CN105113215A - Method for preparing chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber - Google Patents
Method for preparing chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber Download PDFInfo
- Publication number
- CN105113215A CN105113215A CN201510557518.XA CN201510557518A CN105113215A CN 105113215 A CN105113215 A CN 105113215A CN 201510557518 A CN201510557518 A CN 201510557518A CN 105113215 A CN105113215 A CN 105113215A
- Authority
- CN
- China
- Prior art keywords
- polyacrylonitrile
- yttrium nitrate
- preparation
- conductive fiber
- chemical silvering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber. The method comprises the following steps: preparing 100mL of a polyacrylonitrile DMF solution of which the mass percentage is 20-50%, dropping 1-5g of yttrium nitrate into the polyacrylonitrile DMF solution, stirring, filtering, and defoaming, thereby preparing a polyacrylonitrile/yttrium nitrate mixed spinning liquid; filtering and measuring the polyacrylonitrile/yttrium nitrate mixed spinning liquid, extruding through spinneret holes, feeding into a coagulating bath, washing with water, performing drying thermal shaping, and coiling, thereby obtaining polyacrylonitrile/yttrium nitrate fiber; adding 1g of the polyacrylonitrile/yttrium nitrate fiber into 100mL of a silvering liquid to react for 30-60 minutes at 50 DEG C, sufficiently washing with water, drying, and weighing, thereby obtaining a product. The chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber has the advantages of stable structure, rapid silver ion sedimentation speed, good conductivity and the like.
Description
Technical field
The present invention relates to a kind of preparation method of conductive material, particularly relate to the preparation method of a kind of chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber.
Background technology
Polyacrylonitrile fibre, since realizing suitability for industrialized production, has received doting on of people with its excellent intensity, fluffy outward appearance and bright-coloured color and luster.But acrylic fiber hydrophily is poor, very easily produces electrostatic.
By carrying out chemical silvering process to acrylic fiber, the electric conductivity of acrylic fibers can be improved.Traditional chemical silvering process mainly improves silver-plated speed by improving the concentration of silver ion or the concentration of reductant in silver-plated temperature, increase plating solution.But silver-plated temperature is higher, the concentration of silver ion or the concentration of reductant larger, plating solution more easily decomposes, and causes silver-plated efficiency lower, affects the electric conductivity of finished product.
Summary of the invention
The present invention is directed to the defect of current techniques, disclose the preparation method of a kind of chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber.
The present invention solves the problems of the technologies described above by the following technical solutions: a kind of preparation method of chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber, and described preparation method comprises the following steps:
(1) polyacrylonitrile powder taking 20 ~ 50g is added in DMF, obtained mass fraction be 20% ~ 50% polyacrylonitrile solution add 1 ~ 5g yttrium nitrate to described polyacrylonitrile solution, after abundant stirring 30 ~ 90min, through filtration under diminished pressure, vacuum defoamation, obtained polyacrylonitrile/yttrium nitrate blend spinning liquid;
(2) on routine little formula wet process equipment, described polyacrylonitrile/yttrium nitrate blend spinning liquid is filtered, after metering, extruded by spinneret orifice, enter the coagulating bath be made up of DMF solvent and water, then through washing, dry heat sizing and rolling step, obtained polyacrylonitrile/yttrium nitrate fiber;
(3) silver ammino solution taking 30mL is added in the reducing solution of 70mL, and liquid is crossed in preparation; Add described 1g polyacrylonitrile/yttrium nitrate fiber to described in cross in liquid, at 50 DEG C react 30 ~ 60min, after fully washing with water, dry and weigh, obtaining product.
Preferably: the consumption of described polyacrylonitrile is 40g, the addition of described yttrium nitrate is 1 ~ 5g.
Preferably: the consumption of described polyacrylonitrile is 20 ~ 50g, the addition of described yttrium nitrate is 4g.
Preferably: described mixing time is 60min.
Preferably: the described reaction time is 60min.
The present invention, by preparation polyacrylonitrile/yttrium nitrate blend spinning liquid, carries out solution-polymerized SBR, obtained polyacrylonitrile/yttrium nitrate fiber, then through Electroless Silver Plating, utilizes Rare Earth Y
3+can with NH
3form coordination thing, the main salt argent ion concentration of silver ammino solution is increased, promotes the transition of silver ion, assist silver-plated process, thus preparative chemistry silver-plated polyacrylonitrile/yttrium nitrate conductive fiber.
The invention has the advantages that: chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber disclosed by the invention have Stability Analysis of Structures, silver ion deposition velocity fast, conduct electricity very well.
Accompanying drawing explanation
Fig. 1 be the present invention with the consumption of yttrium nitrate for variable, the chemical silvering deposition velocity curve map of test.
Fig. 2 be the present invention with the consumption of polyacrylonitrile for variable, the powerful curve map of the conductive fiber of test.
Detailed description of the invention
Below in conjunction with instantiation, the present invention is described in detail; should understand; embodiment is only for illustration of the present invention, instead of for limiting the present invention, any amendment, equivalent replacement etc. made on basis of the present invention is all in protection scope of the present invention.
Embodiment 1
The experiment that the consumption of different yttrium nitrate affects chemical silvering deposition velocity:
The polyacrylonitrile powder taking 40g is added in DMF, obtained mass fraction is the polyacrylonitrile solution of 40%, instill the yttrium nitrate of 1g, 2g, 3g, 4g, 5g respectively to described polyacrylonitrile solution, after abundant stirring 60min, through filtration under diminished pressure, vacuum defoamation, obtained polyacrylonitrile/yttrium nitrate blend spinning liquid.By after described polyacrylonitrile/yttrium nitrate blend spinning liquid filtration, metering on routine little formula wet process equipment, extruded by spinneret orifice, enter the coagulating bath be made up of DMF solvent and water, then through washing, dry heat sizing and rolling step, obtained polyacrylonitrile/yttrium nitrate fiber.The silver ammino solution taking 30mL is added in the reducing solution of 70mL, and liquid is crossed in preparation; Adding 1g polyacrylonitrile/yttrium nitrate fiber to crossing in liquid, at 50 DEG C, reacting 60min, after fully washing with water, dry and weigh, obtaining product.
The mensuration of sedimentation rate: after silver-plated a period of time, determine sedimentation rate, uses the quality of the silver-plated front and back of electronic balance weighing sample chemical, and by under time calculate sedimentation rate:
In formula, V is sedimentation rate (um/h), m
1and m
2be respectively the quality (g) of silver-plated forward and backward sample, p is the density (10.5g/cm of silver coating
3), A is the surface area (cm of sample
2), t is silver-plated time (h).
Shown in Fig. 1 curve, along with the increase of yttrium nitrate initial content, the deposition velocity of silver ion increases gradually, and when the consumption of yttrium nitrate is 4g, the deposition velocity of silver ion reaches maximum, and maximum deposition speed is 14.2um/h; The consumption of further increase yttrium nitrate, the deposition velocity of anion declines to some extent.This is because, when the consumption of yttrium nitrate is between 1 ~ 4g, along with the continuous increase of yttrium nitrate concentration in the plating solution, there is more Y
3+can with NH
3form coordination thing, consume a part of NH in silver ammino solution
3, main salt concentration of metal ions free in plating solution is increased, thus adds the some potential difference at interface, facilitate the transition of silver particles to catalytic surface, improve sedimentation rate; After the concentration of yttrium nitrate is greater than 4g, along with the increase of yttrium nitrate concentration, because excessive rare-earth yttrium is adsorbed on the surface of fiber, the outside of coated with silver particle, the autocatalysis of silver is restricted, and deposition velocity declines to some extent.
Embodiment 2
The consumption of different polyacrylonitrile is to the experiment of conductive fiber strong influence:
The polyacrylonitrile powder taking 10g, 20g, 30g, 40g, 50g is respectively added in DMF, obtained mass fraction is the polyacrylonitrile solution of 40%, instill the yttrium nitrate of 3g respectively to described polyacrylonitrile solution, after abundant stirring 60min, through filtration under diminished pressure, vacuum defoamation, obtained polyacrylonitrile/yttrium nitrate blend spinning liquid.By after described polyacrylonitrile/yttrium nitrate blend spinning liquid filtration, metering on routine little formula wet process equipment, extruded by spinneret orifice, enter the coagulating bath be made up of DMF solvent and water, then through washing, dry heat sizing and rolling step, obtained polyacrylonitrile/yttrium nitrate fiber.The silver ammino solution taking 30mL is added in the reducing solution of 70mL, and liquid is crossed in preparation; Adding 1g polyacrylonitrile/yttrium nitrate fiber to crossing in liquid, at 50 DEG C, reacting 60min, after fully washing with water, dry and weigh, obtaining product.
Broken filament brute force measures: at setting folder apart from d=20mm, retest frequency n=250 time, carry out constant speed tension test under draw speed v=30mm/min condition.
Shown in Fig. 2 curve, along with the increase of polyacrylonitrile initial content, the broken filament intensity of conductive fiber increases gradually, when polyacrylonitrile initial content is more than 40g, because concentration of dope is too high, macromolecular entanglements and crystallization, often make uniform dissolution become very difficult.Even and if dissolve, the mobility of solution and spinnability are also very poor, cannot realize spinning smoothly.
The foregoing is only the preferred embodiment of the invention; not in order to limit the invention; the any amendment done within all spirit in the invention and principle, equivalently to replace and improvement etc., within the protection domain that all should be included in the invention.
Claims (5)
1. a preparation method for chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber, is characterized in that: described preparation method comprises the following steps:
(1) polyacrylonitrile powder taking 20 ~ 50g is added in DMF, obtained mass fraction is the polyacrylonitrile solution of 20% ~ 50%, add the yttrium nitrate of 1 ~ 5g to described polyacrylonitrile solution, after abundant stirring 30 ~ 90min, through filtration under diminished pressure, vacuum defoamation, obtained polyacrylonitrile/yttrium nitrate blend spinning liquid;
(2) on routine little formula wet process equipment, described polyacrylonitrile/yttrium nitrate blend spinning liquid is filtered, after metering, extruded by spinneret orifice, enter the coagulating bath be made up of DMF solvent and water, then through washing, dry heat sizing and rolling step, obtained polyacrylonitrile/yttrium nitrate fiber;
(3) silver ammino solution taking 30mL is added in the reducing solution of 70mL, and preparation 100mL crosses liquid; Add described 1g polyacrylonitrile/yttrium nitrate fiber to described in cross in liquid, at 50 DEG C react 30 ~ 60min, after fully washing with water, dry and weigh, obtaining product.
2. the preparation method of a kind of chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber according to claim 1, it is characterized in that: the consumption of described polyacrylonitrile is 40g, the consumption of described yttrium nitrate is 1 ~ 5g.
3. the preparation method of a kind of chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber according to claim 1, it is characterized in that: the consumption of described polyacrylonitrile is 10 ~ 50g, the consumption of described yttrium nitrate is 3g.
4. the preparation method of a kind of chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber according to claim 1, is characterized in that: described mixing time is 60min.
5. the preparation method of a kind of chemical silvering polyacrylonitrile/yttrium nitrate conductive fiber according to claim 1, is characterized in that: the described reaction time is 60min.