CN105238271A - Smoke-suppression non-cured rubber bitumen waterproof coating material - Google Patents
Smoke-suppression non-cured rubber bitumen waterproof coating material Download PDFInfo
- Publication number
- CN105238271A CN105238271A CN201510622377.5A CN201510622377A CN105238271A CN 105238271 A CN105238271 A CN 105238271A CN 201510622377 A CN201510622377 A CN 201510622377A CN 105238271 A CN105238271 A CN 105238271A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof coating
- styrene
- cigarette
- asphalt waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a smoke-suppression non-cured rubber bitumen waterproof coating material, wherein the raw materials comprise, by weight, 20-28 parts of bitumen, 3-7 parts of a styrene-butadiene-styrene block copolymer, 2.5-3.5 parts of styrene butadiene rubber, 15-20 parts of paraffin oil, 1-3 parts of solvent oil, 5-15 parts of recycled rubber powder, 20-25 parts of heavy calcium carbonate, 3-7 parts of asbestos wool, 4-8 parts of fly ash, 3-6 parts of a terpene resin, 0.5-2 parts of an epoxy resin, 1-3 parts of epoxy soybean oil, 0.5-1.5 parts of an antioxidant 1076, 0.1-0.3 part of a light stabilizer 292, 0.3-0.5 part of 2,4-dihydroxydiphenyl benzophenone, 0.5-1 part of ABS-g-MAH, 0.3-0.7 parts of dicumyl peroxide, 0.3-0.5 part of vinyltriethoxysilane, 4-6 parts of microencapsulated red phosphorus, 1-2 parts of a modified smoke suppressant, and 0.5-1 part of a C9 petroleum resin. The smoke-suppression non-cured rubber bitumen waterproof coating material of the present invention has characteristics of good smoke suppression performance and good water resistance.
Description
Technical field
The present invention relates to waterproof paint technical field, particularly relate to one and press down the uncured rubber asphalt waterproof coating of cigarette.
Background technology
Uncured rubber asphalt waterproof coating solve cause to waterproof layer because of base course crack Stress transmit waterproof layer fracture, disturb bent fatigure failure or make waterproof layer be in high-stress state and the problems such as premature aging; Meanwhile, due to the glutinousness of this coating, pore and the crack of basic unit well can be closed, complicated operation side can be adapted to, and automatically can look for leakage area, repair the waterproof layer that damaged, solve a channeling water difficult problem for waterproof layer, waterproof reliability is greatly improved.
But uncured rubber asphalt waterproof coating needs to carry out high temperature melt before construction, in the process of high temperature melt, uncured rubber asphalt waterproof coating can discharge a large amount of smog.Containing material harmful in a large number in these smog, affect people healthy, destroy surrounding enviroment.
Summary of the invention
Based on the technical problem that background technology exists, the present invention proposes and a kind of press down the uncured rubber asphalt waterproof coating of cigarette, flame-proof smoke-suppressing of the present invention is good, and snappiness is good, high temperature resistant, low-temperature performance good, and mechanical property is high, good waterproof performance.
The one that the present invention proposes presses down the uncured rubber asphalt waterproof coating of cigarette, its raw material comprises by weight: pitch 20-28 part, styrene-butadiene-styrene block copolymer 3-7 part, styrene-butadiene rubber(SBR) 2.5-3.5 part, paraffin oil 15-20 part, solvent oil 1-3 part, ground rubber 5-15 part, water-ground limestone 20-25 part, asbestos wool 3-7 part, flyash 4-8 part, terpine resin 3-6 part, epoxy resin 0.5-2 part, epoxy soybean oil 1-3 part, antioxidant 1076 0.5-1.5 part, photostabilizer 2920.1-0.3 part, 2, 4-dihydroxy benaophenonel 0.3-0.5 part, ABS-g-MAH0.5-1 part, dicumyl peroxide 0.3-0.7 part, vinyltriethoxysilane 0.3-0.5 part, microencapsulated powder oil 4-6 part, modification smoke suppressant 1-2 part, C9 petroleum resin 0.5-1 part.
Preferably, pitch is the one in No. 10 building asphalts or No. 100 road bitumens.
Preferably, in styrene-butadiene-styrene block copolymer, the inlay character of vinylbenzene and divinyl is 30-40:60-70.
Preferably, solvent oil is No. 200 solvent oils.
Preferably, ground rubber is 60-90 order.
Preferably, water-ground limestone is 200-300 order, and asbestos wool is 100-150 order, and flyash is 150-200 order.
Preferably, the preparation method of modification smoke suppressant is: joined by expansible black lead in ethanol, be warming up to 50-60 DEG C, ultrasonic disperse is even, add the ethanolic soln that massfraction is sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester of 10-15wt%, insulation 1-2h, adds ammonium octamolybdate, be warming up to 60-70 DEG C, ultrasonic disperse is even, and insulation 1-2h, adds Calcium Phosphomolybdate, be warming up to 70-80 DEG C, ultrasonic disperse is even, and insulation 1-2h, is cooled to room temperature, soak 3-5h, drying under reduced pressure obtains modification smoke suppressant.
Preferably, in the preparation method of modification smoke suppressant, the weight ratio of ammonium octamolybdate, Calcium Phosphomolybdate, expansible black lead, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is 15-20:5-10:70-80:1.5-1.8.
Preferably, in the preparation method of modification smoke suppressant, ammonium octamolybdate, Calcium Phosphomolybdate and expansible black lead are 800-1000 order.
Preferably, its raw material comprises by weight: pitch 22-26 part, styrene-butadiene-styrene block copolymer 4-6 part, styrene-butadiene rubber(SBR) 2.8-3.2 part, paraffin oil 17-19 part, solvent oil 1.5-2.5 part, ground rubber 8-12 part, water-ground limestone 22-24 part, asbestos wool 4-6 part, flyash 5-7 part, terpine resin 4-5 part, epoxy resin 1-1.5 part, epoxy soybean oil 1.5-2.5 part, antioxidant 1076 0.7-1.3 part, photostabilizer 2920.15-0.25 part, 2, 4-dihydroxy benaophenonel 0.35-0.45 part, ABS-g-MAH0.7-0.9 part, dicumyl peroxide 0.4-0.6 part, vinyltriethoxysilane 0.35-0.45 part, microencapsulated powder oil 4.5-5.5 part, modification smoke suppressant 1.3-1.7 part, C9 petroleum resin 0.6-0.8 part.
In the preparation method of above-mentioned modification smoke suppressant, the effect of ethanol is dispersion expansible black lead, does not specify its consumption.
Preparation method of the present invention is as follows: by paraffin oil and solvent oil mixing, be warming up to 185 DEG C, add styrene-butadiene-styrene block copolymer and styrene-butadiene rubber(SBR), with the speed insulated and stirred 2h of 800r/min, add pitch, ground rubber, terpine resin, epoxy resin, modification smoke suppressant, C9 petroleum resin, with the speed insulated and stirred 2h of 800r/min, add water-ground limestone, asbestos wool, flyash, epoxy soybean oil, antioxidant 1076, photostabilizer 292, 2, 4-dihydroxy benaophenonel, ABS-g-MAH, dicumyl peroxide, vinyltriethoxysilane, microencapsulated powder oil, obtain pressing down the uncured rubber asphalt waterproof coating of cigarette with the speed insulated and stirred 1h of 800r/min.
When the expansible black lead that the present invention selects is heated, the compound of graphite carbon interlayer will decompose, and laterally produces huge bulging force, make expansible black lead undergoes rapid expansion along graphite linings, form density very low, the vermiform expanded graphite that volume is very large, defines thermal insulation layer, isolated thermal source, and this expanded graphite has abundant pore structure, there is excellent absorption property, a large amount of smog can be adsorbed, thus considerably increase smoke-suppressing of the present invention and flame retardant resistance; Ammonium octamolybdate, Calcium Phosphomolybdate also can increase smoke-suppressing of the present invention and flame retardant resistance; Expansible black lead, ammonium octamolybdate, Calcium Phosphomolybdate act synergistically, and considerably increase smoke-suppressing of the present invention; By sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester, modification smoke suppressant is obtained to expansible black lead, ammonium octamolybdate, Calcium Phosphomolybdate modification, add the lipophilicity of expansible black lead, ammonium octamolybdate, Calcium Phosphomolybdate, expansible black lead, ammonium octamolybdate, Calcium Phosphomolybdate are dispersed in pitch uniformly, thus further increase smoke-suppressing of the present invention, and snappiness of the present invention can be increased; Styrene-butadiene-styrene block copolymer, styrene-butadiene rubber(SBR) are by constraint, crosslinked action, and the light constituent in fixing pitch, stops departing from from pitch of light constituent, thus enter an increase smoke-suppressing of the present invention; Pitch can be adsorbed in the space net structure of styrene-butadiene-styrene block copolymer, styrene-butadiene rubber(SBR), and effect between asphaltene molecule is strengthened, and force of cohesion improves, thus considerably increases tensile strength of the present invention, high and low temperature resistance, water resistance; Suitable vinylbenzene and the inlay character of divinyl and suitable pitch kind, can increase the consistency of pitch, styrene-butadiene-styrene block copolymer and styrene-butadiene rubber(SBR), thus enter one and increase mechanical property of the present invention and water resistance; Styrene-butadiene rubber(SBR) can improve resistance to low temperature of the present invention and creep property; Ground rubber can significantly increase elasticity of the present invention, ageing-resistant performance; ABS-g-MAH can increase pitch, styrene-butadiene-styrene block copolymer, consistency between styrene-butadiene rubber(SBR) and ground rubber, under the crosslinked action of dicumyl peroxide and vinyltriethoxysilane, greatly increase mechanical property and the water resistancees such as snappiness of the present invention, tension, resistance to compression; Vinyltriethoxysilane can also increase the consistency of organic substance and inorganic substance, increases mechanical property of the present invention; Water-ground limestone, asbestos wool, flyash can reduce the consumption of pitch, increase high and low temperature resistance of the present invention; Terpine resin, epoxy resin can increase the cohesive strength between the present invention and adherend; Antioxidant 1076, photostabilizer 292,2,4 dihydroxyl benzophenone interact increases stability of the present invention; Paraffin oil, solvent oil can make each material be uniformly dispersed, and epoxy soybean oil can increase snappiness of the present invention; Microencapsulated powder oil, modification smoke suppressant, C9 petroleum resin interact increases flame-retardant smoke inhibition effect of the present invention.
Embodiment
Below, by specific embodiment, technical scheme of the present invention is described in detail.
Embodiment 1
One presses down the uncured rubber asphalt waterproof coating of cigarette, its raw material comprises by weight: No. 10 building asphalts 28 parts, the inlay character of vinylbenzene and divinyl is the styrene-butadiene-styrene block copolymer 3 parts of 30:70, 3.5 parts, styrene-butadiene rubber(SBR), paraffin oil 15 parts, No. 200 solvent oils 3 parts, 60 order ground rubbers 15 parts, 200 order water-ground limestones 25 parts, 100 order asbestos wools 7 parts, 150 8 parts, order flyash, terpine resin 3 parts, epoxy resin 2 parts, epoxy soybean oil 1 part, antioxidant 1076 1.5 parts, photostabilizer 2920.1 parts, 2, 4-dihydroxy benaophenonel 0.5 part, ABS-g-MAH0.5 part, dicumyl peroxide 0.7 part, vinyltriethoxysilane 0.3 part, microencapsulated powder oil 6 parts, modification smoke suppressant 1 part, C9 petroleum resin 1 part,
Wherein, the preparation method of modification smoke suppressant is: join in ethanol by 800 order expansible black leads, be warming up to 60 DEG C, ultrasonic disperse is even, add the ethanolic soln that massfraction is sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester of 10wt%, insulation 2h, add 800 order ammonium octamolybdates, be warming up to 70 DEG C, ultrasonic disperse is even, insulation 1h, add 1000 order Calcium Phosphomolybdates, be warming up to 70 DEG C, ultrasonic disperse is even, insulation 2h, be cooled to room temperature, soak 3h, drying under reduced pressure obtains modification smoke suppressant, wherein, ammonium octamolybdate, Calcium Phosphomolybdate, expansible black lead, the weight ratio of sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is 20:5:80:1.5.
Embodiment 2
One presses down the uncured rubber asphalt waterproof coating of cigarette, its raw material comprises by weight: No. 100 road bitumens 20 parts, the inlay character of vinylbenzene and divinyl is the styrene-butadiene-styrene block copolymer 7 parts of 40:60, 2.5 parts, styrene-butadiene rubber(SBR), paraffin oil 20 parts, No. 200 solvent oils 1 part, 90 order ground rubbers 5 parts, 300 order water-ground limestones 20 parts, 150 order asbestos wools 3 parts, 200 4 parts, order flyash, terpine resin 6 parts, epoxy resin 0.5 part, epoxy soybean oil 3 parts, antioxidant 1076 0.5 part, photostabilizer 2920.3 parts, 2, 4-dihydroxy benaophenonel 0.3 part, ABS-g-MAH1 part, dicumyl peroxide 0.3 part, vinyltriethoxysilane 0.5 part, microencapsulated powder oil 4 parts, modification smoke suppressant 2 parts, C9 petroleum resin 0.5 part,
Wherein, the preparation method of modification smoke suppressant is: join in ethanol by 1000 order expansible black leads, be warming up to 50 DEG C, ultrasonic disperse is even, add the ethanolic soln that massfraction is sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester of 15wt%, insulation 1h, add 1000 order ammonium octamolybdates, be warming up to 60 DEG C, ultrasonic disperse is even, insulation 2h, add 800 order Calcium Phosphomolybdates, be warming up to 80 DEG C, ultrasonic disperse is even, insulation 1h, be cooled to room temperature, soak 5h, drying under reduced pressure obtains modification smoke suppressant, wherein, ammonium octamolybdate, Calcium Phosphomolybdate, expansible black lead, the weight ratio of sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is 15:10:70:1.8.
Embodiment 3
One presses down the uncured rubber asphalt waterproof coating of cigarette, its raw material comprises by weight: No. 10 building asphalts 26 parts, the inlay character of vinylbenzene and divinyl is the styrene-butadiene-styrene block copolymer 4 parts of 30:70, 3.2 parts, styrene-butadiene rubber(SBR), paraffin oil 17 parts, No. 200 solvent oils 2.5 parts, 65 order ground rubbers 12 parts, 230 order water-ground limestones 24 parts, 120 order asbestos wools 6 parts, 160 7 parts, order flyash, terpine resin 4 parts, epoxy resin 1.5 parts, epoxy soybean oil 1.5 parts, antioxidant 1076 1.3 parts, photostabilizer 2920.15 parts, 2, 4-dihydroxy benaophenonel 0.45 part, ABS-g-MAH0.7 part, dicumyl peroxide 0.6 part, vinyltriethoxysilane 0.35 part, microencapsulated powder oil 5.5 parts, modification smoke suppressant 1.3 parts, C9 petroleum resin 0.8 part,
Wherein, the preparation method of modification smoke suppressant is: join in ethanol by 800 order expansible black leads, be warming up to 58 DEG C, ultrasonic disperse is even, add the ethanolic soln that massfraction is sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester of 12wt%, insulation 1.7h, add 800 order ammonium octamolybdates, be warming up to 67 DEG C, ultrasonic disperse is even, insulation 1.2h, add 1000 order Calcium Phosphomolybdates, be warming up to 73 DEG C, ultrasonic disperse is even, insulation 1.7h, be cooled to room temperature, soak 3.5h, drying under reduced pressure obtains modification smoke suppressant, wherein, ammonium octamolybdate, Calcium Phosphomolybdate, expansible black lead, the weight ratio of sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is 18:6:77:1.6.
Embodiment 4
One presses down the uncured rubber asphalt waterproof coating of cigarette, its raw material comprises by weight: No. 100 road bitumens 22 parts, the inlay character of vinylbenzene and divinyl is the styrene-butadiene-styrene block copolymer 6 parts of 40:60, 2.8 parts, styrene-butadiene rubber(SBR), paraffin oil 19 parts, No. 200 solvent oils 1.5 parts, 80 order ground rubbers 8 parts, 270 order water-ground limestones 22 parts, 140 order asbestos wools 4 parts, 180 5 parts, order flyash, terpine resin 5 parts, epoxy resin 1 part, epoxy soybean oil 2.5 parts, antioxidant 1076 0.7 part, photostabilizer 2920.25 parts, 2, 4-dihydroxy benaophenonel 0.35 part, ABS-g-MAH0.9 part, dicumyl peroxide 0.4 part, vinyltriethoxysilane 0.45 part, microencapsulated powder oil 4.5 parts, modification smoke suppressant 1.7 parts, C9 petroleum resin 0.6 part,
Wherein, the preparation method of modification smoke suppressant is: join in ethanol by 1000 order expansible black leads, be warming up to 52 DEG C, ultrasonic disperse is even, add the ethanolic soln that massfraction is sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester of 14wt%, insulation 1.3h, add 1000 order ammonium octamolybdates, be warming up to 63 DEG C, ultrasonic disperse is even, insulation 1.8h, add 800 order Calcium Phosphomolybdates, be warming up to 77 DEG C, ultrasonic disperse is even, insulation 1.3h, be cooled to room temperature, soak 4.5h, drying under reduced pressure obtains modification smoke suppressant, wherein, ammonium octamolybdate, Calcium Phosphomolybdate, expansible black lead, the weight ratio of sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is 16:8:73:1.7.
Embodiment 5
One presses down the uncured rubber asphalt waterproof coating of cigarette, its raw material comprises by weight: No. 10 building asphalts 24 parts, the inlay character of vinylbenzene and divinyl is the styrene-butadiene-styrene block copolymer 5 parts of 30:70, 3 parts, styrene-butadiene rubber(SBR), paraffin oil 18 parts, No. 200 solvent oils 2 parts, 70 order ground rubbers 10 parts, 250 order water-ground limestones 23 parts, 130 order asbestos wools 5 parts, 170 6 parts, order flyash, terpine resin 4.5 parts, epoxy resin 1.3 parts, epoxy soybean oil 2 parts, antioxidant 1076 1 part, photostabilizer 2920.2 parts, 2, 4-dihydroxy benaophenonel 0.4 part, ABS-g-MAH0.8 part, dicumyl peroxide 0.5 part, vinyltriethoxysilane 0.4 part, microencapsulated powder oil 5 parts, modification smoke suppressant 1.5 parts, C9 petroleum resin 0.7 part,
Wherein, the preparation method of modification smoke suppressant is: join in ethanol by 1000 order expansible black leads, be warming up to 55 DEG C, ultrasonic disperse is even, add the ethanolic soln that massfraction is sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester of 13wt%, insulation 1.5h, add 1000 order ammonium octamolybdates, be warming up to 65 DEG C, ultrasonic disperse is even, insulation 1.5h, add 1000 order Calcium Phosphomolybdates, be warming up to 75 DEG C, ultrasonic disperse is even, insulation 1.5h, be cooled to room temperature, soak 4h, drying under reduced pressure obtains modification smoke suppressant, wherein, ammonium octamolybdate, Calcium Phosphomolybdate, expansible black lead, the weight ratio of sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is 17:7:75:1.65.
Performance test is carried out to embodiment 1-5, with existing uncured rubber asphalt waterproof coating for control group, wherein, according to the method test flue gas toxity grade in the People's Republic of China (PRC) " classification of material producing smoke toxicity risk " (GB/T20285-2006), according to the method test smoke density grade in the People's Republic of China (PRC) " material of construction burning or the smoke density test method of decomposing " (GB/T8627-2007), its result is as shown in the table:
Smoke suppressing effect of the present invention is good as can be seen from the above table, and snappiness is good, high temperature resistant, low-temperature performance good, and water resistance is good.
The above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (10)
1. one kind is pressed down the uncured rubber asphalt waterproof coating of cigarette, it is characterized in that, its raw material comprises by weight: pitch 20-28 part, styrene-butadiene-styrene block copolymer 3-7 part, styrene-butadiene rubber(SBR) 2.5-3.5 part, paraffin oil 15-20 part, solvent oil 1-3 part, ground rubber 5-15 part, water-ground limestone 20-25 part, asbestos wool 3-7 part, flyash 4-8 part, terpine resin 3-6 part, epoxy resin 0.5-2 part, epoxy soybean oil 1-3 part, antioxidant 1076 0.5-1.5 part, photostabilizer 2920.1-0.3 part, 2, 4-dihydroxy benaophenonel 0.3-0.5 part, ABS-g-MAH0.5-1 part, dicumyl peroxide 0.3-0.7 part, vinyltriethoxysilane 0.3-0.5 part, microencapsulated powder oil 4-6 part, modification smoke suppressant 1-2 part, C9 petroleum resin 0.5-1 part.
2. press down the uncured rubber asphalt waterproof coating of cigarette according to claim 1, it is characterized in that, pitch is the one in No. 10 building asphalts or No. 100 road bitumens.
3. according to claim 1 or 2, press down the uncured rubber asphalt waterproof coating of cigarette, it is characterized in that, in styrene-butadiene-styrene block copolymer, the inlay character of vinylbenzene and divinyl is 30-40:60-70.
4. according to any one of claim 1-3, press down the uncured rubber asphalt waterproof coating of cigarette, it is characterized in that, solvent oil is No. 200 solvent oils.
5. according to any one of claim 1-4, press down the uncured rubber asphalt waterproof coating of cigarette, it is characterized in that, ground rubber is 60-90 order.
6. according to any one of claim 1-5, press down the uncured rubber asphalt waterproof coating of cigarette, it is characterized in that, water-ground limestone is 200-300 order, and asbestos wool is 100-150 order, and flyash is 150-200 order.
7. according to any one of claim 1-6, press down the uncured rubber asphalt waterproof coating of cigarette, it is characterized in that, the preparation method of modification smoke suppressant is: joined by expansible black lead in ethanol, be warming up to 50-60 DEG C, ultrasonic disperse is even, add the ethanolic soln that massfraction is sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester of 10-15wt%, insulation 1-2h, add ammonium octamolybdate, be warming up to 60-70 DEG C, ultrasonic disperse is even, insulation 1-2h, add Calcium Phosphomolybdate, be warming up to 70-80 DEG C, ultrasonic disperse is even, insulation 1-2h, be cooled to room temperature, soak 3-5h, drying under reduced pressure obtains modification smoke suppressant.
8. according to any one of claim 1-7, press down the uncured rubber asphalt waterproof coating of cigarette, it is characterized in that, in the preparation method of modification smoke suppressant, the weight ratio of ammonium octamolybdate, Calcium Phosphomolybdate, expansible black lead, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is 15-20:5-10:70-80:1.5-1.8.
9. according to any one of claim 1-8, press down the uncured rubber asphalt waterproof coating of cigarette, it is characterized in that, in the preparation method of modification smoke suppressant, ammonium octamolybdate, Calcium Phosphomolybdate and expansible black lead are 800-1000 order.
10. according to any one of claim 1-9, press down the uncured rubber asphalt waterproof coating of cigarette, it is characterized in that, its raw material comprises by weight: pitch 22-26 part, styrene-butadiene-styrene block copolymer 4-6 part, styrene-butadiene rubber(SBR) 2.8-3.2 part, paraffin oil 17-19 part, solvent oil 1.5-2.5 part, ground rubber 8-12 part, water-ground limestone 22-24 part, asbestos wool 4-6 part, flyash 5-7 part, terpine resin 4-5 part, epoxy resin 1-1.5 part, epoxy soybean oil 1.5-2.5 part, antioxidant 1076 0.7-1.3 part, photostabilizer 2920.15-0.25 part, 2, 4-dihydroxy benaophenonel 0.35-0.45 part, ABS-g-MAH0.7-0.9 part, dicumyl peroxide 0.4-0.6 part, vinyltriethoxysilane 0.35-0.45 part, microencapsulated powder oil 4.5-5.5 part, modification smoke suppressant 1.3-1.7 part, C9 petroleum resin 0.6-0.8 part.