CN105086128A - 125 DEG C irradiation cross-linking low-smoke halogen-free flame-retardant polyolefin cable material - Google Patents
125 DEG C irradiation cross-linking low-smoke halogen-free flame-retardant polyolefin cable material Download PDFInfo
- Publication number
- CN105086128A CN105086128A CN201510600291.2A CN201510600291A CN105086128A CN 105086128 A CN105086128 A CN 105086128A CN 201510600291 A CN201510600291 A CN 201510600291A CN 105086128 A CN105086128 A CN 105086128A
- Authority
- CN
- China
- Prior art keywords
- parts
- linking
- cable material
- smoke halogen
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a 125 DEG C irradiation cross-linking low-smoke halogen-free flame-retardant polyolefin cable material, and belongs to the field of cable material formulas. The 125 DEG C irradiation cross-linking low-smoke halogen-free flame-retardant polyolefin cable material comprises 60-90 parts of EVA, 40-60 parts of HDPE, 45-60 parts of aluminum hydroxide, 45-60 parts of magnesium hydroxide, 5-10 parts of calcium-zinc compound stabilizer, 10-15 parts of softening and strengthening agents, 5-10 parts of flame retardant agents, 10-18 parts of compatibilizer, 1-1.5 parts of antioxygen OSP-1, 0.5-1 part of lubricant and 4-6 parts of cross-linking agents. The environmentally friendly cable material has the advantages of being low in smoke, free of halogen and toxin, flame retardant and resistant to high temperature, and meanwhile the mechanical property, the processing property, the flame retardant property and the high temperature resistance of the cable material all reach a higher level.
Description
Technical field
The invention belongs to a kind of cable material formula, specifically, particularly relate to a kind of 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials.
Background technology
125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials are for meeting the characteristics such as low cigarette, Halogen be nontoxic, fire-retardant, high temperature resistant and a kind of retardant cable material developed.It is use polyolefine as base material, the inorganic anti-flaming material such as aluminium hydroxide, magnesium hydroxide makes fire retardant, through blended, plasticizing, granulation can cross-linking radiation CABLE MATERIALS.The exploitation of 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials, solve following several key problem in technology: (1) is owing to can not use the fire retardant containing halogen, and the inorganic combustion inhibitor that aluminium hydroxide, magnesium hydroxide, zinc borate etc. are nontoxic can only be used, these fire retardants need interpolation 50% ~ 60% (weight percent) just to play good fire retardation, a large amount of interpolations of inorganic combustion inhibitor then significantly reduce the mechanical property of material, so how to ensure the balance of mechanical property and flame retardant properties, this is most important key problem in technology.(2) after adding a large amount of inorganic combustion inhibitors, the processing fluidity of material is very poor, and screw torque sharply rises, and granulation is produced very difficult, insulating exruded also very difficult, how to improve these Drawing abillities and be second key problem in technology.(3) if material melting drippage when burning, more easily make fire spread, the aggravation condition of a fire, also makes material expose the surperficial accelerate combustion made new advances.For this reason, anti-drippage just becomes another research of technique difficult point of this product of exploitation.(4) temperature resistant grade of material requirements is 125 DEG C, for making material can reach this class requirement, will solve the heat-proof aging problem of material well.
Summary of the invention
The object of the invention is to provide a kind of 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials, to overcome above-mentioned defect of the prior art.
The present invention realizes by the following technical solutions:
A kind of 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials, comprise following weight ratio formula: EVA60-90 part, HDPE40-60 part, aluminium hydroxide 45-60 part, magnesium hydroxide 45-60 part, calcium-zinc composite stabilizing agent 5-10 part, soft strong agent 10-15 part, fire retardant 5-10 part, compatilizer 10-18 part, oxidation inhibitor OSP-11-1.5 part, lubricant 0.5-1 part, linking agent 4-6 part.
Described compatilizer is maleic anhydride graft PE.
Preferably, following weight ratio formula is comprised: EVA65 part, HDPE45 part, 50 parts, aluminium hydroxide, magnesium hydroxide 50 parts, calcium-zinc composite stabilizing agent 8 parts, soft strong agent 12 parts, fire retardant 8 parts, compatilizer 15 parts, oxidation inhibitor OSP-11.2 part, lubricant 0.8 part, linking agent 5 parts.
Compared with prior art, the invention has the beneficial effects as follows:
(1) EVA and HDPE co-mixing system selected by base-material of the present invention, can obtain more satisfactory tensile strength and elongation at break;
(2) the present invention adds the compatilizer of 8% ~ 15% in the material, obviously can strengthen the avidity between inorganic combustion inhibitor and high molecular polymer, greatly improve tensile strength;
(3) the present invention selects the flame-retardant system of Al (OH) 3, Mg (OH) 2, fire retardant, can give the flame retardant properties of material comparative superiority, and more effectively prevents the drip phenomenon of material when burning;
(4) antioxidant system of the present invention makes material have outstanding heat aging property, makes the temperature resistant grade of material reach 125 DEG C;
(5) extrusion capacity of the present invention significantly improves, remarkable reduction melt viscosity, improve product surface light smooth finish, make goods feel good, pigment stability is increased, color is more lastingly bright-coloured, in elastic material, significantly improve snappiness and the elasticity of goods, and liquid towards plasticizing oil there is strong affinity, plasticizing oil is fixed in goods and does not move, anti-fuel-displaced and goods glue hand, and Article Stiffness Determination is stablized.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
A kind of 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials, comprise following weight ratio formula: EVA60 part, HDPE40 part, 45 parts, aluminium hydroxide, magnesium hydroxide 45 parts, calcium-zinc composite stabilizing agent 5 parts, soft strong agent 10 parts, fire retardant 5 parts, compatilizer 10 parts, oxidation inhibitor OSP-11 part, lubricant 0.5 part, linking agent 4 parts, compatilizer is maleic anhydride graft PE.
Embodiment 2:
A kind of 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials, comprise following weight ratio formula: EVA65 part, HDPE45 part, 50 parts, aluminium hydroxide, magnesium hydroxide 50 parts, calcium-zinc composite stabilizing agent 8 parts, soft strong agent 12 parts, fire retardant 8 parts, compatilizer 15 parts, oxidation inhibitor OSP-11.2 part, lubricant 0.8 part, linking agent 5 parts, compatilizer is maleic anhydride graft PE.
Embodiment 3:
A kind of 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials, comprise following weight ratio formula: EVA90 part, HDPE60 part, 60 parts, aluminium hydroxide, magnesium hydroxide 60 parts, calcium-zinc composite stabilizing agent 10 parts, soft strong agent 15 parts, fire retardant 10 parts, compatilizer 18 parts, oxidation inhibitor OSP-11.5 part, lubricant 1 part, linking agent 6 parts, compatilizer is maleic anhydride graft PE.
After tested, product properties is all up to standard, and test result joins carbon products DFDA21472NT with VDE standard, IEC standard and the U.S. and compares in table 1.
Table 1:
Claims (3)
1. 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials, it is characterized in that, comprise following weight ratio formula: EVA60-90 part, HDPE40-60 part, aluminium hydroxide 45-60 part, magnesium hydroxide 45-60 part, calcium-zinc composite stabilizing agent 5-10 part, soft strong agent 10-15 part, fire retardant 5-10 part, compatilizer 10-18 part, oxidation inhibitor OSP-11-1.5 part, lubricant 0.5-1 part, linking agent 4-6 part.
2. 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials according to claim 1, is characterized in that: described compatilizer is maleic anhydride graft PE.
3. a kind of 125 DEG C of irradiation cross-linking low smoke halogen-free fire retardant polyolefin cable materials according to claim 1 and 2, it is characterized in that, comprise following weight ratio formula: EVA65 part, HDPE45 part, 50 parts, aluminium hydroxide, magnesium hydroxide 50 parts, calcium-zinc composite stabilizing agent 8 parts, soft strong agent 12 parts, fire retardant 8 parts, compatilizer 15 parts, oxidation inhibitor OSP-11.2 part, lubricant 0.8 part, linking agent 5 parts.