CN105112788A - 一种球磨机用中碳中铬合金钢球及其制备方法 - Google Patents

一种球磨机用中碳中铬合金钢球及其制备方法 Download PDF

Info

Publication number
CN105112788A
CN105112788A CN201510485093.6A CN201510485093A CN105112788A CN 105112788 A CN105112788 A CN 105112788A CN 201510485093 A CN201510485093 A CN 201510485093A CN 105112788 A CN105112788 A CN 105112788A
Authority
CN
China
Prior art keywords
medium
steel ball
insulation
carbon
alloy steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510485093.6A
Other languages
English (en)
Inventor
周浩
周洁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huoqiu Zhongzhen Wear-Resistant Material Co Ltd
Original Assignee
Huoqiu Zhongzhen Wear-Resistant Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huoqiu Zhongzhen Wear-Resistant Material Co Ltd filed Critical Huoqiu Zhongzhen Wear-Resistant Material Co Ltd
Priority to CN201510485093.6A priority Critical patent/CN105112788A/zh
Publication of CN105112788A publication Critical patent/CN105112788A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种球磨机用中碳中铬合金钢球及其制备方法，其各化学成分及质量百分比为：C0.4-0.7、Si0.5-1.0、Cr4.4-5.8、Mn0.7-1.1、Mo0.5-0.8、Cu0.3-0.6、V0.05-0.1、Ti0.08-0.14、B0.03-0.05、Co0.1-0.2、Al0.05-0.1、Pr0.06-0.08、Sm0.03-0.06、S≤0.03、P≤0.04、余量为Fe。本发明制得的钢球具有较高的硬度和韧性，耐磨性优异，使用寿命长，可以广泛应用于各类球磨机，市场前景广阔。

Description

一种球磨机用中碳中铬合金钢球及其制备方法
技术领域
本发明涉及铸铁材料技术领域，具体涉及一种球磨机用中碳中铬合金钢球及其制备方法。
背景技术
球磨机钢球是球磨机设备研磨物料介质，通过球磨机钢球之间钢球与物料之间的碰撞摩擦产生磨剥作用，重要的基础零部件，尤其是精密工业钢球在国民经济发展中起着巨大作用，广泛应用于水泥建材、金属矿山、煤浆火电、化学工程、陶瓷等行业的粉体制备与超细深加工。钢球是球磨机主要的易磨损件，其工作繁重,工作条件苛刻,因此对钢球材质的耐磨性和韧性具有较高的要求。
发明内容
本发明的目的在于针对现有技术的不足，提供一种球磨机用中碳中铬合金钢球及其制备方法。
为实现上述目的，本发明采用的技术方案如下：
一种球磨机用中碳中铬合金钢球，其各化学成分及质量百分比为：C0.4-0.7、Si0.5-1.0、Cr4.4-5.8、Mn0.7-1.1、Mo0.5-0.8、Cu0.3-0.6、V0.05-0.1、Ti0.08-0.14、B0.03-0.05、Co0.1-0.2、Al0.05-0.1、Pr0.06-0.08、Sm0.03-0.06、S≤0.03、P≤0.04、余量为Fe。
一种球磨机用中碳中铬合金钢球的制备方法，包括以下步骤：
（1）在中频感应炉中进行熔炼，先加入废钢、生铁、硅铁熔清，再依次加入铬铁、硼铁、钼铁、钛铁、钴铁、铜，待其全部熔化后调整铁水成分，在出炉前4-6min内先后加入锰铁和钒铁，在出炉前2-4min内加入纯铝进行脱氧，出炉前进行化学成分分析，合格后即可出炉，铁水出炉温度控制在1505-1545℃；
（2）在包内冲入稀土硅铁合金变质剂进行变质孕育处理，变质剂使用前进行250-300℃的预热，变质孕育处理温度为1460-1490℃，然后往包内撒入适量的珍珠岩保温聚渣覆盖剂覆盖，并镇静6-12min，扒渣后进行浇注，浇注温度控制在1435-1455℃；
（3）将上述得到的钢球进行热处理：先加热至890-960℃，保温4-5h，再降温至460-520℃，保温2-3h，雾冷淬火后再在140-180℃下回火6-8h，然后加热至650-700℃，保温3-4h，再加热至980-1040℃，保温5-6h，沙冷淬火后再在240-320℃下回火4-6h，最后加热至1060-1120℃，保温3-5h，再降温至720-760℃，保温2-4h，油冷淬火后再在300-350℃下回火5-6h，空冷至室温即可。
本发明的有益效果：
（1）本发明成分设计合理，通过调整C、Cr的含量以及添加碳化物形成元素的Mn、Mo、Cu、V、Ti、B、Co，发挥多元合金元素的综合作用进行合金化，可以显著细化晶粒，改善组织形态，提高冲击韧性和耐磨性；
（2）本发明热处理工艺合理，经过三次淬火以及相应的回火处理后，组织为马氏体基体+奥氏体（沿晶界分布）+弥散的颗粒状碳化物，热处理过程中发生再结晶，晶粒细小，可显著提高硬度和冲击韧性；
（3）本发明制得的钢球具有较高的硬度和韧性，耐磨性优异，使用寿命长，可以广泛应用于各类球磨机，市场前景广阔。
具体实施方式
一种球磨机用中碳中铬合金钢球，其各化学成分及质量百分比为：C0.4-0.7、Si0.5-1.0、Cr4.4-5.8、Mn0.7-1.1、Mo0.5-0.8、Cu0.3-0.6、V0.05-0.1、Ti0.08-0.14、B0.03-0.05、Co0.1-0.2、Al0.05-0.1、Pr0.06-0.08、Sm0.03-0.06、S≤0.03、P≤0.04、余量为Fe。
一种球磨机用中碳中铬合金钢球的制备方法，包括以下步骤：
（1）在中频感应炉中进行熔炼，先加入废钢、生铁、硅铁熔清，再依次加入铬铁、硼铁、钼铁、钛铁、钴铁、铜，待其全部熔化后调整铁水成分，在出炉前4-6min内先后加入锰铁和钒铁，在出炉前2-4min内加入纯铝进行脱氧，出炉前进行化学成分分析，合格后即可出炉，铁水出炉温度控制在1505-1545℃；
（2）在包内冲入稀土硅铁合金变质剂进行变质孕育处理，变质剂使用前进行250-300℃的预热，变质孕育处理温度为1460-1490℃，然后往包内撒入适量的珍珠岩保温聚渣覆盖剂覆盖，并镇静6-12min，扒渣后进行浇注，浇注温度控制在1435-1455℃；
（3）将上述得到的钢球进行热处理：先加热至890-960℃，保温4-5h，再降温至460-520℃，保温2-3h，雾冷淬火后再在140-180℃下回火6-8h，然后加热至650-700℃，保温3-4h，再加热至980-1040℃，保温5-6h，沙冷淬火后再在240-320℃下回火4-6h，最后加热至1060-1120℃，保温3-5h，再降温至720-760℃，保温2-4h，油冷淬火后再在300-350℃下回火5-6h，空冷至室温即可。
经检验，产品化学成分为C0.58%、Si0.74%、Cr5.21%、Mn0.95%、Mo0.77%、Cu0.43%、V0.084%、Ti0.011%、B0.044%、Co%0.16、Al0.082%、Pr0.075%、Sm0.048%、S0.024%、P0.033%、余量为Fe。力学性能为：硬度：63.7HRC，冲击韧性：26.4J/cm2。

Claims (2)

1.一种球磨机用中碳中铬合金钢球，其特征在于，其各化学成分及质量百分比为：C0.4-0.7、Si0.5-1.0、Cr4.4-5.8、Mn0.7-1.1、Mo0.5-0.8、Cu0.3-0.6、V0.05-0.1、Ti0.08-0.14、B0.03-0.05、Co0.1-0.2、Al0.05-0.1、Pr0.06-0.08、Sm0.03-0.06、S≤0.03、P≤0.04、余量为Fe。
2.一种如权利要求1所述的球磨机用中碳中铬合金钢球的制备方法，其特征在于包括以下步骤：
（1）在中频感应炉中进行熔炼，先加入废钢、生铁、硅铁熔清，再依次加入铬铁、硼铁、钼铁、钛铁、钴铁、铜，待其全部熔化后调整铁水成分，在出炉前4-6min内先后加入锰铁和钒铁，在出炉前2-4min内加入纯铝进行脱氧，出炉前进行化学成分分析，合格后即可出炉，铁水出炉温度控制在1505-1545℃；
（2）在包内冲入稀土硅铁合金变质剂进行变质孕育处理，变质剂使用前进行250-300℃的预热，变质孕育处理温度为1460-1490℃，然后往包内撒入适量的珍珠岩保温聚渣覆盖剂覆盖，并镇静6-12min，扒渣后进行浇注，浇注温度控制在1435-1455℃；
（3）将上述得到的钢球进行热处理：先加热至890-960℃，保温4-5h，再降温至460-520℃，保温2-3h，雾冷淬火后再在140-180℃下回火6-8h，然后加热至650-700℃，保温3-4h，再加热至980-1040℃，保温5-6h，沙冷淬火后再在240-320℃下回火4-6h，最后加热至1060-1120℃，保温3-5h，再降温至720-760℃，保温2-4h，油冷淬火后再在300-350℃下回火5-6h，空冷至室温即可。
CN201510485093.6A 2015-08-10 2015-08-10 一种球磨机用中碳中铬合金钢球及其制备方法 Pending CN105112788A (zh)