CN105088862A - Surface sizing agent improving water resistance of paperboard - Google Patents
Surface sizing agent improving water resistance of paperboard Download PDFInfo
- Publication number
- CN105088862A CN105088862A CN201510494961.7A CN201510494961A CN105088862A CN 105088862 A CN105088862 A CN 105088862A CN 201510494961 A CN201510494961 A CN 201510494961A CN 105088862 A CN105088862 A CN 105088862A
- Authority
- CN
- China
- Prior art keywords
- water resistance
- cypres
- add
- parts
- sizing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a surface sizing agent improving water resistance of a paperboard. The surface sizing agent comprises, by weight, 15-20 parts of hydroxy propyl cellulose, 2-6 parts of medical stone, 0.5-1.5 parts of cationic etherifying agent, 12-18 parts of alkyl ketene dimmer, 0.06-0.08 part of sodium bicarbonate, 0.02-0.04 part of initiator, 0.4-1.4 parts of viscosity stabilizer and 65-70 parts of deionized water. Compared with the prior art, the surface sizing agent has the advantages that after the hydroxy propyl cellulose is modified, the production technology is simplified, the activity of a water-resistant monomer is improved, the use amount of the hydroxy propyl cellulose is reduced, the production cost is reduced, the water resistance of the obtained surface sizing agent is high, stability is good, the paper tension is strengthened, the sizing efficiency is high, and economic benefits are obvious.
Description
Technical field
The invention belongs to field of packaging material, be specifically related to a kind of Cypres improving cardboard WATER RESISTANCE.
Background technology
Top sizing is an operation in paper or board making process, be usually located at the oven dry portion end of paper machine, page is made to spray one deck glue when non-bone dry but has certain intensity, form one deck glued membrane through follow-up drying on paper and paperboard surface, thus reach the object changing Paper or cardboard surface property.From the development of paper industry, paper surface-sizing is one of indispensable process, can add by top sizing the surface additive that people improves page characteristic or increase Paper or cardboard WATER RESISTANCE.Now commercially all types of Cypres, aborning because cellulose is suitably processed, makes WATER RESISTANCE monomer reactivity more weak, affects the WATER RESISTANCE of Cypres.
Summary of the invention
The object of the invention is, for the more weak problem of existing WATER RESISTANCE monomer reactivity, to provide a kind of Cypres improving cardboard WATER RESISTANCE.
The present invention is achieved by the following technical solutions: a kind of Cypres improving cardboard WATER RESISTANCE, comprise the component of following weight portion: hydroxypropyl cellulose 15-20 part, medical stone 2-6 part, cationic etherifying agent 0.5-1.5 part, alkyl ketene dimer 12-18 part, sodium bicarbonate 0.06-0.08 part, initator 0.02-0.04 part, viscosity stabiliser 0.4-1.4 part, deionized water 65-70 part.
As further improvement of these options, described initator is one or both combination solvents of acrylate solvent or vinyl acetate solvent, and solvent strength is 20-25wt%.
As further improvement of these options, described viscosity stabiliser is the diethylene glycol solution of 2 ethyl hexanoic acid potassium, and solution density is 1.09-1.13g/mL.
As further improvement of these options, its preparation method is as follows:
(1) add hydroxypropyl cellulose in deionized water, medical stone and alkyl ketene dimer mix in proportion in inert gas, add cationic etherifying agent, sodium bicarbonate and initator, make it react, and obtain CATION jelly;
(2) in CATION jelly, add viscosity stabiliser mixing, add NaOH simultaneously and solution pH value is adjusted to 7-9, reaction;
(3) by gained solution after reaction in step (2), add deionized water, after water-solubleization, heat up in a steamer organic compound, the Cypres of the cardboard WATER RESISTANCE that is improved.
As further improvement of these options, step reacts 4-6 hour in (1) in 30-50 DEG C.
As further improvement of these options, in step (2), after jelly cooling in step (1), in 55-65 DEG C, react 1-2 hour, then cool to 25-35 DEG C.
The present invention has the following advantages compared to existing technology: by modified for hydroxypropyl cellulose simplification production technology, improve the activity of water resistant monomer, thus reduce the consumption of hydroxypropyl cellulose, reduce production cost, gained Cypres WATER RESISTANCE improves, and stability is better, strengthens paper pull, sizing efficiency is high, and economic benefit is obvious.
Detailed description of the invention
Embodiment 1
The deionized water of 50 weight portions is equipped with in the reaction unit that inert gas is housed, add the hydroxypropyl cellulose of 20 weight portions, the medical stone of 4 weight portions and the alkyl ketene dimer of 14 weight portions, reaction unit is heated to 45 DEG C, stir and add the acrylate solvent that the cationic etherifying agent of 0.5 weight portion, the sodium bicarbonate of 0.06 weight portion and 0.04 weight portion concentration are 20wt%, react 4 hours; Then cool to 30 DEG C, place and to add diethylene glycol solution that 0.5 parts by weight solution density is the 2 ethyl hexanoic acid potassium of 1.10g/L after 2 hours and be heated to 60 DEG C, add NaOH and solution pH value is adjusted to 8, react after 1 hour, cool to 25 DEG C; Add the deionized water of 10 weight portions, after dissolving, heat up in a steamer organic compound, obtain Cypres.
Embodiment 2
The deionized water of 55 weight portions is equipped with in the reaction unit that inert gas is housed, add the hydroxypropyl cellulose of 15 weight portions, the medical stone of 2 weight portions and the alkyl ketene dimer of 16 weight portions, reaction unit is heated to 45 DEG C, stir and add the acrylate solvent that the cationic etherifying agent of 0.5 weight portion, the sodium bicarbonate of 0.07 weight portion and 0.03 weight portion concentration are 25wt%, react 5 hours; Then cool to 30 DEG C, place and to add diethylene glycol solution that 0.5 parts by weight solution density is the 2 ethyl hexanoic acid potassium of 1.10g/L after 1 hour and be heated to 55 DEG C, add NaOH and solution pH value is adjusted to 7, react after 1 hour, cool to 30 DEG C; Add the deionized water of 10 weight portions, after dissolving, heat up in a steamer organic compound, obtain Cypres.
Embodiment 3
The deionized water of 55 weight portions is equipped with in the reaction unit that inert gas is housed, add the hydroxypropyl cellulose of 20 weight portions, the medical stone of 6 weight portions and the alkyl ketene dimer of 12 weight portions, reaction unit is heated to 30 DEG C, stir and add the vinyl acetate solvent that the cationic etherifying agent of 0.5 weight portion, the sodium bicarbonate of 0.08 weight portion and 0.02 weight portion concentration are 25wt%, react 5 hours; Then cool to 30 DEG C, place and to add diethylene glycol solution that 0.5 parts by weight solution density is the 2 ethyl hexanoic acid potassium of 1.13g/L after 1.5 hours and be heated to 60 DEG C, add NaOH and solution pH value is adjusted to 8, react after 1 hour, cool to 25 DEG C; Add the deionized water of 15 weight portions, after dissolving, heat up in a steamer organic compound, obtain Cypres.
Embodiment 4
Select the mode of size press to carry out gluing, select the cardboard that four groups are identical, one group of blank does not process, and other three components do not impose product in embodiment 1-3, and detect applying glue rate respectively, the surface strength after a week and the parameter of ring crush index draw following table:
Data determination: applying glue rate measures and adopts GB/T460-1989 method to detect pattern to be measured; Cobb pH-value determination pH adopts GB/T1540-2002 method to detect pattern to be measured; Surface strength measures and adopts GB/T22365-2008 method to detect pattern to be measured; Ring crush intensity measures and adopts GB/T2679.8-1995 method to detect pattern to be measured.
Table 1
Data as can be seen from table 1, the sizing agent produced in the present invention, unit are water imbibition obviously reduces, explanation WATER RESISTANCE strengthens, applying glue rate, and surface strength and ring crush index have increase to a certain degree, illustrate that applying glue back cardboard stability improves, paper pull strengthens.
Claims (6)
1. one kind is improved the Cypres of cardboard WATER RESISTANCE, it is characterized in that, comprise the component of following weight portion: hydroxypropyl cellulose 10-20 part, medical stone 2-6 part, cationic etherifying agent 0.5-1.5 part, alkyl ketene dimer 12-18 part, sodium bicarbonate 0.06-0.08 part, initator 0.02-0.04 part, viscosity stabiliser 0.4-1.4 part, deionized water 65-70 part.
2. a kind of Cypres improving cardboard WATER RESISTANCE as claimed in claim 1, it is characterized in that, described initator is one or both combination solvents of acrylate solvent or vinyl acetate solvent, and solvent strength is 25wt%.
3. a kind of Cypres improving cardboard WATER RESISTANCE as claimed in claim 1, it is characterized in that, described viscosity stabiliser is the diethylene glycol solution of 2 ethyl hexanoic acid potassium, and solution density is 1.09-1.13g/mL.
4. a kind of Cypres improving cardboard WATER RESISTANCE as claimed in claim 1, it is characterized in that, its preparation method is as follows:
(1) add hydroxypropyl cellulose in deionized water, medical stone and alkyl ketene dimer mix in proportion in inert gas, add cationic etherifying agent, sodium bicarbonate and initator, make it react, and obtain CATION jelly;
(2) in CATION jelly, add viscosity stabiliser mixing, add NaOH simultaneously and solution pH value is adjusted to 7-9, reaction;
(3) by gained solution after reaction in step (2), add deionized water, after water-solubleization, heat up in a steamer organic compound, the Cypres of the cardboard WATER RESISTANCE that is improved.
5. a kind of Cypres improving cardboard WATER RESISTANCE as claimed in claim 1, it is characterized in that, step reacts 4-6 hour in (1) in 30-50 DEG C.
6. a kind of Cypres improving cardboard WATER RESISTANCE as claimed in claim 1, is characterized in that, in step (2), after jelly cooling in step (1), reacts 1-2 hour, then cool to 25-35 DEG C in 55-65 DEG C.