CN105062026A - Preparation method of impact-resistance environmentally-friendly resin communication tubing - Google Patents
Preparation method of impact-resistance environmentally-friendly resin communication tubing Download PDFInfo
- Publication number
- CN105062026A CN105062026A CN201510476287.XA CN201510476287A CN105062026A CN 105062026 A CN105062026 A CN 105062026A CN 201510476287 A CN201510476287 A CN 201510476287A CN 105062026 A CN105062026 A CN 105062026A
- Authority
- CN
- China
- Prior art keywords
- parts
- impact
- preparation
- friendly resin
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of impact-resistance environmentally-friendly resin communication tubing, which comprises the following steps: 1)preparing the raw materials by weight part: 55-60 parts of chlorine-containing alkyd resin, 4.5-5.5 parts of xylene, 8.5-9.5 parts of methyl methacrylate, 4.5-6.5 parts of potassium iodide, 2.2-3.4 parts of lubricant, 4.3-4.6 parts of impact-resistance agent, 2.5-5 parts of wooden fiber and 7.5-8.5 parts of micron order wollastonite powder; and 2)placing the raw materials in a high speed mixer for uniformly mixing for 1-1.5 hours at stirring speed is 800-900r/min. The product has the advantages of strong stability, good impact resistance, no shrinkage deformation and repeated recovery for usage. In addition, the preparation technology is simple and easy to operate, and cost is low.
Description
Technical field
The present invention relates to tubing field, specifically belong to a kind of anti-impact environment-friendly resin communication tube material, preparation method.
Background technology
A lot of injecting products in the market are mainly formed with injectable plastic materials such as vinylbenzene, polycarbonate and polystyrene, these materials are on the one hand containing many harmful chemical components, can damage HUMAN HEALTH, cost is higher on the other hand, can not recycle, and be difficult to degraded after discarding, serious environmental pollution can be caused.
For anti-impact environment-friendly resin communication tubing, raising variety seldom in market, but all has the shortcomings such as expensive, environmental-protecting performance is poor, and various performance index are not good.
Summary of the invention
The object of this invention is to provide a kind of anti-impact environment-friendly resin communication tubing, product stability is strong, good impact resistance, and ungauged regions is out of shape, and also repeatedly can reclaim use, in addition, its preparation technology is simple to operation, with low cost.
The technical solution used in the present invention is as follows:
A kind of anti-impact environment-friendly resin communication tube material, preparation method, is made up of following raw material:
1) raw material prepares: by weight: chloride Synolac 55-60 part, dimethylbenzene 4.5-5.5 part, methyl methacrylate 8.5-9.5 part, potassiumiodide 4.5-6.5 part, lubricant 2.2-3.4 part, anti-impact agent 4.3-4.6 part, xylon 2.5-5 part, micron silicon limestone flour 7.5-8.5 part;
2) above-mentioned raw materials is put into homogenizer mixing, stirring velocity is 800-900r/min, and churning time is 1-1.5 hour;
3) by step 2) the stirring material that obtains extrudes in an extruder, extrusion condition: barrel temperature: 180 ± 2 DEG C, merging core temperature: 170 ± 2 DEG C, head temperature: 180 ± 5 DEG C, traction: 0.5-0.8m/min, engine speed: 30-32 rev/min.
By step 2) the stirring material that obtains extrudes in an extruder, extrusion condition: barrel temperature: 180 DEG C, merging core temperature: 170 DEG C, head temperature: 180 DEG C, traction: 0.65m/min, engine speed: 31 revs/min.
Cheaper starting materials of the present invention is easy to get, and significantly can reduce the unicity using and change injection moulding material of plastics, the product stability simultaneously made is strong, good impact resistance, ungauged regions is out of shape, and also repeatedly can reclaim use, in addition, its preparation technology is simple to operation, with low cost.
Embodiment
A kind of anti-impact environment-friendly resin communication tube material, preparation method, is made up of following raw material:
1) raw material prepares: by weight: chloride Synolac 55-60 part, dimethylbenzene 4.5-5.5 part, methyl methacrylate 8.5-9.5 part, potassiumiodide 4.5-6.5 part, lubricant 2.2-3.4 part, anti-impact agent 4.3-4.6 part, xylon 2.5-5 part, micron silicon limestone flour 7.5-8.5 part;
2) above-mentioned raw materials is put into homogenizer mixing, stirring velocity is 800-900r/min, and churning time is 1-1.5 hour;
3) by step 2) the stirring material that obtains extrudes in an extruder, extrusion condition: barrel temperature: 180 DEG C, merging core temperature: 170 DEG C, head temperature: 180 DEG C, traction: 0.65m/min, engine speed: 31 revs/min.
The pipe performance parameter that the present invention produces is:
Tensile strength (MPa): 42-45
Yield strength (MPa): 46
Modulus in tension (MPa): 2880
Ultimate compression strength (MPa): 98
Rate extending longitudinally (%): 0.9
Thermal conductivity λ (W/mk): 0.12.
Claims (2)
1. an anti-impact environment-friendly resin communication tube material, preparation method, is characterized in that, is made up of following raw material:
1) raw material prepares: by weight: chloride Synolac 55-60 part, dimethylbenzene 4.5-5.5 part, methyl methacrylate 8.5-9.5 part, potassiumiodide 4.5-6.5 part, lubricant 2.2-3.4 part, anti-impact agent 4.3-4.6 part, xylon 2.5-5 part, micron silicon limestone flour 7.5-8.5 part;
2) above-mentioned raw materials is put into homogenizer mixing, stirring velocity is 800-900r/min, and churning time is 1-1.5 hour;
3) by step 2) the stirring material that obtains extrudes in an extruder, extrusion condition: barrel temperature: 180 ± 2 DEG C, merging core temperature: 170 ± 2 DEG C, head temperature: 180 ± 5 DEG C, traction: 0.5-0.8m/min, engine speed: 30-32 rev/min.
2. anti-impact environment-friendly resin communication tube material, preparation method according to claim 1, it is characterized in that, by step 2) the stirring material that obtains extrudes in an extruder, extrusion condition: barrel temperature: 180 DEG C, merging core temperature: 170 DEG C, head temperature: 180 DEG C, traction: 0.65m/min, engine speed: 31 revs/min.