CN105238914A - Method for preparing thermal treatment protective agent for detecting tool for detection of foot-pedal sawing machine - Google Patents
Method for preparing thermal treatment protective agent for detecting tool for detection of foot-pedal sawing machine Download PDFInfo
- Publication number
- CN105238914A CN105238914A CN201510616838.8A CN201510616838A CN105238914A CN 105238914 A CN105238914 A CN 105238914A CN 201510616838 A CN201510616838 A CN 201510616838A CN 105238914 A CN105238914 A CN 105238914A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- foot
- thermal treatment
- sawing machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of machining, in particular to a method for preparing a thermal treatment protective agent for a detecting tool for detection of a foot-pedal sawing machine. Firstly, 20 parts of sodium laureth sulfate and 20 parts of water are added into a container and stirred for 5 minutes; then 0.3 part of hydrochloric acid is slowly added with stirring and stirred for 5 minutes after adding is finished; 15 parts of polydimethylsiloxane and 10 parts of water are slowly added with stirring and stirred for 5 minutes after adding is finished; 2 parts of beta-homochelidonine are slowly added with stirring and stirred for 5 minutes after adding is finished; finally, 15 parts of sodium benzoate and 17.7 parts of water are slowly added and stirred for 10 minutes. According to the method for preparing the thermal treatment protective agent for the detecting tool for detection of the foot-pedal sawing machine, by means of the gradual adding method, the dissolving properties among all substances can be improved, the possibility of particle agglomeration can be avoided, and the surface protecting function of the protective agent can be remarkably improved.
Description
Technical field
The present invention relates to Machining Technology field, specifically relate to a kind of protectant preparation method of thermal treatment of the cubing detected for foot-operated sawing machine.
Background technology
Cubing is that industrial production enterprise is for controlling the simple and direct instrument of product various size (such as aperture, bulk etc.), enhance productivity and Mass Control, be applicable to the product produced in enormous quantities, as automobile component, with alternative professional survey instrument, as smooth feeler gauge, threaded plug gauge, caliber gauge etc.
Foot-operated sawing machine cubing, as the one in the above-mentioned cubing mentioned, it is of wide application.In the course of processing, thermal treatment is absolutely necessary critical process.The protectant preparation method of thermal treatment of the existing cubing detected for foot-operated sawing machine, the defects such as ubiquity complex process.The protective material used in heat treatment process, main exist and can not thoroughly protect, to such an extent as to when heating in follow-up naked light formula normalizing furnace, and its surface can not be processed the defect such as evenly.This has just had a strong impact on the process for processing of cubing, and serious conditions can cause thoroughly scrapping of cubing, therefore virtually adds the production cost of enterprise.
Summary of the invention
For the technical problem existed in prior art, the object of the present invention is to provide a kind of protectant preparation method of thermal treatment of the cubing detected for foot-operated sawing machine, for achieving the above object, present invention employs following technical scheme:
For the protectant preparation method of thermal treatment of the cubing that foot-operated sawing machine detects, step is as follows:
First in container, add 20 parts of laureth sodium sulfovinates and 20 parts of water, stir 5 minutes; Then slowly add 0.3 part of hydrochloric acid, limit edged stirs, and stirs 5 minutes after interpolation; Then slowly add 15 parts of polydimethylsiloxanes and 10 parts of water, limit edged stirs, and stirs 5 minutes after interpolation; Then slowly add 2 parts of β-homochelidonine, limit edged stirs, and stirs 5 minutes after interpolation; Finally slowly add 15 parts of Sodium Benzoates and 17.7 parts of water, stir 10 minutes.
Beneficial effect of the present invention shows:
1), the protective material that uses in heat treating method, its formulating of recipe is reasonable, particularly with the addition of a small amount of β-homochelidonine (extract component of plant Yanhusuo), can significantly improve protectant processing efficiency.By protectant with the use of, when cubing is heated in follow-up naked light formula normalizing furnace, surface process very even.
2), protectant preparation method, by the method for progressively adding, the solubility property between each material can not only be improved, the possibility of particle agglomeration can also be avoided, protectant surface protecting function is promoted significantly.
3), the heat treating method of cubing; operating procedure is succinct, focuses on the step being sprayed by protective material and then heat-treat, by the protectant formula of appropriate design; thus realize being protected of cubing surface, then improve thermal effectiveness and the quality of cubing.
Embodiment
Below with reference to embodiment, the present invention is described in detail.But; embodiment content is only citing made for the present invention and explanation; affiliated those skilled in the art make various amendment to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from the design of invention or surmount this scope as defined in the claims, protection scope of the present invention all should be belonged to.
One, protectant composition
Polydimethylsiloxane 15 parts of laureth sodium sulfovinates 20 parts
Hydrochloric acid 0.3 part of β-homochelidonine 2 parts
47.7 parts, Sodium Benzoate 15 parts of water.
Two, protectant preparation method is:
First in container, add 20 parts of laureth sodium sulfovinates and 20 parts of water, stir 5 minutes; Then slowly add 0.3 part of hydrochloric acid, limit edged stirs, and stirs 5 minutes after interpolation; Then slowly add 15 parts of polydimethylsiloxanes and 10 parts of water, limit edged stirs, and stirs 5 minutes after interpolation; Then slowly add 2 parts of β-homochelidonine, limit edged stirs, and stirs 5 minutes after interpolation; Finally slowly add 15 parts of Sodium Benzoates and 17.7 parts of water, stir 10 minutes.
The protectant preparation method of thermal treatment of the cubing three, detected for foot-operated sawing machine, step is as follows:
Step 1., the greasy dirt on erasing cubing surface, then to rinse with water.
Step 2., the protective material being heated to 50 DEG C is in advance sprayed into the surface of cubing.
Step 3., cubing put into naked light formula normalizing furnace carry out heat treated.
Step 4., the cubing after heat treated proceeded in non restraint quencher and quenches, thus complete thermal treatment.
Claims (1)
1. the protectant preparation method of thermal treatment of the cubing detected for foot-operated sawing machine, is characterized in that step is as follows:
First in container, add 20 parts of laureth sodium sulfovinates and 20 parts of water, stir 5 minutes; Then slowly add 0.3 part of hydrochloric acid, limit edged stirs, and stirs 5 minutes after interpolation; Then slowly add 15 parts of polydimethylsiloxanes and 10 parts of water, limit edged stirs, and stirs 5 minutes after interpolation; Then slowly add 2 parts of β-homochelidonine, limit edged stirs, and stirs 5 minutes after interpolation; Finally slowly add 15 parts of Sodium Benzoates and 17.7 parts of water, stir 10 minutes.