CN105219240A - For the coating of the exterior glass steel part of electromobile - Google Patents
For the coating of the exterior glass steel part of electromobile Download PDFInfo
- Publication number
- CN105219240A CN105219240A CN201410297705.4A CN201410297705A CN105219240A CN 105219240 A CN105219240 A CN 105219240A CN 201410297705 A CN201410297705 A CN 201410297705A CN 105219240 A CN105219240 A CN 105219240A
- Authority
- CN
- China
- Prior art keywords
- coating
- electromobile
- steel part
- glass steel
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of coating for the exterior glass steel part of electromobile, its component and weight percent as follows: urethane resin 40-45%, melamine resin 18-20%, pigment 20-25%, auxiliary agent 3-6%, xylene solvent 8-10%, 150# solvent 2.5-3.5%.Described auxiliary agent comprises one or more of defoamer, flow agent, adhesion promoter, dispersion agent, anti-settling agent etc.The coating for electromobile exterior glass steel part of the application has carried out effective adjustment to coating internal chemical structure, molecular structure, the molecule content of coating is between 15000-30000, coating is improved in secondary coating postadhesion power, have stronger bonding strength, and when repairing recoat, primer base is without the need to beating putty coating, this coating can use, thus repair recoat performance good, do not affect technique and quality, both saved and manually again reduced environmental pollution.
Description
Technical field
The present invention relates to a kind of coating, specifically a kind of based on the coating of urethane resin and melamine resin, be applicable on the exterior glass steel part of electromobile.
Background technology
The Putty of primer base, when carrying out reparation recoat, generally need be beaten and wipe off, and then apply by the exterior glass steel part of electromobile, and therefore not only cost of labor is large, and to being unfavorable for environmental protection.
Summary of the invention
Technical problem to be solved by this invention is to provide the coating for the exterior glass steel part of electromobile that a kind of bonding strength is high, recoat performance is good.
For solving the problems of the technologies described above, the invention provides a kind of coating for the exterior glass steel part of electromobile, its component and weight percent as follows: urethane resin 40-45%, melamine resin 18-20%, pigment 20-25%, auxiliary agent 3-6%, xylene solvent 8-10%, 150# solvent 2.5-3.5%.
Described auxiliary agent comprises one or more of defoamer, flow agent, adhesion promoter, dispersion agent, anti-settling agent etc.
The preparation method of the above-mentioned coating for the exterior glass steel part of electromobile comprises the steps:
(1) by urethane resin, melamine resin mixing, formation base hybrid resin is stirred;
(2) basic hybrid resin drops into pigment in stirring, and is dropped into by various to defoamer, flow agent, adhesion promoter, dispersion agent, anti-settling agent etc. auxiliary agent by spray method when stirring, and forms paint vehicle;
(3) in paint vehicle, drop into xylene solvent, 150# solvent, stir and within 3-5 minute, namely can be configured to this coating for the exterior glass steel part of electromobile.
Technique effect of the present invention: the coating for electromobile exterior glass steel part of the application has carried out effective adjustment to coating internal chemical structure, molecular structure, the molecule content of coating is between 15000-30000, coating is improved in secondary coating postadhesion power, have stronger bonding strength, and when repairing recoat, primer base is without the need to beating putty coating, this coating can use, thus repair recoat performance good, do not affect technique and quality, both saved and manually again reduced environmental pollution.
Embodiment
Embodiment 1
The coating for the exterior glass steel part of electromobile of the present embodiment, its component and weight percent as follows: urethane resin 45%, melamine resin 18%, pigment 22%, auxiliary agent 4%, xylene solvent 8%, 150# solvent 3%.
Described auxiliary agent comprises one or more of defoamer, flow agent, adhesion promoter, dispersion agent, anti-settling agent etc.
The preparation method of the above-mentioned coating for the exterior glass steel part of electromobile comprises the steps:
(1) by proportioning, urethane resin, melamine resin are mixed, stir formation base hybrid resin;
(2) basic hybrid resin drops into pigment in stirring, and is dropped into by various to defoamer, flow agent, adhesion promoter, dispersion agent, anti-settling agent etc. auxiliary agent by spray method when stirring, and forms paint vehicle;
(3) in paint vehicle, drop into xylene solvent, 150# solvent, stir and within 3-5 minute, namely can be configured to this coating for the exterior glass steel part of electromobile.
Embodiment 2
The coating for the exterior glass steel part of electromobile of the present embodiment, its component and weight percent as follows: urethane resin 40%, melamine resin 20%, pigment 23%, auxiliary agent 4%, xylene solvent 10%, 150# solvent 3%.
Described auxiliary agent comprises one or more of defoamer, flow agent, adhesion promoter, dispersion agent, anti-settling agent etc.
The preparation method of the above-mentioned coating for the exterior glass steel part of electromobile comprises the steps:
(1) by proportioning, urethane resin, melamine resin are mixed, stir formation base hybrid resin;
(2) basic hybrid resin drops into pigment in stirring, and is dropped into by various to defoamer, flow agent, adhesion promoter, dispersion agent, anti-settling agent etc. auxiliary agent by spray method when stirring, and forms paint vehicle;
(3) in paint vehicle, drop into xylene solvent, 150# solvent, stir and within 3-5 minute, namely can be configured to this coating for the exterior glass steel part of electromobile.
Sticking power detects: sticking power, by hot and cold facture, after first paintings test plate (panel) being boiled 15 minutes in 100 DEG C of boiling water, then will to be coated with in refrigerated tank that test plate (panel) puts into-20 DEG C maintenance 15 minutes, finally etc. painting test plate (panel) separate at normal temperatures cold after carry out cross cut test; Cross cut test refers to the measuring method that standard GB/T/T9286-1998 " cross cut test of paint and varnish paint film " specify.This standard adopting by equivalent international standard ISO2409:1992.The standard specifies when penetrating into ground with cartesian mesh pattern cut coating, evaluate a kind of experimental technique of the resistance that coating departs from from ground.Test-results is divided into 0 ~ 5 grade, and 0 grade stands intact, and after testing, the paint adhesion of the application is 1 grade, is therefore better than 3 to 4 grades of prior art.
Moire detects: will be coated with test plate (panel) and pass through after cold-heat treatment, and put 2-3 hour at normal temperature, and after testing, painting test plate (panel) is flawless, without moire.
Claims (3)
1., for a coating for the exterior glass steel part of electromobile, it is characterized in that: its component and weight percent as follows: urethane resin 45%, melamine resin 18%, pigment 22%, auxiliary agent 4%, xylene solvent 8%, 150# solvent 3%.
2., as claimed in claim 1 for the coating of the exterior glass steel part of electromobile, it is characterized in that: described auxiliary agent comprise defoamer, flow agent, adhesion promoter, dispersion agent, anti-settling agent one or more.
3. a preparation method for the coating for the exterior glass steel part of electromobile according to claim 1, is characterized in that comprising the steps:
(1) by proportioning, urethane resin, melamine resin are mixed, stir formation base hybrid resin;
(2) basic hybrid resin drops into pigment in stirring, and is dropped into by various to defoamer, flow agent, adhesion promoter, dispersion agent, anti-settling agent etc. auxiliary agent by spray method when stirring, and forms paint vehicle;
(3) in paint vehicle, drop into xylene solvent, 150# solvent, stir and within 3-5 minute, namely can be configured to this coating for the exterior glass steel part of electromobile.