CN105130266A - 一种复合型水泥助磨剂及其水泥 - Google Patents

一种复合型水泥助磨剂及其水泥 Download PDF

Info

Publication number
CN105130266A
CN105130266A CN201510600732.9A CN201510600732A CN105130266A CN 105130266 A CN105130266 A CN 105130266A CN 201510600732 A CN201510600732 A CN 201510600732A CN 105130266 A CN105130266 A CN 105130266A
Authority
CN
China
Prior art keywords
parts
cement
grinding aid
composite
cement grinding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510600732.9A
Other languages
English (en)
Inventor
叶飚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Lu Jia Bridge Survey And Design Co Ltd
Original Assignee
Guangxi Lu Jia Bridge Survey And Design Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Lu Jia Bridge Survey And Design Co Ltd filed Critical Guangxi Lu Jia Bridge Survey And Design Co Ltd
Priority to CN201510600732.9A priority Critical patent/CN105130266A/zh
Publication of CN105130266A publication Critical patent/CN105130266A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种复合型水泥助磨剂及其水泥，属于水泥制造领域。所述水泥助磨剂包括如下重量份数的原料：羟乙基纤维素6～12份、三聚磷酸钠2～6份、甲酸钙1～5份、聚乙二醇3～9份、不饱和聚酯树脂2～6份、二乙醇单异丙醇胺2～8份、木质素4～8份、羟乙基二亚乙基三胺2～6份和腐植酸钠1～5份。同时，本发明还公开了一种包含如上所述复合型水泥助磨剂的水泥。本发明的复合型水泥助磨剂，掺量低、增强效果好，能够改善水泥性能和台时产量，降低水泥生产的成本，本发明的水泥，熟料配比少，可减少环境污染，节约矿产资源。

Description

一种复合型水泥助磨剂及其水泥
技术领域
本发明涉及一种复合型水泥助磨剂及其水泥，属于水泥制造领域。
背景技术
水泥是人类生活和社会生产中不可缺少的一种建筑材料，其使用范围广，用量大，素有“建筑工业的粮食之称”。但是，水泥生产工业污染大，能源消耗大。为了节能降耗，最佳途径就是在粉磨过程中添加水泥助磨剂，一方面，水泥助磨剂能够提高水泥磨机的台时产量，从而直接降低了粉磨电耗；另一方面，水泥助磨剂还可以激发工业废渣的活性，降低水泥熟料的使用量，从而节省了因生产水泥熟料而造成的煤、电消耗，并降低了大气污染物的排放，提高了工业废渣的利用效率，使其资源化效率提高，在实现“节能”效果的同时，也达到了“减排”的目的。
目前我国助磨剂产品一直普遍存在的组分单一、成本高昂、产品质量稳定性差、对工艺条件适应性不佳等缺陷影响助磨剂的推广应用，因此亟需通过试验研究，开发一类具备助磨效果优异、成本低廉、产品性能稳定、普适性高兼具改善水泥物理性能、激发混合材活性、提高混合材掺量的多功能复合助磨剂。
发明内容
本发明的目的是弥补现有技术的不足，提供一种复合型水泥助磨剂及其水泥。本发明的复合型水泥助磨剂，掺量低、增强效果好，能够改善水泥性能和台时产量，降低水泥生产的成本，本发明的水泥，熟料配比少，可减少环境污染，节约矿产资源。
本发明解决上述技术问题的技术方案如下：一种复合型水泥助磨剂，包括如下重量份数的原料：羟乙基纤维素6～12份、三聚磷酸钠2～6份、甲酸钙1～5份、聚乙二醇3～9份、不饱和聚酯树脂2～6份、二乙醇单异丙醇胺2～8份、木质素4～8份、羟乙基二亚乙基三胺2～6份和腐植酸钠1～5份。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，包括如下重量份数的原料：羟乙基纤维素9份、三聚磷酸钠4份、甲酸钙3份、聚乙二醇6份、不饱和聚酯树脂4份、二乙醇单异丙醇胺5份、木质素6份、羟乙基二亚乙基三胺4份和腐植酸钠3份。
一种包含如上所述复合型水泥助磨剂的水泥。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，所述助磨剂的质量为水泥质量的0.04～0.1wt％。
进一步，所述助磨剂的质量为水泥质量的0.07wt％。
本发明的有益效果是：
(1)本发明的复合型水泥助磨剂，掺量低、增强效果好，能够改善水泥性能和台时产量，降低水泥生产的成本。
(2)采用本发明的复合型水泥助磨剂生产的水泥，熟料配比少，可减少环境污染，节约矿产资源。
(3)本发明的价格低廉、生产工艺简单、成本低，适合规模化生产。
具体实施方式
以下结合具体实施例对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1：
一种复合型水泥助磨剂，包括如下重量份数的原料：羟乙基纤维素6份、三聚磷酸钠6份、甲酸钙1份、聚乙二醇9份、不饱和聚酯树脂2份、二乙醇单异丙醇胺8份、木质素4份、羟乙基二亚乙基三胺6份和腐植酸钠1份。
一种包含如上任一项所述复合型水泥助磨剂的水泥，所述助磨剂的质量为水泥质量的0.04wt％。
实施例2：
一种复合型水泥助磨剂，包括如下重量份数的原料：羟乙基纤维素9份、三聚磷酸钠4份、甲酸钙3份、聚乙二醇6份、不饱和聚酯树脂4份、二乙醇单异丙醇胺5份、木质素6份、羟乙基二亚乙基三胺4份和腐植酸钠3份。
一种包含如上任一项所述复合型水泥助磨剂的水泥，所述助磨剂的质量为水泥质量的0.07wt％。
实施例3：
一种复合型水泥助磨剂，包括如下重量份数的原料：羟乙基纤维素12份、三聚磷酸钠2份、甲酸钙5份、聚乙二醇3份、不饱和聚酯树脂6份、二乙醇单异丙醇胺2份、木质素8份、羟乙基二亚乙基三胺2份和腐植酸钠5份。
一种包含如上任一项所述复合型水泥助磨剂的水泥，所述助磨剂的质量为水泥质量的0.1wt％。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (5)

1.一种复合型水泥助磨剂，其特征在于，包括如下重量份数的原料：羟乙基纤维素6～12份、三聚磷酸钠2～6份、甲酸钙1～5份、聚乙二醇3～9份、不饱和聚酯树脂2～6份、二乙醇单异丙醇胺2～8份、木质素4～8份、羟乙基二亚乙基三胺2～6份和腐植酸钠1～5份。
2.根据权利要求1所述的一种复合型水泥助磨剂，其特征在于，包括如下重量份数的原料：羟乙基纤维素9份、三聚磷酸钠4份、甲酸钙3份、聚乙二醇6份、不饱和聚酯树脂4份、二乙醇单异丙醇胺5份、木质素6份、羟乙基二亚乙基三胺4份和腐植酸钠3份。
3.一种包含权利要求1或2所述复合型水泥助磨剂的水泥。
4.根据权利要求3所述的水泥，其特征在于，所述助磨剂的质量为水泥质量的0.04～0.1wt％。
5.根据权利要求4所述的水泥，其特征在于，所述助磨剂的质量为水泥质量的0.07wt％。
CN201510600732.9A 2015-09-18 2015-09-18 一种复合型水泥助磨剂及其水泥 Pending CN105130266A (zh)