CN105128453A - Precious metal frosted mirror surface copy printing method and flake - Google Patents
Precious metal frosted mirror surface copy printing method and flake Download PDFInfo
- Publication number
- CN105128453A CN105128453A CN201510504815.8A CN201510504815A CN105128453A CN 105128453 A CN105128453 A CN 105128453A CN 201510504815 A CN201510504815 A CN 201510504815A CN 105128453 A CN105128453 A CN 105128453A
- Authority
- CN
- China
- Prior art keywords
- noble metal
- printing
- polyester resin
- minute surface
- imitative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a precious metal frosted mirror surface copy printing method and a flake. The precious metal frosted mirror surface copy printing method comprises following steps: (1) corresponding printing templates are prepared based on imagines, patterns, or characters to be printed; (2) one side surface of a transparent polyester resin rubber flake is coated with a hot melt adhesive used for adhesion of metal materials, and the other side surface is subjected to printing with the printing templates obtained in step (1) and printing ink, and solidification of the printing ink is carried out rapidly; and (3) two transparent polyester resin rubber flakes obtained via step (2) are glued onto the two sides of a double-mirror surface precious metal product with the hot melt adhesive, and thermocompression bonding is carried out. The invention also discloses products obtained via the precious metal frosted mirror surface copy printing method. According to the precious metal frosted mirror surface copy printing method, conventional die is not used; production cost is reduced; production speed is accelerated; and large-size products can be produced.
Description
Technical field
The present invention relates to noble metal processing technique field, especially a kind of noble metal frosted minute surface imitative print technique and thin slice.
Background technology
Under nowadays economic development carries out situation fast, many people have had the hobby of collection noble metal, and one is to preserve value, and another noble metal itself also has reserve value.On market, noble metal is generally all made into pattern, and the making of these patterns uses traditional mould punching mode in the prior art, first makes the mould of corresponding pattern, uses machine punching press in the thin version of noble metal afterwards, produces corresponding artistic effect.
Use mould to produce in prior art, cost is higher; Mould, owing to being in use easily out of shape, making mould just need to eliminate or finishing at the certain number of times of use, adds financial cost and time cost; Due to the restriction of die size, the product size for compacting is general all less, cannot realize the production of large-size product.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, propose a kind of noble metal frosted minute surface imitative print technique and thin slice, easy and simple to handle, cost is low, and efficiency is high.
In order to realize foregoing invention object, the invention provides following technical scheme: a kind of noble metal frosted minute surface imitates print technique, comprises the following steps:
(1), according to the picture pattern that will make or printing stencil corresponding to word production;
, can the PUR of bonded metal material with coating on transparent polyester resin film one side, another side uses step printing stencil (1) and printing-ink print, rapid curing printing-ink;
(3) the polyester resin film, by two pieces of steps (2) produced, is bonded in noble metal both sides, bimirror face with PUR face, hot pressing laminating process.
Preferably, step (1) in, printing stencil is offset printing PS plate, knitmesh printing forme, gravure cylinder steel plate or flexo plate.
Preferably, step (2) in, polyester resin film stock thickness is 20 μm ~ 500 μm; Hot melt adhesive layer thickness is 50 μm ~ 100 μm.
Preferably, step (3) in, noble metal is the sheet of thickness 6 μm ~ 100 μm.
Preferably, this precious metal sheets is proof gold sheet or fine silver sheet.
Preferably, step (3) in, hot pressing binding temperature is 90 DEG C ~ 120 DEG C.
Preferably, step (2) in, printing-ink is frosted UV ink.
Preferably, ultraviolet photo-curing is cured as.
Present invention also offers a kind of noble metal frosted minute surface imitative print thin slice adopting above-mentioned manufacture craft to obtain, its technical scheme is: comprise printing ink layer, polyester resin film layers, hot melt adhesive layer and noble metal lamella, the both sides of noble metal lamella set gradually described hot melt adhesive layer and described polyester resin film layers respectively, and the lateral surface of described polyester resin film layers arranges described printing ink layer.
Compared with prior art, the present invention has the following advantages: do not re-use traditional mould, reduce production cost; Speed of production is fast; Large-sized product can be produced.
Accompanying drawing explanation
Fig. 1 is the structural representation that a kind of noble metal frosted minute surface provided by the invention imitates print thin slice.
Fig. 2 is the flow chart that a kind of noble metal frosted minute surface provided by the invention imitates print technique.
Detailed description of the invention
Describe the present invention below in conjunction with accompanying drawing, the description of this part is only exemplary and explanatory, should not have any restriction to protection scope of the present invention.
The imitative print of a kind of noble metal frosted minute surface as shown in Figure 1 thin slice, be made up of noble metal lamella 1, two hot melt adhesive layers 2, two polyester resin film layers 3 and printing ink layer 4, the both sides of noble metal lamella 1 set gradually hot melt adhesive layer 2, polyester resin film layers 3 respectively, and printing ink layer 4 is printed on the lateral surface of polyester resin film layers 3; According to use needs, printing ink layer 4 can be set the lateral surface of two polyester resin film layers 3 is one or more.
The thickness of described noble metal lamella 1 is 6 μm ~ 100 μm, and the rubberised layer thickness of described PUR is 50 μm ~ 100 μm, and the thickness of described polyester resin film layers 3 is 20 μm ~ 500 μm.Described printing ink layer 4 can also republish various pattern and character, reach more colourful effect to make printed patterns.Through the test of our great many of experiments material, preferably, the thickness of described noble metal lamella 1 is 50 μm, and the rubberised layer thickness of described PUR is 75 μm, and the thickness of described polyester resin film layers 3 is 300 μm.
This product has the following advantages: do not re-use traditional mould punching for the frosted pattern on noble metal, and use mode of printing to realize pattern effect, reduce production cost, and speed of production is fast, can produce large-sized product.
Your noble metal frosted minute surface above-mentioned imitates print technique, comprises the steps:
S101: adopt cut line software or other existing front picture and text process software, the picture pattern that will make or word arrange and are made into color separation file.Wherein, design is needed to manifest frosted metal-like part in color separation file, be divided into separately printing special edition; Design being needed the part hollow out manifesting metallic mirror surface, staying when printing white.Subsequently color separation file is exported printing stencil in CTP platemaking machine, this printing stencil can be offset printing PS plate, knitmesh printing forme, gravure cylinder steel plate or flexo plate.
S102: select high grade of transparency polyester resin (PET) film and coating can bonded metal material PUR, wherein the thickness of polyester resin (PET) film is 20 μm ~ 500 μm, the rubberised layer thickness of PUR is 50 μm ~ 100 μm, PUR requires the colloid high grade of transparency, without dregs, is coated with evenly, enters without any dust.
S103: by transparent for two panels polyester resin (PET) film glue in the face of the monolateral bonding in glue face, and cut into the size corresponding with printed patterns.
S104: use the printing stencil having made output and the printing-ink selected especially, polyester resin (PET) film after having cut prints, preferably uses frosted UV ink to print.In printing process, ink by carrying out the solidification of rapid ultraviolet linear light, to ensure prolonged nondiscolouring, wear-resisting, damage resistant, again at the various pattern and character of printing-ink printed thereon, need can also reach more colourful effect to make printed patterns simultaneously.
The proof gold thin slice in S105: make noble metal thin slice, especially bimirror face or fine silver thin slice, the sheet thickness of making is 6 μm ~ 100 μm.The noble metal thin slice completed is clamped in the middle of polyester resin (PET) film be completed for printing, namely between the PUR face in the middle of two-layer polyester resin (PET) film, carry out the process of hot pressing attaching process, make two-layer polyester resin (PET) film fit into the entirety of " three-in-one " completely with the proof gold mediated or fine silver silver thin slice.Binding temperature is between 90 DEG C ~ 120 DEG C.
After having fitted, complete the imitative print technique of noble metal frosted minute surface.
By using above method: after the thin slice of triad completes, the place of transparent PET film hollow out blank has then showed the mirror effect of gold and silver thin slice completely thoroughly, the place of frosted ink then shows the mute sand face effect as shown after metal mold pressing, with the visual effect of direct pressing on noble metal face, completely the same.Meanwhile, the PET film of outer surface plays good protection effect to gold and silver thin slice again.Avoid oxidation and stained.And when needs carry out collection use to precious metal sheets, as long as light PET film.Under fired state, PET film can after-flame voluntarily, and the proof gold silver strip in three-in-one thin slice can at all nondestructively take out.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (10)
1. the imitative print technique of noble metal frosted minute surface, comprises the following steps:
(1), according to the picture pattern that will make or printing stencil corresponding to word production;
(2), on transparent polyester resin film one side coating can the PUR of bonded metal material, another side uses step printing stencil (1) and printing-ink print, rapid curing printing-ink;
(3), with two pieces of steps (2) polyester resin film, be bonded in noble metal both sides, bimirror face with PUR face, hot pressing laminating process.
2. the imitative print technique of noble metal frosted minute surface as claimed in claim 1, is characterized in that: step (1) in, printing stencil is offset printing PS plate, knitmesh printing forme, gravure cylinder steel plate or flexo plate.
3. the imitative print technique of noble metal frosted minute surface as claimed in claim 1, is characterized in that: step (2) in, polyester resin film stock thickness is 20 μm ~ 500 μm; Hot melt adhesive layer thickness is 50 μm ~ 100 μm.
4. the imitative print technique of noble metal frosted minute surface as claimed in claim 1, is characterized in that: step (3) in, noble metal is the sheet of thickness 6 μm ~ 100 μm.
5. noble metal frosted minute surface imitates print technique as claimed in claim 4, it is characterized in that: this precious metal sheets is proof gold sheet or fine silver sheet.
6. the imitative print technique of noble metal frosted minute surface as claimed in claim 1, is characterized in that: step (3) in, hot pressing binding temperature is 90 DEG C ~ 120 DEG C.
7. the imitative print technique of noble metal frosted minute surface as claimed in claim 1, is characterized in that: step (2) in, printing-ink is frosted UV ink.
8. noble metal frosted minute surface imitates print technique as claimed in claim 7, it is characterized in that: be cured as ultraviolet photo-curing.
9. a noble metal frosted minute surface imitative print thin slice, it is characterized in that: comprise printing ink layer, polyester resin film layers, hot melt adhesive layer and noble metal lamella, the both sides of noble metal lamella set gradually described hot melt adhesive layer and described polyester resin film layers respectively, and the lateral surface of described polyester resin film layers arranges described printing ink layer.
10. noble metal frosted minute surface is imitative as claimed in claim 9 prints thin slice, it is characterized in that, the thickness of described noble metal lamella is 6 μm ~ 100 μm, and the thickness of described hot melt adhesive layer is 50 μm ~ 100 μm, and the thickness of described polyester resin film layers is 20 μm ~ 500 μm.