CN105238079A - 一种纳米电气工程用绝缘材料 - Google Patents
一种纳米电气工程用绝缘材料 Download PDFInfo
- Publication number
- CN105238079A CN105238079A CN201510768925.5A CN201510768925A CN105238079A CN 105238079 A CN105238079 A CN 105238079A CN 201510768925 A CN201510768925 A CN 201510768925A CN 105238079 A CN105238079 A CN 105238079A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulating material
- earth
- rare
- compound rare
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种纳米电气工程用绝缘材料，包括以下材料：松香改性马来酸树10-20份，聚乙二醇二甲基丙烯酸酯8-20份，聚甲基丙烯酸羟乙酯5-9份，二甘醇二苯甲酸酯3-10份，纳米氮化铝4-6份，铝酸酯偶联剂DL-411-A？2-6份，复合稀土1-5份，粘合剂2-6份，煅烧云母10-18份，陶土9-16，本发明采用电气工程绝缘材料具有较高的拉伸强度和弯曲强度，并且还有较高的体积电阻，具备了较高的拉伸强度和弯曲强度，有效的做到了防湿防潮。
Description
技术领域
本发明涉及一种电气工程绝缘材料，具体地说是一种纳米电气工程用绝缘材料。
背景技术
目前电力产业处于高速发展时期，电器产品已经普及到各个行业，电器产品的绝缘要求是非常高的，目前市场上绝缘材料已有很多，但任然做不到防潮防湿，性能比较单一，其中，通过对绝缘材料中的成分进行改性处理，可以获得性能优良的高分子绝缘材料，这将极大的推动绝缘材料研发水平的提升。
发明内容
本发明的目的，在于提出一种纳米电气工程用绝缘材料。
为实现上述目的，本发明的技术解决方案是：
一种纳米电气工程用绝缘材料，包括以下材料：
松香改性马来酸树脂10-20份
聚乙二醇二甲基丙烯酸酯8-20份
聚甲基丙烯酸羟乙酯5-9份
二甘醇二苯甲酸酯3-10份
纳米氮化铝4-6份
铝酸酯偶联剂DL-411-A2-6份
复合稀土1-5份
粘合剂2-6份
煅烧云母10-18份
陶土9-16份
复合稀土按质量百分比计包括以下组分：镝：11-14%，镧：5-10%，铈：12-15%，镨：10-13%，钕：5-10%，其余为镧系元素，以上镧系稀土各组分之和为100%。
本发明进一步限定的技术方案为：
前述的纳米电气工程用绝缘材料，粘合剂为硅酸钠、硅烷偶联剂、硅油和液体石蜡。
前述的纳米电气工程用绝缘材料，包括以下材料：
松香改性马来酸树脂10份
聚乙二醇二甲基丙烯酸酯8份
聚甲基丙烯酸羟乙酯5份
二甘醇二苯甲酸酯3份
纳米氮化铝4份
铝酸酯偶联剂DL-411-A2份
复合稀土1份
粘合剂2份
煅烧云母10份
陶土9份
复合稀土按质量百分比计包括以下组分：镝：11%，镧：5%，铈：12%，镨：10%，钕：5%，其余为镧系元素，以上镧系稀土各组分之和为100%。
前述的纳米电气工程用绝缘材料，包括以下材料：
松香改性马来酸树脂20份
聚乙二醇二甲基丙烯酸酯20份
聚甲基丙烯酸羟乙酯9份
二甘醇二苯甲酸酯10份
纳米氮化铝6份
铝酸酯偶联剂DL-411-A6份
复合稀土5份
粘合剂6份
煅烧云母18份
陶土16份
复合稀土按质量百分比计包括以下组分：镝：14%，镧：10%，铈：15%，镨：13%，钕：10%，其余为镧系元素，以上镧系稀土各组分之和为100%
本发明的有益效果：本发明采用电气工程绝缘材料具有较高的拉伸强度和弯曲强度，并且还有较高的体积电阻，具备了较高的拉伸强度和弯曲强度，有效的做到了防湿防潮。
具体实施方式
实施例1
一种纳米电气工程用绝缘材料，包括以下材料：
松香改性马来酸树脂10份
聚乙二醇二甲基丙烯酸酯8份
聚甲基丙烯酸羟乙酯5份
二甘醇二苯甲酸酯3份
纳米氮化铝4份
铝酸酯偶联剂DL-411-A2份
复合稀土1份
粘合剂2份
煅烧云母10份
陶土9份
复合稀土按质量百分比计包括以下组分：镝：11%，镧：5%，铈：12%，镨：10%，钕：5%，其余为镧系元素，以上镧系稀土各组分之和为100%，粘合剂为硅酸钠、硅烷偶联剂、硅油和液体石蜡。
实施例2
一种纳米电气工程用绝缘材料，包括以下材料：
松香改性马来酸树脂20份
聚乙二醇二甲基丙烯酸酯20份
聚甲基丙烯酸羟乙酯9份
二甘醇二苯甲酸酯10份
纳米氮化铝6份
铝酸酯偶联剂DL-411-A6份
复合稀土5份
粘合剂6份
煅烧云母18份
陶土16份
复合稀土按质量百分比计包括以下组分：镝：14%，镧：10%，铈：15%，镨：13%，钕：10%，其余为镧系元素，以上镧系稀土各组分之和为100%，粘合剂为硅酸钠、硅烷偶联剂、硅油和液体石蜡。
除上述实施例外，本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案，均落在本发明要求的保护范围。
Claims (4)
1.一种纳米电气工程用绝缘材料，其特征在于包括以下材料：
松香改性马来酸树脂10-20份
聚乙二醇二甲基丙烯酸酯8-20份
聚甲基丙烯酸羟乙酯5-9份
二甘醇二苯甲酸酯3-10份
纳米氮化铝4-6份
铝酸酯偶联剂DL-411-A2-6份
复合稀土1-5份
粘合剂2-6份
煅烧云母10-18份
陶土9-16份
所述的复合稀土按质量百分比计包括以下组分：镝：11-14%，镧：5-10%，铈：12-15%，镨：10-13%，钕：5-10%，其余为镧系元素，以上镧系稀土各组分之和为100%。
2.根据权利要求1所述的纳米电气工程用绝缘材料，其特征在于，所述粘合剂为硅酸钠、硅烷偶联剂、硅油和液体石蜡。
3.根据权利要求1所述的纳米电气工程用绝缘材料，其特征在于包括以下材料：
松香改性马来酸树脂10份
聚乙二醇二甲基丙烯酸酯8份
聚甲基丙烯酸羟乙酯5份
二甘醇二苯甲酸酯3份
纳米氮化铝4份
铝酸酯偶联剂DL-411-A2份
复合稀土1份
粘合剂2份
煅烧云母10份
陶土9份
所述的复合稀土按质量百分比计包括以下组分：镝：11%，镧：5%，铈：12%，镨：10%，钕：5%，其余为镧系元素，以上镧系稀土各组分之和为100%。
4.根据权利要求1所述的纳米电气工程用绝缘材料，其特征在于包括以下材料：
松香改性马来酸树脂20份
聚乙二醇二甲基丙烯酸酯20份
聚甲基丙烯酸羟乙酯9份
二甘醇二苯甲酸酯10份
纳米氮化铝6份
铝酸酯偶联剂DL-411-A6份
复合稀土5份
粘合剂6份
煅烧云母18份
陶土16份
所述的复合稀土按质量百分比计包括以下组分：镝：14%，镧：10%，铈：15%，镨：13%，钕：10%，其余为镧系元素，以上镧系稀土各组分之和为100%。