CN1051755C - Ceramic handiwork with drifted red glaze and its production - Google Patents

Ceramic handiwork with drifted red glaze and its production Download PDF

Info

Publication number
CN1051755C
CN1051755C CN95111834A CN95111834A CN1051755C CN 1051755 C CN1051755 C CN 1051755C CN 95111834 A CN95111834 A CN 95111834A CN 95111834 A CN95111834 A CN 95111834A CN 1051755 C CN1051755 C CN 1051755C
Authority
CN
China
Prior art keywords
red glaze
red
glaze
temperature
ceramic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN95111834A
Other languages
Chinese (zh)
Other versions
CN1139090A (en
Inventor
邢良坤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN95111834A priority Critical patent/CN1051755C/en
Publication of CN1139090A publication Critical patent/CN1139090A/en
Application granted granted Critical
Publication of CN1051755C publication Critical patent/CN1051755C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The present invention relates to ceramic handicraft with drifted red glaze. The ceramic handicraft is bright red, and has red glaze in a foam and blood block shape flowing from top to bottom, and the effect that blood just flows on the ceramic handicraft is obtained. The present invention has a production method that high-temperature red glaze with high-temperature foaming agents is coated on the top of ceramic blanks coated with high-temperature color glaze, and obtained materials are fired at 1300 to 1330 DEG C with high air flow rate.

Description

Ceramic handiwork with drifted red glaze and method for making thereof
The invention belongs to ceramics and method for making thereof, particularly trickling is as the red glaze ceramic handiwork and the method for making thereof of blood.
Color glaze can make ceramic develop bright and colourfully, and firing of color is ever-changing, and very complicated; Particularly red, extremely difficulty is fired into like the blood red; As for the trickling red glaze, the red glaze of low temperature in Jing Dezhen is only arranged, it is a bit darkish in color, glaze is that planar does not have the effect of " work ".
The present invention is by allocating red glaze formula, be fired into the scarlet blood glaze pottery of trickling in the high temperature kiln.
Method of the present invention is: after crossing ground-coat enamel on the greenwave, coat the red glaze of being furnished with high-temperature foaming agent at the top, its thickness is 1～3mm, go into kiln, under 1300～1330 ℃, fire 14～16h, when firing during the firing at ordinary times of air amount ratio many 5～10%, red glaze fusing this moment, high-temperature foaming agent bubbles and the red glaze of fusing is guttered down simultaneously, after the cooling, appreciablely be not only bright-coloured red glaze and trickle from top to down, this red glaze is to be with foam, clot shape, just as blood is just under the overhead stream, present the shape of " work ", very true to nature.High-temperature foaming agent is made up of the low temperature ground-coat enamel, accounts for 5～25% of red glaze.
Characteristics of the present invention are: so bright-coloured as blood, have the red glaze of trickling of foam and block blood, like under the blood manifold, play the effect of " work ", this pottery art product are initiative, with high-temperature foaming agent with increase air capacity to fire the technology that makes it to produce the transmutation effect also be very special.
Example
Be coated with on the vertical fish shape greenwave with the blue look high temperature of 0.5～1.0mm ground-coat enamel, dried slightly, the fish mouth be coated with have high-temperature foaming agent (the red ground-coat enamel of low temperature, account for glaze 15%) the red glaze of high temperature, its thickness is 1～3mm, go into kiln, burn down 15h, strengthen air capacity when firing (than usual many 10%) therebetween at 1300～1330 ℃, kiln is opened in cooling, as seen the Yu Zui both sides blood red color glaze that trickling from top to bottom has spumescence, bulk therebetween, like blood just from dropping down.

Claims (2)

1, a kind of red glaze ceramic handiwork, it is characterized by is to scribble the red glaze of the high temperature that contains high-temperature foaming agent by being used in ceramic base top, the method that strengthens air flow in the high temperature kiln is fired the red glaze of the trickling that forms, and presents the red glaze that has spumescence, the blocky trickling form of blood on the light ground-coat enamel of pottery from top to down.
2, a kind of manufacturing side of red glaze ceramic handiwork determines, and it is characterized by at the top of the greenwave of last ground-coat enamel and coats the red glaze of the high temperature of being furnished with high-temperature foaming agent, and its thickness is 1～3mm, under 1300～1330 ℃, burn 14～16h, the air amount ratio is many at ordinary times 5～10% therebetween, reduces to room temperature and forms; Described high-temperature foaming agent is that the red ground-coat enamel of low temperature is formed, and consumption accounts for 5～25% of red glaze.
CN95111834A 1995-06-26 1995-06-26 Ceramic handiwork with drifted red glaze and its production Expired - Fee Related CN1051755C (en)