CN105153833A - Low baking water-based environment-friendly dip-coating primer for motor tricycle and preparation method of primer - Google Patents
Low baking water-based environment-friendly dip-coating primer for motor tricycle and preparation method of primer Download PDFInfo
- Publication number
- CN105153833A CN105153833A CN201510607697.3A CN201510607697A CN105153833A CN 105153833 A CN105153833 A CN 105153833A CN 201510607697 A CN201510607697 A CN 201510607697A CN 105153833 A CN105153833 A CN 105153833A
- Authority
- CN
- China
- Prior art keywords
- agent
- aqueous
- motor tricycle
- composite
- environmental protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses low baking water-based environment-friendly dip-coating primer for a motor tricycle and a preparation method of the primer. The primer is prepared from deionized water, a wetting agent, dispersant, neutralizer, preservative, defoamer, an anti-flash-rust agent, carbon black, phthalocyanine, titanium dioxide, iron oxide yellow color paste, barium sulfate, sericite, nanosilicon dioxide, anti-rust pigment, stabilizer, a coalescing agent, film-forming matter, a base material wetting agent, a thickening agent and surface auxiliaries. PVDC which is used for improving water resistance and heat resistance and is good in adhesive force serves as the film-forming matter to be matched with the environment-friendly anti-rust pigment and filler, the base material wetting agent, the imported water-based auxiliaries and other non-pollution auxiliaries, the low baking water-based environment-friendly dip-coating primer for the motor tricycle is prepared, the raw materials are easy to obtain, safe and environmentally friendly, the performance meets the requirements of the baking water-based environment-friendly dip-coating primer for the motor tricycle, and cost performance is high.
Description
Technical field
The invention belongs to chemical article field, be specifically related to low-temperature bake aqueous, environmental protective primer dipping and coating after the passivation of a kind of motor tricycle phosphatization, higher than traditional amino-stoving varnish cost performance, construction stability is good; Than electrophoretic paint save energy, price has superiority.
Background technology
PVDC is a kind of macromolecular material of barrier property excellence, resistance oxygen, and resistance is wet, resistance chloride ion permeability successful.Be not afraid of Phosphating Solution in addition.Traditional waterborne dip paint is water alcohol acid amino-stoving varnish such as, and storing temperature is high, and solvent is high, and the stability painted after being polluted by Phosphating Solution reduces even paint destruction and cannot use.The investment of electrocoating paint disposable apparatus is high, and the problem managed in practical application does not reach his due effect.Synthesized novel PVDC dispersion resin for this problem test of many times, done film forming matter with it, mediated water tolerance next through the test of hundreds of time, sticking power, the silver grey low-temperature bake aqueous, environmental protective primer dipping and coating of good heat resistance is supplied to client and gets the nod.
Summary of the invention
Goal of the invention: the invention provides a kind of motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating and preparation method thereof, its raw material is easy to get, requirement that safety and environmental protection, performance meet motor tricycle baking aqueous, environmental protective primer dipping and coating, cost performance is high.
Technical scheme: a kind of motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, described motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating is made up of according to parts by weight following component:
Deionized water 5-15 part;
Wetting agent 0.1-0.5 part
Dispersion agent 0.1-0.5 part
Neutralizing agent 0.2-0.6 part
Sanitas 0.1-0.3 part
Defoamer 0.1-0.6 part
Anti-sudden strain of a muscle rust agent 1-3 part
Carbon black 0.1-0.5 part
The blue or green blue 0.02-0.05 part of phthalein
Titanium dioxide 5-8 part
Iron oxide yellow mill base 0.5-1 part
Barium sulfate 2-7 part
Sericite 2-7 part
Nano silicon 1-3 part
Rust-stabilising pigment 3-8 part
Stablizer 1-4 part
Film coalescence aid 1-2 part
Filmogen 40-70 part
Substrate wetting agents 0.3-0.6 part
Thickening material 1-5 part
Surface modifier 0.1-0.5 part
As optimization: described aqueous promoter adopts aqueous dispersant 27000 or this FX-6000.2-0.5 part of byk-154 hamming one or composite wherein, wetting agent is 104E or this FX-365 of hamming, OP-100.1-0.5 part, neutralizing agent is 0.2-0.6 part, and sanitas is DF or potassium sorbate 0.1-0.3, defoamer is sieve ground sub-691,, 681F or 642,6460.1-0.6 part, anti-settling agent is A-200 or A-3000.2-1.7 part, stablizer PE/F871-4 part; The agent of anti-sudden strain of a muscle rust is 179 or h-101-3 part.
As optimization: described antirust color stuffing adopts titanium dioxide 5-8 part, carbon black 0.1-0.5 part, the blue or green blue 0.02-0.05 part of phthalein, iron oxide yellow mill base 0.5-1 part, barium sulfate 2-7 part, sericite 2-7 part, nano silicon 1-3 part, rust-stabilising pigment aluminium triphosphate or zinc phosphate, HALOX-391 one wherein or composite 3-8 part.
As optimization: described filmogen adopts acrylic acid modified vinyl multi-component copolymer vinylidene chloride emulsion, Gu containing being 54%.
As optimization: described film coalescence aid adopts one or more in alcohol ester 12, dipropylene glycol methyl ether, dipropylene.
As optimization: described substrate wetting agents adopts film coalescence aid alcohol ester 12 or butyl glycol ether propylene glycol phenylate, propylene glycol monomethyl ether one wherein or composite 1-2 part.
As optimization: described thickening material adopts HEC or xanthan gum or wilkinite or lh-400
As optimization: described substrate wetting agents adopts this W77 of hamming, the one in peaceful 165F or composite is declared in Guangdong.
As optimization: described surface modifier is FC-54 or BYK-3330.1-0.5 part one or composite wherein.
A preparation method for motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, comprises the steps:
(1) by deionized water 5 ~ 15 parts, wetting agent is 104E or this FX-365 of hamming, OP-100.1-0.5 part, dispersion agent 27000 or this FX-6000.2-0.5 part of byk-154 hamming one or composite wherein, neutralizing agent 0.2-0.6 part, sanitas is DF or potassium sorbate 0.1-0.3, defoamer is sieve ground sub-691, , 681F or 642, 6460.1-0.6 part is thrown in and disperse 5 minutes 500-600 rev/min in stainless steel scuffing of cylinder bore, add antirust color stuffing titanium dioxide 5-8 part again, carbon black 0.1-0.5 part, the blue or green blue 0.02-0.05 part of phthalein, iron oxide yellow mill base 0.5-1 part, barium sulfate 2-7 part, sericite 2-7 part, nano silicon 1-3 part, rust-stabilising pigment aluminium triphosphate or zinc phosphate, HALOX-391 one wherein or composite 3-8 part, stablizer PE/F871-4 part, the agent of anti-sudden strain of a muscle rust is 179 or h-101-3 part, film coalescence aid alcohol ester 12 or butyl glycol ether propylene glycol phenylate, propylene glycol monomethyl ether one wherein or composite 1-2 part, dispersed with stirring 30 points, rotating speed is 500-1200 rev/min, add water coolant with shredder and be ground to fineness less than 30 microns, temperature of charge controls below 45 degree,
(2) look for a stainless cylinder of steel again, add 40-70 part filmogen, add the finish paint slurry agitation 15 points of milled while stirring, speed 400-700 rev/min;
(3) add thickening material 1-5 part again, substrate wetting agents 0.3-0.6 part, surface modifier FC-54, BYK-3330.1-0.5 stir 15 points, speed 400-700 rev/min, and product indices detects qualified rear stirring to be terminated, 100 order filter screen filtration packagings.
Beneficial effect: the present invention is water-fast to improve, thermotolerance, the PVDC that sticking power is good is the antirust color stuffing that film forming matter is equipped with environmental protection, the non-harmful auxiliary agents such as substrate wetting agents, import aqueous promoter, be prepared into a kind of motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, the requirement that its raw material is easy to get, safety and environmental protection, performance meet motor tricycle baking aqueous, environmental protective primer dipping and coating, cost performance is high.
Embodiment
Below in conjunction with specific embodiment, the present invention will be described in detail.
Summary, a kind of motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, described motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating is made up of according to parts by weight following component:
Deionized water 5-15 part;
Wetting agent 0.1-0.5 part
Dispersion agent 0.1-0.5 part
Neutralizing agent 0.2-0.6 part
Sanitas 0.1-0.3 part
Defoamer 0.1-0.6 part
Anti-sudden strain of a muscle rust agent 1-3 part
Carbon black 0.1-0.5 part
The blue or green blue 0.02-0.05 part of phthalein
Titanium dioxide 5-8 part
Iron oxide yellow mill base 0.5-1 part
Barium sulfate 2-7 part
Sericite 2-7 part
Nano silicon 1-3 part
Rust-stabilising pigment 3-8 part
Stablizer 1-4 part
Film coalescence aid 1-2 part
Filmogen 40-70 part
Substrate wetting agents 0.3-0.6 part
Thickening material 1-5 part
Surface modifier 0.1-0.5 part.
Wherein, described aqueous promoter adopts aqueous dispersant 27000 or this FX-6000.2-0.5 part of byk-154 hamming one or composite wherein, and wetting agent is 104E or this FX-365, OP-100.1-0.5 part of hamming, neutralizing agent is 0.2-0.6 part, sanitas is DF or potassium sorbate 0.1-0.3, and defoamer is sieve ground sub-691,681F or 642,6460.1-0.6 part, anti-settling agent is A-200 or A-3000.2-1.7 part, stablizer PE/F871-4 part; The agent of anti-sudden strain of a muscle rust is 179 or h-101-3 part.
Described antirust color stuffing adopts titanium dioxide 5-8 part, carbon black 0.1-0.5 part, the blue or green blue 0.02-0.05 part of phthalein, iron oxide yellow mill base 0.5-1 part, barium sulfate 2-7 part, sericite 2-7 part, nano silicon 1-3 part, rust-stabilising pigment aluminium triphosphate or zinc phosphate, HALOX-391 one wherein or composite 3-8 part.
Described filmogen adopts acrylic acid modified vinyl multi-component copolymer vinylidene chloride emulsion, Gu containing being 54%.
Described film coalescence aid adopts one or more in alcohol ester 12, dipropylene glycol methyl ether, dipropylene.
Described substrate wetting agents adopts film coalescence aid alcohol ester 12 or butyl glycol ether propylene glycol phenylate, propylene glycol monomethyl ether one wherein or composite 1-2 part.
Described thickening material adopts HEC or xanthan gum or wilkinite or lh-400
Described substrate wetting agents adopts this W77 of hamming, the one in peaceful 165F or composite is declared in Guangdong.
Described surface modifier is FC-54 or BYK-3330.1-0.5 part one or composite wherein.
A preparation method for motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, comprises the steps:
(1) by deionized water 5 ~ 15 parts, wetting agent is 104E or this FX-365 of hamming, OP-100.1-0.5 part, dispersion agent 27000 or this FX-6000.2-0.5 part of byk-154 hamming one or composite wherein, neutralizing agent 0.2-0.6 part, sanitas is DF or potassium sorbate 0.1-0.3, defoamer is sieve ground sub-691, , 681F or 642, 6460.1-0.6 part is thrown in and disperse 5 minutes 500-600 rev/min in stainless steel scuffing of cylinder bore, add antirust color stuffing titanium dioxide 5-8 part again, carbon black 0.1-0.5 part, the blue or green blue 0.02-0.05 part of phthalein, iron oxide yellow mill base 0.5-1 part, barium sulfate 2-7 part, sericite 2-7 part, nano silicon 1-3 part, rust-stabilising pigment aluminium triphosphate or zinc phosphate, HALOX-391 one wherein or composite 3-8 part, stablizer PE/F871-4 part, the agent of anti-sudden strain of a muscle rust is 179 or h-101-3 part, film coalescence aid alcohol ester 12 or butyl glycol ether propylene glycol phenylate, propylene glycol monomethyl ether one wherein or composite 1-2 part, dispersed with stirring 30 points, rotating speed is 500-1200 rev/min, add water coolant with shredder and be ground to fineness less than 30 microns, temperature of charge controls below 45 degree,
(2) look for a stainless cylinder of steel again, add 40-70 part filmogen, add the finish paint slurry agitation 15 points of milled while stirring, speed 400-700 rev/min;
(3) add thickening material 1-5 part again, substrate wetting agents 0.3-0.6 part, surface modifier FC-54, BYK-3330.1-0.5 stir 15 points, speed 400-700 rev/min, and product indices detects qualified rear stirring to be terminated, 100 order filter screen filtration packagings.
Specific embodiment one:
A kind of motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, described motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating is made up of according to parts by weight following component:
Deionized water 19 parts;
Wetting agent 0.55 part
Dispersion agent 0.5 part
Neutralizing agent 0.2 part
Sanitas 0.1 part
Defoamer 0.2 part
The agent 2 parts of anti-sudden strain of a muscle rust
Carbon black 0.1148 part
Blue or green blue 0.0042 part of phthalein
Titanium dioxide 6.53 parts
Iron oxide yellow mill base 0.525 part
5 parts, barium sulfate
Sericite 5 parts
Nano silicon 1 part
Rust-stabilising pigment 6 parts
Stablizer 1 part
Film coalescence aid 2 parts
Filmogen 45 parts
Substrate wetting agents 0.3 part
Thickening material 4 parts
Surface modifier 0.5 part
A preparation method for motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, comprises the steps:
(1) by deionized water 19 parts, wetting agent is 104E or this FX-365 of hamming, OP-100.55 part, dispersion agent 27000 or this FX-6000.5 part of byk-154 hamming one or composite wherein, neutralizing agent 0.2 part, sanitas is DF or potassium sorbate 0.1 part, defoamer is sieve ground sub-691, , 681F or 642, throw in for 6460.2 parts and disperse 5 minutes 500-600 rev/min in stainless steel scuffing of cylinder bore, add antirust color stuffing titanium dioxide 6.53 parts again, carbon black 0.1148 part, blue or green blue 0.0042 part of phthalein, iron oxide yellow mill base 0.525 part, 5 parts, barium sulfate, sericite 5 parts, nano silicon 1 part, rust-stabilising pigment aluminium triphosphate or zinc phosphate, HALOX-391 one wherein or composite 6 parts, stablizer PE/F871 part, the agent of anti-sudden strain of a muscle rust is 179 or h-102 part, film coalescence aid alcohol ester 12 or butyl glycol ether propylene glycol phenylate, propylene glycol monomethyl ether one wherein or composite 2 parts, dispersed with stirring 30 points, rotating speed is 500-1200 rev/min, add water coolant with shredder and be ground to fineness less than 30 microns, temperature of charge controls below 45 degree,
(2) look for a stainless cylinder of steel again, add 45 parts of filmogens, add the finish paint slurry agitation 15 points of milled while stirring, speed 400-700 rev/min;
(3) add thickening material 4 parts again, substrate wetting agents 0.3 part, surface modifier FC-54, BYK-3330.5 part stirs 15 points, speed 400-700 rev/min, and product indices detects qualified rear stirring to be terminated, 100 order filter screen filtration packagings.
Specific embodiment two:
A kind of motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, described motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating is made up of according to parts by weight following component:
Deionized water 19 parts;
Wetting agent 0.55 part
Dispersion agent 0.5 part
Neutralizing agent 0.2 part
Sanitas 0.1 part
Defoamer 0.2 part
The agent 2 parts of anti-sudden strain of a muscle rust
Carbon black 0.1148 part
Blue or green blue 0.0042 part of phthalein
Titanium dioxide 6.53 parts
Iron oxide yellow mill base 0.525 part
7.5 parts, barium sulfate
Sericite 2.5 parts
Nano silicon 1 part
Rust-stabilising pigment 6 parts
Stablizer 1 part
Film coalescence aid 2 parts
Filmogen 40 parts
Substrate wetting agents 0.3 part
Thickening material 4 parts
Surface modifier 0.5 part
A preparation method for motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, comprises the steps:
(1) by deionized water 19 parts, wetting agent is 104E or this FX-365 of hamming, OP-100.55 part, dispersion agent 27000 or this FX-6000.5 part of byk-154 hamming one or composite wherein, neutralizing agent 0.2 part, sanitas is DF or potassium sorbate 0.1 part, defoamer is sieve ground sub-691, , 681F or 642, throw in for 6460.2 parts and disperse 5 minutes 500-600 rev/min in stainless steel scuffing of cylinder bore, add antirust color stuffing titanium dioxide 6.53 parts again, carbon black 0.1148 part, blue or green blue 0.0042 part of phthalein, iron oxide yellow mill base 0.525 part, 7.5 parts, barium sulfate, sericite 2.5 parts, nano silicon 1 part, rust-stabilising pigment aluminium triphosphate or zinc phosphate, HALOX-391 one wherein or composite 6 parts, stablizer PE/F871 part, the agent of anti-sudden strain of a muscle rust is 179 or h-102 part, film coalescence aid alcohol ester 12 or butyl glycol ether propylene glycol phenylate, propylene glycol monomethyl ether one wherein or composite 2 parts, dispersed with stirring 30 points, rotating speed is 500-1200 rev/min, add water coolant with shredder and be ground to fineness less than 30 microns, temperature of charge controls below 45 degree,
(2) look for a stainless cylinder of steel again, add 40 parts of filmogens, add the finish paint slurry agitation 15 points of milled while stirring, speed 400-700 rev/min;
(3) add thickening material 4 parts again, substrate wetting agents 0.3 part, surface modifier FC-54, BYK-3330.5 part stirs 15 points, speed 400-700 rev/min, and product indices detects qualified rear stirring to be terminated, 100 order filter screen filtration packagings.
It is below its technical indicator
Storage period, condition: the shady and cool dry place of 5-30 degree, 6 months quality guaranteed perioves.
The present invention is not limited to above-mentioned preferred forms; anyone can draw other various forms of products under enlightenment of the present invention; no matter but any change is done in its shape or structure; every have identical with the application or akin technical scheme, all drops within protection scope of the present invention.
Claims (9)
1. a motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating, is characterized in that: described motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating is made up of according to parts by weight following component:
Deionized water 5-15 part
Wetting agent 0.1-0.5 part
Dispersion agent 0.1-0.5 part
Neutralizing agent 0.2-0.6 part
Sanitas 0.1-0.3 part
Defoamer 0.1-0.6 part
Anti-sudden strain of a muscle rust agent 1-3 part
Carbon black 0.1-0.5 part
The blue or green blue 0.02-0.05 part of phthalein
Titanium dioxide 5-8 part
Iron oxide yellow mill base 0.5-1 part
Barium sulfate 2-7 part
Sericite 2-7 part
Nano silicon 1-3 part
Rust-stabilising pigment 3-8 part
Stablizer 1-4 part
Film coalescence aid 1-2 part
Filmogen 40-70 part
Substrate wetting agents 0.3-0.6 part
Thickening material 1-5 part
Surface modifier 0.1-0.5 part.
2. motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating according to claim 1, it is characterized in that: described aqueous promoter adopts aqueous dispersant 27000 or this FX-6000.2-0.5 part of byk-154 hamming one or composite wherein, wetting agent is 104E or this FX-365 of hamming, OP-100.1-0.5 part, neutralizing agent is 0.2-0.6 part, sanitas is DF or potassium sorbate 0.1-0.3, defoamer is sieve ground sub-691,681F or 642,6460.1-0.6 part, anti-settling agent is A-200 or A-3000.2-1.7 part, stablizer PE/F871-4 part; The agent of anti-sudden strain of a muscle rust is 179 or h-101-3 part.
3. motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating according to claim 1, it is characterized in that: described antirust color stuffing adopts titanium dioxide 5-8 part, carbon black 0.1-0.5 part, the blue or green blue 0.02-0.05 part of phthalein, iron oxide yellow mill base 0.5-1 part, barium sulfate 2-7 part, sericite 2-7 part, nano silicon 1-3 part, rust-stabilising pigment aluminium triphosphate or zinc phosphate, HALOX-391 one wherein or composite 3-8 part.
4. motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating according to claim 1, is characterized in that: described filmogen adopts acrylic acid modified vinyl multi-component copolymer vinylidene chloride emulsion, Gu containing being 54%.
5. motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating according to claim 1, is characterized in that: described film coalescence aid adopts film coalescence aid alcohol ester 12 or butyl glycol ether propylene glycol phenylate, propylene glycol monomethyl ether one wherein or composite 1-2 part.
6. motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating according to claim 1, is characterized in that: described substrate wetting agents adopts this W77 of hamming, the one in peaceful 165F or composite is declared in Guangdong.
7. motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating according to claim 1, is characterized in that: described thickening material adopts HEC or xanthan gum or wilkinite or lh-400.
8. motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating according to claim 1, is characterized in that: described surface modifier is FC-54 or BYK-3330.1-0.5 part one or composite wherein.
9. a preparation method for motor tricycle low-temperature bake aqueous, environmental protective primer dipping and coating according to claim 1, is characterized in that: comprise the steps:
(1) by deionized water 5 ~ 15 parts, wetting agent is 104E or this FX-365 of hamming, OP-100.1-0.5 part, dispersion agent 27000 or this FX-6000.2-0.5 part of byk-154 hamming one or composite wherein, neutralizing agent 0.2-0.6 part, sanitas is DF or potassium sorbate 0.1-0.3, defoamer is sieve ground sub-691, , 681F or 642, 6460.1-0.6 part is thrown in and disperse 5 minutes 500-600 rev/min in stainless steel scuffing of cylinder bore, add antirust color stuffing titanium dioxide 5-8 part again, carbon black 0.1-0.5 part, the blue or green blue 0.02-0.05 part of phthalein, iron oxide yellow mill base 0.5-1 part, barium sulfate 2-7 part, sericite 2-7 part, nano silicon 1-3 part, rust-stabilising pigment aluminium triphosphate or zinc phosphate, HALOX-391 one wherein or composite 3-8 part, stablizer PE/F871-4 part, the agent of anti-sudden strain of a muscle rust is 179 or h-101-3 part, film coalescence aid alcohol ester 12 or butyl glycol ether propylene glycol phenylate, propylene glycol monomethyl ether one wherein or composite 1-2 part, dispersed with stirring 30 points, rotating speed is 500-1200 rev/min, add water coolant with shredder and be ground to fineness less than 30 microns, temperature of charge controls below 45 degree,
(2) look for a stainless cylinder of steel again, add 40-70 part filmogen, add the finish paint slurry agitation 15 points of milled while stirring, speed 400-700 rev/min;
(3) add thickening material 1-5 part again, substrate wetting agents 0.3-0.6 part, surface modifier FC-54, BYK-3330.1-0.5 stir 15 points, speed 400-700 rev/min, and product indices detects qualified rear stirring to be terminated, 100 order filter screen filtration packagings.