CN105086710A - Emulsion paint topcoat with functions of absorbing carbon dioxide and purifying air and preparation method thereof - Google Patents
Emulsion paint topcoat with functions of absorbing carbon dioxide and purifying air and preparation method thereof Download PDFInfo
- Publication number
- CN105086710A CN105086710A CN201510548874.5A CN201510548874A CN105086710A CN 105086710 A CN105086710 A CN 105086710A CN 201510548874 A CN201510548874 A CN 201510548874A CN 105086710 A CN105086710 A CN 105086710A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion paint
- carbon dioxide
- powder
- realized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an emulsion paint topcoat with functions of absorbing carbon dioxide and purifying air. The emulsion paint topcoat is characterized by being prepared by the following raw materials in parts by weight: 28 to 33 parts of silicone acrylic emulsion, 3 to 5 parts of polyurethane prepolymer, 13 to 16 parts of far-infrared ceramic powder, 1 to 2 parts of polyacrylamide, 0.1 to 0.2 part of potassium persulfate, 0.8 to 1.2 parts of APM (aspartame)-95, 10 to 13 parts of ash calcium powder, 3 to 5 parts of calcium peroxide, 95 to 100 parts of water, and 7 to 9 parts of mixed plant size. The emulsion paint topcoat has the advantages that by using the ash calcium powder to react with the carbon dioxide, the content of carbon dioxide is reduced; by adding the far-infrared ceramic powder, the effect of releasing negative ions is realized, and the certain health-care effect is realized; by adding the mixed plant size, the safety, environment-friendly and poisonless effects are realized, the volatizing amount of organic chemical compounds is reduced, the fragrance is particular, the refreshing effect is realized, the antibacterial and sterilization effects are realized, and the air can be purified; the emulsion paint topcoat can provide high-quality health indoor environments for hospitals, nursing homes, scientific and research organizations, and the like.
Description
Technical field
The present invention relates to a kind of coating and preparation method thereof, particularly emulsion paint finish paint of purifying air of a kind of absorbing carbon dioxide and preparation method thereof.
Background technology
Along with the development with emulsion paint technology that improves constantly of living standards of the people, healthy particularly important to people of indoor environment, especially the environment of public place enjoys people to pay close attention to, movement of population and the intensive places such as picture hospital, school, hotel, will regularly carry out disinfection in multicell, reduce bacteria breed, thus ensure that the air of people is healthy pure and fresh.The present invention attempts to start with from emulsion paint, invent a kind of interiro wall latex paint, natural vegetable powder is made slurry mix with emulsion paint, not only smell is pure and fresh, and has certain sterilization and health-care effect, be applicable to the place such as medical institutions, gymnasium to use, and the plant constituent that emulsion paint adds, there is natural pigment, not only healthy nontoxic, and color is simple and elegant, attractive in appearance.
Present emulsion paint all develops into the emulsion paint improving indoor environment, and the present invention is while interpolation plant slurry, and being prepared into can the emulsion paint of absorbing carbon dioxide, improves indoor environment further.The main component of sierozem power is calcium hydroxide, when gas concentration lwevel height in air, can react, reduce gas concentration lwevel with sierozem power.
Summary of the invention
The object of this invention is to provide emulsion paint finish paint that a kind of absorbing carbon dioxide purifies air and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
The emulsion paint finish paint that absorbing carbon dioxide purifies air, is made up of the raw material of following weight part: organosilicon crylic acid latex 28-33, base polyurethane prepolymer for use as 3-5, far infrared ceramic powder 13-16, polyacrylamide 1-2, Potassium Persulphate 0.1-0.2, APM-950.8-1.2, sierozem power 10-13, calcium peroxide 3-5, water 95-100, mixed plant slurry 7-9;
Described mixed plant slurry is prepared from by the raw material of following weight part: bastard tamarind legume 1-2, elscholtiza 2-3, Medcinal Evodia Fruit 2-3, root of Dahurain angelica 3-5, lotus root starch 2-4, gum arabic powder 1-2, Leafy twigs of Oriental Arborvitae 3-4, flores aurantii 0.5-0.8, rosin 0.8-1, attapulgite clay 2.5-3.5, water 45-50; Preparation method is after bastard tamarind legume, elscholtiza, Medcinal Evodia Fruit, the root of Dahurain angelica, Leafy twigs of Oriental Arborvitae, flores aurantii being cleaned up, and then dry 3-5 hour at 60 DEG C-70 DEG C puts into pulverizer and be ground into 300-500 object mixed powder; Then lotus root starch, gum arabic powder are put into water and stirred, be heated to 75 DEG C-90 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.
The emulsion paint finish paint that a kind of absorbing carbon dioxide of the present invention purifies air, be made up of following concrete steps:
(1) by base polyurethane prepolymer for use as heating in water bath to 60 DEG C-70 DEG C, be incubated 0.5-1 hour while stirring, be then cooled to room temperature, slowly add organosilicon crylic acid latex, stirring reaction 30-40 minute, stand-by;
(2) far infrared ceramic powder, potassium sulfate, sierozem power, calcium peroxide are put into sand mill, grinding 1.5-2 hour, obtain levigate powder, then all the other remaining components except mixed plant slurry are added, under 900-1000 rev/min of condition, stir 30-40 minute, then grinding obtains 600-800 order slurry;
(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, stir and get final product.
The invention has the beneficial effects as follows: the present invention utilizes sierozem power can react with carbonic acid gas, thus reduce content, add far infrared ceramic powder, there is the effect of anion releasing, there is certain health-care effect; Add mixed plant slurry, safety and environmental protection is nontoxic, and can reduce the volatile quantity of organic compound, fragrance is special, can produce refreshing effect to the mind, and can antibiotic and sterilizing, reaches the effect purified air; The present invention can provide the indoor environment of high-quality health for hospital, nursing house, scientific research institution etc.
Specific embodiments
Below by specific examples, the present invention is described in detail.
The emulsion paint finish paint that absorbing carbon dioxide purifies air, is made up of the raw material of following weight part (kilogram): organosilicon crylic acid latex 28, base polyurethane prepolymer for use as 3, far infrared ceramic powder 13, polyacrylamide 1, Potassium Persulphate 0.1, APM-950.8, sierozem power 10, calcium peroxide 3, water 95, mixed plant slurry 7;
Described mixed plant slurry is prepared from by the raw material of following weight part (kilogram): bastard tamarind legume 1, elscholtiza 2, Medcinal Evodia Fruit 2, the root of Dahurain angelica 3, lotus root starch 2, gum arabic powder 1, Leafy twigs of Oriental Arborvitae 3, flores aurantii 0.5, rosin 0.8, attapulgite clay 2.5, water 45; Preparation method is after bastard tamarind legume, elscholtiza, Medcinal Evodia Fruit, the root of Dahurain angelica, Leafy twigs of Oriental Arborvitae, flores aurantii being cleaned up, and then dry 3-5 hour at 60 DEG C-70 DEG C puts into pulverizer and be ground into 300-500 object mixed powder; Then lotus root starch, gum arabic powder are put into water and stirred, be heated to 75 DEG C-90 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.
The emulsion paint finish paint that a kind of absorbing carbon dioxide of the present invention purifies air, be made up of following concrete steps:
(1) by base polyurethane prepolymer for use as heating in water bath to 60 DEG C-70 DEG C, be incubated 0.5-1 hour while stirring, be then cooled to room temperature, slowly add organosilicon crylic acid latex, stirring reaction 30-40 minute, stand-by;
(2) far infrared ceramic powder, potassium sulfate, sierozem power, calcium peroxide are put into sand mill, grinding 1.5-2 hour, obtain levigate powder, then all the other remaining components except mixed plant slurry are added, under 900-1000 rev/min of condition, stir 30-40 minute, then grinding obtains 600-800 order slurry;
(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, stir and get final product.
This emulsion paint can adopt the form of construction work of roller coating to construct.The emulsion paint appearance of film obtained according to the method is normal, and be less than 2 hours time of drying, opacifying power is 0.964, and water-fast 96 hours without exception, and alkaline-resisting 48 hours without exception, and abrasion resistance is greater than 2000 times.
Claims (2)
1. the emulsion paint finish paint that purifies air of an absorbing carbon dioxide, it is characterized in that, be made up of the raw material of following weight part: organosilicon crylic acid latex 28-33, base polyurethane prepolymer for use as 3-5, far infrared ceramic powder 13-16, polyacrylamide 1-2, Potassium Persulphate 0.1-0.2, APM-950.8-1.2, sierozem power 10-13, calcium peroxide 3-5, water 95-100, mixed plant slurry 7-9;
Described mixed plant slurry is prepared from by the raw material of following weight part: bastard tamarind legume 1-2, elscholtiza 2-3, Medcinal Evodia Fruit 2-3, root of Dahurain angelica 3-5, lotus root starch 2-4, gum arabic powder 1-2, Leafy twigs of Oriental Arborvitae 3-4, flores aurantii 0.5-0.8, rosin 0.8-1, attapulgite clay 2.5-3.5, water 45-50; Preparation method is after bastard tamarind legume, elscholtiza, Medcinal Evodia Fruit, the root of Dahurain angelica, Leafy twigs of Oriental Arborvitae, flores aurantii being cleaned up, and then dry 3-5 hour at 60 DEG C-70 DEG C puts into pulverizer and be ground into 300-500 object mixed powder; Then lotus root starch, gum arabic powder are put into water and stirred, be heated to 75 DEG C-90 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.
2. the emulsion paint finish paint that purifies air of a kind of absorbing carbon dioxide according to claim 1, is characterized in that, be made up of following concrete steps:
(1) by base polyurethane prepolymer for use as heating in water bath to 60 DEG C-70 DEG C, be incubated 0.5-1 hour while stirring, be then cooled to room temperature, slowly add organosilicon crylic acid latex, stirring reaction 30-40 minute, stand-by;
(2) far infrared ceramic powder, potassium sulfate, sierozem power, calcium peroxide are put into sand mill, grinding 1.5-2 hour, obtain levigate powder, then all the other remaining components except mixed plant slurry are added, under 900-1000 rev/min of condition, stir 30-40 minute, then grinding obtains 600-800 order slurry;
(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, stir and get final product.