CN105113230A - Multifunctional wall cloth coating for decoration and preparation method of multifunctional wall cloth coating - Google Patents
Multifunctional wall cloth coating for decoration and preparation method of multifunctional wall cloth coating Download PDFInfo
- Publication number
- CN105113230A CN105113230A CN201510620807.XA CN201510620807A CN105113230A CN 105113230 A CN105113230 A CN 105113230A CN 201510620807 A CN201510620807 A CN 201510620807A CN 105113230 A CN105113230 A CN 105113230A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass fraction
- wall paper
- decorative decoration
- paper coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a multifunctional wall cloth coating for decoration. The multifunctional wall cloth coating for decoration consists of the following components in part by mass: 46-52 parts of azodicarbonamide, 50-54 parts of cobalt iso-octoate, 46-50 parts of dicyandiamidine phosphate, 50-54 parts of titanium dioxide, 46-50 parts of toluene diisocyanate, 50-54 parts of isocyanate, 46-50 parts of polyether-tribasic alcohol, 52-56 parts of seaweed gel salt, 46-50 parts of methanesulfonic acid, 50-54 parts of acetyl trioctyl citrate, 46-50 parts of butyronitrile methacrylate, 50-54 parts of permethrin, 46-50 parts of nanocomposite antibacterial plastic masterbatch, 50-54 parts of sodium glutamate, 46-50 parts of carnauba wax, 50-54 parts of salicylanilide, 46-50 parts of tetrabutyl titanate, 50-54 parts of triethoxyisobutylsilane and 1000-2000 parts of water. The multifunctional wall cloth coating for decoration has excellent flame retardancy, acid and alkali resistance, waterproofness and anti-bacterial property, and is suitable to be used in the field of various buildings in needs of indoor and outdoor decoration; and performance of products is improved.
Description
Technical field
The present invention relates to a kind of multifunction decorative decoration wall paper coating and preparation method thereof, belong to interior decoration decoration technical field.
Background technology
Wall paper is the fabric of paper metope.Be base fabric with cotton, and on base fabric, impose stamp or embossing embossment, also have and be made into large jacquard weave, grain pattern used mostly is geometric figure and ramage.In order to make wall paper have fire-retardant, waterproof, the function such as antibacterial, need at wall paper surface coating coatings.Coating is that coating once applies obtained solid-state continuous film, is to protect, and insulation, the objects such as decoration use, coat on wall paper matrix and obtain plastic sheet.
Summary of the invention
The object of the present invention is to provide a kind of multifunction decorative decoration wall paper coating and preparation method thereof, to realize the function of multifunction decorative decoration wall paper coating better.
To achieve these goals, technical scheme of the present invention is as follows.
Wall paper coating is used in a kind of multifunction decorative decoration, be made up of the component of following mass fraction: Celogen Az 48 ~ 52 parts, cobalt iso-octoate 50 ~ 54 parts, guanyl-urea-phosphate 46 ~ 50 parts, titanium dioxide 50 ~ 54 parts, toluene-2,4-diisocyanate 46 ~ 50 parts, isocyanates 50 ~ 54 parts, polyether-tribasic alcohol 46 ~ 50 parts, algin salt 52 ~ 56 parts, pyrovinic acid 46 ~ 50 parts, citric acid acetyl three monooctyl ester 50 ~ 54 parts, the positive fourth of methacrylic acid 46 ~ 50 parts, Permethrin 50 ~ 54 parts, nano composite antibacterial plastic master batch 46 ~ 50 parts, sodium glutamate 50 ~ 54 parts, Brazil wax 46 ~ 50 parts, salicylanilide 50 ~ 54 parts, butyl titanate 46 ~ 50 parts, isobutyl triethoxy silane 50 ~ 54 parts, 1000 ~ 2000 parts, water.
Further, above-mentioned multifunction decorative decoration wall paper coating, be made up of the component of following mass fraction: Celogen Az 48 parts, cobalt iso-octoate 50 parts, guanyl-urea-phosphate 46 parts, titanium dioxide 50 parts, toluene-2,4-diisocyanate 46 parts, isocyanates 50 parts, polyether-tribasic alcohol 46 parts, algin salt 52 parts, pyrovinic acid 46 parts, citric acid acetyl three monooctyl ester 50 parts, the positive fourth of methacrylic acid 46 parts, Permethrin 50 parts, nano composite antibacterial plastic master batch 46 parts, sodium glutamate 50 parts, Brazil wax 46 parts, salicylanilide 50 parts, butyl titanate 46 parts, isobutyl triethoxy silane 50 parts, 1000 parts, water.
Further, above-mentioned multifunction decorative decoration wall paper coating, be made up of the component of following mass fraction: Celogen Az 50 parts, cobalt iso-octoate 52 parts, guanyl-urea-phosphate 48 parts, titanium dioxide 52 parts, toluene-2,4-diisocyanate 48 parts, isocyanates 52 parts, polyether-tribasic alcohol 48 parts, algin salt 54 parts, pyrovinic acid 48 parts, citric acid acetyl three monooctyl ester 52 parts, the positive fourth of methacrylic acid 48 parts, Permethrin 52 parts, nano composite antibacterial plastic master batch 48 parts, sodium glutamate 52 parts, Brazil wax 48 parts, salicylanilide 52 parts, butyl titanate 48 parts, isobutyl triethoxy silane 52 parts, 1500 parts, water.
Further, above-mentioned multifunction decorative decoration wall paper coating, be made up of the component of following mass fraction: Celogen Az 52 parts, cobalt iso-octoate 54 parts, guanyl-urea-phosphate 50 parts, titanium dioxide 54 parts, toluene-2,4-diisocyanate 50 parts, isocyanates 54 parts, polyether-tribasic alcohol 50 parts, algin salt 56 parts, pyrovinic acid 50 parts, citric acid acetyl three monooctyl ester 54 parts, the positive fourth of methacrylic acid 50 parts, Permethrin 54 parts, nano composite antibacterial plastic master batch 50 parts, sodium glutamate 54 parts, Brazil wax 50 parts, salicylanilide 54 parts, butyl titanate 50 parts, isobutyl triethoxy silane 54 parts, 2000 parts, water.
Further, above-mentioned multifunction decorative decoration wall paper preparation method for coating step is as follows:
(1) Celogen Az of described mass fraction, guanyl-urea-phosphate, titanium dioxide, toluene-2,4-diisocyanate, isocyanates, polyether-tribasic alcohol, algin salt, pyrovinic acid, citric acid acetyl three monooctyl ester, the positive fourth of methacrylic acid, Permethrin, sodium glutamate, Brazil wax, salicylanilide, butyl titanate, isobutyl triethoxy silane are added in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min;
(2) add the nano composite antibacterial plastic master batch of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the cobalt iso-octoate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix rear obtained this product.
Above-mentioned each component function is as follows:
(1) Celogen Az: a kind of white or pale yellow powder, nontoxic, odorless, nonflammable, there is self-extinguishment.Be dissolved in alkali, be insoluble to gasoline, alcohol, benzene, pyridine and water.The blowing agent commonly used in the industry, can be used for the production such as Yoga mat, rubber soles, to increase the elasticity of product.
(2) cobalt iso-octoate: purple liquid, the main drier being used as paint, ink, the curing accelerator of unsaturated polyester resin, PVC stabilizer, polymerisation catalysts etc.
(3) guanyl-urea-phosphate: they have the right synergistic effect of collaborative resistance containing N, P ignition-proof element, have good flame retardant effect for fiber-like material.For fiberboard, glued board fire-retardant.
(4) titanium dioxide: a kind of white inorganic pigment, has nontoxic, best opacity, best whiteness and brightness.Be widely used in the industry such as coating, plastics, papermaking, printing-ink, chemical fibre, rubber, cosmetics.Its fusing point is very high, is also used to manufacture fireproof glass, glaze, enamel, potter's clay, resistant to elevated temperatures experimental ware etc.
(5) toluene-2,4-diisocyanate: colourless or light yellow clear liquid, has pungent odor.Water insoluble, be dissolved in acetone, ether.Be mainly used in polyurethane products, comprise foamed plastics, polyurethane coating, polyurethane rubber; Polyimide fiber and adhesive etc. also have some to apply.
(6) isocyanates: this product is the important intermediate of organic synthesis, can be made into a series of carbamate insecticides, bactericide, herbicide, also for improvement of the water proofing property of plastics, fabric, leather etc.; Can be used for the polyurethane foam plastics, rubber, elastic fibers, coating, adhesive, synthetic leather, imitation wood etc. that synthesize a series of function admirable.
(7) polyether-tribasic alcohol: colourless or pale yellow transparent thick liquid, slightly bitter taste, be insoluble in water, is soluble in the organic solvent such as ethanol, toluene.
(8) algin salt: in thickening property, stability, gelling, conformality, film shaped property etc., there is significant advantage, and there is unique health care, the also main raw material of Chang Zuowei skin protection cosmetics.
(9) pyrovinic acid: colourless or micro-brown oil liquid is solid under low temperature, higher boiling strong acid.Water-soluble, alcohol and ether release a large amount of heat, are insoluble to alkane, benzene, toluene etc., do not decompose boiling water, heat alkali liquid, have strong corrosion effect to metallic iron, copper and lead etc.As dehydrating agent, paint solidification promoter, fibre finish, solvent, alkanisation, esterification and polymerisation catalysts.
(10) citric acid acetyl three monooctyl ester: this product is colourless transparent oil liquid.Cold resistance is good, and volatility is minimum.Can be used as the plasticizer of polyvinyl chloride, vinyl chloride copolymer, also can be used as the stabilizing agent of polyvinylidene chloride.This product is nontoxic plasticizer, can be used for nontoxic PVC granulation, the soft toy of children, medical product, food packaging articles, coating and printing ink industry etc.
(11) the positive fourth of methacrylic acid: the liquid colourless, there is sweet taste and ester smell, water insoluble, miscible in alcohol, ether, be dissolved in most organic solvent.For organic synthesis, manufacture the binding agent of plastics, optical glass, weaving, leather and papermaking.
(12) Permethrin: its mode of action is to tag and stomach toxicity, and without interior suction fumigation action, insecticidal spectrum is wide, easy decomposition failure in alkaline medium and soil.Low to higher mammal toxicity, easily decompose under sunlight irradiates.
(13) nano composite antibacterial plastic master batch: for making antiseptic give play to good antibiotic property, antimicrobial long-acting in anti-biotic material, and in use stable performance, make antibiotic plastic and anti-bacterial fibre generally adopts female granulation technique.Make each based article add in manufacturing process some nano materials just can this to realize product antibacterial, sterilization, mildew-resistant, deodorizing, self-cleaning additional function.
(14) sodium glutamate: a kind of salt formed by sodium ion and glutamate ion.
(15) Brazil wax: the complex mixture formed primarily of ester that is sour and carboxylic acid is the adamantine nontoxic pure natural wax of a kind of quality.
(16) salicylanilide: white crystals, is dissolved in chloroform, alcohol, ether, benzene etc., is slightly soluble in water.Stable in the air, meet light color and deepen, toxicity is little, and mildew-resistant ability is general.Be mainly used in the mildew-resistant such as the plastics such as polyvinyl chloride, cotton, hair, rubber, binder, fiber, leather, coating.Antifungic action is comparatively strong, to sporidiole bacteria and some trichophyta effective.
(17) butyl titanate: colourless to light yellow transparent liquid, can be dissolved in the majority of organic solvent except ketone.For ester exchange reaction, can be used as high-strength polyester paint modifier, high-temperature resistant coating additive, adhesive of medical, crosslinking agent and condensation catalyst etc.For ester exchange reaction, be applied to coating and can improve heat resistanceheat resistant performance, improve coating, rubber and plastics to the adhesion of metal surface, be also used as condensation catalyst, crosslinking agent.
(18) isobutyl triethoxy silane: colourless transparent liquid, has excellent chemical resistance, weatherability, ABRASION RESISTANCE, stain resistance, self-cleaning effect; Significantly reduce Chloride Attack, freeze-thaw damage, corrosion and mould to grow; Only need the protected effect that less coated weight can reach excellent.
This beneficial effect of the invention is: this multifunction decorative decoration wall paper Paint preparation technology method is simple, prepared product has comparatively superior fire-retardant, acid and alkali-resistance, water-proof antibiotic performance, is adapted at multiple indoor exterior decoration decoration building field and uses.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is described, better to understand the present invention.
embodiment 1
Wall paper coating is used in multifunction decorative decoration in the present embodiment, be made up of the component of following mass fraction: Celogen Az 48 parts, cobalt iso-octoate 50 parts, guanyl-urea-phosphate 46 parts, titanium dioxide 50 parts, toluene-2,4-diisocyanate 46 parts, isocyanates 50 parts, polyether-tribasic alcohol 46 parts, algin salt 52 parts, pyrovinic acid 46 parts, citric acid acetyl three monooctyl ester 50 parts, the positive fourth of methacrylic acid 46 parts, Permethrin 50 parts, nano composite antibacterial plastic master batch 46 parts, sodium glutamate 50 parts, Brazil wax 46 parts, salicylanilide 50 parts, butyl titanate 46 parts, isobutyl triethoxy silane 50 parts, 1000 parts, water.
Above-mentioned multifunction decorative decoration wall paper preparation method for coating step is as follows:
(1) Celogen Az of described mass fraction, guanyl-urea-phosphate, titanium dioxide, toluene-2,4-diisocyanate, isocyanates, polyether-tribasic alcohol, algin salt, pyrovinic acid, citric acid acetyl three monooctyl ester, the positive fourth of methacrylic acid, Permethrin, sodium glutamate, Brazil wax, salicylanilide, butyl titanate, isobutyl triethoxy silane are added in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, jitter time is 60min;
(2) add the nano composite antibacterial plastic master batch of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min;
(3) add the cobalt iso-octoate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min; Mix rear obtained this product.
embodiment 2
Wall paper coating is used in multifunction decorative decoration in the present embodiment, be made up of the component of following mass fraction: Celogen Az 50 parts, cobalt iso-octoate 52 parts, guanyl-urea-phosphate 48 parts, titanium dioxide 52 parts, toluene-2,4-diisocyanate 48 parts, isocyanates 52 parts, polyether-tribasic alcohol 48 parts, algin salt 54 parts, pyrovinic acid 48 parts, citric acid acetyl three monooctyl ester 52 parts, the positive fourth of methacrylic acid 48 parts, Permethrin 52 parts, nano composite antibacterial plastic master batch 48 parts, sodium glutamate 52 parts, Brazil wax 48 parts, salicylanilide 52 parts, butyl titanate 48 parts, isobutyl triethoxy silane 52 parts, 1500 parts, water.
Above-mentioned multifunction decorative decoration wall paper preparation method for coating step is as follows:
(1) Celogen Az of described mass fraction, guanyl-urea-phosphate, titanium dioxide, toluene-2,4-diisocyanate, isocyanates, polyether-tribasic alcohol, algin salt, pyrovinic acid, citric acid acetyl three monooctyl ester, the positive fourth of methacrylic acid, Permethrin, sodium glutamate, Brazil wax, salicylanilide, butyl titanate, isobutyl triethoxy silane are added in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, jitter time is 45min;
(2) add the nano composite antibacterial plastic master batch of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min;
(3) add the cobalt iso-octoate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min; Mix rear obtained this product.
embodiment 3
Wall paper coating is used in multifunction decorative decoration in the present embodiment, be made up of the component of following mass fraction: Celogen Az 52 parts, cobalt iso-octoate 54 parts, guanyl-urea-phosphate 50 parts, titanium dioxide 54 parts, toluene-2,4-diisocyanate 50 parts, isocyanates 54 parts, polyether-tribasic alcohol 50 parts, algin salt 56 parts, pyrovinic acid 50 parts, citric acid acetyl three monooctyl ester 54 parts, the positive fourth of methacrylic acid 50 parts, Permethrin 54 parts, nano composite antibacterial plastic master batch 50 parts, sodium glutamate 54 parts, Brazil wax 50 parts, salicylanilide 54 parts, butyl titanate 50 parts, isobutyl triethoxy silane 54 parts, 2000 parts, water.
Above-mentioned multifunction decorative decoration wall paper preparation method for coating step is as follows:
(1) Celogen Az of described mass fraction, guanyl-urea-phosphate, titanium dioxide, toluene-2,4-diisocyanate, isocyanates, polyether-tribasic alcohol, algin salt, pyrovinic acid, citric acid acetyl three monooctyl ester, the positive fourth of methacrylic acid, Permethrin, sodium glutamate, Brazil wax, salicylanilide, butyl titanate, isobutyl triethoxy silane are added in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min;
(2) add the nano composite antibacterial plastic master batch of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) add the cobalt iso-octoate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min; Mix rear obtained this product.
Carry out performance measurement for the wall paper coating in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available wall paper coating, measured data are as shown in table 1.Fire protection flame retarding level estimate adopts UL94 standard.
Table 1 the performance test results
Visible, material of the present invention has corrosion-resistant, fire protection flame retarding, waterproof, anti-microbial property preferably.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (5)
1. wall paper coating is used in a multifunction decorative decoration, it is characterized in that: be made up of the component of following mass fraction: Celogen Az 48 ~ 52 parts, cobalt iso-octoate 50 ~ 54 parts, guanyl-urea-phosphate 46 ~ 50 parts, titanium dioxide 50 ~ 54 parts, toluene-2,4-diisocyanate 46 ~ 50 parts, isocyanates 50 ~ 54 parts, polyether-tribasic alcohol 46 ~ 50 parts, algin salt 52 ~ 56 parts, pyrovinic acid 46 ~ 50 parts, citric acid acetyl three monooctyl ester 50 ~ 54 parts, the positive fourth of methacrylic acid 46 ~ 50 parts, Permethrin 50 ~ 54 parts, nano composite antibacterial plastic master batch 46 ~ 50 parts, sodium glutamate 50 ~ 54 parts, Brazil wax 46 ~ 50 parts, salicylanilide 50 ~ 54 parts, butyl titanate 46 ~ 50 parts, isobutyl triethoxy silane 50 ~ 54 parts, 1000 ~ 2000 parts, water.
2. multifunction decorative decoration wall paper coating according to claim 1, it is characterized in that: described multifunction decorative decoration wall paper coating is made up of the component of following mass fraction: Celogen Az 48 parts, cobalt iso-octoate 50 parts, guanyl-urea-phosphate 46 parts, titanium dioxide 50 parts, toluene-2,4-diisocyanate 46 parts, isocyanates 50 parts, polyether-tribasic alcohol 46 parts, algin salt 52 parts, pyrovinic acid 46 parts, citric acid acetyl three monooctyl ester 50 parts, the positive fourth of methacrylic acid 46 parts, Permethrin 50 parts, nano composite antibacterial plastic master batch 46 parts, sodium glutamate 50 parts, Brazil wax 46 parts, salicylanilide 50 parts, butyl titanate 46 parts, isobutyl triethoxy silane 50 parts, 1000 parts, water.
3. according to the multifunction decorative decoration wall paper coating described in claim 1 to 2, it is characterized in that: described multifunction decorative decoration wall paper coating is made up of the component of following mass fraction: Celogen Az 50 parts, cobalt iso-octoate 52 parts, guanyl-urea-phosphate 48 parts, titanium dioxide 52 parts, toluene-2,4-diisocyanate 48 parts, isocyanates 52 parts, polyether-tribasic alcohol 48 parts, algin salt 54 parts, pyrovinic acid 48 parts, citric acid acetyl three monooctyl ester 52 parts, the positive fourth of methacrylic acid 48 parts, Permethrin 52 parts, nano composite antibacterial plastic master batch 48 parts, sodium glutamate 52 parts, Brazil wax 48 parts, salicylanilide 52 parts, butyl titanate 48 parts, isobutyl triethoxy silane 52 parts, 1500 parts, water.
4. the multifunction decorative decoration wall paper coating according to claims 1 to 3, it is characterized in that: described multifunction decorative decoration wall paper coating is made up of the component of following mass fraction: Celogen Az 52 parts, cobalt iso-octoate 54 parts, guanyl-urea-phosphate 50 parts, titanium dioxide 54 parts, toluene-2,4-diisocyanate 50 parts, isocyanates 54 parts, polyether-tribasic alcohol 50 parts, algin salt 56 parts, pyrovinic acid 50 parts, citric acid acetyl three monooctyl ester 54 parts, the positive fourth of methacrylic acid 50 parts, Permethrin 54 parts, nano composite antibacterial plastic master batch 50 parts, sodium glutamate 54 parts, Brazil wax 50 parts, salicylanilide 54 parts, butyl titanate 50 parts, isobutyl triethoxy silane 54 parts, 2000 parts, water.
5. the multifunction decorative decoration wall paper coating according to claim 1 or 4, is characterized in that: described multifunction decorative decoration wall paper preparation method for coating step is as follows:
(1) Celogen Az of described mass fraction, guanyl-urea-phosphate, titanium dioxide, toluene-2,4-diisocyanate, isocyanates, polyether-tribasic alcohol, algin salt, pyrovinic acid, citric acid acetyl three monooctyl ester, the positive fourth of methacrylic acid, Permethrin, sodium glutamate, Brazil wax, salicylanilide, butyl titanate, isobutyl triethoxy silane are added in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min;
(2) add the nano composite antibacterial plastic master batch of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the cobalt iso-octoate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix rear obtained this product.