CN105061843A - Carbon fiber tyre and preparation method thereof - Google Patents
Carbon fiber tyre and preparation method thereof Download PDFInfo
- Publication number
- CN105061843A CN105061843A CN201510449703.7A CN201510449703A CN105061843A CN 105061843 A CN105061843 A CN 105061843A CN 201510449703 A CN201510449703 A CN 201510449703A CN 105061843 A CN105061843 A CN 105061843A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon fiber
- rubber
- mixing
- tyre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a carbon fiber tyre and a preparation method thereof. The carbon fiber tyre comprises the following raw materials by weight: 10 to 20 parts of polyvinyl chloride, 40 to 100 parts of carbon fiber, 60 to 70 parts of calcium stearate, 70 to 150 parts of rubber, 10 to 20 parts of zinc oxide, 20 to 40 parts of bran oleic acid and 1 to 8 parts of sodium pyrithione. The preparation method comprises the following steps: mixing rubber in an internal mixer at 60 to 100 DEG C for 5 to 10 min; then adding carbon fiber, calcium stearate and calcium carbonate into the internal mixer and continuing mixing; then adding zinc oxide, polyvinyl chloride, bran oleic acid and sodium pyrithione and carrying out mixing; and after completion of mixing, carrying out rubber discharging and putting the obtained rubber in a forming die so as to obtain the carbon fiber tyre. The carbon fiber tyre provided by the invention has an abrasion resistance index of 343 to 360 while a standard abrasion resistance index is 100; and addition of bran oleic acid enables abrasion resistance of the tyre to be obviously improved, so the service life of the tyre is prolonged.
Description
Technical field
The present invention relates to a kind of carbon fiber tire and preparation method thereof.
Background technology
Carbon fiber be carbon content higher than 90% inorganic polymer fiber, carbon fiber can be processed into fabric, felt, seat, band, paper and other materials.Carbon fiber, except being used as heat-insulating material, not generally being used alone, how joining in the materials such as resin, metal, pottery, concrete as strongthener, forms matrix material.Carbon fiber reinforced matrix material can be used as aircraft construction material, electromagnetic shielding except the health such as electric material, artificial ligament substitute material and for the manufacture of rocket casing, powership, industrial robot, leaf springs of car and drive shaft etc.The tire of prior art adopts rubber to make mostly, and along with the increase of duration of service, rubber easily weares and teares, and affects the wear resisting property of tire.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, provide a kind of carbon fiber tire and preparation method thereof, wear resisting property is good, long service life.
The present invention is by the following technical solutions:
Carbon fiber tire, comprises the raw material of following parts by weight: polyvinyl chloride 10 ~ 20 parts, 40 ~ 100 parts, carbon fiber, calcium stearate 60 ~ 70 parts, rubber 70 ~ 150 parts, 10 ~ 20 parts, zinc oxide, 10 ~ 20 parts, calcium carbonate, oil extracted from rice husks acid 20 ~ 40 parts, sodium pyrithione 1 ~ 8 part.
As preferably, carbon fiber tire, comprises the raw material of following parts by weight: the acid of polyvinyl chloride 15 parts, 60 parts, carbon fiber, calcium stearate 65 parts, rubber 90 parts, 15 parts, zinc oxide, 15 parts, calcium carbonate, oil extracted from rice husks 30 parts, sodium pyrithione 5 parts.
As preferably, the carbon content of carbon fiber is more than 98%.
As preferably, rubber is mass ratio is the carboxy nitrile rubber of 1:5 and the mixture of solution polymerized butadiene styrene rubber.
The preparation method of above-mentioned carbon fiber tire, comprise the following steps: first by rubber mixing 5 ~ 10min in Banbury mixer, melting temperature is 60 ~ 100 DEG C, then carbon fiber, calcium stearate, calcium carbonate are joined in Banbury mixer continue mixing, add zinc oxide, polyvinyl chloride, oil extracted from rice husks acid again, sodium pyrithione carries out mixing, complete mixing after carry out binder removal, put into shaping mould.
beneficial effect
The abrasion resistance index of carbon fiber tire of the present invention is 343 ~ 360, and standard abrasion resistance index is 100, and the tire adding oil extracted from rice husks acid can significantly improve the wear resisting property of tire, extends the work-ing life of tire.
Embodiment
Below in conjunction with specific embodiment, the present invention is further described in detail.
embodiment 1
Carbon fiber tire, comprises the raw material of following parts by weight: the acid of polyvinyl chloride 15 parts, 60 parts, carbon fiber, calcium stearate 65 parts, rubber 90 parts, 15 parts, zinc oxide, 15 parts, calcium carbonate, oil extracted from rice husks 30 parts, sodium pyrithione 5 parts.
The carbon content of carbon fiber is more than 98%.
Rubber is mass ratio is the carboxy nitrile rubber of 1:5 and the mixture of solution polymerized butadiene styrene rubber.
The preparation method of above-mentioned carbon fiber tire, comprise the following steps: first by rubber mixing 8min in Banbury mixer, melting temperature is 80 DEG C, then carbon fiber, calcium stearate, calcium carbonate are joined in Banbury mixer continue mixing, add zinc oxide, polyvinyl chloride, oil extracted from rice husks acid again, sodium pyrithione carries out mixing, complete mixing after carry out binder removal, put into shaping mould.
embodiment 2
Carbon fiber tire, comprises the raw material of following parts by weight: the acid of polyvinyl chloride 10 parts, 40 parts, carbon fiber, calcium stearate 60 parts, rubber 70 parts, 10 parts, zinc oxide, 10 parts, calcium carbonate, oil extracted from rice husks 20 parts, sodium pyrithione 1 part.
The carbon content of carbon fiber is more than 98%.
Rubber is mass ratio is the carboxy nitrile rubber of 1:5 and the mixture of solution polymerized butadiene styrene rubber.
The preparation method of above-mentioned carbon fiber tire, comprise the following steps: first by rubber mixing 5min in Banbury mixer, melting temperature is 60 DEG C, then carbon fiber, calcium stearate, calcium carbonate are joined in Banbury mixer continue mixing, add zinc oxide, polyvinyl chloride, oil extracted from rice husks acid again, sodium pyrithione carries out mixing, complete mixing after carry out binder removal, put into shaping mould.
embodiment 3
Carbon fiber tire, comprises the raw material of following parts by weight: the acid of polyvinyl chloride 20 parts, 100 parts, carbon fiber, calcium stearate 70 parts, rubber 150 parts, 20 parts, zinc oxide, 20 parts, calcium carbonate, oil extracted from rice husks 40 parts, sodium pyrithione 8 parts.
The carbon content of carbon fiber is more than 98%.
Rubber is mass ratio is the carboxy nitrile rubber of 1:5 and the mixture of solution polymerized butadiene styrene rubber.
The preparation method of above-mentioned carbon fiber tire, comprise the following steps: first by rubber mixing 10min in Banbury mixer, melting temperature is 100 DEG C, then carbon fiber, calcium stearate, calcium carbonate are joined in Banbury mixer continue mixing, add zinc oxide, polyvinyl chloride, oil extracted from rice husks acid again, sodium pyrithione carries out mixing, complete mixing after carry out binder removal, put into shaping mould.
embodiment 4
Carbon fiber tire, comprises the raw material of following parts by weight: the acid of polyvinyl chloride 18 parts, 90 parts, carbon fiber, calcium stearate 63 parts, rubber 78 parts, 18 parts, zinc oxide, 18 parts, calcium carbonate, oil extracted from rice husks 28 parts, sodium pyrithione 3 parts.
The carbon content of carbon fiber is more than 98%.
Rubber is mass ratio is the carboxy nitrile rubber of 1:5 and the mixture of solution polymerized butadiene styrene rubber.
The preparation method of above-mentioned carbon fiber tire, comprise the following steps: first by rubber mixing 7min in Banbury mixer, melting temperature is 70 DEG C, then carbon fiber, calcium stearate, calcium carbonate are joined in Banbury mixer continue mixing, add zinc oxide, polyvinyl chloride, oil extracted from rice husks acid again, sodium pyrithione carries out mixing, complete mixing after carry out binder removal, put into shaping mould.
comparative example 1
Identical with embodiment 1, difference is: not with oil extracted from rice husks acid.
performance test
Performance test is carried out to the product of embodiment 1 ~ 4 and comparative example 1, the results are shown in Table 1.
Table 1
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Comparative example 1 | |
Abrasion resistance index | 343 | 350 | 363 | 354 | 110 |
Conclusion: the abrasion resistance index of carbon fiber tire of the present invention is 343 ~ 360, and standard abrasion resistance index is 100, and the tire adding oil extracted from rice husks acid can significantly improve the wear resisting property of tire, extends the work-ing life of tire.
Claims (5)
1. carbon fiber tire, it is characterized in that, comprise the raw material of following parts by weight: polyvinyl chloride 10 ~ 20 parts, 40 ~ 100 parts, carbon fiber, calcium stearate 60 ~ 70 parts, rubber 70 ~ 150 parts, 10 ~ 20 parts, zinc oxide, 10 ~ 20 parts, calcium carbonate, oil extracted from rice husks acid 20 ~ 40 parts, sodium pyrithione 1 ~ 8 part.
2. carbon fiber tire according to claim 1, it is characterized in that, comprise the raw material of following parts by weight: the acid of polyvinyl chloride 15 parts, 60 parts, carbon fiber, calcium stearate 65 parts, rubber 90 parts, 15 parts, zinc oxide, 15 parts, calcium carbonate, oil extracted from rice husks 30 parts, sodium pyrithione 5 parts.
3. carbon fiber tire according to claim 1, is characterized in that, the carbon content of carbon fiber is more than 98%.
4. carbon fiber tire according to claim 1, is characterized in that, rubber is mass ratio is the carboxy nitrile rubber of 1:5 and the mixture of solution polymerized butadiene styrene rubber.
5. based on the preparation method of carbon fiber tire according to claim 1, it is characterized in that, comprise the following steps: first by rubber mixing 5 ~ 10min in Banbury mixer, melting temperature is 60 ~ 100 DEG C, then carbon fiber, calcium stearate, calcium carbonate are joined in Banbury mixer continue mixing, then add zinc oxide, polyvinyl chloride, oil extracted from rice husks acid, sodium pyrithione carry out mixing, complete mixing after carry out binder removal, put into shaping mould.