CN105111896A - Reflective colored vibration deceleration marking composition, and construction method and application thereof - Google Patents
Reflective colored vibration deceleration marking composition, and construction method and application thereof Download PDFInfo
- Publication number
- CN105111896A CN105111896A CN201510189370.9A CN201510189370A CN105111896A CN 105111896 A CN105111896 A CN 105111896A CN 201510189370 A CN201510189370 A CN 201510189370A CN 105111896 A CN105111896 A CN 105111896A
- Authority
- CN
- China
- Prior art keywords
- marked line
- reflective color
- vibration deceleration
- color vibration
- deceleration marked
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a reflective colored vibration deceleration marking composition, and a construction method and application thereof. The reflective colored vibration deceleration marking composition is characterized by comprising the following main raw materials by weight: 5 to 80% of an adhesive, 0.2 to 60% of a curing agent, 10 to 50% of wear resistant aggregate, 5 to 50% of a reflective material, 10 to 40% of an anti-slip material, 0 to 10% of a promoter, 5 to 20% of pigment, 1 to 30% of a diluent or solvent and 5 to 60% of an inorganic and organic filling material. The reflective colored vibration deceleration marking composition is applied to traffic safety facility signs and can be directly casted on traffic accident blackspots like the square of a highway toll station, the entry of a bridge and a tunnel, a continuous downhill of a road, a curve and a sharp turn of the road, intersections and crossroads of the road and slippery positions of a wet pavement and on pavements needing deceleration of automobiles, e.g., places in front of gates of schools, hospitals and government agencies.
Description
Technical field
The present invention relates to a kind of novel highway traffic safety facility logo material, particularly relate to a kind of reflective color vibration deceleration marked line composite and constructional method and purposes.
Background technology
Highway vibration deceleration marked line material conventional both at home and abroad at present mainly uses graticule to paint and brushes, hot-melt coating blade coating, and molded rubber band (ridge) is pasted or reflector perforating is fixed, cement concrete cast molding etc.There are a lot of quality problems in the speed reduction marking (band) manufactured with this different materials, result of use is very poor: the usage period is short, and some materials will be brushed again every some months, not only time-consuming, block the traffic, cost is also high, poor adhesive force, be full of cracks comes off serious.Night, graticule was not reflective, indicated not obvious, did not shake deceleration, caused night traffic accident to increase.The complicated cost of manufacturing process is high, must destroy road surface perforating and fix or could use by knife-coat application after high-temperature hot melt material during construction and installation.
Summary of the invention
The object of the present invention is to provide one can overcome above-mentioned defect, there is reflecting at night, colored eye-catching, concussion is slowed down, and sleet is anti-skidding, and color is selected arbitrarily, shape is arbitrarily constructed, the adjustment of thickness scene, convenient and quick construction, with low cost, usage period is long, and glistening intensity is high, and the reflective life-span is long, concussion slowing effect is good, distinct eye-catching novel trans light type color vibration deceleration marked line composite and constructional method and purposes.
Technical scheme of the present invention is: a kind of reflective color vibration deceleration marked line composite, is characterized in that, wherein containing main raw material(s) by weight proportioning be:
Caking agent 5-80%;
Solidifying agent 0.2-60%;
Abrasive aggregates 10-50%;
Light reflecting material 5-50%;
Anti-slip material 10-40%;
Promotor 0-10%;
Pigment 5-20%;
Thinner or solvent 1-30%;
Inorganic and organic filler 5-60%.
Described a kind of reflective color vibration deceleration marked line composite, is characterized in that, wherein containing main raw material(s) by weight proportioning be:
Caking agent 10-50%;
Solidifying agent 5-25%;
Abrasive aggregates 25-45%;
Light reflecting material 5-30%;
Anti-slip material 10-40%;
Promotor 0-8%;
Pigment 12-20%;
Thinner or solvent 10-30%;
Described a kind of reflective color vibration deceleration marked line composite, is characterized in that, wherein containing main raw material(s) by weight proportioning be:
Caking agent 28%;
Solidifying agent 5%;
Abrasive aggregates 25%;
Light reflecting material 5%;
Anti-slip material 10%;
Promotor 0;
Pigment 12%;
Thinner or solvent 10%;
Inorganic and organic filler 5%.
Described reflective color vibration deceleration marked line composite, is characterized in that, described caking agent is alkyd resin, vinyl ester resin, acrylic resin, unsaturated polyester resin, epoxy resin.
Described reflective color vibration deceleration marked line composite, is characterized in that: described solidifying agent is methylethyl ketone peroxide, cycloethanone peroxide paste, quadrol, fatty amine, cycloaliphatic amines.
Described reflective color vibration deceleration marked line composite, is characterized in that, described abrasive aggregates is that 1-6mm calcines aluminium vanadine, silicon carbide, colored ceramic particle, white quartz sand.
Described reflective color vibration deceleration marked line composite, is characterized in that: described light reflecting material is plated film high-refractivity reflecting glass microballon, reflector.
Described reflective color vibration deceleration marked line composite, is characterized in that, described anti-slip material is high-temperature calcination ceramic particle or colored pyroceramic particle.
Described reflective color vibration deceleration marked line composite, is characterized in that, described promotor is cobalt naphthenate solution or PM-30 or E54.
Described reflective color vibration deceleration marked line composite, is characterized in that: described pigment is pigment or pigment paste, and described pigment is Rutile type Titanium Dioxide, medium chrome yellow medium yellow, and described pigment paste is bright red mill base, phthalocyanine blue mill base, phthalocyanine green mill base.
Described reflective color vibration deceleration marked line composite, it is characterized in that, described thinner is phthalic acid dimethyl ester, vinylbenzene, acetone, ethanol, toluene, dimethylbenzene, pimelinketone, described solvent is, as epoxy-reactive solvent: rare propyl glycidyl ether, simple function group 501 butyl glycidyl ten thousand ether, 692 card base glycidyl ethers.
Described reflective color vibration deceleration marked line composite, is characterized in that, described mineral filler and organic filler comprise: kaolin, water-ground limestone, light calcium carbonate, talcum powder, dry powder, silica powder.
The constructional method of described reflective color vibration deceleration marked line composite, it is characterized in that, constructional method one: blade coating high-strength anti-skid pavement binders, the colored pyroceramic particle of spreading, thickness 3-8mm, the color of ceramic particle is selected by user, as the two component porcelain gage mark coating of brush one deck again after needing the reflective wait graticule of graticule slightly dry, plated film high-refractivity reflecting glass microballon is spread in face, and the color of colored ceramic particle wants consistent with the color of two component gage mark coating;
Constructional method two: 828 toluene dissolved dilution used for epoxy resin or add strong solvent dilution, add middle chrome pigment or titanium white powder pigment, after organic and mineral filler agitation grinding, barrelling is for subsequent use, add quadrol rapid stirring before using to mix, add appropriate yellow ceramic particle again and plated film high-refractivity reflecting glass microballon stirs, to cast immediately use, when epoxy resin uses, yellowing is serious, configure yellow vibration deceleration marked line proper, require clean for earth cleaning in road surface during construction, according to shape need, mould is placed road surface, the concussion graticule of casting 3-8mm thickness, can use after within 30 minutes, solidifying drying, usage period reaches 10 years, because concussion graticule is mixed with plated film high-refractivity reflecting glass microballon, still reflective after the wearing and tearing of graticule top layer, before earthquake graticule does not solidify, for increasing reflecting at night brightness, one deck plated film high-refractivity reflecting glass microballon can be sowed on surface.
A kind of reflective color vibration deceleration marked line composite purposes, it is characterized in that, described reflective color vibration deceleration marked line composite is used for highway traffic safety facility logo, the reflective color vibration deceleration marked line of above combination of materials, can direct pouring construct on freeway toll station square, bridge, tunnel entrances place, highway long and steep downgrade, highway bend and sharp turn, highway crossing and crossroad, traffic accident multi-happening section and the schools such as rainwater road surface slippery situation place, hospital, government bodies need greatly in front of the door etc. the road surface of car deceleration.
The present invention compared to the prior art advantage and effect is:
Reflective color vibration deceleration marked line composite provided by the invention, participates in curing reaction directly after adding strong solvent in material composition, without any solvent evaporates, and zero release, environmental protection, to workmen's toxicological harmless, pollution-free to air.Add light reflecting material, make graticule become clear reflective night, effective guarantee driving at night safety, reduce night traffic accident, improve driving at night efficiency, highway reflector marking is love life " help line ".Add abrasive aggregates, make graticule hard wear resistant, increase the service life, during construction, thin and thick is determined arbitrarily, has the function of concussion deceleration warning, effectively can reduce the generation of traffic accident.Add caking agent, make the multiple material of composition solidify one, simultaneously with road surface strong bond, strong adhesion, does not need to destroy road surface perforating and fixes during construction.Add solidifying agent, caking agent and multiple material composition fast setting can be made, do not block the traffic, do not affect automobile normal running.Add the pigment of shades of colour, can make the variation of vibration deceleration marked line color, can be formulated into white as required, yellow, red, blue, green shades of colour such as grade, pieces together concussion graticule and the color pattern of multiple color.Graticule shape chooses at random, and work-ing life is determined according to graticule coating thickness, and intensity high texture is hard, shock resistance, indeformable, do not chap, not aging, colour-fast, high temperature resistant, resistance to low cold, wear-resistant, acid and alkali-resistance, resistance to rainwater, be applicable to cement and bituminous highway use, better than the vibration deceleration marked line quality of other kinds by working life, cost is low, can save a large amount of manpower and materials, easy construction, has reflecting at night, colored eye-catching, concussion is slowed down, the multinomial traffic safety functions such as sleet is anti-skidding.
Reflective color vibration deceleration marked line composite is used for highway traffic safety facility logo, the reflective color vibration deceleration marked line of above combination of materials, can direct pouring construct on freeway toll station square, bridge, tunnel entrances place, highway long and steep downgrade, highway bend and sharp turn, highway crossing and crossroad, traffic accident multi-happening section and the schools such as rainwater road surface slippery situation place, hospital, government bodies need greatly in front of the door etc. the road surface of car deceleration.
Have reflecting at night, colored eye-catching, concussion is slowed down, the multinomial traffic safety functions such as sleet is anti-skidding, and strong adhesion does not come off, usage period long excellent wear resistance, and easy construction cost is low, effectively can reduce the generation of traffic accident.
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment
A kind of reflective color vibration deceleration marked line composite of the present invention, is characterized in that, wherein containing main raw material(s) by weight proportioning be:
Caking agent 5-80%;
Solidifying agent 0.2-60%;
Abrasive aggregates 10-50%;
Light reflecting material 5-50%;
Anti-slip material 10-40%;
Promotor 0-10%;
Pigment 5-20%;
Thinner or solvent 1-30%;
Inorganic and organic filler 5-60%.
Described a kind of reflective color vibration deceleration marked line composite, is characterized in that, wherein containing main raw material(s) by weight proportioning be:
Caking agent 10-50%;
Solidifying agent 5-25%;
Abrasive aggregates 25-45%;
Light reflecting material 5-30%;
Anti-slip material 10-40%;
Promotor 0-8%;
Pigment 12-20%;
Thinner or solvent 10-30%;
Inorganic and organic filler 5-60%.
Described a kind of reflective color vibration deceleration marked line composite, is characterized in that, wherein containing main raw material(s) by weight proportioning be:
Caking agent 28%;
Solidifying agent 5%;
Abrasive aggregates 25%;
Light reflecting material 5%;
Anti-slip material 10%;
Promotor 0;
Pigment 12%;
Thinner or solvent 10%;
Inorganic and organic filler 5%.
Described reflective color vibration deceleration marked line composite, is characterized in that, described caking agent is alkyd resin, vinyl ester resin, acrylic resin, unsaturated polyester resin, epoxy resin.
Described reflective color vibration deceleration marked line composite, is characterized in that: described solidifying agent is methylethyl ketone peroxide, cycloethanone peroxide paste, quadrol, fatty amine, cycloaliphatic amines.
Described reflective color vibration deceleration marked line composite, is characterized in that, described abrasive aggregates is that 1-6mm calcines aluminium vanadine, silicon carbide, colored ceramic particle, white quartz sand.
Described reflective color vibration deceleration marked line composite, is characterized in that: described light reflecting material is plated film high-refractivity reflecting glass microballon, reflector.
Described reflective color vibration deceleration marked line composite, is characterized in that, described anti-slip material is high-temperature calcination ceramic particle or colored pyroceramic particle.
Described reflective color vibration deceleration marked line composite, is characterized in that, described promotor is cobalt naphthenate solution or PM-30 or E54.
Described reflective color vibration deceleration marked line composite, is characterized in that: described pigment is pigment or pigment paste, and described pigment is Rutile type Titanium Dioxide, medium chrome yellow medium yellow, and described pigment paste is bright red mill base, phthalocyanine blue mill base, phthalocyanine green mill base.
Described reflective color vibration deceleration marked line composite, it is characterized in that, described thinner is phthalic acid dimethyl ester, vinylbenzene, acetone, ethanol, toluene, dimethylbenzene, pimelinketone, described solvent is, as epoxy-reactive solvent: rare propyl glycidyl ether, simple function group 501 butyl glycidyl ten thousand ether, 692 card base glycidyl ethers.
Described reflective color vibration deceleration marked line composite, is characterized in that, described mineral filler and organic filler comprise: kaolin, water-ground limestone, light calcium carbonate, talcum powder, dry powder, silica powder.
The constructional method of described reflective color vibration deceleration marked line composite, it is characterized in that, constructional method one: blade coating high-strength anti-skid pavement binders, the colored pyroceramic particle of spreading, thickness 3-8mm, the color of colored pyroceramic particle is selected by user, as the two component porcelain gage mark coating of brush one deck again after needing the reflective wait graticule of graticule slightly dry, plated film high-refractivity reflecting glass microballon is spread in face, and the color of colored pyroceramic particle wants consistent with the color of two component gage mark coating;
Constructional method two: 828 toluene dissolved dilution used for epoxy resin or add solvent cut, add middle chrome pigment or titanium white powder pigment, after organic and mineral filler agitation grinding, barrelling is for subsequent use, add quadrol rapid stirring before using to mix, add appropriate yellow pyroceramic particle again and plated film high-refractivity reflecting glass microballon stirs, to cast immediately use, when epoxy resin uses, yellowing is serious, configure yellow vibration deceleration marked line proper, require clean for earth cleaning in road surface during construction, according to shape need, mould is placed road surface, the concussion graticule of casting 3-8mm thickness, can use after within 30 minutes, solidifying drying, usage period reaches 10 years, because concussion graticule is mixed with plated film high-refractivity reflecting glass microballon, still reflective after the wearing and tearing of graticule top layer, before earthquake graticule does not solidify, for increasing reflecting at night brightness, one deck plated film high-refractivity reflecting glass microballon can be sowed on surface.
A kind of reflective color vibration deceleration marked line composite purposes, it is characterized in that, described reflective color vibration deceleration marked line composite is used for highway traffic safety facility logo, the reflective color vibration deceleration marked line of above combination of materials, can direct pouring construct on freeway toll station square, bridge, tunnel entrances place, highway long and steep downgrade, highway bend and sharp turn, highway crossing and crossroad, traffic accident multi-happening section and the schools such as rainwater road surface slippery situation place, hospital, government bodies need greatly in front of the door etc. the road surface of car deceleration.
Embodiment one
Starting material by weight proportioning are:
Unsaturated polyester resin 28%;
Methylethyl ketone peroxide 5%;
Calcining aluminium vanadine 25%;
Plated film high-refractivity reflecting glass microballon 5%;
High-temperature calcination ceramic particle 10%;
Cobalt naphthenate solution 2;
Rutile type Titanium Dioxide 12%;
Vinylbenzene or phthalic acid dimethyl ester 8%;
Kaolin 5%.
E54 toluene dissolved dilution used for epoxy resin or add strong solvent dilution, after adding middle chrome pigment or titanium white powder pigment, filler agitation grinding, barrelling is for subsequent use.Add quadrol rapid stirring before using to mix, then add appropriate yellow pyroceramic particle and plated film high-refractivity reflecting glass microballon stirs, cast molding immediately.And plated film high-refractivity reflecting glass microballon is spread in face, when epoxy resin uses, yellowing is serious, configures yellow vibration deceleration marked line proper.Require during construction, by clean for earth cleaning in road surface, according to shape need, mould to be placed road surface, the concussion graticule of casting 3-8mm thickness, can use after within 30 minutes, solidifying drying, the usage period reaches 10 years.Because concussion graticule is mixed with reflective glass beads, still continuing reflective after the wearing and tearing of graticule top layer, before earthquake graticule does not solidify, for increasing reflecting at night brightness, one deck plated film high-refractivity reflecting glass microballon can be sowed on surface.
Constructional method one: blade coating high-strength anti-skid pavement binders, the colored pyroceramic particle of spreading, thickness 3-8mm, the color of ceramic particle is selected by user, as the two component porcelain gage mark coating of brush one deck again after needing the reflective wait graticule of graticule slightly dry, plated film high-refractivity reflecting glass microballon is spread in face, and the color of colored ceramic particle wants consistent with the color of two component gage mark coating;
Constructional method two: 828 toluene dissolved dilution used for epoxy resin or add strong solvent dilution, add middle chrome pigment or titanium white powder pigment, after organic and mineral filler agitation grinding, barrelling is for subsequent use, add quadrol rapid stirring before using to mix, add appropriate yellow ceramic particle again and plated film high-refractivity reflecting glass microballon stirs, to cast immediately use, when epoxy resin uses, yellowing is serious, configure yellow vibration deceleration marked line proper, require clean for earth cleaning in road surface during construction, according to shape need, mould is placed road surface, the concussion graticule of casting 3-8mm thickness, can use after within 30 minutes, solidifying drying, usage period reaches 10 years, because concussion graticule is mixed with plated film high-refractivity reflecting glass microballon, still reflective after the wearing and tearing of graticule top layer, before earthquake graticule does not solidify, for increasing reflecting at night brightness, one deck plated film high-refractivity reflecting glass microballon can be sowed on surface.
Embodiment two
Starting material by weight proportioning are:
Epoxy resin 61%;
Fatty amine 0.2%;
Silicon carbide 10%;
Plated film high-refractivity reflecting glass microballon 5%;
High-temperature calcination ceramic particle 10%;
PM-302；
Rutile type Titanium Dioxide 5%;
Toluene or rare propyl glycidyl ether or 692 card base glycidyl ethers 1.8%;
Water-ground limestone 5%.
Unsaturated polyester resin vinylbenzene dilutes, and adds the barrelling of titanium white powder pigment agitation grinding.First add after solidifying agent methylethyl ketone peroxide stirs before using, after add promotor cobalt naphthenate solution and stir, solidifying agent and promotor can't be added simultaneously, to avoid sudden and violent poly-reaction.Add appropriate white quartz sand again and reflective glass beads stirs, construction of casting immediately.Unsaturated polyester resin is water white liquid, and life-time service not yellowing prepares white vibration deceleration marked line suitable.Constructional method is identical with embodiment one.
Embodiment three
Starting material by weight proportioning are:
Alkyd resin 5%;
Cycloethanone peroxide sticks with paste 51%;
Colored ceramic particle 10%;
Plated film high-refractivity reflecting glass microballon 6%;
High-temperature calcination ceramic particle 10%;
Cobalt naphthenate solution 1;
Medium chrome yellow medium yellow 6%;
Pimelinketone 6%;
Light calcium carbonate 5%.
Acrylic resin dimethylbenzene dilutes, and adds the barrelling of rutile titanium white powder pigment agitation grinding.First add promotor stirring before using, after add solidifying agent and stir and add calcining aluminium vanadine mix and blend again, construct immediately, sow one deck plated film high-refractivity reflecting glass microballon on surface after concussion graticule is shaped, realize graticule reflecting at night.Constructional method is identical with embodiment one.
Embodiment four
Starting material by weight proportioning are:
Vinyl ester resin 6%;
Cycloaliphatic amines 52%;
White quartz sand 10%;
Plated film high-refractivity reflecting glass microballon 5%;
Colored pyroceramic particle 10%;
Promotor 0;
Bright red mill base 10%;
Acetone 1%;
Talcum powder 6%.
Vinyl ester resin phthalic acid dimethyl ester dilutes, and adds the barrelling of red pigment paste agitation grinding.First add cobalt naphthenate solution before using to stir, after add cyclohexanone peroxide and stir.Add silicon carbide mix and blend again, construct immediately.The not dry front surface of earthquake graticule sows one deck reflective glass beads, shakes graticule night and becomes clear reflective.Constructional method is identical with embodiment one.
Embodiment five
Starting material by weight proportioning are:
Acrylic acid epoxy resin 7%;
Quadrol 0.2%;
Colored ceramic particle 15%;
Plated film high-refractivity reflecting glass microballon 51%;
Colored pyroceramic particle 10%;
E541；
Phthalocyanine blue mill base 5%;
Dimethylbenzene or simple function group 501 butyl glycidyl ten thousand ether 5%;
Dry powder 5.8%.
828 acetone diluted used for epoxy resin, add phthalocyanine blue or the barrelling of phthalocyanine green mill base pigment paste agitation grinding.Add after fatty amine stirs before using, then add green ceramic particle and mix construction.The not dry front surface of earthquake graticule sows one deck plated film high-refractivity reflecting glass microballon, realizes graticule reflecting at night.Constructional method is identical with embodiment one.
Embodiment six
Starting material by weight proportioning are:
Acrylic resin 6.5%;
Quadrol 25%;
Silicon carbide 19.5%;
Plated film high-refractivity reflecting glass microballon 8%;
Colored pyroceramic particle 20%;
Promotor 0;
Phthalocyanine green mill base 6%;
Ethanol 10%;
Silica powder 5%.
Constructional method: blade coating high-strength anti-skid pavement binders, the colored pyroceramic particle of spreading, thickness 3-8mm, the color of ceramic particle is selected by user, as the two component porcelain gage mark coating of brush one deck again after needing the reflective wait graticule of graticule slightly dry, plated film high-refractivity reflecting glass microballon is spread in face, and the color of colored ceramic particle wants consistent with the color of two component gage mark coating.
The above; be only the present invention's preferably embodiment; protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses, the simple change of the technical scheme that can obtain apparently or equivalence are replaced and are all fallen within the scope of protection of the present invention.
Claims (14)
1. a reflective color vibration deceleration marked line composite, is characterized in that, wherein containing main raw material(s) by weight proportioning be:
Caking agent 5-80%;
Solidifying agent 0.2-60%;
Abrasive aggregates 10-50%;
Light reflecting material 5-50%;
Anti-slip material 10-40%;
Promotor 0-10%;
Pigment 5-20%;
Thinner or solvent 1-30%;
Inorganic and organic filler 5-60%.
2. a kind of reflective color vibration deceleration marked line composite according to claim 1, is characterized in that, wherein containing main raw material(s) by weight proportioning be:
Caking agent 10-50%;
Solidifying agent 5-25%;
Abrasive aggregates 25-45%;
Light reflecting material 5-30%;
Anti-slip material 10-40%;
Promotor 0-8%;
Pigment 12-20%;
Thinner or solvent 10-30%;
Inorganic and organic filler 5-60%.
3. a kind of reflective color vibration deceleration marked line composite according to claim 1, is characterized in that, wherein containing main raw material(s) by weight proportioning be:
Caking agent 28%;
Solidifying agent 5%;
Abrasive aggregates 25%;
Light reflecting material 5%;
Anti-slip material 10%;
Promotor 0;
Pigment 12%;
Thinner or solvent 10%;
Inorganic and organic filler 5%.
4. reflective color vibration deceleration marked line composite according to claim 1, is characterized in that, described caking agent is alkyd resin, vinyl ester resin, acrylic acid epoxy resin, unsaturated polyester resin, epoxy resin.
5. reflective color vibration deceleration marked line composite according to claim 1, is characterized in that, described solidifying agent is methylethyl ketone peroxide, cycloethanone peroxide paste, quadrol, fatty amine, cycloaliphatic amines.
6. reflective color vibration deceleration marked line composite according to claim 1, is characterized in that, described abrasive aggregates is that 1-6mm calcines aluminium vanadine, silicon carbide, colored ceramic particle, white quartz sand.
7. reflective color vibration deceleration marked line composite according to claim 1, is characterized in that: described light reflecting material is plated film high-refractivity reflecting glass microballon, reflector.
8. reflective color vibration deceleration marked line composite according to claim 1, is characterized in that, described anti-slip material is high-temperature calcination ceramic particle or colored pyroceramic particle.
9. reflective color vibration deceleration marked line composite according to claim 1, is characterized in that, described promotor is cobalt naphthenate solution or PM-30 or E54.
10. reflective color vibration deceleration marked line composite according to claim 1, it is characterized in that, described pigment is pigment or pigment paste, and described pigment is Rutile type Titanium Dioxide, medium chrome yellow medium yellow, and described pigment paste is bright red mill base, phthalocyanine blue mill base, phthalocyanine green mill base.
11. reflective color vibration deceleration marked line composites according to claim 1, it is characterized in that, described thinner is phthalic acid dimethyl ester, vinylbenzene, acetone, ethanol, toluene, dimethylbenzene, pimelinketone, described solvent is, as epoxy-reactive solvent: rare propyl glycidyl ether, simple function group 501 butyl glycidyl ten thousand ether, 692 card base glycidyl ethers.
12. reflective color vibration deceleration marked line composites according to claim 1, is characterized in that, described mineral filler and organic filler comprise: kaolin, water-ground limestone, light calcium carbonate, talcum powder, dry powder, silica powder.
The constructional method of 13. reflective color vibration deceleration marked line composites according to any one of claim 1-3, it is characterized in that, constructional method one: blade coating high-strength anti-skid pavement binders, the colored pyroceramic particle of spreading, thickness 3-8mm, the color of ceramic particle is selected by user, as the two component porcelain gage mark coating of brush one deck again after needing the reflective wait graticule of graticule slightly dry, plated film high-refractivity reflecting glass microballon is spread in face, and the color of colored ceramic particle wants consistent with the color of two component gage mark coating;
Constructional method two: 828 toluene dissolved dilution used for epoxy resin or add strong solvent dilution, add middle chrome pigment or titanium white powder pigment, after organic and mineral filler agitation grinding, barrelling is for subsequent use, add quadrol rapid stirring before using to mix, add appropriate yellow pyroceramic particle again and plated film high-refractivity reflecting glass microballon stirs, to cast immediately use, when epoxy resin uses, yellowing is serious, configure yellow vibration deceleration marked line proper, require clean for earth cleaning in road surface during construction, according to shape need, mould is placed road surface, the concussion graticule of casting 3-8mm thickness, can use after within 30 minutes, solidifying drying, usage period reaches 10 years, because concussion graticule is mixed with plated film high-refractivity reflecting glass microballon, still reflective after the wearing and tearing of graticule top layer, before earthquake graticule does not solidify, for increasing reflecting at night brightness, one deck plated film high-refractivity reflecting glass microballon can be sowed on surface.
14. 1 kinds of reflective color vibration deceleration marked line composite purposes, it is characterized in that, described reflective color vibration deceleration marked line composite is used for highway traffic safety facility logo, the reflective color vibration deceleration marked line of above combination of materials, can direct pouring construct on freeway toll station square, bridge, tunnel entrances place, highway long and steep downgrade, highway bend and sharp turn, highway crossing and crossroad, traffic accident multi-happening section and the schools such as rainwater road surface slippery situation place, hospital, government bodies need the road surface of car deceleration greatly in front of the door.