CN105132194A - Cleaning agent for clearing oxide layer from surface of diesel engine oil tank processing mold - Google Patents
Cleaning agent for clearing oxide layer from surface of diesel engine oil tank processing mold Download PDFInfo
- Publication number
- CN105132194A CN105132194A CN201510610291.0A CN201510610291A CN105132194A CN 105132194 A CN105132194 A CN 105132194A CN 201510610291 A CN201510610291 A CN 201510610291A CN 105132194 A CN105132194 A CN 105132194A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide layer
- cleaning agent
- oil tank
- clearing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of mechanical processing, in particular to a cleaning agent for clearing an oxide layer from the surface of a diesel engine oil tank processing mold. The cleaning agent is prepared from 15 parts of diethanol amine, 15 parts of dimethylbenzenesulfonic acid sodium salt, 5 parts of citric acid, 2 parts of flavoxanthin, 15 parts of sodium ethylene diamine tetracetate and 48 parts of water. The cleaning agent for clearing the oxide layer from the surface of the diesel engine oil tank processing mold has the advantages that the recipe design is reasonable; the oxide layer clearing efficiency is high; particularly, a small amount of plant groundsel (Senecio scandens Buch.-Ham) extraction ingredient that is, flavoxanthin is added; the cleaning efficiency of the cleaning agent can be obviously improved, so that the oxide layer on the surface of the mold can be thoroughly cleared.
Description
Technical field
The present invention relates to Machining Technology field, specifically relating to a kind of clean-out system for removing diesel oil tank processing mold surface oxide layer.
Background technology
Mould be in industrial production in order to injection moulding, blowing, extrude, various mould and instrument that the method such as die casting or forging forming, smelting, punching press obtains desired product.In brief, mould is used to the instrument of formed article, and this instrument is made up of various part, and different moulds is made up of different parts.It realizes the processing of article profile mainly through the change of institute's formed material physical condition.Have the title of " mother of industry ".
Blank is made to become the instrument of the product having specified shape and size under external force.Be widely used in stamping-out, die forging, cold-heading, extruding, metallic sintered products compacting, pressure die casting, and in the compression moulding of goods such as engineering plastics, rubber, pottery or the formed machining of injection moulding.Mould has specific profile or cavity shape, and the outline shape that application has cutting edge can make blank be separated (stamping-out) by skeletal lines shape.Application cavity shape can make blank obtain corresponding three-dimensional shape.Mould generally comprises dynamic model and cover half (or punch and die) two parts, the two partable.Take out product time separately, make blank inject mold cavity when closing up and be shaped.Mould is precision tool, complex-shaped, bears the expansive force of blank, all has higher requirements to structural strength, rigidity, surface hardness, surfaceness and working accuracy, and the developmental level of die production is one of important symbol of machinofacture level.
The processing mold of diesel oil tank, as the one in the above-mentioned mould mentioned, it is of wide application.Due to the increase along with its access times, there is some greases and zone of oxidation in the surface of mould, therefore, mould needs periodic maintenance, to remove degrease and zone of oxidation.Existing clean-out system for removing above-mentioned substance and treatment process, the defects such as ubiquity complex process, what is more important, these clean-out systems coordinate corresponding surface treatment method to be cannot be thoroughly for the removal of zone of oxidation.This has just had a strong impact on reusing of mould, and serious conditions can cause thoroughly scrapping of mould, therefore virtually adds the cost of manufacturing enterprise.
Summary of the invention
For the technical problem existed in prior art, the object of the present invention is to provide a kind of clean-out system for removing diesel oil tank processing mold surface oxide layer, for achieving the above object, present invention employs following technical scheme:
For removing a clean-out system for diesel oil tank processing mold surface oxide layer, be made up of the component of following weight part:
15 parts, diethanolamine 15 parts of acid dimethyl sodium
Citric acid 5 parts of flavoxanthins 2 parts
48 parts, sodium ethylene diamine tetracetate 15 parts of water.
Beneficial effect of the present invention shows:
1) clean-out system, used in surface treatment method, its formulating of recipe is reasonable, remove zone of oxidation efficiency high, particularly with the addition of extract component---the flavoxanthin of a small amount of plant squaw weed (Herba Senecionis Scandentis), the cleaning efficiency of clean-out system can be significantly improved, the zone of oxidation of die surface is thoroughly removed.
2), the preparation method of clean-out system, by the method for progressively adding, the solubility property between each material can not only be improved, the possibility of particle agglomeration can also be avoided, the removing oxide layer function of clean-out system is promoted significantly.
3), the surface treatment method of mould, operating procedure is succinct, focuses on clean-out system soaking step, by the formula of appropriate design clean-out system, thus the zone of oxidation realizing die surface is removed quickly and efficiently, then improve the recycling degree of mould, reduce the production cost of enterprise.
Embodiment
Below with reference to embodiment, the present invention is described in detail.But; embodiment content is only citing made for the present invention and explanation; affiliated those skilled in the art make various amendment to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from the design of invention or surmount this scope as defined in the claims, protection scope of the present invention all should be belonged to.
One, the composition of clean-out system
15 parts, diethanolamine 15 parts of acid dimethyl sodium
Citric acid 5 parts of flavoxanthins 2 parts
48 parts, sodium ethylene diamine tetracetate 15 parts of water.
Two, the preparation method of clean-out system is:
First in container, add 15 parts of diethanolamine and 15 parts of water, stir 5 minutes; Then slowly add 5 parts of citric acids, limit edged stirs, and stirs 10 minutes after interpolation; Then slowly add 15 parts of acid dimethyl sodium and 15 parts of water, limit edged stirs, and stirs 15 minutes after interpolation; Then slowly add 2 parts of flavoxanthins, limit edged stirs, and stirs 5 minutes after interpolation; Finally add 15 parts of sodium ethylene diamine tetracetates and 18 parts of water fast, stir 30 minutes.
Three, for removing the clean-out system of diesel oil tank processing mold surface oxide layer
Step 1., use that absorbent cotton is sticky to be got ethyl acetate and clean die surface, then with dry cloth, mould to be dried.
Step 2., the mould after drying put into the clean-out system being heated to 45 DEG C in advance soak 30 minutes.
Step 3., pull out rear water rinse until the pH value of wash-down water returns to neutrality.
Step 4., polishing die surface, then carry out anodizing to it, anodized processing parameter is: temperature is 35 DEG C, voltage is risen to 10V in 25 minutes and keeps 15 minutes, then in 10 minutes, voltage is risen to 40V and keeps 5 minutes.
Step 5., pull rear water out and rinse until the pH value of wash-down water returns to neutrality, then dry.
Claims (1)
1., for removing a clean-out system for diesel oil tank processing mold surface oxide layer, it is characterized in that being made up of the component of following weight part:
15 parts, diethanolamine 15 parts of acid dimethyl sodium
Citric acid 5 parts of flavoxanthins 2 parts
48 parts, sodium ethylene diamine tetracetate 15 parts of water.