CN105200430A - 一种新型Mn-4%Al-La-Sc合金腐蚀溶液 - Google Patents
一种新型Mn-4%Al-La-Sc合金腐蚀溶液 Download PDFInfo
- Publication number
- CN105200430A CN105200430A CN201410290764.9A CN201410290764A CN105200430A CN 105200430 A CN105200430 A CN 105200430A CN 201410290764 A CN201410290764 A CN 201410290764A CN 105200430 A CN105200430 A CN 105200430A
- Authority
- CN
- China
- Prior art keywords
- etchant solution
- alloy
- acid
- novel
- hydrochloric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型Mn-4%Al-La-Sc合金腐蚀溶液，在蒸馏水中加入一定量的氢氧化钾、盐酸和磷酸，其中以质量分数计的组分为：氢氟酸为9%，盐酸为4.5%、磷酸为7.5%，余量为蒸馏水，且加入顺序为先加入磷酸，再加入盐酸，最后加入氢氟酸即可。本发明所制的腐蚀溶液，可使Mn-4%Al-La-Sc合金的金相腐蚀变得与铝合金一样简单快捷，且节省成本，特别适用Mn-4%Al-La-Sc合金的腐蚀。
Description
技术领域
本发明涉及一种新型Mn-4%Al-La-Sc合金腐蚀溶液，属于腐蚀溶液技术领域。
背景技术
Mn-4%Al-La-Sc合金的金相组织很难腐蚀，即使腐蚀出来其组织也往往显示的不完全，因而通常都采用阳极覆膜加偏光来观察其金相。但这种观察方法不仅耗时，而且提高了制作成本。因此如何使Mn-4%Al-La-Sc合金的金相腐蚀变得与铝合金一样简单快捷是尚待解决的难题。
发明内容
本发明要解决的技术问题：提供一种新型Mn-4%Al-La-Sc合金腐蚀溶液，Mn-4%Al-La-Sc合金经其腐蚀后能直接观察金相组织而不需阳极覆膜处理和偏光来观察，以克服现有技术的不足。
本发明的技术方案：
一种新型Mn-4%Al-La-Sc合金腐蚀溶液，在蒸馏水中加入一定量的氢氧化钾、盐酸和磷酸制成腐蚀溶液，其中以质量分数计的组分为：氢氟酸为9%，盐酸为4.5%、磷酸为7.5%，余量为蒸馏水，且加入顺序为先加入磷酸，再加入盐酸，最后加入氢氟酸即可。
作为优选，所述腐蚀溶液采用常规的溶液配制方法进行配制。
本发明的有益效果：
与现有技术相比，本发明的Mn-4%Al-La-Sc合金的腐蚀溶液具有以下的特点：
①腐蚀后的晶界和晶粒显示清晰，只要操作得当，不存在组织腐蚀不完全的情况；
②腐蚀后可直接用于金相组织观察，无需采用阳极覆膜和偏关观察，大大的缩短了金相制样时间；
③该腐蚀溶液在常温下即可腐蚀，无需加热到一定温度再进行腐蚀；
综上所述，本发明的腐蚀溶液可使Mn-4%Al-La-Sc合金的金相腐蚀变得简单而快捷，且节省成本。
附图说明：
图1为100倍腐蚀效果的SEM图。
具体实施方式：
实施例：
一种新型Mn-4%Al-La-Sc合金腐蚀溶液，以混合酸为原料，采用常规的溶液配制方法进行配制，在一定量的蒸馏水中先后加入占重为7.5%的磷酸、4.5%的盐酸和9%的氢氟酸，然后用玻璃棒搅拌均匀。将经上述步骤制成的腐蚀溶液用来腐蚀Mn-4%Al-La-Sc合金，具体效果见图1。
Claims (2)
1.一种新型Mn-4%Al-La-Sc合金腐蚀溶液，其特征在于：在蒸馏水中加入一定量的氢氧化钾、盐酸和磷酸制成腐蚀溶液，其中以质量分数计的组分为：氢氟酸为9%，盐酸为4.5%、磷酸为7.5%，余量为蒸馏水，且加入顺序为先加入磷酸，再加入盐酸，最后加入氢氟酸即可。
2.根据权利要求1所述的一种新型Mn-4%Al-La-Sc合金腐蚀溶液，其特征在于：所述腐蚀溶液采用常规的溶液配制方法进行配制。