CN105086518A - Black iron oxide pigment containing bamboo charcoal powder and preparation method thereof - Google Patents

Black iron oxide pigment containing bamboo charcoal powder and preparation method thereof Download PDF

Info

Publication number
CN105086518A
CN105086518A CN201510455518.9A CN201510455518A CN105086518A CN 105086518 A CN105086518 A CN 105086518A CN 201510455518 A CN201510455518 A CN 201510455518A CN 105086518 A CN105086518 A CN 105086518A
Authority
CN
China
Prior art keywords
iron oxide
black
bamboo charcoal
charcoal powder
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510455518.9A
Other languages
Chinese (zh)
Inventor
崔前志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd
Original Assignee
ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd filed Critical ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd
Priority to CN201510455518.9A priority Critical patent/CN105086518A/en
Publication of CN105086518A publication Critical patent/CN105086518A/en
Pending legal-status Critical Current

Abstract

The invention discloses black iron oxide pigment containing bamboo charcoal powder. The black iron oxide pigment is characterized by comprising, by weight, 80-100 parts of modified black iron oxide, 4-8 parts of the bamboo charcoal powder, 1-2 parts of nano calcium carbonate, 3-5 parts of sodium tripolyphosphate, 6-8 parts of sodium silicate, 0.1-0.2 part of azodiisobutyronitrile, 10-15 parts of styrene, 1-2 parts of sucrose fatty acid ester, 1-2 parts of palm oil and 1-2 parts of barium stearate. The black iron oxide pigment is high in tinting strength, good in temperature tolerance and weather resistance, easy to disperse, good in processability, capable of further achieving good effects of deodorization, degerming, harmful peculiar smell absorption and elimination and the like, and good in usability.

Description

A kind of black iron oxide pigment containing bamboo charcoal powder and preparation method thereof
Technical field
The present invention relates to iron oxide pigment field, be specifically related to a kind of black iron oxide pigment containing bamboo charcoal powder and preparation method thereof.
Background technology
Iron oxide black is the one of iron pigment, and its moiety is Z 250, has saturated indigo plant ink light blue.Black iron oxide pigment has good weathering resistance, to light and atmospheric stability, opacifying power and tinting strength high, form and aspect are pure, with low cost, can be widely used in the industries such as building, plastics, pottery, coating.Along with the development of economy, the requirement of market to black iron oxide pigment also improves constantly, and its Application Areas and purposes are just constantly widened.But in actual applications, because the heat resistance of iron oxide black is poor, can fade at relatively high temperatures, the phenomenon such as variable color, easily reunite in addition, be difficult to problems such as being uniformly dispersed, limit the use range of iron oxide black.Therefore, need to carry out surface treatment to black iron oxide pigment, to reach lifting use properties, enrich product function, the object of meeting the market requirement.
Summary of the invention
The object of this invention is to provide a kind of black iron oxide pigment containing bamboo charcoal powder, there is good temperature tolerance and erosion resistance, be easy to dispersion, also have good antibacterial, purify air effect, use properties is good.
The present invention is achieved by the following technical solutions:
Containing a black iron oxide pigment for bamboo charcoal powder, it is obtained by the raw material of following weight parts:
Modified oxidized iron black 80-100, bamboo charcoal powder 4-8, nano-calcium carbonate 1-2, tripoly phosphate sodium STPP 3-5, water glass 6-8, Diisopropyl azodicarboxylate 0.1-0.2, vinylbenzene 10-15, sucrose fatty ester 1-2, plam oil 1-2, barium stearate 1-2;
Wherein modified oxidized iron oxide black is obtained by the raw material of following weight parts: ferrous sulfate 40-50, imidazoline quaternary ammonium salt 0.3-0.5, citric acid 0.3-0.5, dimethyl silicone oil 0.2-0.4; Citric acid is added to the water by solid-liquid weight ratio 1:100-1:150 to dissolve completely by the preparation method of described modified oxidized iron oxide black, and all the other raw materials 800-1000r/min added outside sulfuric acid ferrous iron stirs 5-10min, obtains modification liquid; Ferrous sulfate is added to the water the solution being mixed with 150-200g/L, in solution, adds described modification liquid, pH regulator is stirred to 7-8, pass into oxygen to be oxidized under 80-90 DEG C of condition, react the iron oxide black of terminating in rear separating slurry, through washing, oven dry, pulverize, to obtain final product.
Containing a preparation method for the black iron oxide pigment of bamboo charcoal powder, comprise the following steps:
(1) grinding after modified oxidized iron oxide black, bamboo charcoal powder, nano-calcium carbonate and tripoly phosphate sodium STPP mixing evenly, is then added the water of 2-3 times of weight, obtains iron oxide black slurries after dispersed with stirring;
(2) water glass is added to the water the solution being mixed with 20-30g/L, then be added dropwise in the iron oxide black slurries in (1) and stir, by pH regulator to 8-8.5, then ageing 2-3h, filters, washs and obtain coated with silica iron oxide black after drying;
(3) Diisopropyl azodicarboxylate is dissolved in a small amount of toluene obtains initiation solution; Coated with silica iron oxide black in (2) and vinylbenzene to be added jointly in appropriate dehydrated alcohol and to be uniformly dispersed; pass into nitrogen protection and temperature is adjusted to 70-80 DEG C; drip initiation solution reaction 2-4h; mix with all the other raw materials after filtration, washing and grind evenly, after drying, namely obtaining the black iron oxide pigment containing bamboo charcoal powder.
Bamboo charcoal powder can absorb the various obnoxious flavoures in air, makes room air be purified and become pure and fresh, has deodorizing, the effect that degerming, adsorption removal is harmful to peculiar smell.
Advantage of the present invention is:
The present invention utilizes the properties-correcting agent such as imidazoline quaternary ammonium salt and citric acid to carry out modification to iron oxide black, plays good dissemination in particle formation, effectively improves the tinting strength of iron oxide black, has corrosion inhibition simultaneously; Then carry out silicon-dioxide and vinylbenzene double-coated, both improved the temperature tolerance of black iron oxide pigment, make it have again good erosion resistance, and its dispersing property in the base can be improved; Composite simultaneously by with raw materials such as bamboo charcoal powder, not only tinting strength is high to make the black iron oxide pigment that obtains, temperature tolerance and weathering resistance good, be easy to dispersion, good processability, also have good deodorizing, degerming, adsorption removal is harmful to the effects such as peculiar smell, use properties is good.
Embodiment
Non-limiting examples of the present invention is as follows:
Containing a black iron oxide pigment for bamboo charcoal powder, be prepared from by the component raw material of following weight (kg):
Modified oxidized iron black 90, bamboo charcoal powder 6, nano-calcium carbonate 1.5, tripoly phosphate sodium STPP 4, water glass 7, Diisopropyl azodicarboxylate 0.15, vinylbenzene 12, sucrose fatty ester 1.5, plam oil 1.5, barium stearate 1.5;
Wherein modified oxidized iron oxide black is obtained by the raw material of following weight parts: ferrous sulfate 45, imidazoline quaternary ammonium salt 0.4, citric acid 0.4, dimethyl silicone oil 0.3; Citric acid is added to the water by solid-liquid weight ratio 1:100 to dissolve completely by the preparation method of described modified oxidized iron oxide black, and all the other raw materials 1000r/min added outside sulfuric acid ferrous iron stirs 5min, obtains modification liquid; Ferrous sulfate is added to the water the solution being mixed with 150g/L, in solution, adds described modification liquid, pH regulator is stirred to 7-8, pass into oxygen to be oxidized under 80 DEG C of conditions, react the iron oxide black of terminating in rear separating slurry, through washing, oven dry, pulverize, to obtain final product.
Preparation method containing the black iron oxide pigment of bamboo charcoal powder comprises the following steps:
(1) grinding after modified oxidized iron oxide black, bamboo charcoal powder, nano-calcium carbonate and tripoly phosphate sodium STPP mixing evenly, is then added the water of 3 times of weight, obtains iron oxide black slurries after dispersed with stirring;
(2) water glass is added to the water the solution being mixed with 25g/L, then be added dropwise in the iron oxide black slurries in (1) and stir, by pH regulator to 8-8.5, then ageing 2h, filters, washs and obtain coated with silica iron oxide black after drying;
(3) Diisopropyl azodicarboxylate is dissolved in a small amount of toluene obtains initiation solution; Coated with silica iron oxide black in (2) and vinylbenzene to be added jointly in appropriate dehydrated alcohol and to be uniformly dispersed; pass into nitrogen protection and temperature is adjusted to 80 DEG C; drip initiation solution reaction 2h; mix with all the other raw materials after filtration, washing and grind evenly, after drying, namely obtaining the black iron oxide pigment containing bamboo charcoal powder.
Above-mentioned obtained black iron oxide pigment performance is as following table:
Project Analytical results
105 DEG C of volatile matter/% 1.3
Screenings (320 mesh sieve) 0.4
Tinctorial strength/% 98.5
Coloured light (with standard specimen ratio) Slightly
Resistance to 260 DEG C/30min △ E 0.33

Claims (2)

1., containing a black iron oxide pigment for bamboo charcoal powder, it is characterized in that, it is obtained by the raw material of following weight parts:
Modified oxidized iron black 80-100, bamboo charcoal powder 4-8, nano-calcium carbonate 1-2, tripoly phosphate sodium STPP 3-5, water glass 6-8, Diisopropyl azodicarboxylate 0.1-0.2, vinylbenzene 10-15, sucrose fatty ester 1-2, plam oil 1-2, barium stearate 1-2;
Described modified oxidized iron oxide black is obtained by the raw material of following weight parts: ferrous sulfate 40-50, imidazoline quaternary ammonium salt 0.3-0.5, citric acid 0.3-0.5, dimethyl silicone oil 0.2-0.4; Citric acid is added to the water by solid-liquid weight ratio 1:100-1:150 to dissolve completely by the preparation method of described modified oxidized iron oxide black, and all the other raw materials 800-1000r/min added outside sulfuric acid ferrous iron stirs 5-10min, obtains modification liquid; Ferrous sulfate is added to the water the solution being mixed with 150-200g/L, in solution, adds described modification liquid, pH regulator is stirred to 7-8, pass into oxygen to be oxidized under 80-90 DEG C of condition, react the iron oxide black of terminating in rear separating slurry, through washing, oven dry, pulverize, to obtain final product.
2. the preparation method of a kind of black iron oxide pigment containing bamboo charcoal powder according to claim 1, is characterized in that, comprise the following steps:
(1) grinding after modified oxidized iron oxide black, bamboo charcoal powder, nano-calcium carbonate and tripoly phosphate sodium STPP mixing evenly, is then added the water of 2-3 times of weight, obtains iron oxide black slurries after dispersed with stirring;
(2) water glass is added to the water the solution being mixed with 20-30g/L, is then added dropwise in the iron oxide black slurries in (1) and stirs, by pH regulator to 8-8.5, then ageing 2-3h, filters, washs and obtain coated with silica iron oxide black after drying;
(3) Diisopropyl azodicarboxylate is dissolved in a small amount of toluene obtains initiation solution; Coated with silica iron oxide black in (2) and vinylbenzene to be added jointly in appropriate dehydrated alcohol and to be uniformly dispersed; pass into nitrogen protection and temperature is adjusted to 70-80 DEG C; initiation solution reaction 2-4h described in dropping; mix with all the other raw materials after filtration, washing and grind evenly, after drying, namely obtaining the black iron oxide pigment containing bamboo charcoal powder.
CN201510455518.9A 2015-07-27 2015-07-27 Black iron oxide pigment containing bamboo charcoal powder and preparation method thereof Pending CN105086518A (en)