foam material is made to be refined to regulation by grinding or attrition process
Surface roughness method.
Wherein, method (1) is to be kept surface roughness to the method for defined value using mold, it is therefore desirable to accurately
The roughness of the inner surface of Measurement die, and its management is not easy.In method (2), material can be when being exposed to high temperature
Restore original-shape, therefore its management is not easy.On the other hand, high molecular foam material is controlled by grinding or attrition process
The method (3) of surface roughness be advantageous, this is because managing and maintaining for mold is unnecessary, and be exposed to
The recovery of original-shape will not occur when high temperature.
In method (3), that is, the developer supply roller finished and grinding high molecular foam material using grinding stone
In manufacturing method, the present invention is made by following: the developer replenishing with specific surface roughness of the invention
Roller can be obtained and the low speed to be not yet used for usual method is ground using RF grinding stone by easy production management.
Specifically, grinding is 800rpm or more and 2,000rpm hereinafter, and more preferably 800rpm or more in grinding stone revolution
And 1,000rpm it is below under the conditions of carry out, thus provide the developer supply roller with aforementioned surfaces roughness.
The RF grinding stone herein being related to is the metal with the surface of pin shape (pinholder) form as shown in Figure 3
Grinding stone.The use of grinding stone under grinding condition according to the present invention ensures to produce with simple procedure with good yield
The developer supply roller of surface roughness with high molecular foam material of the invention.
Even if using RF grinding stone, when revolution is common grinding condition, that is, when 5,000 to 7,000rpm, surface roughness
60 μm are become smaller than, therefore fails to provide developer supply roller of the invention.
In the case where grinding to be carried out greater than 2,000rpm and 5,000rpm RF grinding stone used below, when macromolecule is sent out
When foam material has stomatal number for less than 60, the developer supply roller with surface roughness of the invention can be obtained, but
When it is less than 60 that high molecular foam material, which has stomatal number, will not steadily produce with surface roughness of the invention
Developer supply roller.
In addition, by high molecular foam material under 800rpm grinding stone revolution below using RF grinding stone to grind the case where
Under, surface roughness can become 140 μm or more.
Using the grinding stone such as GC60, GC80, NX60 and NX80 commonly used in grinding rubber rollers 1,000 to 2,
In the case that the grinding stone revolution of 000rpm gets off to grind high molecular foam material, surface roughness can become 60 μm or less.Example
The grinding stone of such as GC60, GC80, NX60 and NX80 cannot be carried out due to its big quality under the revolution of 2,000rpm or more
Grinding operation, and helical form grinding marks is formed on the surface of high molecular foam material under 1,000rpm revolution below
Mark, therefore it is bad when supplying developer due to uneven to generate image.
Fig. 4 is the photo for being shown as the surface state of NX grinding stone of porous sintered ceramic.GC grinding stone shape having the same
State, and developer supply roller of the invention cannot be produced using the grinding stone of these types.
The high molecular foam material on the surface of developer supply roller of the invention is not particularly limited, and it is preferred real
Example includes silicon rubber, epichlorohydrin rubber, acrylic-nitrile rubber, ethylene-propylene rubber, Ethylene-Propylene-Diene rubber and polyurethane
Resin.High molecular foam material can be used individually or as its a variety of mixture.The bulk volume ratio of high molecular foam material
Weight preferably 0.03 to 0.2.When bulk specific gravity is 0.03 or more, the part that foam inside skeleton occupies will not be too small, really
The removing of remaining developer after developing is protected.In view of the removing of developer remaining after development, bulk specific gravity is more excellent
Select 0.06 or more.When bulk specific gravity is 0.2 or less, the deterioration (abnormality of developer of developer after to long-time service
The increase of the occurrence frequency of charging) inhibition viewpoint, to be advantageous;And bulk specific gravity more preferable 0.12 hereinafter, this
It is because further suppressing the deterioration of developer.Therefore, the bulk specific gravity of high molecular foam material more preferably 0.06 to
In the range of 0.12.
The providing method of used foamed material can be using the method for chemical foaming agent and by air or indifferent gas
The method of body mechanical mixture;And can be it is preferable to use the polyurethane resin of Water blown, wherein carbon dioxide is produced from as hair
The reaction of the water and polyisocyanates of infusion.
The preferred stomatal number of high molecular foam material in the present invention be 60 or more, more preferable 70 or more, and
Further preferred 80 or more.When stomatal number is 60 or more, can steadily produce with surface roughness of the invention
Developer supply roller.
By electric conductivity assign be used for developer supply roller foaming polymer material method may is that by such as carbon black,
The method that the electroconductive powder of metal powder and conductive metal oxide etc. is added to high molecular material;For high molecular material
It is the high molecular situation of polarity, adds alkali and such as hydrochloric acid, perchloric acid and alkane by such as alkali metal, alkaline-earth metal and quaternary ammonium etc.
The method of the electrolyte of the acid group composition of base sulfuric acid etc.;With use wherein the conductive material such as carbon black be added to such as propylene
The conductive coating paint of the resin of acid resin etc. is come the method that is coated with foaming polymer material.
The axis of used developer supply roller may is that by being rule by sulphur automatic steel or the cutting of lead and easy-cutting steel
Fixed shape and the axis for being carried out electroless nickel plating acquisition: or by being the axis for providing shape and obtaining by stainless steel cutting.
The foaming polymer material and axis for constituting developer supply roller can be used adhesive and be fixed to one another.Do not have to adhesive
It is restricted, and its used preferred embodiment includes epoxy adhesive, cyanoacrylate system adhesive and by polyurethane
Or the hotmelt of the formation such as vinyl-vinyl acetate copolymer.
Known method can be by using the manufacturing method of the developer supply roller of high molecular foam material.This method
Example includes the method recorded in Japan Patent No.4916129.More specifically, manufacturing method may comprise steps of (1)
To (3).
(1) the insertion hole of axis is formed in high molecular foam material.
(2) hot melt urethane adhesives of form membrane are wrapped in the metal shaft of insertion high molecular foam material, then
Assembly is heated to bond axis and high molecular foam material.
(3) after being cooled to room temperature nearby, the commercially available cylindrical shape that high molecular foam material is used for rubber rollers is ground
Grinding machine is ground to defined size.
Embodiment
The present invention will be described in more detail for reference implementation example, but the present invention is not limited to these Examples.
The measurement of embodiment and comparative example is carried out in the following manner.
Embodiment 1
By Bridgestone Diversified Chemical Products Co., the polyurethane foam of Ltd. production
HPN70 is cut into length 58mm × width 510mm × thickness 18mm, and using producing containing Lion Corporation
26.9% Lionpaste W-311N, Shin-Etsu Chemical Co., Ltd. production 0.2% defoaming agent KS-
502,18.1% acryloid cement aqueous solution of Enex Co., Ltd. production and the conductive coating paint of 54.8% pure water
It impregnates, then at 150 DEG C drying and curing 1 hour.The bulk specific gravity of polyurethane foam is 0.065, and hardness is Ask F
80 °, volume resistivity when stomatal number 70 and voltage are 1V is 104(Ωcm)。
Then, the axis pre-add obtained by the way that the SUM23 steel shaft of the diameter with 6mm to 6 μm is carried out electroless nickel plating
Heat is wound with the adhesiveness film for being cut into the Daicel Finechem Ltd. production of 240mm × 20mm to 100 DEG C thereon
Thermolite 6501;And assembly is heated to 140 DEG C in 30 minutes, is then cooled down.Therefore the axis obtained is passed through
The method recorded in Japan Patent No.4916129 uses and has been cut into 240mm × 18mm × 18mm size and at it
Center is provided with the aforementioned polyurethane foam in the hole of the diameter with 5.0mm to cover, and assembly is added in 90 minutes
Then heat is cooled down to 130 DEG C, therefore axis and polyurethane foam are bonded.
Use the commercially available cylinder for rubber rollers for the RF grinding stone #60 for being equipped with the size with 305 × 40 × 76.2mm
Shape grinder is 1,000rpm in grinding stone revolution, and the revolution of polyurethane foam is 2,500rpm, and the positive movement speed of grinding stone is
When to move backward speed be 3,000 (mm/min) of 2,000 (mm/min) and grinding stone, will be adhered to the polyurethane foam of axis
Foam is ground to the cylindrical shape with the diameter of 15mm, therefore produces developer supply roller.The surface of developer supply roller is thick
Rugosity is 100 μm.
Be equipped with developer supply roller non-magnetic single component developer electrofax processing image forming apparatus it is long when
Phase provides good image without generating fuzzy and striped in the picture.
Comparative example 1
In addition to changing into grinding stone revolution other than 6,500rpm, supplied in the same manner as example 1 to produce developer
To roller.The surface roughness of developer supply roller is 40 μm.The non-magnetic single component developer electricity of developer supply roller is installed
The image forming apparatus of son photograph processing generates vertical white band line in image rear end when printing solid black image.It is thought that
Because lacking toner supply capacity.
Embodiment 2
Polyurethane foam is produced by the method recorded in Japan Patent No.2855335 and is cut into 240mm
The size of × 18mm × 18mm.The bulk specific gravity of polyurethane foam is 0.105, and hardness is 70 ° of Ask F, stomatal number 80,
It is 10 with the volume resistivity when voltage is 100V4(Ωcm).Produce developer replenishing in the same manner as example 1
Roller.The surface roughness of developer supply roller is 95 μm.The non-magnetic single component developer electronics of developer supply roller is installed
The image forming apparatus handled of taking a picture provides good image without generating fuzzy and striped in the picture over a long time.
Comparative example 2
There is the GC grinding stone #60 of the size of 760 × 75 × 304.8mm in addition to using, be in the revolution of polyurethane foam
300rpm, the positive movement speed of grinding stone are 900 (mm/min) and when to move backward speed be Isosorbide-5-Nitrae 00 (mm/min) of grinding stone,
Polyurethane foam is ground to other than the cylindrical shape with the diameter of 15mm, it is aobvious to produce in the same manner as example 1
Shadow agent supply roller.The surface roughness of developer supply roller is 40 μm.The non-magnetic mono-component for being equipped with developer supply roller is aobvious
The image forming apparatus of shadow agent electrofax processing generates vertical white band line in image rear end when printing solid black image.Recognize
For this is because lacking toner supply capacity.
Industrial availability
Developer supply roller of the invention ensures that high speed image forms the production of the developing apparatus of device, and long-term is not
Lead to the undesirable formation of image, therefore is suitable for the component of image forming apparatus.
Description of symbols
1 photoreceptor
2 developer rolls
3 developer supply rollers
4 layers of adjusting scraper plate
5 transfer rolls
6 clearers
7 charging rollers
8 transfer materials
11 axis
12 rubber rollers (high molecular foam material)
13 measurements line (laser)
Claims (5)
1. a kind of manufacturing method of developer supply roller, the developer supply roller is the developer confession for image forming apparatus
It on the surface thereof include high molecular foam material to roller, the surface roughness defined below of the high molecular foam material is
60 μm more than and less than 140 μm, which is characterized in that the described method includes: the surface of high molecular foam material is carried out with grinding stone
Grinding is to polish;The grinding stone used is RF grinding stone, and the grinding is 800rpm or more in the revolution of the RF grinding stone
And 2,000rpm it is below under the conditions of carry out;
The surface roughness is defined as in measurement length being 40mm, and 1mm is divided between measurement and measures the case where points are 40
Under, the standard deviation of the displacement for whole measurement points that the slave baseline measured is started.
2. the manufacturing method of developer supply roller according to claim 1, wherein the revolution is 800rpm or more and 1,
000rpm or less.
3. the manufacturing method of developer supply roller according to claim 1, wherein the stomata of the high molecular foam material
Number is 60 or more.
4. the manufacturing method of developer supply roller according to claim 3, wherein the stomata of the high molecular foam material
Number is 80 or more.
5. the manufacturing method of developer supply roller according to any one of claims 1 to 4, wherein the macromolecule foaming material
The bulk specific gravity of material is 0.03 to 0.2.