CN105081708A - Drawing technology of 430 material steel cylinder - Google Patents
Drawing technology of 430 material steel cylinder Download PDFInfo
- Publication number
- CN105081708A CN105081708A CN201510625673.0A CN201510625673A CN105081708A CN 105081708 A CN105081708 A CN 105081708A CN 201510625673 A CN201510625673 A CN 201510625673A CN 105081708 A CN105081708 A CN 105081708A
- Authority
- CN
- China
- Prior art keywords
- time
- steel cylinder
- carried out
- carry out
- blank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a drawing technology of a 430 material steel cylinder. The drawing technology comprises the steps of material selecting, annealing, grinding, drawing, closing, cleaning and the like. The first-time cold drawing is carried out on a ground blank, the annealing step is carried out after the first-time cold drawing, and then the second-time cold drawing is carried out. The third-time hot drawing shaping is carried out on the blank on which the second-time cold drawing is carried out, and pressure maintaining processing is carried out when the third-time cold drawing shaping is carried out. The overall quality of the steel cylinder is guaranteed through multi-time drawing and annealing.
Description
Technical field
The present invention relates to gas cylinder processing technique field, specifically a kind of 430 material steel cylinder deep-drawing techniques.
Background technology
As clean energy resource, natural gas is widely used in every field, no matter be that life production all plays key player.Accordingly, the development of the pressure vessel of filling natural gas compressing gas just seems particularly necessary, due to the inflammable and explosive characteristic of natural gas, very high to its bubble-tight requirement of container.The technique of bad manufacture can cause the Wall-Thickness Difference of container bottle excessive, and the difference in quality of seamless cylinder is very large, equally, if temperature controls to cause bottom gas cylinder for bad time and leaks gas when hot spinning receives the end in large batch of production process, leaves major safety risks.
Summary of the invention
The present invention aims to provide a kind of 430 material steel cylinder deep-drawing techniques, to solve the problem.
For achieving the above object, technical scheme of the present invention is as follows:
A kind of 430 material steel cylinder deep-drawing techniques, is characterized in that, comprise the following steps:
Select materials: select 430 stainless iron sheet materials as blank, carry out Size calculation according to steel cylinder size, then according to the target size after calculating, blank is cut into plectane with cutting machine;
Annealing: the plectane after cutting is placed in annealing furnace and carries out annealing in process, annealing furnace keeps temperature more than 1095 DEG C, 15 minutes duration, then cools rapidly;
Polishing: carry out surface finish, sanding burr is clean;
Drawing: the blank after polishing is carried out first time deeply cold drawn, first time cold drawn dark after carry out above-mentioned annealing steps again, carry out second time more deeply cold drawn, cold drawn for secondary dark rear blank is carried out third time Hot drawing school shape, carries out pressurize process when third time Hot drawing school shape;
Close up: by the gas cylinder semi-finished product after drawing at 760 ~ 815 DEG C of temperature, squeeze out bottleneck by mould;
Cleaning: acid solution is injected into metal bottle inner chamber, fills rear maintenance 15 minutes, finally discharge acid solution.
Further, described drawing step, in forming process, needs after each drawing to observe the drawing state of part, need carry out smoothing wrinkle process, then carry out drawing next time if there is fold.
Further, described drawing step, first time drawing up to final drawing and forming residue 20mm ~ 30mm height, second time drawing is up to final drawing and forming 5 ~ 8mm height.
Further, described drawing step keeps deep drawing speed to be 80 ~ 110mm/min.
Beneficial effect of the present invention is: effectively improve rolling accuracy by repeatedly load-unload process, make the steel cylinder wall thickness accuracy error not super many 2% of drawing aftershaping, and adopt 430 stainless irons, can effective anticorrosive oxidation, avoid the problem of steel cylinder shortening in service life in specific environment, have employed acid solution to clean, go out the iron filings on top layer, make it more attractive in appearance.
Detailed description of the invention
Below by specific embodiment, the present invention will be further described.
A kind of 430 material steel cylinder deep-drawing techniques, is characterized in that, comprise the following steps:
Select materials: select 430 stainless iron sheet materials as blank, carry out Size calculation according to steel cylinder size, then according to the target size after calculating, blank is cut into plectane with cutting machine;
Annealing: the plectane after cutting is placed in annealing furnace and carries out annealing in process, annealing furnace keeps temperature 1095 DEG C, 15 minutes duration, then cools rapidly;
Polishing: carry out surface finish, sanding burr is clean;
Drawing: the blank after polishing is carried out first time deeply cold drawn, first time cold drawn dark after carry out above-mentioned annealing steps again, carry out second time more deeply cold drawn, cold drawn for secondary dark rear blank is carried out third time Hot drawing school shape, carries out pressurize process when third time Hot drawing school shape; Described drawing step, in forming process, needs after each drawing to observe the drawing state of part, need carry out smoothing wrinkle process, then carry out drawing next time if there is fold.Described drawing step, first time drawing up to final drawing and forming residue 20mm ~ 30mm height, second time drawing is up to final drawing and forming 5 ~ 8mm height.Described drawing step keeps deep drawing speed to be 80 ~ 110mm/min.
Close up: by the gas cylinder semi-finished product after drawing at 760 ~ 815 DEG C of temperature, squeeze out bottleneck by mould;
Cleaning: acid solution is injected into metal bottle inner chamber, fills rear maintenance 15 minutes, finally discharge acid solution.
The present invention effectively improves rolling accuracy by repeatedly load-unload process, make the steel cylinder wall thickness accuracy error not super many 2% of drawing aftershaping, and adopt 430 stainless irons, can effective anticorrosive oxidation, avoid the problem of steel cylinder shortening in service life in specific environment, have employed acid solution to clean, go out the iron filings on top layer, make it more attractive in appearance.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (4)
1. 430 material steel cylinder deep-drawing techniques, is characterized in that, comprise the following steps:
Select materials: select 430 stainless iron sheet materials as blank, carry out Size calculation according to steel cylinder size, then according to the target size after calculating, blank is cut into plectane with cutting machine;
Annealing: the plectane after cutting is placed in annealing furnace and carries out annealing in process, annealing furnace keeps temperature 1095 DEG C, 15 minutes duration, then cools rapidly;
Polishing: carry out surface finish, sanding burr is clean;
Drawing: the blank after polishing is carried out first time deeply cold drawn, first time cold drawn dark after carry out above-mentioned annealing steps again, carry out second time more deeply cold drawn, cold drawn for secondary dark rear blank is carried out third time Hot drawing school shape, carries out pressurize process when third time Hot drawing school shape;
Close up: by the gas cylinder semi-finished product after drawing at 760 ~ 815 DEG C of temperature, squeeze out bottleneck by mould;
Cleaning: acid solution is injected into metal bottle inner chamber, fills rear maintenance 15 minutes, finally discharge acid solution.
2. 430 material steel cylinder deep-drawing techniques according to claim 1, it is characterized in that: described drawing step is in forming process, need after each drawing to observe the drawing state of part, need smoothing wrinkle process be carried out if there is fold, then carry out drawing next time.
3. 430 material steel cylinder deep-drawing techniques according to claim 1, is characterized in that: described drawing step, first time drawing up to final drawing and forming residue 20mm ~ 30mm height, second time drawing is up to final drawing and forming 5 ~ 8mm height.
4. 430 material steel cylinder deep-drawing techniques according to claim 1, is characterized in that: described drawing step keeps deep drawing speed to be 80 ~ 110mm/min.