CN105218749A - 一种吸水式降温颗粒及其制备方法 - Google Patents
一种吸水式降温颗粒及其制备方法 Download PDFInfo
- Publication number
- CN105218749A CN105218749A CN201510705876.0A CN201510705876A CN105218749A CN 105218749 A CN105218749 A CN 105218749A CN 201510705876 A CN201510705876 A CN 201510705876A CN 105218749 A CN105218749 A CN 105218749A
- Authority
- CN
- China
- Prior art keywords
- water
- temperature
- cooling
- preparation
- polyacrylic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种吸水式降温颗粒,所述颗粒包括以下重量百分比组份:聚丙烯酸20%~80%、丙烯酰胺80%~20%和添加剂氧化烯烃;所述添加剂氧化烯烃其重量为聚丙烯酸和丙烯酰胺总量的2%~5%;其制备方法,包括以下步骤:步骤一:加温搅拌;步骤二:升温搅拌,步骤三:升温反应,步骤四:冷却过筛。制备的晶体聚合物吸水性超强,可达1000倍以上,在常温下晶体聚合物能自发吸水,常温即使施加压力,水也不会从晶体聚合物中逸出,保持性超强,在一定的压力下吸少量晶体,不会破碎;改进了导热系数,自动吸收热量,散发热量,自动释放凉气,产生降温效果。
Description
技术领域
本发明涉及一种吸水式降温颗粒及其制备方法,属于化学技术领域。
背景技术
炎炎夏季,高温往往让人觉得烦闷,难以忍受,在室内,开空调往往成为人们用来降温度的最常用方法之一,但空调不仅费电,使用久了还可能让人患上空调病,影响人体的健康;在室外,烈日炎炎,没有任何的降温电器进行降温,人们普遍采用喝水的方式来降温,但这只能起到暂时的降温效果,无法真正起到降温的作用。
发明内容
(一)要解决的技术问题
为解决上述问题,本发明提出了一种吸水式降温颗粒及其制备方法,制备的大颗粒晶体聚合物降温效果好,制冷持续时间长,且可重复使用。
(二)技术方案
本发明的吸水式降温颗粒,由以下重量百分比组成:所述颗粒包括以下重量百分比组份:聚丙烯酸20%~80%、丙烯酰胺80%~20%和添加剂氧化烯烃;所述添加剂氧化烯烃其重量为聚丙烯酸和丙烯酰胺总量的2%~5%。
一种吸水式降温颗粒的制备方法,包括以下步骤:
步骤一:将聚丙烯酸和丙烯酰胺依次投入至反应器皿中,加温搅拌;
步骤二:升温搅拌,反应器皿的反应温度升温至80度,加入添加剂氧化烯烃,继续加温搅拌;
步骤三:升温反应,反应器皿的反应温度升温至150~180度,产生颗粒状聚合物;
步骤四:冷却过筛,将步骤三中产生的颗粒状聚合物冷却过筛,筛选出5~20目大颗粒晶体聚合物。
(三)有益效果
与现有技术相比,本发明的吸水式降温颗粒及其制备方法,制备的晶体聚合物吸水性超强,可达1000倍以上,在常温下晶体聚合物能自发吸水,常温即使施加压力,水也不会从晶体聚合物中逸出,保持性超强,在一定的压力下吸少量晶体,不会破碎;改进了导热系数,自动吸收热量,散发热量,自动释放凉气,产生降温效果,在夏日高温室外环境下,连续使用可达8~72小时,降温效果明显,可重复使用。
具体实施方式
一种吸水式降温颗粒,由以下重量百分比组成:所述颗粒包括以下重量百分比组份:聚丙烯酸20%~80%、丙烯酰胺80%~20%和添加剂氧化烯烃;所述添加剂氧化烯烃其重量为聚丙烯酸和丙烯酰胺总量的2%~5%。
一种吸水式降温颗粒的制备方法,包括以下步骤:
步骤一:将聚丙烯酸和丙烯酰胺依次投入至反应器皿中,加温搅拌;
步骤二:升温搅拌,反应器皿的反应温度升温至80度,加入添加剂氧化烯烃,继续加温搅拌;
步骤三:升温反应,反应器皿的反应温度升温至150~180度,产生颗粒状聚合物;
步骤四:冷却过筛,将步骤三中产生的颗粒状聚合物冷却过筛,筛选出5~20目大颗粒晶体聚合物。
本发明的吸水式降温颗粒的使用方法:采用特殊专业设备将大颗粒晶体聚合物制成降温组件填充在系列降温产品纤维织物内层,制作成降温背心、降温头巾、降温帽子、降温帽垫及降温汽车座垫等产品;在夏日高温室外环境下使用,使用时,只需将上述所述的产品在冷水中浸泡3~5分钟,绞干后,或敷或带在身体某一部位,就能起到吸汗、降温的作用,并获得凉爽的感觉;持续使用可达8~72小时,降温效果明显,且可重复使用;将产品放置于冰箱内冷藏后使用,效果更佳。
上面所述的实施例仅仅是对本发明的优选实施方式进行描述,并非对本发明的构思和范围进行限定。在不脱离本发明设计构思的前提下,本领域普通人员对本发明的技术方案做出的各种变型和改进,均应落入到本发明的保护范围,本发明请求保护的技术内容,已经全部记载在权利要求书中。
Claims (2)
1.一种吸水式降温颗粒,其特征在于:所述颗粒包括以下重量百分比组份:聚丙烯酸20%~80%、丙烯酰胺80%~20%和添加剂氧化烯烃;所述添加剂氧化烯烃其重量为聚丙烯酸和丙烯酰胺总量的2%~5%。
2.一种吸水式降温颗粒的制备方法,其特征在于:包括以下步骤:
步骤一:将聚丙烯酸和丙烯酰胺依次投入至反应器皿中,加温搅拌;
步骤二:升温搅拌,反应器皿的反应温度升温至80度,加入添加剂氧化烯烃,继续加温搅拌;
步骤三:升温反应,反应器皿的反应温度升温至150~180度,产生颗粒状聚合物;
步骤四:冷却过筛,将步骤三中产生的颗粒状聚合物冷却过筛,筛选出5~20目大颗粒晶体聚合物。