CN105176417A - Solvent type strong-viscous-force pressure-sensitive adhesive - Google Patents
Solvent type strong-viscous-force pressure-sensitive adhesive Download PDFInfo
- Publication number
- CN105176417A CN105176417A CN201510627922.XA CN201510627922A CN105176417A CN 105176417 A CN105176417 A CN 105176417A CN 201510627922 A CN201510627922 A CN 201510627922A CN 105176417 A CN105176417 A CN 105176417A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- solvent
- sensitive adhesive
- force pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a solvent type strong-viscous-force pressure-sensitive adhesive. The solvent type strong-viscous-force pressure-sensitive adhesive is characterized by being prepared from, by weight, 70 parts of methyl methacrylate, 26 parts of ethyl acrylate, 15 parts of dimethyldiethoxysilane, 40 parts of solvent, 2.8 parts of nanoscale SiO2 powder, 1.2 parts of nanoscale Al2O3 powder, 0.2 part of nanoscale SiO2 powder, 0.4 part of micron-size Al2O3 powder, 0.8 part of isocyanate, 4.2 parts of rosin resin, 4.5 parts of terpene resin, 1.5 parts of azoic compounds, 4.6 parts of N-nitro compounds and 1.2 parts of silane coupling agents. The high-temperature-resistant performance is improved, and the viscosity stability under the temperature difference changes is improved.
Description
Technical field
The present invention relates to a kind of high sticky pressure sensitive adhesive, the particularly agent of a kind of solvent-borne type strong viscous force pressure-sensitive adhesive.
Background technology
Sizing agent is applied range, and wherein acrylate adhesive characteristic is: the Performance Ratio solvent-borne types such as intensity is high, toughness, hardness or aqueous solution type good, has good cementability to multiple material, easy to use, cheap.Due to electronic product, this is also more and more higher to the requirement of adhesive tape, usually need clinging power strong and thickness at thinner adhesive tape.For electronic product or other products, once use adhesive tape, then need this adhesive tape can maintain viscosity when difference variation is large always, and can easily sizing agent be peeled off from film, secondly, prior art is being taken into account under other performances such as homogeneity, improves cloudy surface roughness and there is bottleneck.
Summary of the invention
The invention provides the agent of a kind of solvent-borne type strong viscous force pressure-sensitive adhesive, the agent of this solvent-borne type strong viscous force pressure-sensitive adhesive improves vinylformic acid sizing agent roughness when not increasing particle diameter, avoid cluster, it also avoid SiO
2powder, Al
2o
3the sedimentation of powder in system, improves and base material bonding force.
For achieving the above object, the technical solution used in the present invention is: the agent of a kind of solvent-borne type strong viscous force pressure-sensitive adhesive, and the agent of described solvent-borne type strong viscous force pressure-sensitive adhesive is made up of following parts by weight of component: methyl methacrylate 70 parts, ethyl propenoate 26 parts, dimethyldiethoxysilane 15 parts, solvent 40 parts, nano level SiO
2powder 2.8 parts, nano level Al
2o
3powder 1.2 parts, micron order SiO
2powder 0.2 part, micron order Al
2o
3powder 0.4 part, isocyanic ester 0.8 part, Gum Rosin 4.2 parts, note olefine resin 4.5 parts, azo-compound 1.5 parts, N-nitroso compound 4.6 parts, silane coupling agent 1.2 parts;
Described coupling agent chemical formula is: CH
2=CH-Si(OC
2h
5)
3.
The technical scheme improved further in technique scheme is as follows:
1. in such scheme, described nanometer Al
2o
3powder is on average 30nm so far.
2. in such scheme, described Nano-meter SiO_2
2powder mean diameter is 12nm.
3., in such scheme, described solvent is solvent is butanone, ethyl acetate or toluene.
Because technique scheme is used, the present invention compared with prior art has following advantages and effect:
1. solvent-borne type of the present invention strong viscous force pressure-sensitive adhesive agent, it adopts nano level and micron order SiO
2powder Al
2o
3powder and methyl methacrylate 70 parts, ethyl propenoate 26 parts, dimethyldiethoxysilane 15 parts and silane coupling agent, isocyanic ester acting in conjunction, relatively single use nano level or micron order SiO
2powder, Al
2o
3powder, improves vinylformic acid sizing agent roughness, is also conducive to SiO
2powder, Al
2o
3powder is uniformly distributed and dispersion in system, avoids cluster; Secondly, azo-compound 1.5 parts, adding of N-nitroso compound 4.6 parts, it also avoid SiO
2powder, Al
2o
3the sedimentation of powder in system, improves and base material bonding force.
2. solvent-borne type of the present invention strong viscous force pressure-sensitive adhesive agent, it comprises Gum Rosin 4.2 parts, and note olefine resin 4.5 parts and methyl methacrylate 70 parts, ethyl propenoate 26 parts, dimethyldiethoxysilane 15 parts of actings in conjunction, avoid by SiO
2powder, Al
2o
3powder adds the decline of the resistance to elevated temperatures caused, and improves resistance to elevated temperatures, and the stability of viscosity under difference variation, thus improves the reliability of product.
Embodiment
Below in conjunction with embodiment, the invention will be further described:
Embodiment: a kind of solvent-borne type strong viscous force pressure-sensitive adhesive agent, the agent of described solvent-borne type strong viscous force pressure-sensitive adhesive is made up of following parts by weight of component: methyl methacrylate 70 parts, ethyl propenoate 26 parts, dimethyldiethoxysilane 15 parts, solvent 40 parts, nano level SiO
2powder 2.8 parts, nano level Al
2o
3powder 1.2 parts, micron order SiO
2powder 0.2 part, micron order Al
2o
3powder 0.4 part, isocyanic ester 0.8 part, Gum Rosin 4.2 parts, note olefine resin 4.5 parts, azo-compound 1.5 parts, N-nitroso compound 4.6 parts, silane coupling agent 1.2 parts;
Described coupling agent chemical formula is: CH
2=CH-Si(OC
2h
5)
3;
The agent of a kind of solvent-borne type strong viscous force pressure-sensitive adhesive, comprises the following steps:
Step 1. is by 0.2 part of micron order SiO
2powder, 0.4 part of micron order Al
2o
3powder and 1.2 parts of silane coupling agents add in the first solvent and carry out ultrasonication and obtain pre-dispersed liquid, and this coupling agent chemical formula is: CH
2=CH-Si(OC
2h
5)
3;
Step 2. is by 2.8 parts of nano level SiO
2powder, 1.2 parts of nano level Al
2o
3powder and isocyanic ester 0.8 part add in pre-dispersed liquid carry out ultrasonication obtain modulation after pre-dispersed liquid;
Methyl methacrylate 70 parts, ethyl propenoate 26 parts and dimethyldiethoxysilane 15 parts add in the second solvent by step 3. carries out mechanical stirring acquisition polymers soln;
The mixing of the polymers soln of pre-dispersed liquid, step 3 after the modulation of step 2 is also added Gum Rosin 4.2 parts, note olefine resin 4.5 parts, azo-compound 1.5 parts, N-nitroso compound 4.6 parts by step 4. successively, carry out mechanical high-speed stirring and ultrasonic stirring, thus obtain the sticky pressure sensitive adhesive of solvent-borne type height.
Above-mentioned Nano-meter SiO_2
2powder mean diameter is 12nm, described nanometer Al
2o
3powder mean diameter is 30nm.
Above-mentioned solvent is at least one in toluene, ethyl acetate and butanone.
When adopting the agent of above-mentioned solvent-borne type strong viscous force pressure-sensitive adhesive, its relatively single use nano level or micron order SiO
2powder, Al
2o
3powder, improves vinylformic acid sizing agent roughness, is also conducive to SiO
2powder, Al
2o
3powder is uniformly distributed and dispersion in system, avoids cluster; Next it also avoid SiO
2powder, Al
2o
3the sedimentation of powder in system, improves and base material bonding force; Again, avoid by SiO
2powder, Al
2o
3powder adds the decline of the resistance to elevated temperatures caused, and improves resistance to elevated temperatures, and the stability of viscosity under difference variation, thus improves the reliability of product.
Above-described embodiment, only for technical conceive of the present invention and feature are described, its object is to person skilled in the art can be understood content of the present invention and implement according to this, can not limit the scope of the invention with this.All equivalences done according to spirit of the present invention change or modify, and all should be encompassed within protection scope of the present invention.
Claims (4)
1. a solvent-borne type strong viscous force pressure-sensitive adhesive agent, is characterized in that: the agent of described solvent-borne type strong viscous force pressure-sensitive adhesive is made up of following parts by weight of component: methyl methacrylate 70 parts, ethyl propenoate 26 parts, dimethyldiethoxysilane 15 parts, solvent 40 parts, nano level SiO
2powder 2.8 parts, nano level Al
2o
3powder 1.2 parts, micron order SiO
2powder 0.2 part, micron order Al
2o
3powder 0.4 part, isocyanic ester 0.8 part, Gum Rosin 4.2 parts, note olefine resin 4.5 parts, azo-compound 1.5 parts, N-nitroso compound 4.6 parts, silane coupling agent 1.2 parts;
Described coupling agent chemical formula is: CH
2=CH-Si(OC
2h
5)
3.
2. solvent-borne type according to claim 1 strong viscous force pressure-sensitive adhesive agent, is characterized in that: described Nano-meter SiO_2
2powder mean diameter is 12nm.
3. solvent-borne type according to claim 1 strong viscous force pressure-sensitive adhesive agent, is characterized in that: described nanometer Al
2o
3powder mean diameter is 30nm.
4. solvent-borne type according to claim 1 strong viscous force pressure-sensitive adhesive agent, is characterized in that: described solvent is butanone, ethyl acetate or toluene.