CN105174498B - The composite highly effective low-phosphorus corrosion scale inhibition agent and preparation method of a kind of suitable low-hardness water - Google Patents

The composite highly effective low-phosphorus corrosion scale inhibition agent and preparation method of a kind of suitable low-hardness water Download PDF

Info

Publication number
CN105174498B
CN105174498B CN201510411944.2A CN201510411944A CN105174498B CN 105174498 B CN105174498 B CN 105174498B CN 201510411944 A CN201510411944 A CN 201510411944A CN 105174498 B CN105174498 B CN 105174498B
Authority
CN
China
Prior art keywords
water
scale inhibition
low
highly effective
corrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510411944.2A
Other languages
Chinese (zh)
Other versions
CN105174498A (en
Inventor
张柏鸿
李俊峰
王坤鹏
王志成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Angang Litian (Anshan) water treatment Co.,Ltd.
Original Assignee
Anshan Iron And Steel Plant Bake Lucky Buddhist Nun's Water Treatment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anshan Iron And Steel Plant Bake Lucky Buddhist Nun's Water Treatment Co Ltd filed Critical Anshan Iron And Steel Plant Bake Lucky Buddhist Nun's Water Treatment Co Ltd
Priority to CN201510411944.2A priority Critical patent/CN105174498B/en
Publication of CN105174498A publication Critical patent/CN105174498A/en
Application granted granted Critical
Publication of CN105174498B publication Critical patent/CN105174498B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a kind of composite highly effective low-phosphorus corrosion scale inhibition agent of suitable low-hardness water, its constituent and mass percent are:17 alkenyl hydroxyethyl imidazole hyamines:15%~25%, copolymer of phosphono carboxylic acid:5%~15%, acrylic acrylate co-polymer of sulfonate:10%~20%, BTA:0.1%~1.5%, anhydrous zinc chloride 5%~15%, cosolvent:1%~3%, remaining composition is water.The present invention is applied to soft, high alkalinity, severe corrosive water quality, and basicity is less than 600mg/L, and corrosion and scale inhibition performance is excellent.The complexing agent of the present invention is lower compared with organophosphor phosphate and phosphoric acid ester medicament total phosphorus content, and total phosphorus content≤1.0mg/L in industrial discharge water, pollution-free also with biodegradable ability, more environmentally friendly.Cost of the present invention is low, easily compounding, and stability is good, and dosage is few.There is good concertedness between each component, stable performance, there is excellent corrosion and scale inhibition performance.

Description

The composite highly effective low-phosphorus corrosion scale inhibition agent and preparation method of a kind of suitable low-hardness water
Technical field
The present invention relates to the composite highly effective low-phosphorus corrosion resistance of water-treatment technology field, more particularly to a kind of suitable low-hardness water Dirty medicament and preparation method.
Background technology
The use of water is indispensable in the industrial production, and dosage is huge, in today of water resource increasingly scarcity, industrially Recirculating cooling water system is generally used, and along with the increase of recirculated water cycles of concentration, it may appear that fouling, corrosion and microorganism danger The problems such as evil, the serious problems such as the decline of heat exchange equipment efficiency, blocking, corrosion failure are caused, generally use is to add at present Water treatment agent suppresses corrosion and fouling, and organophosphor system medicament is most widely used.
Organophosphor system corrosion-mitigation scale-inhibition antisludging agent has the double action of corrosion-mitigation scale-inhibition and scale inhibition, and applicable water quality is extensive, still The total phosphorus scope of general organophosphor scale inhibition antisludging agent control causes total phosphorus content in water higher, is discharged into 6~8mg/L After environment, the eutrophication of water body can be caused, forms the harm such as " red tide ", final polluted water.China is at present to industry The total phosphorus content of discharge water, which is made, requires in terms of total phosphorus≤1.0mg/L (GB 13456-2012), so following low-phosphorous and without phosphorus Green medicament by be water treatment agent developing direction.
The content of the invention
It is an object of the invention to provide a kind of composite highly effective low-phosphorus corrosion scale inhibition agent of suitable low-hardness water and preparation side Method, the shortcomings that overcoming prior art, it is low-phosphorous it is green, there is excellent corrosion-mitigation scale-inhibition and scale inhibition and dispersion, suitable for low hard Degree, high alkalinity, the industrial circulating cooling water of severe corrosive.
To achieve the above object, the present invention is realized using following technical scheme:
A kind of composite highly effective low-phosphorus corrosion scale inhibition agent of suitable low-hardness water, its constituent and mass percent are: 17 alkenyl hydroxyethyl imidazole hyamines:15%~25%, copolymer of phosphono carboxylic acid:5%~15%, acrylic acid-acrylic Acid esters-co-polymer of sulfonate:10%~20%, BTA:0.1%~1.5%, anhydrous zinc chloride 5%~15%, hydrotropy Agent:1%~3%, remaining composition is water.
Cosolvent is dimethylformamide.
The preparation method of the composite highly effective low-phosphorus corrosion scale inhibition agent of a kind of suitable low-hardness water, at normal temperatures according to above-mentioned Proportioning, 17 alkenyl hydroxyethyl imidazole quinoline quaternary amines, copolymer of phosphono carboxylic acid, acrylic acid-acrylic ester-sulfonate are copolymerized Thing and water are added in reactor, stir 0.5h under rotating speed 150rpm speed afterwards, after solution is well mixed, are warming up to 40 DEG C -50 DEG C, adding anhydrous zinc chloride and BTA stirring is completely dissolved it, adds dimethylformamide and persistently stirs 0.8h, 1h-2h is incubated, cooling and standings after mixing, produces the present invention.
Compared with prior art, the beneficial effects of the invention are as follows:
1st, suitable for soft, high alkalinity, severe corrosive water quality, basicity is less than 600mg/L (with CaCO3Meter), scale inhibition and Corrosion and scale inhibition performance is excellent.
2nd, complexing agent of the invention is lower compared with organophosphor phosphate and phosphoric acid ester medicament total phosphorus content, and in industrial discharge Total phosphorus content≤1.0mg/L (in terms of total phosphorus) in water, it is pollution-free also with biodegradable ability, it is more environmentally friendly.
3rd, complexing agent cost of the invention is low, easily compounding, and stability is good, and dosage is few.
4th, pH value is applicable in the range of 6.5-9.0, and there is adaptive automatic control function.
5th, there is good concertedness between each component, stable performance, there is excellent corrosion and scale inhibition performance.
Embodiment
The present invention is described in detail below, it should be noted that the implementation of the present invention is not limited to following embodiment party Formula.
A kind of composite highly effective low-phosphorus corrosion scale inhibition agent of suitable low-hardness water, its constituent and mass percent are: 17 alkenyl hydroxyethyl imidazole hyamines:15%~25%, copolymer of phosphono carboxylic acid:5%~15%, acrylic acid-acrylic Acid esters-co-polymer of sulfonate:10%~20%, BTA:0.1%~1.5%, anhydrous zinc chloride 5%~15%, hydrotropy Agent:1%~3%, remaining composition is water.
17 alkenyl hydroxyethyl imidazole quinoline quaternary amines are the OED of Qinhuangdao triumph Chemical Co., Ltd. production, are the present invention In one of host, 17 alkenyl hydroxyethyl imidazole quinoline quaternary amines are a kind of high efficiency corrosion inhibiting scale retardants, not only with good life Thing degradation property, beneficial to environmental protection, also good heat-resistant stability, heat is not decomposed.Content in complexing agent is 15%- 25%, preferably 17%-23%.
The present invention substitutes organophosphor phosphate and phosphoric acid ester medicament using 17 alkenyl hydroxyethyl imidazole quinoline quaternary amines, when When metal contacts with acid medium, 17 alkenyl hydroxyethyl imidazole quinoline quaternary amines can adsorb forms unimolecule on the metal surface Film, in tight, uniform diaphragm.
Copolymer of phosphono carboxylic acid (POCA) is two of the host in the present invention, has excellent resistance calcium carbonate, calcium phosphate Dirty effect, good with conventional water treatment agent compatibility, synergistic effect is obvious.Content in complexing agent is 5%-15%, preferably 7%-13%.
Acrylic acid-acrylic ester-co-polymer of sulfonate is the DT-101 of Dong Tao Chemical Engineering Technologies Co., Ltd production, is this hair Three of host in bright, acrylic acid-acrylic ester-co-polymer of sulfonate are a kind of efficient scales for having corrosion and scale inhibition performance concurrently point Powder, suitable for high temperature, high ph-values, it is high-alkali under the conditions of use, content of the component in complexing agent is 10%-20%, preferably 13%-17%.
BTA (BTA) is a kind of nitrogen azole material, and its anion and cuprous ion forms a kind of insoluble The complex compound of stabilizer pole.This complex compound absorption on the metal surface, forms one layer of stable, inert diaphragm so that gold Category is protected.BTA (BTA) especially has good effect to suppressing copper corrosion, and to suppressing corrosion of carbon steel There is effect.
Anhydrous zinc chloride belongs to zinc salt, is a kind of conventional corrosion inhibiting and descaling agent, generally to be mixed with other types corrosion inhibiting and descaling agent Close and use, the content in complexing agent is 5%-15%, preferably 8%-13%.
Cosolvent selects dimethylformamide, to play solubilization, makes complexing agent be more easy to compound.
The preparation method of the composite highly effective low-phosphorus corrosion scale inhibition agent of a kind of suitable low-hardness water, at normal temperatures according to above-mentioned Proportioning, 17 alkenyl hydroxyethyl imidazole quinoline quaternary amines, copolymer of phosphono carboxylic acid, acrylic acid-acrylic ester-sulfonate are copolymerized Thing and water are added in reactor, stir 0.5h under rotating speed 150rpm speed afterwards, after solution is well mixed, are warming up to 40 DEG C -50 DEG C, adding anhydrous zinc chloride and BTA stirring is completely dissolved it, adds dimethylformamide and persistently stirs 0.8h, 1h-2h is incubated, cooling and standings after mixing, produces the present invention.
A kind of dosage of the composite highly effective low-phosphorus corrosion scale inhibition agent of suitable low-hardness water of the present invention is 30mg/L.
The composite highly effective low-phosphorus corrosion scale inhibition agent formula of three constituent contents is respectively configured according to the present invention, for chemically examining Room and field test, formula are as follows:
Formula 1:
It is prepared by compound low-phosphorus corrosion scale inhibition agent:17 alkenyl hydroxyethyl imidazole quinoline quaternary amines 18%, phosphono-carboxylic acids are common Polymers 12%, acrylic acid-acrylic ester-co-polymer of sulfonate 13%, anhydrous zinc chloride 11%, BTA 0.5%, diformazan Base formamide 2.5%, surplus are water.
Formula 2:
It is prepared by compound low-phosphorus corrosion scale inhibition agent:17 alkenyl hydroxyethyl imidazole quinoline quaternary amines 20%, phosphono-carboxylic acids are common Polymers 10%, acrylic acid-acrylic ester-co-polymer of sulfonate 15%, anhydrous zinc chloride 10%, BTA 0.8%, diformazan Base formamide 3%, surplus are water.
Formula 3:
It is prepared by compound low-phosphorus corrosion scale inhibition agent:17 alkenyl hydroxyethyl imidazole quinoline quaternary amines 23%, phosphono-carboxylic acids are common Polymers 8%, acrylic acid-acrylic ester-co-polymer of sulfonate 17%, anhydrous zinc chloride 8%, BTA 1.0%, dimethyl Formamide 1%, surplus are water.
Embodiment 1:Testing raw water quality is:PH 7.78, μ s/cm of Cond 179, the hard 90mg/L of total calcium are (with CaCO3Meter), Calcium hardness 50mg/L is (with CaCO3Meter), Cl-60mg/L, total alkalinity 80mg/L are (with CaCO3Meter).
Tested by 2.5 times of experiment raw water qualities of concentration, prepare calcium hardness 125mg/L (with CaCO3Meter), Cl-150mg/ L, total alkalinity 200mg/L is (with CaCO3Meter) tested, 40 DEG C of water temperature, complexing agent 30mg/L is respectively added, is pressed《Water treatment agent delays Lose measure -- the rotary hanging plate method of scale-inhibiting properties》(GB-T 18175-2000) standard performs, and result of the test is as follows.
Drawn through experiment and meet industrial circulating cooling water processing design rule in 2.5 times of several lower carbon steel lacing film corrosion rates of concentration The requirement of model (GB 50050--2007), PO in water4 3-Meet wanting for total phosphorus≤1.0mg/L of industrial discharge water (in terms of total phosphorus) Ask.
Embodiment two:
Testing raw water quality is:PH 7.82, μ s/cm of Cond 140, the hard 60mg/L of total calcium are (with CaCO3Meter), calcium hardness 40mg/L is (with CaCO3Meter), Cl-35mg/L, total alkalinity 61mg/L are (with CaCO3Meter).
Tested by 5 times of experiment raw water qualities of concentration, prepare calcium hardness 300mg/L (with CaCO3Meter), Cl-175mg/L、 Total alkalinity 305mg/L is (with CaCO3Meter), 40 DEG C of water temperature, complexing agent 30mg/L is respectively added, is pressed《Water treatment agent corrosion and scale inhibition performance Measure -- rotary hanging plate method》(GB-T 18175-2000) standard performs, and result of the test is as follows.
Drawn through experiment and still meet industrial circulating cooling water processing design in 5 times of several lower carbon steel lacing film corrosion rates of concentration The requirement of specification (GB 50050--2007), PO in water4 3-Meet total phosphorus≤1.0mg/L's of industrial discharge water (in terms of total phosphorus) It is required that.
Embodiment three:
It is applied to certain factory circulation water station from formula 2, it is 6800m that the system, which possesses water,3, quantity of circulating water 6500m3, it is System water quality be:PH 8.72, μ s/cm of Cond 877, the hard 360mg/L of total calcium are (with CaCO3Meter), calcium hardness 280mg/L is (with CaCO3 Meter), Cl-155mg/L, total alkalinity 275mg/L are (with CaCO3Meter).Compound low-phosphorus corrosion scale inhibition agent dosage 30mg/L, run 1 Month, carbon steel lacing film corrosion rate is 0.0203mm/a, PO in recirculated water4 3-(in terms of total phosphorus) daily detection total phosphorus≤1.0mg/ L, systems chiller deposit without carbonate scale, obtain good application effect.
A kind of composite highly effective low-phosphorus corrosion scale inhibition agent of suitable low-hardness water of the present invention has advantages below:
First, there is good concertedness so that composite drug has excellent corrosion-mitigation scale-inhibition and scale inhibition performance between each component Energy.
2nd, soft, high alkalinity, the recirculated cooling water of severe corrosive are applicable.
3rd, complexing agent component of the invention easily compounds, and stability is good, very convenient in operation and management, is advantageous to Ensure treatment effect.
4th, complexing agent of the invention is low-phosphorous environment-friendly medicament, and dosage is low, meets the total phosphorus content of industrial discharge water (in terms of total phosphorus)≤1.0mg/L (GB 13456-2012), belong to environmentally friendly medicament, low toxicity is pollution-free.

Claims (2)

1. the composite highly effective low-phosphorus corrosion scale inhibition agent of a kind of suitable low-hardness water, it is characterised in that its constituent and quality Percentage is:17 alkenyl hydroxyethyl imidazole quinoline quaternary amines 20%, copolymer of phosphono carboxylic acid 10%, acrylic acid-acrylic ester- Co-polymer of sulfonate 15%, anhydrous zinc chloride 10%, BTA 0.8%, dimethylformamide 3%, surplus are water;
The composite highly effective low-phosphorus corrosion scale inhibition agent is applied to the recirculated water of following water quality:It is pH 8.72, μ s/cm of Cond 877, total Calcium is firmly with CaCO3360mg/L, calcium hardness are counted with CaCO3Count 280mg/L, Cl-155mg/L, total alkalinity are with CaCO3Count 275mg/L;
The dosage of composite highly effective low-phosphorus corrosion scale inhibition agent is 30mg/L, and Testing index is that carbon steel lacing film corrosion rate is 0.0203mm/a, PO in recirculated water4 3-Daily detection total phosphorus≤1.0mg/L, systems chiller without carbonate scale deposit.
2. a kind of preparation method of the composite highly effective low-phosphorus corrosion scale inhibition agent of suitable low-hardness water described in claim 1, its Be characterised by, at normal temperatures according to said ratio, by 17 alkenyl hydroxyethyl imidazole quinoline quaternary amines, copolymer of phosphono carboxylic acid, Acrylic acid-acrylic ester-co-polymer of sulfonate and water are added in reactor, stir 0.5h under rotating speed 150rpm speed afterwards, After solution is well mixed, 40 DEG C -50 DEG C are warming up to, adding anhydrous zinc chloride and BTA stirring is completely dissolved it, Add dimethylformamide and persistently stir 0.8h, be incubated 1h-2h, cooling and standings after mixing, produce a kind of suitable low-hardness water Composite highly effective low-phosphorus corrosion scale inhibition agent.
CN201510411944.2A 2015-07-13 2015-07-13 The composite highly effective low-phosphorus corrosion scale inhibition agent and preparation method of a kind of suitable low-hardness water Active CN105174498B (en)