CN105132761A - Aluminium alloy - Google Patents
Aluminium alloy Download PDFInfo
- Publication number
- CN105132761A CN105132761A CN201510594207.0A CN201510594207A CN105132761A CN 105132761 A CN105132761 A CN 105132761A CN 201510594207 A CN201510594207 A CN 201510594207A CN 105132761 A CN105132761 A CN 105132761A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminium
- aluminium alloy
- zirconium
- cobalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses aluminium alloy, which mainly comprises new aluminium and waste aluminium; a certain amount of silicon, zirconium, cobalt, copper, magnesium, chromium and other metal elements are added; the waste aluminium is utilized, so that the resource waste is reduced, and the investment cost of a manufacturer is reduced; since some metal elements are added, the manufactured aluminium alloy is excellent in performance, is suitable for use and is worthy of generalization.
Description
Technical field
The invention belongs to technical field of aluminum alloy technology, be specifically related to a kind of aluminium alloy.
Background technology
The develop rapidly of industrial economy, increasing to the demand of Welded structural part, the usage quantity of aluminium alloy is increasing, and consequent aluminium scrap also gets more and more, usual at present wearing and tearing or obsolete aluminium alloy after use directly to be abandoned, cause a large amount of wastings of resources, very unfortunate, therefore, need to consider how to be used by aluminium scrap, reduce the wasting of resources.
Summary of the invention
In order to solve the deficiencies in the prior art, the invention provides a kind of aluminium alloy, new aluminium and aluminium scrap is mainly comprised in this aluminium alloy, and add the metallic elements such as a certain amount of silicon, zirconium, cobalt, copper, magnesium, chromium, by being used by aluminium scrap, reduce the wasting of resources, and reduce producer's cost of investment, and add some metallic elements wherein, make the aluminium alloy capability excellence of newly making, be suitable for using.
For solving the problem, the present invention specifically by the following technical solutions:
A kind of aluminium alloy, is characterized in that, comprise the component of following weight part: silicon 6-8 part, zirconium 1.0-2.0 part, cobalt 1.0-2.0 part, copper 0.8-2.0 part, magnesium 1.5-2.0 part, chromium 0.7-1.0 part, new aluminium 40-60 part and aluminium scrap 100-180 part.
Aforesaid a kind of aluminium alloy, is characterized in that, comprises the component of following weight part: silicon 6.5-7.8 part, zirconium 1.2-1.9 part, cobalt 1.0-1.8 part, copper 1.0-1.8 part, magnesium 1.5-1.7 part, chromium 0.7-0.9 part, new aluminium 40-55 part and aluminium scrap 150-180 part.
Aforesaid a kind of aluminium alloy, is characterized in that, comprises the component of following weight part: silicon 6.5 parts, zirconium 1.2 parts, cobalt 1.0 parts, copper 1.0 parts, 1.5 parts, magnesium, chromium 0.7 part, 40 parts, new aluminium and aluminium scrap 150 parts.
Aforesaid a kind of aluminium alloy, is characterized in that, comprises the component of following weight part: silicon 6.9 parts, zirconium 1.5 parts, cobalt 1.5 parts, copper 1.2 parts, 1.5 parts, magnesium, chromium 0.7 part, 40 parts, new aluminium and aluminium scrap 160 parts.
Aforesaid a kind of aluminium alloy, is characterized in that, comprises the component of following weight part: silicon 7.2 parts, zirconium 1.7 parts, cobalt 1.5 parts, copper 1.3 parts, 1.6 parts, magnesium, chromium 0.8 part, 50 parts, new aluminium and aluminium scrap 170 parts.
Aforesaid a kind of aluminium alloy, is characterized in that, comprises the component of following weight part: silicon 7.8 parts, zirconium 1.9 parts, cobalt 1.8 parts, copper 1.8 parts, 1.7 parts, magnesium, chromium 0.9 part, 55 parts, new aluminium and aluminium scrap 180 parts.
Beneficial effect of the present invention: a kind of aluminium alloy provided by the invention, new aluminium and aluminium scrap is mainly comprised in this aluminium alloy, and add the metallic elements such as a certain amount of silicon, zirconium, cobalt, copper, magnesium, chromium, by aluminium scrap is used, reduce the wasting of resources, and reduce producer's cost of investment, and add some metallic elements wherein, make the aluminium alloy capability excellence of newly making, be suitable for using.
Embodiment
Embodiment 1:
A kind of aluminium alloy, comprises the component of following weight part: silicon 6.5 parts, zirconium 1.2 parts, cobalt 1.0 parts, copper 1.0 parts, 1.5 parts, magnesium, chromium 0.7 part, 40 parts, new aluminium and aluminium scrap 150 parts.
Embodiment 2:
A kind of aluminium alloy, comprises the component of following weight part: silicon 6.9 parts, zirconium 1.5 parts, cobalt 1.5 parts, copper 1.2 parts, 1.5 parts, magnesium, chromium 0.7 part, 40 parts, new aluminium and aluminium scrap 160 parts.
Embodiment 3:
A kind of aluminium alloy, comprises the component of following weight part: silicon 7.2 parts, zirconium 1.7 parts, cobalt 1.5 parts, copper 1.3 parts, 1.6 parts, magnesium, chromium 0.8 part, 50 parts, new aluminium and aluminium scrap 170 parts.
Embodiment 4:
A kind of aluminium alloy, comprises the component of following weight part: silicon 7.8 parts, zirconium 1.9 parts, cobalt 1.8 parts, copper 1.8 parts, 1.7 parts, magnesium, chromium 0.9 part, 55 parts, new aluminium and aluminium scrap 180 parts.
New aluminium and aluminium scrap is mainly comprised in this aluminium alloy, and add the metallic elements such as a certain amount of silicon, zirconium, cobalt, copper, magnesium, chromium, by aluminium scrap is used, reduce the wasting of resources, and reduce producer's cost of investment, and add some metallic elements wherein, make the aluminium alloy capability excellence of newly making, be suitable for using.
More than show and describe ultimate principle of the present invention, principal character and advantage.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (6)
1. an aluminium alloy, is characterized in that, comprises the component of following weight part: silicon 6-8 part, zirconium 1.0-2.0 part, cobalt 1.0-2.0 part, copper 0.8-2.0 part, magnesium 1.5-2.0 part, chromium 0.7-1.0 part, new aluminium 40-60 part and aluminium scrap 100-180 part.
2. a kind of aluminium alloy according to claim 1, is characterized in that, comprises the component of following weight part: silicon 6.5-7.8 part, zirconium 1.2-1.9 part, cobalt 1.0-1.8 part, copper 1.0-1.8 part, magnesium 1.5-1.7 part, chromium 0.7-0.9 part, new aluminium 40-55 part and aluminium scrap 150-180 part.
3. a kind of aluminium alloy according to claim 2, is characterized in that, comprises the component of following weight part: silicon 6.5 parts, zirconium 1.2 parts, cobalt 1.0 parts, copper 1.0 parts, 1.5 parts, magnesium, chromium 0.7 part, 40 parts, new aluminium and aluminium scrap 150 parts.
4. a kind of aluminium alloy according to claim 2, is characterized in that, comprises the component of following weight part: silicon 6.9 parts, zirconium 1.5 parts, cobalt 1.5 parts, copper 1.2 parts, 1.5 parts, magnesium, chromium 0.7 part, 40 parts, new aluminium and aluminium scrap 160 parts.
5. a kind of aluminium alloy according to claim 2, is characterized in that, comprises the component of following weight part: silicon 7.2 parts, zirconium 1.7 parts, cobalt 1.5 parts, copper 1.3 parts, 1.6 parts, magnesium, chromium 0.8 part, 50 parts, new aluminium and aluminium scrap 170 parts.
6. a kind of aluminium alloy according to claim 2, is characterized in that, comprises the component of following weight part: silicon 7.8 parts, zirconium 1.9 parts, cobalt 1.8 parts, copper 1.8 parts, 1.7 parts, magnesium, chromium 0.9 part, 55 parts, new aluminium and aluminium scrap 180 parts.