CN105199440A - Environment-friendly bedroom paint and preparation method thereof - Google Patents
Environment-friendly bedroom paint and preparation method thereof Download PDFInfo
- Publication number
- CN105199440A CN105199440A CN201510668922.4A CN201510668922A CN105199440A CN 105199440 A CN105199440 A CN 105199440A CN 201510668922 A CN201510668922 A CN 201510668922A CN 105199440 A CN105199440 A CN 105199440A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- water
- bedroom
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to environment-friendly bedroom paint which comprises the following components in parts by mass: 30-50 parts of diatomite, 10-15 parts of a diatomite loaded nano TiO2 material, 5-10 parts of modified nano titanium dioxide, 8-12 parts of glass bead, 2-2.4 parts of fumed silica, 3-6 parts of hydroxypropyl methyl cellulose, 1-1.3 parts of an inorganic aluminium salt water-proofing agent, 0.5-1.5 parts of aluminium-magnesium silicate, 5-6 parts of white bamboo charcoal and 100-125 parts of water. The environment-friendly bedroom paint is prepared by the following steps: putting 30-50 parts of diatomite, 10-15 parts of the diatomite loaded nano TiO2 material and 5-10 parts of modified nano titanium dioxide into a high-speed pulverizer, sealing, shearing at the rotating speed of 8000-15000 r/min for 30-60 s, discharging a main material, adding 8-12 parts of glass bead, 2-2.4 parts of fumed silica, 3-6 parts of hydroxypropyl methyl cellulose, 1-1.3 parts of the inorganic aluminium salt water-proofing agent, 0.5-1.5 parts of aluminium-magnesium silicate, 5-6 parts of white bamboo charcoal and 100-125 parts of water into the main material in sequence, and stirring for 5-8 min.
Description
Technical field
The present invention relates to a kind of coating, is bedroom, a kind of bedroom environmental protection coating material and preparation method thereof specifically.
Background technology
In finishing, inevasible in Furniture panel, floor board exist the objectionable impuritiess such as formaldehyde, serious harm human body.Existing commercially available popular anti-formaldehyde, absorbing formaldehyde coating mostly adopt diatomite as raw material, but existing coating adopts the traditional coating such as resin, rubber powder raw material in a large number, and blocking diatomite space, reduces its adsorption effect, affect its use properties.
Summary of the invention
For the above-mentioned deficiency of prior art, the invention provides excellent, stable, effective bedroom environmental protection coating material of a kind of use properties and preparation method thereof.
The technical solution used in the present invention is: a kind of bedroom environmental protection coating material, is characterized in that: comprise by massfraction: diatomite 30-50 part, tripolite loading nano TiO2 material 10-15 part, modified nano-titanium dioxide 5-10 part, glass bead 8-12 part, aerosil 2-2.4 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, neusilin 0.5-1.5 part, white bamboo charcoal 5-6 part and water 100-125 part.
A kind of bedroom environmental protection coating material preparation method, it is characterized in that: comprise the following steps: by diatomite 30-50 part, tripolite loading nano TiO2 material 10-15 part, modified nano-titanium dioxide 5-10 part puts into high speed disintegrator, sealing, in the rotating speed down cut 30-60 second of 8000-15000r/min, go out major ingredient: in major ingredient, add glass bead 8-12 part successively, aerosil 2-2.4 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, neusilin 0.5-1.5 part, white bamboo charcoal 5-6 part, after water 100-125 part, stir 5-8 minute.
Adopt technique scheme, the invention has the beneficial effects as follows: adopt diatomite, tripolite loading nano TiO2 material, modified nano-titanium dioxide blended, effective expansion diatomite major ingredient aperture 60-80%, improves and stable adsorptive power, avoids auxiliary material blocking in coating; Glass bead improves its Jue Re ﹑ Fang Huo ﹑ Xi Yin ﹑ heat-insulating property.Aerosil is used as the auxiliary agent of anti-settling, the thickening of coating, sag prevention, regulates unrestricted flow and improves character as anti-caking agent, having the multiple effects such as good reinforcement, thickening, thixotroping, delustring, uvioresistant and sterilization, auxiliary adsorb harmful components.Inorganic aluminate water-proof agent improves its water resistance, in conjunction with neusilin suspension thickening, improves paint stability simultaneously, guarantees use safety health.
Embodiment
Be described further below in conjunction with embodiment.
Embodiment one
A kind of bedroom environmental protection coating material, comprises by massfraction: 30 parts, diatomite, tripolite loading nano TiO2 material 10 parts, modified nano-titanium dioxide 5 parts, glass bead 8 parts, aerosil 2 parts, Vltra tears 3 parts, inorganic aluminate water-proof agent 1 part, neusilin 0.5 part, white bamboo charcoal 5 parts and 100 parts, water.
A kind of bedroom environmental protection coating material preparation method; comprise the following steps: 30 parts, diatomite, tripolite loading nano TiO2 material 10 parts, modified nano-titanium dioxide 5 parts are put into high speed disintegrator; sealing; at the rotating speed down cut 60 seconds of 8000r/min; go out major ingredient: add glass bead 8 parts, aerosil 2 parts, Vltra tears 3 parts, inorganic aluminate water-proof agent 1 part, neusilin 0.5 part, white bamboo charcoal 5 parts, 100 parts, water successively in major ingredient after, stir 5 minutes.
Embodiment two
A kind of bedroom environmental protection coating material, comprises by massfraction: 50 parts, diatomite, tripolite loading nano TiO2 material 15 parts, modified nano-titanium dioxide 10 parts, glass bead 12 parts, aerosil 2.4 parts, Vltra tears 6 parts, inorganic aluminate water-proof agent 1.3 parts, neusilin 1.5 parts, white bamboo charcoal 6 parts and 125 parts, water.
A kind of bedroom environmental protection coating material preparation method; comprise the following steps: 50 parts, diatomite, tripolite loading nano TiO2 material 15 parts, modified nano-titanium dioxide 10 parts are put into high speed disintegrator; sealing; at the rotating speed down cut 30 seconds of 15000r/min; go out major ingredient: add glass bead 12 parts, aerosil 2.4 parts, Vltra tears 6 parts, inorganic aluminate water-proof agent 1.3 parts, neusilin 1.5 parts, white bamboo charcoal 6 parts, 125 parts, water successively in major ingredient after, stir 8 minutes.
Embodiment three
A kind of bedroom environmental protection coating material, comprises by massfraction: 40 parts, diatomite, tripolite loading nano TiO2 material 12 parts, modified nano-titanium dioxide 8 parts, glass bead 10 parts, aerosil 2.3 parts, Vltra tears 5 parts, inorganic aluminate water-proof agent 1.1 parts, neusilin 1 part, white bamboo charcoal 5.5 parts and 120 parts, water.
A kind of bedroom environmental protection coating material preparation method; comprise the following steps: 40 parts, diatomite, tripolite loading nano TiO2 material 12 parts, modified nano-titanium dioxide 8 parts are put into high speed disintegrator; sealing; at the rotating speed down cut 45 seconds of 12000r/min; go out major ingredient: add glass bead 10 parts, aerosil 2.3 parts, Vltra tears 5 parts, inorganic aluminate water-proof agent 1.1 parts, neusilin 1 part, white bamboo charcoal 5.5 parts, 120 parts, water successively in major ingredient after, stir 6.5 minutes.
Claims (2)
1. a bedroom environmental protection coating material, is characterized in that: comprise by massfraction: diatomite 30-50 part, tripolite loading nano TiO2 material 10-15 part, modified nano-titanium dioxide 5-10 part, glass bead 8-12 part, aerosil 2-2.4 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, neusilin 0.5-1.5 part, white bamboo charcoal 5-6 part and water 100-125 part.
2. a bedroom environmental protection coating material preparation method, it is characterized in that: comprise the following steps: by diatomite 30-50 part, tripolite loading nano TiO2 material 10-15 part, modified nano-titanium dioxide 5-10 part puts into high speed disintegrator, sealing, in the rotating speed down cut 30-60 second of 8000-15000r/min, go out major ingredient: in major ingredient, add glass bead 8-12 part successively, aerosil 2-2.4 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, neusilin 0.5-1.5 part, white bamboo charcoal 5-6 part, after water 100-125 part, stir 5-8 minute.