CN105088327A - Stainless steel electrolytic polishing solution formula and process - Google Patents
Stainless steel electrolytic polishing solution formula and process Download PDFInfo
- Publication number
- CN105088327A CN105088327A CN201510490263.XA CN201510490263A CN105088327A CN 105088327 A CN105088327 A CN 105088327A CN 201510490263 A CN201510490263 A CN 201510490263A CN 105088327 A CN105088327 A CN 105088327A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- sulfuric acid
- phosphoric acid
- electrolytic polishing
- steel electrolytic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a stainless steel electrolytic polishing solution formula and a process, and belongs to the technical field of stainless steel surface treatment. The stainless steel electrolytic polishing solution formula comprises the following raw materials in percentage by mass: 51-55% of phosphoric acid with specific gravity of 1.70 and content of 85%, 42-46% of sulfuric acid with specific gravity of 1.84 and content of 98%, and 3% of a brightening additive with specific gravity of 1.05-1.15, and a TXD110 brightening agent, wherein the brightening additive consists of diethyl methyl methanol, polyoxyethylene ether and polyoxypropylene glycerol ether in a ratio of 1 to 1.5 to 0.03. The stainless steel electrolytic polishing solution formula has the advantages that: the phosphoric acid and the sulfuric acid are selected as basic raw materials, the brightening agent in certain proportion is added, and relevant parameters of temperature, current density and voltage of the brightening agent are reasonably controlled, so that the high-brightness polishing effect can be realized; and moreover, electrolyte can reach a two-year long-period trough replacing period, polishing current is low, energy consumption is low, the formula is simple, and the preparation process is easy to control.
Description
Technical field
The present invention relates to stainless steel surface processing technology field, be specially a kind of stainless steel electrolytic polishing fluid formula and technique.
Background technology
Electropolishing also claims electropolishing, it is the electrochemical dissolution phenomenon utilizing anode to produce in electrolyzer, make microscopic protrusions part generation selective dissolution on anode to form the method for smooth-flat-surface, it is a complicated anode oxidation process, along with dissolving and the oxidation of workpiece surface, but be different from anodic oxidation.
Stainless electropolishing solution, general all based on phosphate solution and phosphoric acid, sulfuric acid is auxiliary, add some additives to be again made, and the material concentration of phosphoric acid and sulfuric acid and ratio requirement are determined according to wanted polishing workpiece, its controling parameters of simultaneously different polishing fluids is different, and the conservative control of temperature, current density, polishing time plays vital effect to final polishing effect.
The present invention is mainly for 304 and the stainless surface treatment of 420 class number, and provide one electropolishing liquid formula targetedly, it mainly solves the problem that existing stainless steel electrolytic polishing fluid contains the harmful ions such as chromium.
Summary of the invention
The present invention for the technical problem that solves for providing a kind of stainless steel electrolytic polishing fluid formula and technique, it is for solving 304 and No. 420 stainless surface treatment problems, it selects phosphoric acid and sulfuric acid to be basic raw material, and add a certain proportion of brightening agent, its temperature of conservative control, current density, voltage correlation parameter, thus can realize the polishing effect of high light, and the long period that electrolytic solution can reach 2 years changes the groove phase.
Technical solution problem of the present invention adopts following technical scheme:
A kind of stainless steel electrolytic polishing fluid formula, it is characterized in that: its phosphoric acid, sulfuric acid and by diethylmethyl methyl alcohol, Soxylat A 25-7, the brightener of polypropylene glycerol aether composition, TXD110 brightening agent, the mass percent of described phosphoric acid is 51-55%, proportion is 1.70, content is 85%, the mass percent of described sulfuric acid is 42-46%, proportion is 1.84, content is 98%, described brightener mass percent is 3%, proportion is 1.05-1.15%, the diethylmethyl methyl alcohol of described brightener, Soxylat A 25-7, polypropylene glycerol aether proportioning is 1:1.5:0.03.
A technique for stainless steel electrolytic polishing fluid, is characterized in that it comprises the steps:
(1) phosphoric acid and sulfuric acid mix and blend are uniformly dissolved and make nitration mixture;
(2) in above-mentioned nitration mixture, add brightener, stirring and dissolving evenly obtains electrolytic solution;
(3) during polishing workpiece, electrolytic solution working temperature controls at 55-80 DEG C, and rectified voltage is 7-9V, and current density is 8-15A/dm
2.
The present invention compared with prior art, its beneficial effect is: it selects phosphoric acid and sulfuric acid to be basic raw material, and add a certain proportion of brightening agent, its temperature of conservative control, current density, voltage correlation parameter, thus the polishing effect that can realize high light, and the long period that electrolytic solution can reach 2 years changes the groove phase, polishing electric current is low, energy consumption is low, and formula is simple, and configuration technique is easy to manipulation.
Embodiment
The technique means realized to make the present invention, character of innovation, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
A kind of stainless steel electrolytic polishing fluid formula, its phosphoric acid, sulfuric acid and the brightener be made up of diethylmethyl methyl alcohol, Soxylat A 25-7, polypropylene glycerol aether, TXD110 brightening agent, the mass percent of phosphoric acid is 55%, proportion is 1.70, content is 85%, the mass percent of sulfuric acid is 42%, proportion is 1.84, content is 98%, brightener mass percent is 3%, proportion is 1.05%, and the diethylmethyl methyl alcohol of brightener, Soxylat A 25-7, polypropylene glycerol aether proportioning are 1:1.5:0.03.
A technique for stainless steel electrolytic polishing fluid, it comprises the steps:
(1) phosphoric acid and sulfuric acid mix and blend are uniformly dissolved and make nitration mixture;
(2) in above-mentioned nitration mixture, add brightener, stirring and dissolving evenly obtains electrolytic solution;
(3) during polishing workpiece, electrolytic solution working temperature controls at 60 DEG C, and rectified voltage is 8V, and current density is 10A/dm
2.
More than show and describe ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (2)
1. a stainless steel electrolytic polishing fluid formula, it is characterized in that: its phosphoric acid, sulfuric acid and by diethylmethyl methyl alcohol, Soxylat A 25-7, the brightener of polypropylene glycerol aether composition, TXD110 brightening agent, the mass percent of described phosphoric acid is 51-55%, proportion is 1.70, content is 85%, the mass percent of described sulfuric acid is 42-46%, proportion is 1.84, content is 98%, described brightener mass percent is 3%, proportion is 1.05-1.15%, the diethylmethyl methyl alcohol of described brightener, Soxylat A 25-7, polypropylene glycerol aether proportioning is 1:1.5:0.03.
2. a technique for stainless steel electrolytic polishing fluid, is characterized in that it comprises the steps:
(1) phosphoric acid and sulfuric acid mix and blend are uniformly dissolved and make nitration mixture;
(2) in above-mentioned nitration mixture, add brightener, stirring and dissolving evenly obtains electrolytic solution;
(3) during polishing workpiece, electrolytic solution working temperature controls at 55-80 DEG C, and rectified voltage is 7-9V, and current density is for being 8-15A/dm
2.