CN105154595A - Method for improving ductility and softness of tibe lamb skin - Google Patents
Method for improving ductility and softness of tibe lamb skin Download PDFInfo
- Publication number
- CN105154595A CN105154595A CN201510476555.8A CN201510476555A CN105154595A CN 105154595 A CN105154595 A CN 105154595A CN 201510476555 A CN201510476555 A CN 201510476555A CN 105154595 A CN105154595 A CN 105154595A
- Authority
- CN
- China
- Prior art keywords
- premium
- currency
- add
- sodium sulfate
- salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for improving ductility and softness of tibe lamb skin. Pretreatment is carried out on the tibe lamb skin through the steps of soaking washing, impurity removing, degreasing, pickling, softening of first time, tanning, neutralizing and softening of second time. Through of a preset number additives added in all the steps and the intercoordination and continuity of all the steps, the pretreated tibe lamb skin is soft in surface, bright in hair color, good in firmness of the hair surface and resistant to high temperature. Therefore, when the tibe lamb skin is perforated, it is guaranteed that the walls of extending and softening holes obtained through perforation are smooth, then a leather board of the tibe lamb skin has ductility, it is guaranteed that the leather board stretches out and draws back freely when bearing external fore, and the body of a consumer wearing a tibe lamb skin product has no strong sense of pressure.
Description
Technical field
The present invention relates to animal fur processing technique field, particularly a kind of method improving tibet lamp ductility and pliability.
Background technology
Sheep known for its fine thick wool multiplies and lives under vast Helan Mountain, bank of the torrential currents of the Yellow River, has exceeded centuries history, is the peculiar fur sheep kind treasured in Ningxia.Ningxia Tan Sheep skin is with its distinctive snappiness, heat retention, sinuousness and deeply favoring by domestic and international travelling trader.In recent years, along with the development of international fur processing technology, fur complete processing has had revolutionary breakthrough, and the Application Areas of fur is constantly expanded.
At present, the dermatotome complete processing of tibet lamp mainly contains the technique such as cutting, splicing, but due to the singularity of tibet lamp weave construction and fur, cannot promote ductility and the pliability of dermatotome.
Summary of the invention
The object of the present invention is to provide a kind of method improving tibet lamp ductility and pliability.
Improve a method for tibet lamp ductility and pliability, comprise the following steps:
Immersion is washed, and adds Soaking to obtain soaking solution, be then immersed in soaking solution by tibet lamp to normal-temperature water, and wherein, in soaking solution, the consumption of Soaking is add 1g Soaking in every premium on currency, and immersion duration is 16h;
Impurity elimination, Xiang Shuizhong adds hair detergent, washing powder to obtain impurity elimination solution, the tibet lamp soaked is placed on impurity elimination solution clean and utilize tsaoko machine, beam machine, fleshing machine to remove the foreign material on the fleece of the tibet lamp soaked and the slough on dermatotome, wherein, the consumption of hair detergent, washing powder adds in every premium on currency in hair detergent 3g, every premium on currency to add washing powder 2g, and water temperature controls at 40 DEG C ~ 50 DEG C;
Degreasing, to obtain skim soln after Xiang Shuizhong interpolation hair detergent, washing powder, tibet lamp after impurity elimination is put into skim soln and carries out degreasing, wherein, the consumption of hair detergent, washing powder is: add in every premium on currency in hair detergent 3g, every premium on currency and add washing powder 2g, water temperature controls at 40 DEG C ~ 50 DEG C, and degreasing time controls at 50 ~ 70min;
Rinsing, with the tibet lamp after clear water rinsing degreasing.Wherein, rinsing duration is 15 ~ 25min, and water temperature controls at 40 DEG C ~ 50 DEG C;
Pickling, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent to obtain pickling solutions, then the tibet lamp after rinsing is immersed in pickling solutions, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in formic acid 2g, every premium on currency and add permeate agent 0.5g, immersion duration is 24h, and water temperature controls at 35 DEG C ~ 40 DEG C;
First time is softening, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid to obtain tenderising soln, then the tibet lamp after pickling is immersed in tenderising soln, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in proteinase-10 .2g, every premium on currency and add sulfuric acid 1.5g, immersion duration is 24h, and water temperature controls at 35 DEG C ~ 40 DEG C;
Tanning, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent to obtain tanning solution, then the tibet lamp after softening is immersed in tanning solution, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in formic acid 5g, every premium on currency and add permeate agent 0.5g, immersion duration is 24h, and water temperature controls at 35 DEG C ~ 40 DEG C, and the PH of tanning solution is 8.2;
Neutralization, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), sulfuric acid, ammonium sulfate to obtain neutralization solution, then tanned tibet lamp is immersed in neutralization solution, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), sulfuric acid, ammonium sulfate is: add in every premium on currency in salt 20g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 30g, every premium on currency to add in sulfuric acid 1.5g, every premium on currency and add ammonium sulfate 0.5g, tanned tibet lamp is soaked 6 ~ 8h, and water temperature controls at 34 DEG C ~ 38 DEG C;
Second time is softening, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid to obtain tenderising soln, then the tibet lamp after neutralization is immersed in tenderising soln, after neutralizing treatment, the tibet lamp after softening is dried, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in proteinase-10 .2g, every premium on currency and add sulfuric acid 1.5g, immersion duration is 24h, water temperature controls at 35 DEG C ~ 40 DEG C, goes out skin and dry after the tibet lamp after neutralizing treatment is soaked 24h;
Extend softening, be laid in by tibet lamp and tailor in case, hole is softened in the extension of getting predetermined size and quantity from the dermatotome face of tibet lamp uniformly, and wherein the spacing between hole is softened in adjacent extension is 0.5 ~ 1cm.
Above-mentionedly improve in the method for tibet lamp ductility and pliability, washed by immersion, impurity elimination, degreasing, pickling, first time is softening, tanning, neutralization and second time sofening treatment step carry out pre-treatment to tibet lamp, the additive of the predetermined amount of the interpolation in each step and each step are coordinated mutually and continuity makes the space of a whole page of pretreated tibet lamp soft, hair color light, the stability of hair side is good, high temperature resistant, so when punching to tibet lamp, the hole wall that hole is softened in the extension that ensureing punches obtains is smooth-going, and then make the dermatotome of tibet lamp have ductility, ensure that dermatotome is capable of expansion and contraction when receiving External Force Acting, make the human consumer's health wearing tibet lamp goods without strong constriction.
Accompanying drawing explanation
Fig. 1 is the schema of the improvement tibet lamp ductility of a better embodiment and the method for pliability.
In figure: the method steps S500 ~ S510 improving tibet lamp ductility and pliability.
Embodiment
Referring to Fig. 1, improve the method for tibet lamp ductility and pliability, comprise the following steps:
Step S500, immersion is washed, and adds Soaking to obtain soaking solution, be then immersed in soaking solution by tibet lamp to normal-temperature water.Wherein, in soaking solution, the consumption of Soaking is add 1g Soaking in every premium on currency, and immersion duration is 16h.
Step S501, impurity elimination, Xiang Shuizhong adds hair detergent, washing powder to obtain impurity elimination solution, the tibet lamp soaked is placed on impurity elimination solution and cleans and utilize tsaoko machine, beam machine, fleshing machine to remove the foreign material on the fleece of the tibet lamp soaked and the slough on dermatotome.Wherein, the consumption of hair detergent, washing powder adds in every premium on currency in hair detergent 3g, every premium on currency to add washing powder 2g, and water temperature controls at 40 DEG C ~ 50 DEG C.
Step S502, degreasing, to obtain skim soln after Xiang Shuizhong interpolation hair detergent, washing powder, puts into skim soln by the tibet lamp after impurity elimination and carries out degreasing.Wherein, the consumption of hair detergent, washing powder is: add in every premium on currency in hair detergent 3g, every premium on currency and add washing powder 2g, water temperature controls at 40 DEG C ~ 50 DEG C, and degreasing time controls at 50 ~ 70min.
Step S503, rinsing, with the tibet lamp after clear water rinsing degreasing.Wherein, rinsing duration is 15 ~ 25min, and water temperature controls at 40 DEG C ~ 50 DEG C.
Step S504, pickling, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent to obtain pickling solutions, is then immersed in pickling solutions by the tibet lamp after rinsing.Wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in formic acid 2g, every premium on currency and add permeate agent 0.5g, immersion duration is 24h, and water temperature controls at 35 DEG C ~ 40 DEG C.
Step S505, first time is softening, and Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid to obtain tenderising soln, is then immersed in tenderising soln by the tibet lamp after pickling.Wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in proteinase-10 .2g, every premium on currency and add sulfuric acid 1.5g, immersion duration is 24h, and water temperature controls at 35 DEG C ~ 40 DEG C.
Step S506, tanning, Xiang Shuizhong add salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent to obtain tanning solution, then by soften after tibet lamp be immersed in tanning solution.Wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in formic acid 5g, every premium on currency and add permeate agent 0.5g, immersion duration is 24h, water temperature controls at 35 DEG C ~ 40 DEG C, and the PH of tanning solution is 8.2.
Step S507, neutralization, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), sulfuric acid, ammonium sulfate to obtain neutralization solution, is then immersed in neutralization solution by tanned tibet lamp.Wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), sulfuric acid, ammonium sulfate is: add in every premium on currency in salt 20g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 30g, every premium on currency to add in sulfuric acid 1.5g, every premium on currency and add ammonium sulfate 0.5g, tanned tibet lamp is soaked 6 ~ 8h, and water temperature controls at 34 DEG C ~ 38 DEG C.
Step S508, second time is softening, and Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid to obtain tenderising soln, is then immersed in tenderising soln by the tibet lamp after neutralization, is dried by the tibet lamp after softening after neutralizing treatment.Wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in proteinase-10 .2g, every premium on currency and add sulfuric acid 1.5g, immersion duration is 24h, water temperature controls at 35 DEG C ~ 40 DEG C, goes out skin and dry after the tibet lamp after neutralizing treatment is soaked 24h.
Step S509, chrome retanned, Xiang Shuizhong adds salt, chromium powder, sulfuric acid to obtain chrome retanned solution, by after softening for second time and the tibet lamp dried dry to obtain the good tibet lamp of pre-treatment after putting into the immersion of chrome retanned solution.Wherein, the consumption of salt, chromium powder, sulfuric acid is: add in every premium on currency in salt 35g, every premium on currency to add in chromium powder 6g, every premium on currency and add sulfuric acid 1g, and the PH of chrome retanned solution is 3.8 ~ 4.0, and immersion duration is 48h, and water temperature is 38 DEG C.If when tibet lamp is true qualities skin, above-mentioned steps S509 can omit.
Step S510, extend softening, be laid in by tibet lamp and tailor in case, hole is softened in the extension of getting predetermined size and quantity from the dermatotome face of tibet lamp uniformly, and wherein the spacing between hole is softened in adjacent extension is 0.5 ~ 1cm.Wherein, softening hole of extending is diameter is 0.4 ~ 0.6cm circular hole, and extending, softening hole can be also 0.1cm for width, length is the strip hole of 2cm.
Above-mentionedly improve in the method for tibet lamp ductility and pliability, washed by immersion, impurity elimination, degreasing, pickling, first time is softening, tanning, neutralization and second time sofening treatment step carry out pre-treatment to tibet lamp, the additive of the predetermined amount of the interpolation in each step and each step are coordinated mutually and continuity makes the space of a whole page of pretreated tibet lamp soft, hair color light, the stability of hair side is good, high temperature resistant, so when punching to tibet lamp, the hole wall that hole is softened in the extension that ensureing punches obtains is smooth-going, and then make the dermatotome of tibet lamp have ductility, ensure that dermatotome is capable of expansion and contraction when receiving External Force Acting, make the human consumer's health wearing tibet lamp goods without strong constriction.
Claims (3)
1. improve a method for tibet lamp ductility and pliability, comprise the following steps:
Immersion is washed, and adds Soaking to obtain soaking solution, be then immersed in soaking solution by tibet lamp to normal-temperature water, and wherein, in soaking solution, the consumption of Soaking is add 1g Soaking in every premium on currency, and immersion duration is 16h;
Impurity elimination, Xiang Shuizhong adds hair detergent, washing powder to obtain impurity elimination solution, the tibet lamp soaked is placed on impurity elimination solution clean and utilize tsaoko machine, beam machine, fleshing machine to remove the foreign material on the fleece of the tibet lamp soaked and the slough on dermatotome, wherein, the consumption of hair detergent, washing powder adds in every premium on currency in hair detergent 3g, every premium on currency to add washing powder 2g, and water temperature controls at 40 DEG C ~ 50 DEG C;
Degreasing, to obtain skim soln after Xiang Shuizhong interpolation hair detergent, washing powder, tibet lamp after impurity elimination is put into skim soln and carries out degreasing, wherein, the consumption of hair detergent, washing powder is: add in every premium on currency in hair detergent 3g, every premium on currency and add washing powder 2g, water temperature controls at 40 DEG C ~ 50 DEG C, and degreasing time controls at 50 ~ 70min;
Rinsing, with the tibet lamp after clear water rinsing degreasing, wherein, rinsing duration is 15 ~ 25min, and water temperature controls at 40 DEG C ~ 50 DEG C;
Pickling, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent to obtain pickling solutions, then the tibet lamp after rinsing is immersed in pickling solutions, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in formic acid 2g, every premium on currency and add permeate agent 0.5g, immersion duration is 24h, and water temperature controls at 35 DEG C ~ 40 DEG C;
First time is softening, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid to obtain tenderising soln, then the tibet lamp after pickling is immersed in tenderising soln, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in proteinase-10 .2g, every premium on currency and add sulfuric acid 1.5g, immersion duration is 24h, and water temperature controls at 35 DEG C ~ 40 DEG C;
Tanning, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent to obtain tanning solution, then the tibet lamp after softening is immersed in tanning solution, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), formic acid, permeate agent is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in formic acid 5g, every premium on currency and add permeate agent 0.5g, immersion duration is 24h, and water temperature controls at 35 DEG C ~ 40 DEG C, and the PH of tanning solution is 8.2;
Neutralization, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), sulfuric acid, ammonium sulfate to obtain neutralization solution, then tanned tibet lamp is immersed in neutralization solution, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), sulfuric acid, ammonium sulfate is: add in every premium on currency in salt 20g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 30g, every premium on currency to add in sulfuric acid 1.5g, every premium on currency and add ammonium sulfate 0.5g, tanned tibet lamp is soaked 6 ~ 8h, and water temperature controls at 34 DEG C ~ 38 DEG C;
Second time is softening, Xiang Shuizhong adds salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid to obtain tenderising soln, then the tibet lamp after neutralization is immersed in tenderising soln, after neutralizing treatment, the tibet lamp after softening is dried, wherein, the consumption of salt, Sodium sulfate anhydrous.min(99), proteolytic enzyme, sulfuric acid is: add in every premium on currency in salt 30g, every premium on currency to add in Sodium sulfate anhydrous.min(99) 40g, every premium on currency to add in proteinase-10 .2g, every premium on currency and add sulfuric acid 1.5g, immersion duration is 24h, water temperature controls at 35 DEG C ~ 40 DEG C, goes out skin and dry after the tibet lamp after neutralizing treatment is soaked 24h;
Extend softening, be laid in by tibet lamp and tailor in case, hole is softened in the extension of getting predetermined size and quantity from the dermatotome face of tibet lamp uniformly, and wherein the spacing between hole is softened in adjacent extension is 0.5 ~ 1cm.
2. the method improving tibet lamp ductility and pliability according to claim 1, is characterized in that: the diameter in softening hole of extending is 0.4 ~ 0.6cm.
3. the method improving tibet lamp ductility and pliability according to claim 1, is characterized in that: the width in softening hole of extending is 0.1cm, length is 2cm.