CN105238282A - Corrosion-resistant soundproof adhesive containing quartz powder - Google Patents
Corrosion-resistant soundproof adhesive containing quartz powder Download PDFInfo
- Publication number
- CN105238282A CN105238282A CN201510633179.9A CN201510633179A CN105238282A CN 105238282 A CN105238282 A CN 105238282A CN 201510633179 A CN201510633179 A CN 201510633179A CN 105238282 A CN105238282 A CN 105238282A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- water
- corrosion
- silica powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a corrosion-resistant soundproof adhesive containing quartz powder. The adhesive is prepared from the following raw materials in parts by weight: 22 to 25 parts of acrylic emulsion, 10 to 15 parts of sodium silicate with a baume degree of 40, 5 to 7 parts of quartz powder, 2 to 4 parts of silane coupling agent KH-530, 1 to 3 parts of Turkey red oil, 1 to 2 parts of chlorinated paraffin, 1 to 2 parts of alkylphenol polyoxyethylene, 2 to 4 parts of vinyl tert-carbonate, 1.2 to 2.7 parts of polyurethane, 10 to 20 parts of aqueous terpene resin, and 3 to 5 parts of modified composite fiber. The added natural quartz powder can improve the wear-resistant property of the adhesive and can also enhance the strength and soundproof effect. The acrylic emulsion is nontoxic, nonirritant, and harmless to human body, and is accord with the environmental requirements. The non-film-forming glossy resin has excellent luster and transparency and a good anti-adhesion performance.
Description
Technical field
The present invention relates to sound-proof material technical field, particularly relate to a kind of corrosion-resistant sound insulation sizing agent containing silica powder.
Background technology
Sound insulation for building, refers to the development along with modern city, the increase of noisemaker, buildings intensive, the use of high strength light material, effectively to insulate against sound safeguard procedures to buildings.Sound insulation for building, except will considering the acoustic noises in buildings caused by people's activity, also will consider that the outer noise such as communications and transportation, industry and commerce activity of buildings imports caused interference into.
The gap of construction wall, plasterboard, concrete etc., if need not insulate against sound, sealing agent is crammed, capital becomes effective passage of noise transmission, significantly reduce the soundproof effect that engineering can obtain originally, special acoustic mastic is utilized to process gap, hundred times of ground can be become to reduce noises by the propagation in gap, and this acoustic mastic can be directly used in almost on any clean object, comprises plasterboard, cement plate, calcium silicate board, concrete, brick and metal etc.
Natural fiber material has the features such as the moisture absorption, sound insulation, damping, noise reduction, shock-resistance are high, good hand touch, and have in fields such as upholsterys and other materials (as glass reinforced plastic) unrivaled advantage, it is a kind of novel excellent ep-type material.Can natural degradation after natural fibre products is discarded, therefore the impact of natural fiber waste material on environment is less.。
Summary of the invention
The object of the invention is exactly the defect in order to make up prior art, provides a kind of corrosion-resistant sound insulation sizing agent containing silica powder.
The present invention is achieved by the following technical solutions:
A corrosion-resistant sound insulation sizing agent containing silica powder, is obtained by the raw material of following weight parts:
ACRYLIC EMULSION 22-25,40 degree Beaume water glass 10-15, silica powder 5-7, silane coupling agent KH-5302-4, turkey red oil 1-3, clorafin 1-2, alkylphenol polyoxyethylene 1-2, tertiary ethylene carbonate 2-4, urethane 1.2-2.7, water-based terpine resin 10-20, modified composite fiber 3-5;
Described modified composite fiber is obtained by the raw material of following weight parts:
Ramee 3-5, stalk 1-3, pomelo peel 4-6, coir 3-5, cotton 1-2;
The preparation method of described modified composite fiber is:
(1) by pomelo peel, stalk, coir chopping, be soak 1-3 hour in the hydrochloric acid soln of 3-5% in concentration, take out, deionized water wash, dries to obtain pickling raw material;
(2) by all the other raw materials in concentration be 4-5% sodium hydroxide solution in soak 3-5 hour, take out, deionized water wash, dries to obtain alkali cleaning raw material;
(3) by pickling raw material, alkali cleaning raw material blending, boil 4-8 minute, then carry out steam explosion treatment at 70-80 DEG C of Water Under, the pressure of described Steam explosion treatment is 0.9-1.5MPa, and the Steam explosion treatment time is 5-10 minute, to obtain final product.
Described a kind of corrosion-resistant sound insulation sizing agent containing silica powder,
Preparation method's step is as follows:
(1) add tertiary ethylene carbonate, urethane, water-based terpine resin and suitable quantity of water in a kettle. to stir;
(2) be heated to 40-50 DEG C and add ACRYLIC EMULSION, 40 degree Beaume water glass, silica powder, silane coupling agent KH-530, add rear insulation 1-3 hour;
(3) after having reacted, be cooled to 20-35 DEG C, add all the other raw materials and suitable quantity of water mixing, stir, to obtain final product.
Advantage of the present invention is: (1) the present invention is nontoxic; The present invention utilizes the silica powder of sky vacation to increase wear resistance of the present invention, and corrosion-resistant resistance to acids and bases, while also can gain in strength and soundproof effect; ACRYLIC EMULSION is nontoxic, non-stimulated, harmless, meets environmental requirement, non-film height photopolymer resin, and have excellent gloss and the transparency, antiblocking performance is good.
(2) the composite natural fiber of Steam explosion treatment is utilized, steam explosion is as a new technology, be considered to bio-regeneration and utilize one of major progress obtained in process, this method does not need to add any chemical substance, does not need to use any catalyzer yet, therefore very clean, the environmental protection of production process, with acid-alkali treatment before explosion, increase porosity, better can reach the effect of modified fibre, gained fiber and all the other raw materials well composite, the viscosity of viscose glue can also be increased while consistency is high.
(3) the present invention has significant sound insulaton effect, forever keeps visco-elasticity, and sound insulation was never lost efficacy really, was applicable to the sound insulating seal in almost any gap, used very simple; Without organism volatilization, odorlessness; Environmental friendliness, not containing any toxic substance; Very economical Noise abatement scheme.。
Embodiment
A corrosion-resistant sound insulation sizing agent containing silica powder, is obtained by the raw material of following weight parts:
ACRYLIC EMULSION 22,40 degree Beaume water glass 10, silica powder 5, silane coupling agent KH5302, turkey red oil 1, clorafin 1, alkylphenol polyoxyethylene 1, tertiary ethylene carbonate 2, urethane 1.2, water-based terpine resin 10, modified composite fiber 3;
Described modified composite fiber is obtained by the raw material of following weight parts:
Ramee 3, stalk 1, pomelo peel 4, coir 3, cotton 1;
The preparation method of described modified composite fiber is:
(1) by pomelo peel, stalk, coir chopping, be soak 1 hour in the hydrochloric acid soln of 3% in concentration, take out, deionized water wash, dries to obtain pickling raw material;
(2) by all the other raw materials in concentration be 4% sodium hydroxide solution in soak 3 hours, take out, deionized water wash, dries to obtain alkali cleaning raw material;
(3) by pickling raw material, alkali cleaning raw material blending, boil 4 minutes, then carry out steam explosion treatment at 70 DEG C of Water Unders, the pressure of described Steam explosion treatment is 0.9MPa, and the Steam explosion treatment time is 5 minutes, to obtain final product.
Described a kind of corrosion-resistant sound insulation sizing agent containing silica powder,
Preparation method's step is as follows:
(1) add tertiary ethylene carbonate, urethane, water-based terpine resin and suitable quantity of water in a kettle. to stir;
(2) be heated to 40 DEG C and add ACRYLIC EMULSION, 40 degree Beaume water glass, silica powder, silane coupling agent KH, add rear insulation 1 hour;
(3) after having reacted, be cooled to 20 DEG C, add all the other raw materials and suitable quantity of water mixing, stir, to obtain final product.
The present embodiment can form the damping platform that the temperature range of a damping value more than 0.9 reaches more than 100 DEG C, T-stripping strength > 38N/cm, can play sound insulation, bonding dual function.
The plasterboard A not carrying out joint filling sound insulation process is carried out sound insulation contrast with the present embodiment as the plasterboard B of spackling, and plasterboard B more can sound insulation than plasterboard A, noise minimizing 5-7 decibel.
Claims (2)
1. the corrosion-resistant sound insulation sizing agent containing silica powder, is characterized in that, obtained by the raw material of following weight parts:
ACRYLIC EMULSION 22-25,40 degree Beaume water glass 10-15, silica powder 5-7, silane coupling agent KH-5302-4, turkey red oil 1-3, clorafin 1-2, alkylphenol polyoxyethylene 1-2, tertiary ethylene carbonate 2-4, urethane 1.2-2.7, water-based terpine resin 10-20, modified composite fiber 3-5;
Described modified composite fiber is obtained by the raw material of following weight parts:
Ramee 3-5, stalk 1-3, pomelo peel 4-6, coir 3-5, cotton 1-2;
The preparation method of described modified composite fiber is:
(1) by pomelo peel, stalk, coir chopping, be soak 1-3 hour in the hydrochloric acid soln of 3-5% in concentration, take out, deionized water wash, dries to obtain pickling raw material;
(2) by all the other raw materials in concentration be 4-5% sodium hydroxide solution in soak 3-5 hour, take out, deionized water wash, dries to obtain alkali cleaning raw material;
(3) by pickling raw material, alkali cleaning raw material blending, boil 4-8 minute, then carry out steam explosion treatment at 70-80 DEG C of Water Under, the pressure of described Steam explosion treatment is 0.9-1.5MPa, and the Steam explosion treatment time is 5-10 minute, to obtain final product.
2. a kind of corrosion-resistant sound insulation sizing agent containing silica powder according to claim 1, is characterized in that,
Preparation method's step is as follows:
(1) add tertiary ethylene carbonate, urethane, water-based terpine resin and suitable quantity of water in a kettle. to stir;
(2) be heated to 40-50 DEG C and add ACRYLIC EMULSION, 40 degree Beaume water glass, silica powder, silane coupling agent KH-530, add rear insulation 1-3 hour;
(3) after having reacted, be cooled to 20-35 DEG C, add all the other raw materials and suitable quantity of water mixing, stir, to obtain final product.