CN105063891A - Super-soft anti-microbial wet tissue - Google Patents
Super-soft anti-microbial wet tissue Download PDFInfo
- Publication number
- CN105063891A CN105063891A CN201510459347.7A CN201510459347A CN105063891A CN 105063891 A CN105063891 A CN 105063891A CN 201510459347 A CN201510459347 A CN 201510459347A CN 105063891 A CN105063891 A CN 105063891A
- Authority
- CN
- China
- Prior art keywords
- fibre
- wet tissue
- super soft
- soft antibacterial
- super
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed in the invention is a super-soft anti-microbial wet tissue comprising the components of 75% to 80% of bamboo fibers, 10% to 15% of milk fibers, and 10% to 15% of aloe fibers. According to the invention, the super-soft anti-microbial wet tissue is formed by mixing of the bamboo fibers, the milk fibers, and the aloe fibers and has the natural bacteriostatic and anti-microbial effects; the texture is soft; the tissue can be used comfortably; the wet strength is high; the skin can be protected; and the tissue is easy to clean and dry and can be used repeatedly. The tissue can be processed into a non-woven fabric by spunlacing and thus biodegradation can be carried out, so that the environment pollution can be prevented. The process is simple and water used in the preparation process can be recycled, so that the energy and cost can be saved. The non-woven fabric has the anti-microbial function and ultraviolet radiation is carried out and there is no need to add an anti-bacterial agent and a corrosion remover in the immersing solution, so that the usage is safe without any stimulation.
Description
Technical field
The present invention relates to a kind of wet tissue, particularly relate to a kind of super soft antibacterial wet tissue.
Background technology
Bamboo fibre is a kind of natural high polymer that the bamboo known by people processes as a kind of cellulose fibre.Bamboo fibre because of its macromolecular special construction, have good gas permeability, moment water imbibition, stronger ABRASION RESISTANCE etc., natural antibacterial, antibacterial, except mite, deodorization, uvioresistant, biodegradable, be described as the green fiber of new century.
Lyocell bamboo fiber, also known as solvent method bamboo fiber, be a kind of with bamboo cellulose pulp for raw material, adopt the regenerated bamboo fiber of Lyocell bamboo fiber technique spinning.Its preparation technology is: bamboo cellulose pulp is directly dissolved in the aqueous solution of N-methylmorpholine-N-oxide (being called for short NMMO), and prepares regenerated celulose fibre by wet spinning.This friendly process has the features such as abundant raw material, simple, the advanced environmental protection of production procedure, good product performance.Be expected to replace with serious pollution traditional fibre cellulose fiber production technology and adhering process gradually.Solvent method bamboo fiber belongs to the one of Lyocell bamboo fiber, is described as the green fiber of 21 century.Application for a patent for invention prospectus CN101694019A discloses solvent method high-wet-modulus bamboo fiber and preparation method thereof, the discarded object of production Lyocell bamboo fiber can natural degradation, amine oxide solvent in production process can 99.5% recycling, and free from environmental pollution.
The wet tissue that domestic market is sold, pasteurization towelette, wherein contained disinfection composition is all chemical composition, as bleaching powder, bromogeramine, Iodophor, Peracetic acid or glyoxal etc., although have certain bactericidal activity, but there is certain excitant to skin, be not suitable for the use such as damaged skin and baby especially.As stimulated to reduce and reduce the content of chemical disinfection composition, the Disinfection Effect of wet tissue can be made again to weaken, can not the growth of effective anti-bacteria.Therefore one effectively can not produce excitant again by cleaning-sterilizing, and do not have the wet tissue of toxic and side effect to be consumer in the urgent need to.
Summary of the invention
In order to achieve the above object, the present invention utilizes Lyocell bamboo fiber, provides a kind of super soft antibacterial wet tissue.
A kind of super soft antibacterial wet tissue, is made up of following ingredients: bamboo fibre 75% ~ 80%, milk fibre 10% ~ 15%, aloe fibre 10% ~ 15%.
A preparation method for super soft antibacterial wet tissue, comprises the following steps:
(1) bamboo fibre, milk fibre and aloe fibre are cleaned up, smash, obtain the blended fiber that fibre length is 15 ~ 18mm;
(2) by blended fiber routinely water acupuncture manipulation operating process carry out reinforcing, drying, obtain super soft antibacterial nonwoven cloth made;
(3) super soft antibacterial nonwoven cloth made is carried out cutting, be dipped to saturated, and carry out ultraviolet irradiation;
(4) pack, stock.
The fineness of described bamboo fibre, milk fibre and aloe fibre is 1.37dTex.
The density of described super soft antibacterial nonwoven cloth made is 55 ~ 58g/m
2.
Described step 3) does not need when soaking to add antiseptic and preservative agent.
Described super soft antibacterial wet tissue, after opening packaging, can be recycled 2 ~ 3 times.
Milk fibre, using cow's milk as base stock, softness, pro-skin, ventilative, wear-resisting, maintaining skin, anti-mould and anti-moth, intensity is high, durable washable, easily preserves, easily dry after washing, still can keep the permanent performance of product after washing.
Aloe fibre, is rich in vitamin, mineral matter element, amino acid, aloe polysaccharide and aldehydes matter, soft comfortable, pollution resistance be good, can eliminating bacteria and fungi, promotion microcirculation, beauty and skin care, promotion wound healing.
Beneficial effect of the present invention is: super soft antibacterial wet tissue provided by the invention, is mixed, have natural restraining and sterilizing bacteria effect by bamboo fibre, milk fibre and aloe fibre, and quality is soft, and use comfortable, wet strength is high, maintaining skin, easily washes easily dry, can be recycled; Be processed into nonwoven fabric through water acupuncture manipulation, can biodegradation be carried out, can not to environment; Process is simple, and preparation process water used can recycle, economize energy and cost; Nonwoven fabric itself has antibacterial functions, and carries out ultraviolet irradiation, without the need to adding antiseptic and preservative agent, use safety in soak, non-stimulated.
Empirical tests, the fiber fungistatic effect of proportioning of the present invention is obviously better than conventional proportioning, the combination properties such as hygroscopicity are stronger, and through weaving shaping after, the non-deformability of wet tissue is strong, there is not obvious distortion 100 times in folding, immersion, has obvious lifting relative to single bamboo fibre material non-deformability.
Detailed description of the invention
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; those skilled in the art can make to the present embodiment the amendment not having creative contribution as required after reading this description, as long as but be all subject to the protection of Patent Law in right of the present invention.
Embodiment 1
A kind of super soft antibacterial wet tissue, bamboo fibre 75%, milk fibre 10%, aloe fibre 15%.
A preparation method for super soft antibacterial wet tissue, comprises the following steps:
(1) bamboo fibre, milk fibre and aloe fibre are cleaned up, smash, fibre fineness is 1.37dTex, obtains the blended fiber that fibre length is 15mm;
(2) by blended fiber routinely water acupuncture manipulation operating process carry out reinforcing, drying, obtain super soft antibacterial nonwoven cloth made, density is 55g/m
2;
(3) super soft antibacterial nonwoven cloth made is carried out cutting, do not need during immersion to add antiseptic and preservative agent, be dipped to saturated, and carry out ultraviolet irradiation;
(4) pack, stock.
The super soft antibacterial wet tissue of the present embodiment, after opening packaging, can be recycled 2 times.
Embodiment 2
A kind of super soft antibacterial wet tissue, bamboo fibre 77%, milk fibre 11%, aloe fibre 12%.
A preparation method for super soft antibacterial wet tissue, comprises the following steps:
(1) bamboo fibre, milk fibre and aloe fibre are cleaned up, smash, fibre fineness is 1.37dTex, obtains the blended fiber that fibre length is 16mm;
(2) by blended fiber routinely water acupuncture manipulation operating process carry out reinforcing, drying, obtain super soft antibacterial nonwoven cloth made, density is 56g/m
2;
(3) super soft antibacterial nonwoven cloth made is carried out cutting, do not need during immersion to add antiseptic and preservative agent, be dipped to saturated, and carry out ultraviolet irradiation;
(4) pack, stock.
The super soft antibacterial wet tissue of the present embodiment, after opening packaging, can be recycled 3 times.
Embodiment 3
A kind of super soft antibacterial wet tissue, bamboo fibre 80%, milk fibre 10%, aloe fibre 10%.
A preparation method for super soft antibacterial wet tissue, comprises the following steps:
(1) bamboo fibre, milk fibre and aloe fibre are cleaned up, smash, fibre fineness is 1.37dTex, obtains the blended fiber that fibre length is 18mm;
(2) by blended fiber routinely water acupuncture manipulation operating process carry out reinforcing, drying, obtain super soft antibacterial nonwoven cloth made, density is 58g/m
2;
(3) super soft antibacterial nonwoven cloth made is carried out cutting, do not need during immersion to add antiseptic and preservative agent, be dipped to saturated, and carry out ultraviolet irradiation;
(4) pack, stock.
The super soft antibacterial wet tissue of the present embodiment, after opening packaging, can be recycled 3 times.
Comparative example
A kind of wet tissue, cotton fiber 80%, milk fibre 10%, aloe fibre 10%.
Preparation method comprises the following steps:
(1) cotton fiber, milk fibre and aloe fibre are cleaned up, smash, fibre fineness is 1.37dTex, obtains the blended fiber that fibre length is 18mm;
(2) by blended fiber routinely water acupuncture manipulation operating process carry out reinforcing, drying, obtain nonwoven fabric, density is 50g/m
2;
(3) nonwoven fabric is carried out cutting, do not need during immersion to add antiseptic and preservative agent, be dipped to saturated;
(4) pack, stock.
The wet tissue of this comparative example, after opening packaging use, not can be recycled.
With reference to the method that CN103222992B provides, antibacterial experiment is carried out to the super soft antibacterial wet tissue of embodiment and comparative example.Staphylococcus aureus and Escherichia coli are added in respectively on each wet tissue sheet, wash the staphylococcus aureus in lower wet tissue and Escherichia coli respectively when 5 minutes and 10 minutes with phosphate buffer, and cultivate and calculate viable count, draw bacteriostasis rate.Table 1 is that the wet tissue fungistatic effect of embodiment and comparative example measures.
Table 1 is that the wet tissue antibacterial effect of embodiment and comparative example measures
As can be seen from Table 1, within the different time, the bacteriostasis rate of the super soft antibacterial wet tissue of embodiment, all apparently higher than the wet tissue of comparative example, shows the wet tissue good anti-bacterial effect of antibacterial effect compared with comparative example of super soft antibacterial wet tissue of the present invention.
Claims (6)
1. a super soft antibacterial wet tissue, is characterized in that, be made up of following ingredients: bamboo fibre 75% ~ 80%, milk fibre 10% ~ 15%, aloe fibre 10% ~ 15%.
2. a processing method for super soft antibacterial wet tissue, is characterized in that, comprise the following steps:
(1) bamboo fibre, milk fibre and aloe fibre are cleaned up, smash, obtain the blended fiber that fibre length is 15 ~ 18mm;
(2) by blended fiber routinely water acupuncture manipulation operating process carry out reinforcing, drying, obtain super soft antibacterial nonwoven cloth made;
(3) super soft antibacterial nonwoven cloth made is carried out cutting, be dipped to saturated, and carry out ultraviolet irradiation;
(4) pack, stock.
3. a kind of super soft antibacterial wet tissue as claimed in claim 1, it is characterized in that, the fineness of described bamboo fibre, milk fibre and aloe fibre is 1.37dTex.
4. a kind of super soft antibacterial wet tissue as claimed in claim 1, it is characterized in that, the density of described super soft antibacterial nonwoven cloth made is 55 ~ 58g/m
2.
5. a kind of super soft antibacterial wet tissue as claimed in claim 1, is characterized in that, does not need to add antiseptic and preservative agent when described step 3) is soaked.
6. a kind of super soft antibacterial wet tissue as claimed in claim 1, is characterized in that described super soft antibacterial wet tissue, after opening packaging, can be recycled 2 ~ 3 times.