CN105152623A - Durable and fireproof glass magnesium board and production method thereof - Google Patents
Durable and fireproof glass magnesium board and production method thereof Download PDFInfo
- Publication number
- CN105152623A CN105152623A CN201510410938.5A CN201510410938A CN105152623A CN 105152623 A CN105152623 A CN 105152623A CN 201510410938 A CN201510410938 A CN 201510410938A CN 105152623 A CN105152623 A CN 105152623A
- Authority
- CN
- China
- Prior art keywords
- parts
- plate
- magnesia
- durable
- magnesium chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a durable and fireproof glass magnesium board and a production method thereof, and belongs to the technical field of novel boards. The durable and fireproof glass magnesium board with the advantages of simple raw materials, wear resistance, excellent fireproof performances and no moisture absorbing and the production method thereof are provided. The durable and fireproof glass magnesium board comprises, by weight, 20-40 parts of magnesium chloride, 10-20 parts of light-burnt magnesia, 5-15 parts of calcium carbonate, 2-5 parts of silicon oxide, 1-3 parts of glass fibers, 0.5-1 part of phosphate and 50-60 parts of water. The preparation method of the glass magnesium board improves the quality stability of the glass magnesium board and prolongs the service life of the glass magnesium board.
Description
Technical field
The present invention relates to a kind of durable fire-proof glass fiber and magnesia plate and preparation method thereof, belong to board technical field.
Background technology
Glass fibre and magnesium cement board is with magnesium oxide, magnesium chloride, and water ternary system, be configured and add properties-correcting agent and make, the magnesium gelatinous material of stable performance, with neutral and alkali glass fiber net for strongthener, take light material as the novel uninflammability finishing material that weighting material is composited.Adopt special producing processes to form, have fire prevention, waterproof, tasteless, nontoxic, do not freeze, be stale-proof, do not split, constant, do not fire, high-strength light weight, easy construction, the feature such as long service life, in national like product, have the property of compound.
Glass magnesium plate can be used as wallboard, ceiling board, PLASTIC LAMINATED in life, water board, the uses such as tr, dado does in alternative wooden plywood, luffer boards, door-plate, the upholstery apparatus such as furniture, also can do ready mixed paint as required, clear water paint, and various types of plate face can be processed into, can be used for vault, the engineering of the wet environment such as people's air defense and mine simultaneously, can also with multiple lagging material compound, make composite insulating board.
At present, glass magnesium plate conventional on market, because material matching is unreasonable, often exists not wear-resistant, fire resistance poor problem, have a strong impact on the quality of product.
Summary of the invention
The present invention overcomes the deficiencies in the prior art, and technical problem to be solved is to provide that a kind of raw material is simple, wear-resistant, fire resistance is excellent and glass magnesium plate of nonhygroscopic anti-halogen and preparation method thereof.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is: a kind of durable fire-proof glass fiber and magnesia plate, comprises the component of following weight proportion: magnesium chloride 20-40 part, magnesia unslacked 10-20 part, calcium carbonate 5-15 part, silicon oxide 2-5 part, glass fibre 1-3 part, phosphoric acid salt 0.5-1 part, water 50-60 part.
As preferred a kind of durable fire-proof glass fiber and magnesia plate, comprise the component of following weight proportion: 33 parts, magnesium chloride, magnesia unslacked 15 parts, 11 parts, calcium carbonate, silicon oxide 3 parts, 2 parts, glass fibre, phosphoric acid salt 0.6 part, 55 parts, water.
A preparation method for durable fire-proof glass fiber and magnesia plate, mainly comprises following step: by magnesium chloride and water mixing and stirring, obtain magnesium chloride brine; In magnesium chloride brine, add magnesia unslacked, calcium carbonate, silicon oxide, glass fibre and phosphoric acid salt mix, obtain mixed slurry; Pour mixed slurry into mould, roll forming, obtain half-finished product plate; Half-finished product plate is dried, obtains glass magnesium plate.
Compared with prior art the present invention has following beneficial effect.
The present invention adds appropriate calcium carbonate and silicon oxide in the starting material of glass magnesium plate, adds the mobility of slurry, makes raw material be easy to mix, improves Drawing abillity.
Glass magnesium plate of the present invention is wear-resistant, fire resistance is excellent and nonhygroscopic anti-halogen, improves the quality stability of glass magnesium plate, extends the work-ing life of glass magnesium plate.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
A kind of durable fire-proof glass fiber and magnesia plate, comprises the component of following weight proportion: 20 parts, magnesium chloride, magnesia unslacked 20 parts, 5 parts, calcium carbonate, silicon oxide 5 parts, 1 part, glass fibre, phosphoric acid salt 1 part, 50 parts, water.
Embodiment 2
A kind of durable fire-proof glass fiber and magnesia plate, comprises the component of following weight proportion: 33 parts, magnesium chloride, magnesia unslacked 15 parts, 11 parts, calcium carbonate, silicon oxide 3 parts, 2 parts, glass fibre, phosphoric acid salt 0.6 part, 55 parts, water.
Embodiment 3
A kind of durable fire-proof glass fiber and magnesia plate, comprises the component of following weight proportion: 40 parts, magnesium chloride, magnesia unslacked 10 parts, 15 parts, calcium carbonate, silicon oxide 2 parts, 3 parts, glass fibre, phosphoric acid salt 0.5 part, 60 parts, water.
Embodiment 4
A kind of durable fire-proof glass fiber and magnesia plate, comprises the component of following weight proportion: 23 parts, magnesium chloride, magnesia unslacked 17 parts, 11 parts, calcium carbonate, silicon oxide 3 parts, 2 parts, glass fibre, phosphoric acid salt 0.7 part, 55 parts, water.
Embodiment 5
A kind of durable fire-proof glass fiber and magnesia plate, comprises the component of following weight proportion: 33 parts, magnesium chloride, magnesia unslacked 17 parts, 11 parts, calcium carbonate, silicon oxide 4 parts, 2 parts, glass fibre, phosphoric acid salt 0.6 part, 51 parts, water.
In above-mentioned all embodiments, the preparation method of durable fire-proof glass fiber and magnesia plate, mainly comprises following step: by magnesium chloride and water mixing and stirring, obtain magnesium chloride brine; In magnesium chloride brine, add magnesia unslacked, calcium carbonate, silicon oxide, glass fibre and phosphoric acid salt mix, obtain mixed slurry; Pour mixed slurry into mould, roll forming, obtain half-finished product plate; Half-finished product plate is dried, obtains glass magnesium plate.
The present invention can summarize with other the specific form without prejudice to spirit of the present invention or principal character.Therefore, no matter from which point, above-mentioned embodiment of the present invention all can only be thought explanation of the present invention and can not limit invention, claims indicate scope of the present invention, and scope of the present invention is not pointed out in above-mentioned explanation, therefore, any change in the implication suitable with claims of the present invention and scope, all should think to be included in the scope of claims.
Claims (3)
1. a durable fire-proof glass fiber and magnesia plate, is characterized in that, comprises the component of following weight proportion: magnesium chloride 20-40 part, magnesia unslacked 10-20 part, calcium carbonate 5-15 part, silicon oxide 2-5 part, glass fibre 1-3 part, phosphoric acid salt 0.5-1 part, water 50-60 part.
2. the durable fire-proof glass fiber and magnesia plate of one according to claim 1, is characterized in that, comprise the component of following weight proportion: 33 parts, magnesium chloride, magnesia unslacked 15 parts, 11 parts, calcium carbonate, silicon oxide 3 parts, 2 parts, glass fibre, phosphoric acid salt 0.6 part, 55 parts, water.
3. the preparation method of a kind of durable fire-proof glass fiber and magnesia plate according to claim 1 and 2, is characterized in that, comprise following step:
A. by magnesium chloride and water mixing and stirring, magnesium chloride brine is obtained;
B. in magnesium chloride brine, add magnesia unslacked, calcium carbonate, silicon oxide, glass fibre and phosphoric acid salt mix, obtain mixed slurry;
C. pour mixed slurry into mould, roll forming, obtain half-finished product plate;
D. half-finished product plate is dried, obtain glass magnesium plate.