CN105238194A - 一种无异味的耐低温阻尼隔音胶黏剂 - Google Patents
一种无异味的耐低温阻尼隔音胶黏剂 Download PDFInfo
- Publication number
- CN105238194A CN105238194A CN201510633038.7A CN201510633038A CN105238194A CN 105238194 A CN105238194 A CN 105238194A CN 201510633038 A CN201510633038 A CN 201510633038A CN 105238194 A CN105238194 A CN 105238194A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- latex
- styrene
- composite fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种无异味的耐低温阻尼隔音胶黏剂,由下述重量份的原料制得:脂肪醇聚氧乙烯醚1-2、乳液型丙烯酸酯压敏胶粘剂8-13、玻璃粉2-4、邻苯二甲酸二丁酯0.3-0.5、烷基糖苷1-2、酚醛树脂3.5-5、纯丙烯酸乳液8-10、木薯淀粉1-4、丁苯胶乳2-4、天然胶乳1-2、阿拉伯树胶3-5、改性复合纤维1-2、硅酸钠0.1-0.3;本发明添加玻璃粉,有效增加本发明的耐低温抗冻效果;木薯淀粉、丁苯胶乳、天然胶乳、阿拉伯树胶等天然胶体材料的使用,无毒环保,有益于人体健康,同时复配合理,乳化完全,相容性好,不易结块。
Description
技术领域
本发明涉及胶黏剂技术领域,尤其涉及一种无异味的耐低温阻尼隔音胶黏剂。
背景技术
建筑隔声,是指随着现代城市的发展,噪声源的增加,建筑物的密集,高强度轻质材料的使用,对建筑物进行有效的隔声防护措施。建筑隔声除了要考虑建筑物内人们活动所引起的声音干扰外,还要考虑建筑物外交通运输、工商业活动等噪声传入所造成的干扰。
建筑墙体、石膏板、混凝土等的缝隙,如果不用隔声密封剂填堵,都会成为噪音传播的有效通道,大幅度降低工程原本可以取得的隔音效果,利用特制的隔音胶对缝隙进行处理,可以成百倍地降低噪音通过缝隙的传播,该隔音胶可以直接使用在几乎任何清洁的物体上,包括石膏板、水泥板、硅酸钙板、混凝土、砖和金属等。
天然纤维材料具有吸潮、隔音、减震、降噪、耐冲击性高、手感好等特点,在室内装饰等领域具有和其他材料(如玻璃钢)无可比拟的优点,其是一种新型的优良环保型材料。天然纤维制品废弃后可以自然降解,因此天然纤维废料对环境的影响较小。
阿拉伯胶也称为阿拉伯树胶,来源于豆科的金合欢树属的树干渗出物,因此也称金合欢胶。阿拉伯胶主要成分为高分子多糖类及其钙、镁和钾盐。主要包括有树胶醛糖、半乳糖、葡萄糖醛酸等。品质良好的阿拉伯胶颜色呈琥珀色,且颗粒大而圆,主要产于非洲.目前也有经过精制过程而得的粉末状阿拉伯胶,使用上更为方便。。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种无异味的耐低温阻尼隔音胶黏剂。
本发明是通过以下技术方案实现的:
一种无异味的耐低温阻尼隔音胶黏剂,由下述重量份的原料制得:
脂肪醇聚氧乙烯醚1-2、乳液型丙烯酸酯压敏胶粘剂8-13、玻璃粉2-4、邻苯二甲酸二丁酯0.3-0.5、烷基糖苷1-2、酚醛树脂3.5-5、纯丙烯酸乳液8-10、木薯淀粉1-4、丁苯胶乳2-4、天然胶乳1-2、阿拉伯树胶3-5、改性复合纤维1-2、硅酸钠0.1-0.3;
所述的改性复合纤维由下述重量份的原料制得:
苎麻纤维3-5、秸秆1-3、柚子皮4-6、椰子壳纤维3-5、棉花1-2;
所述的改性复合纤维的制备方法为:
(1)将柚子皮、秸秆、椰子壳纤维切碎,在浓度为3-5%的盐酸溶液中浸泡1-3小时,取出,去离子水洗涤,烘干得酸洗原料;
(2)将其余原料在浓度为4-5%的氢氧化钠溶液中浸泡3-5小时,取出,去离子水洗涤,烘干得碱洗原料;
(3)将酸洗原料、碱洗原料混匀,在70-80℃条件下水煮4-8分钟,再进行蒸气爆破处理,所述蒸汽爆破处理的压力为0.9-1.5MPa,蒸汽爆破处理时间为5-10分钟,即得。
所述的一种抗无异味的耐低温阻尼隔音胶黏剂,
制备方法步骤如下:
(1)在反应釜中加入脂肪醇聚氧乙烯醚、乳液型丙烯酸酯压敏胶粘剂、邻苯二甲酸二丁酯、烷基糖苷、酚醛树脂、纯丙烯酸乳液,以及适量水搅拌均匀;
(2)加热至50-60℃加入木薯淀粉、丁苯胶乳、天然胶乳、阿拉伯树胶加完后保温1-3小时;
(3)反应完成后,降温至室温,加入其余原料以及适量水混匀,搅拌均匀,即得。
本发明的优点是:(1)本发明添加玻璃粉,有效增加本发明的耐低温抗冻效果;木薯淀粉、丁苯胶乳、天然胶乳、阿拉伯树胶等天然胶体材料的使用,无毒环保,有益于人体健康,同时复配合理,乳化完全,相容性好,不易结块;
(2)利用蒸汽爆破处理复配天然纤维,蒸汽爆破作为一项新技术,被认为是生物再生利用过程中取得的重大进展之一,该法不需要添加任何化学物质,也不需要使用任何催化剂,因此生产过程十分洁净、环保,在爆破前用酸碱处理,增加孔隙度,能够更好的达到改性纤维的效果,所得纤维与其余原料复配良好,相容性高的同时还能增加粘胶的粘度。
(3)本发明具有显著的密封隔音效果,永远保持粘弹性,隔音永不失效果,适用于几乎任何缝隙的隔音密封,使用非常简单;无有机物挥发、无气味;环境友好、不含任何有毒物质;非常经济的噪音治理方案。。
具体实施方式
一种无异味的耐低温阻尼隔音胶黏剂,由下述重量份的原料制得:
脂肪醇聚氧乙烯醚1、乳液型丙烯酸酯压敏胶粘剂8、玻璃粉2、邻苯二甲酸二丁酯0.3、烷基糖苷1、酚醛树脂3.5、纯丙烯酸乳液8、木薯淀粉1、丁苯胶乳2、天然胶乳1、阿拉伯树胶3、改性复合纤维1、硅酸钠0.1;
所述的改性复合纤维由下述重量份的原料制得:
苎麻纤维3、秸秆1、柚子皮4、椰子壳纤维3、棉花1;
所述的改性复合纤维的制备方法为:
(1)将柚子皮、秸秆、椰子壳纤维切碎,在浓度为3%的盐酸溶液中浸泡1小时,取出,去离子水洗涤,烘干得酸洗原料;
(2)将其余原料在浓度为4%的氢氧化钠溶液中浸泡3小时,取出,去离子水洗涤,烘干得碱洗原料;
(3)将酸洗原料、碱洗原料混匀,在70℃条件下水煮4分钟,再进行蒸气爆破处理,所述蒸汽爆破处理的压力为0.9MPa,蒸汽爆破处理时间为5分钟,即得。
所述的一种抗无异味的耐低温阻尼隔音胶黏剂,
制备方法步骤如下:
(1)在反应釜中加入脂肪醇聚氧乙烯醚、乳液型丙烯酸酯压敏胶粘剂、邻苯二甲酸二丁酯、烷基糖苷、酚醛树脂、纯丙烯酸乳液,以及适量水搅拌均匀;
(2)加热至50℃加入木薯淀粉、丁苯胶乳、天然胶乳、阿拉伯树胶加完后保温1小时;
(3)反应完成后,降温至室温,加入其余原料以及适量水混匀,搅拌均匀,即得。
本实施例可以形成一个阻尼值在0.8以上的温域达100℃以上的阻尼平台,T-剥离强度>33N/cm,能起到隔音、粘结双重作用。
将没有进行填缝隔音处理的石膏板A与用本实施例作为填缝剂的石膏板B进行隔音对比,石膏板B比石膏板A更能够隔音,噪音减少4-6分贝。
Claims (2)
1.一种无异味的耐低温阻尼隔音胶黏剂,其特征在于,由下述重量份的原料制得:
脂肪醇聚氧乙烯醚1-2、乳液型丙烯酸酯压敏胶粘剂8-13、玻璃粉2-4、邻苯二甲酸二丁酯0.3-0.5、烷基糖苷1-2、酚醛树脂3.5-5、纯丙烯酸乳液8-10、木薯淀粉1-4、丁苯胶乳2-4、天然胶乳1-2、阿拉伯树胶3-5、改性复合纤维1-2、硅酸钠0.1-0.3;
所述的改性复合纤维由下述重量份的原料制得:
苎麻纤维3-5、秸秆1-3、柚子皮4-6、椰子壳纤维3-5、棉花1-2;
所述的改性复合纤维的制备方法为:
(1)将柚子皮、秸秆、椰子壳纤维切碎,在浓度为3-5%的盐酸溶液中浸泡1-3小时,取出,去离子水洗涤,烘干得酸洗原料;
(2)将其余原料在浓度为4-5%的氢氧化钠溶液中浸泡3-5小时,取出,去离子水洗涤,烘干得碱洗原料;
(3)将酸洗原料、碱洗原料混匀,在70-80℃条件下水煮4-8分钟,再进行蒸气爆破处理,所述蒸汽爆破处理的压力为0.9-1.5MPa,蒸汽爆破处理时间为5-10分钟,即得。
2.根据权利要求1所述的一种抗无异味的耐低温阻尼隔音胶黏剂,其特征在于,
制备方法步骤如下:
(1)在反应釜中加入脂肪醇聚氧乙烯醚、乳液型丙烯酸酯压敏胶粘剂、邻苯二甲酸二丁酯、烷基糖苷、酚醛树脂、纯丙烯酸乳液,以及适量水搅拌均匀;
(2)加热至50-60℃加入木薯淀粉、丁苯胶乳、天然胶乳、阿拉伯树胶加完后保温1-3小时;
(3)反应完成后,降温至室温,加入其余原料以及适量水混匀,搅拌均匀,即得。