CN105088203A - Anticorrosion chromate-free passivation processing liquid for aluminum profile and preparation method thereof - Google Patents
Anticorrosion chromate-free passivation processing liquid for aluminum profile and preparation method thereof Download PDFInfo
- Publication number
- CN105088203A CN105088203A CN201510521746.1A CN201510521746A CN105088203A CN 105088203 A CN105088203 A CN 105088203A CN 201510521746 A CN201510521746 A CN 201510521746A CN 105088203 A CN105088203 A CN 105088203A
- Authority
- CN
- China
- Prior art keywords
- silane coupling
- coupling agent
- anticorrosion
- modified nano
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed is anticorrosion chromate-free passivation processing liquid for an aluminum profile. The anticorrosion chromate-free passivation processing liquid for the aluminum profile comprises, by weight, 9.8-10.2 parts of cerium nitrate, 2-2.2 parts of potassium permanganate, 0.1-0.2 part of vitamin E, 0.3-0.4 part of succinate, 0.6-0.7 part of fluohafnate, 0.6-0.8 part of styrene, 0.2-0.3 part of acrylamide, 0.4-0.5 part of acrylic acid, 0.05-0.1 part of azodiisobutyronitrile, 0.5-0.6 part of sodium allylsulfonate, 0.02-0.03 part of sodium lauryl sulfate, 0.9-1 part of cetane, 0.3-0.4 part of silane coupling agent KH570 surface modified nano-silica, 0.3-0.4 part of silane coupling agent KH570 surface modified nano titanium dioxide and the appropriate amount of deionized water. A film formed by the anticorrosion chromate-free passivation processing liquid for the aluminum profile is denser and more uniform. Due to the fact that the fluohafnate is used, the densification and the corrosion resistance of the film are improved, and the comprehensive cost is low.
Description
Technical field
The present invention relates to chromium-free metal surface treatment agent technical field, particularly relate to anticorrosion non-chromium passivation treatment fluid of a kind of aluminium section bar and preparation method thereof.
Background technology
Spray-painted aluminum profile normal chromic salt chemistry deactivation method that adopts before application carries out pre-treatment, but hexavalent chromium has carcinogenesis to human body in chromic salt process, deal with improperly and can cause serious pollution to environment, therefore chromating technique receives great concern, and some country has limited it and used.Recent domestic has carried out large quantity research to non-chromium inactivating technique, develops the multiple passivating solution system for handling such as rare earth, cobalt salt, silicate, molybdic acid, titanium/zirconate, has certain corrosion resistance nature.At present, employing rare-earth cerium compound is that the research of the non-chromium inactivating technique of main component is more, but cerium salt and oxidant species various, adopt cerous nitrate and potassium permanganate composite treating agent to carry out Passivation Treatment to aluminium section bar, obtain good film-formation result and outward appearance, but still to there is passive film even not for the passivation effect of this treatment agent, compactness is inadequate, processing speed is slow, the imperfect shortcoming of corrosion resistance, needs to improve.
Summary of the invention
The object of the invention is exactly the defect in order to make up prior art, provides anticorrosion non-chromium passivation treatment fluid of a kind of aluminium section bar and preparation method thereof.
The present invention is achieved by the following technical solutions:
The anticorrosion non-chromium passivation treatment fluid of a kind of aluminium section bar, be made up of the raw material of following weight part: cerous nitrate 9.8-10.2, potassium permanganate 2-2.2, vitamin-E 0.1-0.2, succinate 0.3-0.4, fluorine hafnium acid 0.6-0.7, vinylbenzene 0.6-0.8, acrylamide 0.2-0.3, vinylformic acid 0.4-0.5, Diisopropyl azodicarboxylate 0.05-0.1, sodium allylsulfonate 0.5-0.6, sodium lauryl sulphate 0.02-0.03, n-Hexadecane 0.9-1, silane coupling agent KH570 surface modified nano silicon 0.3-0.4, silane coupling agent KH570 surface-modified nano titanium dioxide 0.3-0.4, deionized water is appropriate.
The preparation method of the anticorrosion non-chromium passivation treatment fluid of described aluminium section bar, comprises the following steps:
(1) sodium lauryl sulphate is dissolved in the deionized water of 7-7.5 weight part and forms the aqueous solution, n-Hexadecane is mixed with vinylbenzene, silane coupling agent KH570 surface modified nano silicon, silane coupling agent KH570 surface-modified nano titanium dioxide, succinate is added after being stirred to dissolving, then by above two kinds of liquid mixing, supersound process 3-4min under ultrasonic cell disruptor, obtains emulsion; Described emulsion and acrylamide, vinylformic acid, sodium allylsulfonate are mixed, stirs, pass into nitrogen 15-16min, regulate pH=8, be warming up to 60-62 DEG C, add Diisopropyl azodicarboxylate, continue stirring reaction 1-2h, obtain membrane-forming agent;
(2) cerous nitrate is mixed with the aqueous solution of 9.8-10.2g/L, add potassium permanganate by the concentration of 2-2.2g/L again and be mixed with solution, add membrane-forming agent and other remaining components that 0.9-1.1wt% (1) step obtains again, stir, supersound process 3-4min under ultrasonic cell disruptor, to obtain final product.
First aluminium section bar is carried out pre-treatment during use, then be immersed in treatment solution by aluminium section bar and carry out Passivation Treatment, temperature is 15-45 DEG C, and pH value is 1.8-4.5, and process 20-23min, takes out, and rinses with water, dries.
Advantage of the present invention is: treatment solution of the present invention, by using cerous nitrate, potassium permanganate, decreases environmental pollution; Film is made into by using nano silicon, nano titanium oxide and organic materials, make nanoparticle dispersed with system, can promote that passivation uniform composition is coated on aluminium shape surface fast, the uniform oxide film of quick formation, and nano silicon, nano titanium oxide have good antioxidant property, slowing down corrosion speed, improve paint application performance, reduce hole simultaneously, make the film of formation finer and close, even; By using vitamin-E, succinate, improve film-forming properties, by using the acid of fluorine hafnium, improve compactness and the erosion resistance of film, comprehensive cost is low.
Embodiment
The anticorrosion non-chromium passivation treatment fluid of a kind of aluminium section bar, is made up of the raw material of following weight part (kilogram): cerous nitrate 9.8, potassium permanganate 2, vitamin-E 0.1, succinate 0.3, fluorine hafnium acid 0.6, vinylbenzene 0.6, acrylamide 0.2, vinylformic acid 0.4, Diisopropyl azodicarboxylate 0.05, sodium allylsulfonate 0.5, sodium lauryl sulphate 0.02, n-Hexadecane 0.9, silane coupling agent KH570 surface modified nano silicon 0.3, silane coupling agent KH570 surface-modified nano titanium dioxide 0.3, deionized water are appropriate.
The preparation method of the anticorrosion non-chromium passivation treatment fluid of described aluminium section bar, comprises the following steps:
(1) sodium lauryl sulphate is dissolved in the deionized water of 7 weight parts and forms the aqueous solution, n-Hexadecane is mixed with vinylbenzene, silane coupling agent KH570 surface modified nano silicon, silane coupling agent KH570 surface-modified nano titanium dioxide, succinate is added after being stirred to dissolving, then by above two kinds of liquid mixing, supersound process 3min under ultrasonic cell disruptor, obtains emulsion; Described emulsion and acrylamide, vinylformic acid, sodium allylsulfonate are mixed, stirs, pass into nitrogen 15min, regulate pH=8, be warming up to 60 DEG C, add Diisopropyl azodicarboxylate, continue stirring reaction 1h, obtain membrane-forming agent;
(2) cerous nitrate is mixed with the aqueous solution of 9.8g/L, add potassium permanganate by the concentration of 2g/L again and be mixed with solution, then add the membrane-forming agent and other remaining components that 0.9wt% (1) step obtains, stir, supersound process 3min under ultrasonic cell disruptor, to obtain final product.
First aluminium section bar is carried out pre-treatment during use, then be immersed in treatment solution by aluminium section bar and carry out Passivation Treatment, temperature is 15 DEG C, and pH value is 1.8, and process 20min, takes out, and rinses with water, dries.
Passive film surface is finer and close, and naked eyes this film visible is golden yellow, has good outward appearance; After the test of the acetic acid salt spray of 1000h, corrosion-free, without obscission.
Claims (2)
1. the anticorrosion non-chromium passivation treatment fluid of aluminium section bar, it is characterized in that being made up of the raw material of following weight part: cerous nitrate 9.8-10.2, potassium permanganate 2-2.2, vitamin-E 0.1-0.2, succinate 0.3-0.4, fluorine hafnium acid 0.6-0.7, vinylbenzene 0.6-0.8, acrylamide 0.2-0.3, vinylformic acid 0.4-0.5, Diisopropyl azodicarboxylate 0.05-0.1, sodium allylsulfonate 0.5-0.6, sodium lauryl sulphate 0.02-0.03, n-Hexadecane 0.9-1, silane coupling agent KH570 surface modified nano silicon 0.3-0.4, silane coupling agent KH570 surface-modified nano titanium dioxide 0.3-0.4, deionized water is appropriate.
2. the preparation method of the anticorrosion non-chromium passivation treatment fluid of aluminium section bar according to claim 1, is characterized in that comprising the following steps:
(1) sodium lauryl sulphate is dissolved in the deionized water of 7-7.5 weight part and forms the aqueous solution, n-Hexadecane is mixed with vinylbenzene, silane coupling agent KH570 surface modified nano silicon, silane coupling agent KH570 surface-modified nano titanium dioxide, succinate is added after being stirred to dissolving, then by above two kinds of liquid mixing, supersound process 3-4min under ultrasonic cell disruptor, obtains emulsion; Described emulsion and acrylamide, vinylformic acid, sodium allylsulfonate are mixed, stirs, pass into nitrogen 15-16min, regulate pH=8, be warming up to 60-62 DEG C, add Diisopropyl azodicarboxylate, continue stirring reaction 1-2h, obtain membrane-forming agent;
(2) cerous nitrate is mixed with the aqueous solution of 9.8-10.2g/L, add potassium permanganate by the concentration of 2-2.2g/L again and be mixed with solution, add membrane-forming agent and other remaining components that 0.9-1.1wt% (1) step obtains again, stir, supersound process 3-4min under ultrasonic cell disruptor, to obtain final product.