CN105153723A - 一种环保无毒铅笔笔杆及其制备方法 - Google Patents
一种环保无毒铅笔笔杆及其制备方法 Download PDFInfo
- Publication number
- CN105153723A CN105153723A CN201510528709.3A CN201510528709A CN105153723A CN 105153723 A CN105153723 A CN 105153723A CN 201510528709 A CN201510528709 A CN 201510528709A CN 105153723 A CN105153723 A CN 105153723A
- Authority
- CN
- China
- Prior art keywords
- parts
- branch
- pencil
- toxic
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种环保无毒铅笔笔杆,涉及学习用品制备技术领域,包括以下原料制成:树枝60-80份、双氧水3-5份、群青6-8份、石蜡5-7份、碳酸钙10-20份、二丁酯8-10份、发泡剂3-5份、固化剂6-8份、保健浸泡液80-100份。本发明的有益效果是:本发明工艺流程简洁,原料配比合理,主原料中采用天然的杀菌药液进行处理,不仅本身无毒,同时具有杀菌消毒的作用,使得铅笔杆不仅具有健康的成分,无毒无害,使用效果明显,便于推广及使用。
Description
技术领域
本发明涉及学习用品制备技术领域,具体涉及一种环保无毒铅笔笔杆及其制备方法。
背景技术
铅笔,是用来进行美术绘画勾勒的主要用具,同时也是学生常用的学习用具之一,铅笔主要是由铅笔杆和铅笔芯组成的,铅笔杆用料主要包括木材和胶合剂,木材用于制作笔杆,要求纹理正直,结构细而匀,质软或稍软,略带脆性,少含树脂,吸湿性低,胀缩性小,不变形。主要有铅笔柏(红柏)、香杉、西达木、椴木、桤木等,胶合剂应有适当粘度、流动性和润湿性,硬化后胶层有韧性,对刀具损伤小,具有一定耐水、耐热、耐老化性能,常温下易固化,硬化时间短,无毒等,主要有动物胶、聚酯酸乙烯乳液、热熔胶等。由于铅笔杆在制作时,会涉及到使用大量的化学原料,因此本身具有一定的危害,长期使用,对人体有着一定的危害。
发明内容:
本发明所要解决的技术问题在于提供一种配方合理,健康安全的环保无毒铅笔笔杆及其制备方法。
本发明所要解决的技术问题采用以下技术方案来实现:
一种环保无毒铅笔笔杆,其特征在于:由以下组分的原料制成:
树枝60-80份、双氧水3-5份、群青6-8份、石蜡5-7份、碳酸钙10-20份、二丁酯8-10份、发泡剂3-5份、固化剂6-8份、保健浸泡液80-100份。
各原料的优选组分为:树枝70份、双氧水4份、群青7份、石蜡6份、碳酸钙15份、二丁酯9份、发泡剂4份、固化剂7份、保健浸泡液90份。
所述的发泡剂为石脑油或者硅酸钠。
所述的固化剂为氯化铵、草酸或甲酸。
所述的保健浸泡液包括:清水30-40份、黄柏3-5份、苦参2-4份、白鲜皮1-2份、野菊花2-3份、蒲公英5-6份;
制备方法为:上述所有中药材进行切段后放入煎锅中,然后将清水加入其中,迅速加热至100℃后,高温煎煮2-3h,在文火炖煮3-5h,冷却后去渣取汁,即可得到。
本发明的另一个目的是提供一种制备本发明环保无毒铅笔笔杆的方法,其特征在于,包括以下步骤:
1)选取符合标准的树枝;
2)在选取的树枝中挑选干燥并且无腐蚀的树枝,并将树枝粉碎,得到粉碎性树枝;
3)将原料中的粉碎性树枝放入保健浸泡液中浸泡20-24h,取出后,自然晾干,再重复进行浸泡,晾干后备用;
4)将原料中的双氧水、群青、石蜡、碳酸钙、二丁酯、发泡剂、固化剂和步骤3处理后的树枝进行混合搅拌,搅拌时间控制在40-45分钟之间;
5)将步骤4处理后的物料投入烘烤机中,烘烤直至含水量为30%后,取出,按照常规的方式后续加工即可得到。
本发明的有益效果是:本发明工艺流程简洁,原料配比合理,主原料中采用天然的杀菌药液进行处理,不仅本身无毒,同时具有杀菌消毒的作用,使得铅笔杆不仅具有健康的成分,无毒无害,使用效果明显,便于推广及使用。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1
树枝60kg、双氧水3kg、群青6kg、石蜡5kg、碳酸钙10kg、二丁酯8kg、石脑油3kg、氯化铵6kg、保健浸泡液80kg。
所述的保健浸泡液包括:清水30-40份、黄柏3-5份、苦参2-4份、白鲜皮1-2份、野菊花2-3份、蒲公英5-6份;
制备方法为:上述所有中药材进行切段后放入煎锅中,然后将清水加入其中,迅速加热至100℃后,高温煎煮2-3h,在文火炖煮3-5h,冷却后去渣取汁,即可得到。
本发明的制备方法为:
1)选取符合标准的树枝;
2)在选取的树枝中挑选干燥并且无腐蚀的树枝,并将树枝粉碎,得到粉碎性树枝;
3)将原料中的粉碎性树枝放入保健浸泡液中浸泡20-24h,取出后,自然晾干,再重复进行浸泡,晾干后备用;
4)将原料中的双氧水、群青、石蜡、碳酸钙、二丁酯、石脑油、氯化铵和步骤3处理后的树枝进行混合搅拌,搅拌时间控制在40-45分钟之间;
5)将步骤4处理后的物料投入烘烤机中,烘烤直至含水量为30%后,取出,按照常规的方式后续加工即可得到。
实施例2
树枝70份、双氧水4份、群青7份、石蜡6份、碳酸钙15份、二丁酯9份、硅酸钠4份、草酸7份、保健浸泡液90份;
所述的保健浸泡液包括:清水30-40份、黄柏3-5份、苦参2-4份、白鲜皮1-2份、野菊花2-3份、蒲公英5-6份;
制备方法为:上述所有中药材进行切段后放入煎锅中,然后将清水加入其中,迅速加热至100℃后,高温煎煮2-3h,在文火炖煮3-5h,冷却后去渣取汁,即可得到。
本发明的制备方法为:
1)选取符合标准的树枝;
2)在选取的树枝中挑选干燥并且无腐蚀的树枝,并将树枝粉碎,得到粉碎性树枝;
3)将原料中的粉碎性树枝放入保健浸泡液中浸泡20-24h,取出后,自然晾干,再重复进行浸泡,晾干后备用;
4)将原料中的双氧水、群青、石蜡、碳酸钙、二丁酯、硅酸钠、草酸和步骤3处理后的树枝进行混合搅拌,搅拌时间控制在40-45分钟之间;
5)将步骤4处理后的物料投入烘烤机中,烘烤直至含水量为30%后,取出,按照常规的方式后续加工即可得到。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (6)
1.一种环保无毒铅笔笔杆,其特征在于:由以下组分的原料制成:
树枝60-80份、双氧水3-5份、群青6-8份、石蜡5-7份、碳酸钙10-20份、二丁酯8-10份、发泡剂3-5份、固化剂6-8份、保健浸泡液80-100份。
2.根据权利要求1所述的一种环保无毒铅笔笔杆,其特征在于:各原料的优选组分为:树枝70份、双氧水4份、群青7份、石蜡6份、碳酸钙15份、二丁酯9份、发泡剂4份、固化剂7份、保健浸泡液90份。
3.根据权利要求1所述的一种低粉尘洁净铅笔芯,其特征在于:所述的发泡剂为石脑油或者硅酸钠。
4.根据权利要求1所述的一种低粉尘洁净铅笔芯,其特征在于:所述的固化剂为氯化铵、草酸或甲酸。
5.根据权利要求1所述的一种低粉尘洁净铅笔芯,其特征在于:所述的保健浸泡液包括:清水30-40份、黄柏3-5份、苦参2-4份、白鲜皮1-2份、野菊花2-3份、蒲公英5-6份;
制备方法为:上述所有中药材进行切段后放入煎锅中,然后将清水加入其中,迅速加热至100℃后,高温煎煮2-3h,在文火炖煮3-5h,冷却后去渣取汁,即可得到。
6.制备权利要求1或2中一种低粉尘洁净铅笔芯的方法,其特征在于,包括以下步骤:
1)选取符合标准的树枝;
2)在选取的树枝中挑选干燥并且无腐蚀的树枝,并将树枝粉碎,得到粉碎性树枝;
3)将原料中的粉碎性树枝放入保健浸泡液中浸泡20-24h,取出后,自然晾干,再重复进行浸泡,晾干后备用;
4)将原料中的双氧水、群青、石蜡、碳酸钙、二丁酯、发泡剂、固化剂和步骤3处理后的树枝进行混合搅拌,搅拌时间控制在40-45分钟之间;
5)将步骤4处理后的物料投入烘烤机中,烘烤直至含水量为30%后,取出,按照常规的方式后续加工即可得到。