CN105199439A - Preparation method for anti-bacteria and anti-mildew environment-friendly paint - Google Patents
Preparation method for anti-bacteria and anti-mildew environment-friendly paint Download PDFInfo
- Publication number
- CN105199439A CN105199439A CN201510668634.9A CN201510668634A CN105199439A CN 105199439 A CN105199439 A CN 105199439A CN 201510668634 A CN201510668634 A CN 201510668634A CN 105199439 A CN105199439 A CN 105199439A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- water
- modified
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to anti-bacteria and anti-mildew environment-friendly paint which comprises the following components in parts by mass: 30-50 parts of diatomite, 10-15 parts of a diatomite loaded nanometer TiO2 material, 5-10 parts of modified nanometer titanium dioxide, 8-12 parts of glass microbeads, 2-2.4 parts of fumed silica, 3-6 parts of hydroxypropyl methyl cellulose, 1-1.3 parts of an inorganic aluminum salt waterproof agent, 0.5-1.5 parts of aluminum-magnesium silicate, 5-6 parts of modified zinc oxide, 2-3 parts of an antioxidant 1076 and 100-125 parts of water. A preparation method of the paint comprises the following steps: putting diatomite, the diatomite loaded nanometer TiO2 material and modified nanometer titanium dioxide into a high-speed crusher, sealing the crusher, performing 30-60 seconds' shearing at a rotating speed of 8000-15000 r/min, and discharging a main material; sequentially adding the glass microbeads, fumed silica, hydroxypropyl methyl cellulose, the inorganic aluminum salt waterproof agent, aluminum-magnesium silicate, modified zinc oxide, the antioxidant 1076 and water into the main material, and performing 5-8 minutes' stirring.
Description
Technical field
The present invention relates to a kind of coating, is a kind of bedroom antibacterial and mouldproof environmental protection coating material and preparation method thereof specifically.
Background technology
In finishing, inevasible in Furniture panel, floor board exist the objectionable impuritiess such as formaldehyde, serious harm human body.Existing commercially available popular anti-formaldehyde, absorbing formaldehyde coating mostly adopt diatomite as raw material, but existing coating adopts the traditional coating such as resin, rubber powder raw material in a large number, and blocking diatomite space, reduces its adsorption effect, affect its use properties.
Summary of the invention
For the above-mentioned deficiency of prior art, the invention provides excellent, stable, effective antibacterial and mouldproof environmental protection coating material of a kind of use properties and preparation method thereof.
The technical solution used in the present invention is: a kind of antibacterial and mouldproof environmental protection coating material, is characterized in that: comprise by massfraction: diatomite 30-50 part, tripolite loading nano TiO2 material 10-15 part, modified nano-titanium dioxide 5-10 part, glass bead 8-12 part, aerosil 2-2.4 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, neusilin 0.5-1.5 part, modified zinc oxide 5-6 part, 1076 oxidation inhibitor 2-3 parts and water 100-125 part.
A kind of antibacterial and mouldproof environmental protection coating material preparation method, it is characterized in that: comprise the following steps: by diatomite 30-50 part, tripolite loading nano TiO2 material 10-15 part, modified nano-titanium dioxide 5-10 part puts into high speed disintegrator, sealing, in the rotating speed down cut 30-60 second of 8000-15000r/min, go out major ingredient: in major ingredient, add glass bead 8-12 part successively, aerosil 2-2.4 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, neusilin 0.5-1.5 part, modified zinc oxide 5-6 part, 1076 oxidation inhibitor 2-3 parts, after water 100-125 part, stir 5-8 minute.
Adopt technique scheme, the invention has the beneficial effects as follows: adopt diatomite, tripolite loading nano TiO2 material, modified nano-titanium dioxide blended, effective expansion diatomite major ingredient aperture 60-80%, improves and stable adsorptive power, avoids auxiliary material blocking in coating; Glass bead improves its Jue Re ﹑ Fang Huo ﹑ Xi Yin ﹑ heat-insulating property.Aerosil is used as the auxiliary agent of anti-settling, the thickening of coating, sag prevention, regulate unrestricted flow and improve character as anti-caking agent, have the multiple effects such as good reinforcement, thickening, thixotroping, delustring, uvioresistant and sterilization, Aided Modification zinc oxide antibacterial effect is better.Inorganic aluminate water-proof agent improves its water resistance, in conjunction with neusilin suspension thickening, coordinates 1076 oxidation inhibitor resistance of oxidation strong, extends its work-ing life, guarantees the stability in use under the kitchen occasion of the high hot high humidity of high temperature and safety and sanitation.
Embodiment
Be described further below in conjunction with embodiment.
Embodiment one
A kind of antibacterial and mouldproof environmental protection coating material, comprises by massfraction: 30 parts, diatomite, tripolite loading nano TiO2 material 10 parts, modified nano-titanium dioxide 5 parts, glass bead 8 parts, aerosil 2 parts, Vltra tears 3 parts, inorganic aluminate water-proof agent 1 part, neusilin 0.5 part, modified zinc oxide 5 parts, 2 parts, 1076 oxidation inhibitor and 100 parts, water.
A kind of antibacterial and mouldproof environmental protection coating material preparation method; comprise the following steps: 30 parts, diatomite, tripolite loading nano TiO2 material 10 parts, modified nano-titanium dioxide 5 parts are put into high speed disintegrator; sealing; at the rotating speed down cut 60 seconds of 8000r/min; go out major ingredient: add glass bead 8 parts, aerosil 2 parts, Vltra tears 3 parts, inorganic aluminate water-proof agent 1 part, neusilin 0.5 part, modified zinc oxide 5 parts, 2 parts, 1076 oxidation inhibitor, 100 parts, water successively in major ingredient after, stir 5 minutes.
Embodiment two
A kind of antibacterial and mouldproof environmental protection coating material, comprises by massfraction: 50 parts, diatomite, tripolite loading nano TiO2 material 15 parts, modified nano-titanium dioxide 10 parts, glass bead 12 parts, aerosil 2.4 parts, Vltra tears 6 parts, inorganic aluminate water-proof agent 1.3 parts, neusilin 1.5 parts, modified zinc oxide 6 parts, 3 parts, 1076 oxidation inhibitor and 125 parts, water.
A kind of antibacterial and mouldproof environmental protection coating material preparation method; comprise the following steps: 50 parts, diatomite, tripolite loading nano TiO2 material 15 parts, modified nano-titanium dioxide 10 parts are put into high speed disintegrator; sealing; at the rotating speed down cut 30 seconds of 15000r/min; go out major ingredient: add glass bead 12 parts, aerosil 2.4 parts, Vltra tears 6 parts, inorganic aluminate water-proof agent 1.3 parts, neusilin 1.5 parts, modified zinc oxide 6 parts, 3 parts, 1076 oxidation inhibitor, 125 parts, water successively in major ingredient after, stir 8 minutes.
Embodiment three
A kind of antibacterial and mouldproof environmental protection coating material, comprises by massfraction: 40 parts, diatomite, tripolite loading nano TiO2 material 12 parts, modified nano-titanium dioxide 8 parts, glass bead 10 parts, aerosil 2.3 parts, Vltra tears 5 parts, inorganic aluminate water-proof agent 1.1 parts, neusilin 1 part, modified zinc oxide 5.5 parts, 2.5 parts, 1076 oxidation inhibitor and 120 parts, water.
A kind of antibacterial and mouldproof environmental protection coating material preparation method; comprise the following steps: 40 parts, diatomite, tripolite loading nano TiO2 material 12 parts, modified nano-titanium dioxide 8 parts are put into high speed disintegrator; sealing; at the rotating speed down cut 45 seconds of 12000r/min; go out major ingredient: add glass bead 10 parts, aerosil 2.3 parts, Vltra tears 5 parts, inorganic aluminate water-proof agent 1.1 parts, neusilin 1 part, modified zinc oxide 5.5 parts, 2.5 parts, 1076 oxidation inhibitor, 120 parts, water successively in major ingredient after, stir 6.5 minutes.
Claims (1)
1. an antibacterial and mouldproof environmental protection coating material preparation method, it is characterized in that: comprise the following steps: by diatomite 30-50 part, tripolite loading nano TiO2 material 10-15 part, modified nano-titanium dioxide 5-10 part puts into high speed disintegrator, sealing, in the rotating speed down cut 30-60 second of 8000-15000r/min, go out major ingredient: in major ingredient, add glass bead 8-12 part successively, aerosil 2-2.4 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, neusilin 0.5-1.5 part, modified zinc oxide 5-6 part, 1076 oxidation inhibitor 2-3 parts, after water 100-125 part, stir 5-8 minute.