CN105108283A - Method for welding dissimilar steel plate of 45 steel and ZG275-485 steel - Google Patents
Method for welding dissimilar steel plate of 45 steel and ZG275-485 steel Download PDFInfo
- Publication number
- CN105108283A CN105108283A CN201510484981.6A CN201510484981A CN105108283A CN 105108283 A CN105108283 A CN 105108283A CN 201510484981 A CN201510484981 A CN 201510484981A CN 105108283 A CN105108283 A CN 105108283A
- Authority
- CN
- China
- Prior art keywords
- welding
- steel
- adopt
- weld
- gas shielded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for welding a dissimilar steel plate of 45 steel and ZG275-485 steel, and relates to the technical field of steel welding. The method mainly comprises three steps of pre-welding preparation, welding and post-welding thermal treatment. According to the welding method, welding joints are good in anti-cracking ability; the welding quality of a component is high; the nondestructive testing of a weld line area is high in qualification rate; and the welding requirement is met.
Description
Technical field
The present invention relates to Plate Welding technical field, is more particularly the welding method of a kind of xenogenesis steel plate 45 steel and ZG275-485 steel.
Background technology
Cast steel ZG275-485H and 45 steel belong to pearlitic steel together, and metallographic structure is identical, and main Welding Problems easily produces hardened structure and welding cold cracking.When cast steel ZG275-485H and 45 steel different steel weld, the carbon equivalent of cast steel ZG275-485H is that 0.37%, 45 steel carbon equivalents reach 0.56%.As w(C) eq < 0.4% time, tendency of hardenability is little, and weldability is good; Work as w(C) eq=0.4%-0.6%, especially w(C) eq>0.5% time, steel easily harden, weldability be deteriorated.In actual components, the thickness of steel-casting and 45 steel is all very large, and anisotropy is large, and crack resistance is poorer.
Summary of the invention
The object of the invention is to make up the deficiencies in the prior art, the welding method of a kind of xenogenesis steel plate 45 steel and ZG275-485 steel is provided.
The object of the invention is to be achieved through the following technical solutions:
A welding method for xenogenesis steel plate 45 steel and ZG275-485 steel, is characterized in that: comprise the following steps:
(1) welds prepares
The first, the selection of welding manner and welding material, adopt the welding of CO2 gas shielded arc welding, welding material is CHT-711 welding wire, and wlding specification is φ 1.2mm;
The second, open double V-groove to welding steel, groove size is 60 °, and root gap is 2mm, and root face size is 2mm;
3rd, adopt oxy-acetylene flame to carry out preheating to bevel for welding and 100mm scope thereof, preheat temperature is 250-300 DEG C;
(2) weld
The first, prime coat welds, and adopt CO2 gas shielded arc welding to weld with the speed of welding of 25-40cm/min, welding current is 200-220A, and weldingvoltage is 23-25V;
The second, packed layer welds, and adopt CO2 gas shielded arc welding to weld with the speed of welding of 20-30cm/min, welding current is 220-260A, and weldingvoltage is 26-30V;
3rd, capping layer welds, and adopt CO2 gas shielded arc welding to weld with the speed of welding of 25-40cm/min, welding current is 180-210A, and weldingvoltage is 22-24V;
(3) post weld heat treatment
By the isothermal holding 3 hours at 300-350 DEG C of the steel plate after welding, then with asbestos cloth insulation slow cooling to environment temperature.
The invention has the advantages that:
The cracking resistance of welding method welding point of the present invention is good, and the welding quality of component is high, and welded seam area Non-Destructive Testing qualification rate is high, meets welding requirements.
Detailed description of the invention
A welding method for xenogenesis steel plate 45 steel and ZG275-485 steel, is characterized in that: comprise the following steps:
(1) welds prepares
The first, the selection of welding manner and welding material, adopt the welding of CO2 gas shielded arc welding, welding material is CHT-711 welding wire, and wlding specification is φ 1.2mm;
The second, open double V-groove to welding steel, groove size is 60 °, and root gap is 2mm, and root face size is 2mm;
3rd, adopt oxy-acetylene flame to carry out preheating to bevel for welding and 100mm scope thereof, preheat temperature is 250-300 DEG C;
(2) weld
The first, prime coat welds, and adopt CO2 gas shielded arc welding to weld with the speed of welding of 25cm/min, welding current is 200A, and weldingvoltage is 23V;
The second, packed layer welds, and adopt CO2 gas shielded arc welding to weld with the speed of welding of 20cm/min, welding current is 220A, and weldingvoltage is 26V;
3rd, capping layer welds, and adopt CO2 gas shielded arc welding to weld with the speed of welding of 25cm/min, welding current is 180A, and weldingvoltage is 22V;
(3) post weld heat treatment
By the isothermal holding 3 hours at 300 DEG C of the steel plate after welding, then with asbestos cloth insulation slow cooling to environment temperature.
Claims (1)
1. a welding method for xenogenesis steel plate 45 steel and ZG275-485 steel, is characterized in that: comprise the following steps:
(1) welds prepares
The first, the selection of welding manner and welding material, adopt the welding of CO2 gas shielded arc welding, welding material is CHT-711 welding wire, and wlding specification is φ 1.2mm;
The second, open double V-groove to welding steel, groove size is 60 °, and root gap is 2mm, and root face size is 2mm;
3rd, adopt oxy-acetylene flame to carry out preheating to bevel for welding and 100mm scope thereof, preheat temperature is 250-300 DEG C;
(2) weld
The first, prime coat welds, and adopt CO2 gas shielded arc welding to weld with the speed of welding of 25-40cm/min, welding current is 200-220A, and weldingvoltage is 23-25V;
The second, packed layer welds, and adopt CO2 gas shielded arc welding to weld with the speed of welding of 20-30cm/min, welding current is 220-260A, and weldingvoltage is 26-30V;
3rd, capping layer welds, and adopt CO2 gas shielded arc welding to weld with the speed of welding of 25-40cm/min, welding current is 180-210A, and weldingvoltage is 22-24V;
(3) post weld heat treatment
By the isothermal holding 3 hours at 300-350 DEG C of the steel plate after welding, then with asbestos cloth insulation slow cooling to environment temperature.