Mobile phone screen repairing paste and its production method
Technical field
The present invention relates to the reparation of mobile phone screen more particularly to mobile phone screen repairing paste and its production methods.
Background technology
With the continuous promotion of mobile phone temperature, the commercial value of periphery industrial chain is also increasing, screen material draw with
The increasingly popular of mobile phone color screen, the material of mobile phone screen also increasingly seems important.The color/graphics of mobile phone are because of LCD qualities
It is different with research and development technology and difference, type have substantially had TFT, TFD, UFB, STN and OLED several.In general it can show
The the color shown the more more can show that complicated image, the level of picture are also more rich.No matter which kind of material used, mobile phone screen is all
It is vulnerable part, for a long time using can damage always, or hard object scratches and leaves cut, can lead to decline or even the hand of user's sense organ degree
The protection of the reduction of machine performance, the today especially largely popularized in smart mobile phone touch screen, mobile phone screen is particularly important.Cause
This safeguard film for cellular phone also just comes into being, but regular safeguard film for cellular phone is expensive, and is attached on mobile phone screen and is easy blistering,
Influence the sense of touch of finger and mobile phone screen.
Invention content
The technical problem to be solved by the present invention is to existing mobile phone screen safeguard only lean on safeguard film for cellular phone, one come cost compared with
Height, two use to influence user, provide a kind of mobile phone screen repairing paste and its production method thus.
The technical scheme is that:The production method of mobile phone screen repairing paste, it includes the following steps:(1), take with weight
Amount part be calculated as 16-29 parts of eucalyptus oil, 4-11 parts of tea tree ethereal oil, 0.6-2.8 parts vaseline, 30-60 parts of lightweight carbon
Sour calcium, 5-13 parts of two water salt of calcium monohydrogen phosphate, 1-3.4 parts of aluminium hydroxide and 3-13 parts of sorbierite are spare;(2), by 16-29
Obtained initial material A is mixed evenly in the eucalyptus oil, 4-11 parts of tea tree ethereal oil and 30-60 parts of precipitated calcium carbonate of part, to first
Material A is kept the temperature after being heated to 60-70 DEG C;(3), by 5-13 parts of two water salt of calcium monohydrogen phosphate, 1-3.4 parts of aluminium hydroxide and 3-13 parts
Sorbierite be added during initial material A high speed homogeneous 6-9min is made and expect B;(4), wait for that middle material B is cooled to room temperature, to its be added dropwise 0.6-
During which 2.8 parts of vaseline persistently stirs and mobile phone screen repairing paste is made.
Mobile phone screen repairing paste can be made using the above method.
The beneficial effects of the invention are as follows eucalyptus oil, tea tree ethereal oils to have effects that disinfecting and decontaminating, can clean Mobile phone screen
Curtain, precipitated calcium carbonate can rub mobile phone screen surface removal stain, and aluminium hydroxide can increase the brightness of mobile phone screen,
Sorbierite and vaseline can form layer protecting film on mobile phone screen surface, therefore the present invention can play mobile phone screen cleaning dirt
Stain, the function of protecting moisturizing, no longer need to patch safeguard film for cellular phone, and it is primary only need to smear mobile phone screen at regular intervals, peace
Loopful is protected, and secondary pollution is not will produce.
Specific implementation mode
With reference to embodiment, the present invention will be further described.
Embodiment 1:(1), take in parts by weight be 16 parts of eucalyptus oil, 4 parts of tea tree ethereal oil, 0.6 part of vaseline,
30 parts of precipitated calcium carbonate, 5 parts of two water salt of calcium monohydrogen phosphate, 1 part of aluminium hydroxide and 3 parts of sorbierite are spare;(2), by 16
Obtained initial material A is mixed evenly in the eucalyptus oil, 4 parts of tea tree ethereal oil and 30 parts of precipitated calcium carbonate of part, is heated to initial material A
It is kept the temperature after to 60 DEG C;(3), will 5 parts of two water salt of calcium monohydrogen phosphate, 1 part of aluminium hydroxide and 3 parts sorbierite be added in initial material A
High speed homogenization 6min expects B in being made;(4), wait for that middle material B is cooled to room temperature, 0.6 part of vaseline is added dropwise to it, during which persistently stirs
Mixing obtains mobile phone screen repairing paste.
Embodiment 2:(1), take in parts by weight be 29 parts of eucalyptus oil, 11 parts of tea tree ethereal oil, 2.8 parts of all scholars
Woods, 60 parts of precipitated calcium carbonate, 13 parts of two water salt of calcium monohydrogen phosphate, 3.4 parts of aluminium hydroxide and 13 parts of sorbierite are spare;
(2), obtained initial material A is mixed evenly in 29 parts of eucalyptus oil, 11 parts of tea tree ethereal oil and 60 parts of precipitated calcium carbonate, it is right
Initial material A is kept the temperature after being heated to 70 DEG C;(3), by 13 parts of two water salt of calcium monohydrogen phosphate, 3.4 parts of aluminium hydroxide and 13 parts of sorb
Alcohol, which is added during initial material A high speed homogeneous 9min is made, expects B;(4), wait for that middle material B is cooled to room temperature, 2.8 parts of all scholars are added dropwise to it
During which woods persistently stirs and mobile phone screen repairing paste is made.
Embodiment 3:(1), take in parts by weight be 20 parts of eucalyptus oil, 8 parts of tea tree ethereal oil, 2 parts of vaseline, 45
Part precipitated calcium carbonate, 8 parts of two water salt of calcium monohydrogen phosphate, 2 parts of aluminium hydroxide and 8 parts of sorbierite it is spare;(2), by 20 parts
Eucalyptus oil, 8 parts of tea tree ethereal oil and 45 parts of precipitated calcium carbonate obtained initial material A is mixed evenly, initial material A is heated to
It is kept the temperature after 65 DEG C;(3), will 8 parts of two water salt of calcium monohydrogen phosphate, 2 parts of aluminium hydroxide and 8 parts sorbierite be added it is high in initial material A
Fast homogeneous 8min expects B in being made;(4), wait for that middle material B is cooled to room temperature, 2 parts of vaseline is added dropwise to it, during which persistently stirs system
Obtain mobile phone screen repairing paste.
Mobile phone screen repairing paste is uniformly applied on mobile phone screen when use and gently wipes 3- with soft silk scarf
5min.Can be directed to screen with mobile phone screen repairing paste produced by the present invention has spot, cut to play repair, makes up hand
The tiny defect of machine screen, repairing paste can form one layer of very thin transparent protective layer on mobile phone screen surface, and not influencing user makes
With may replace currently a popular protecting film of mobile phone screen, safety and environmental protection does not generate secondary pollution.
The transparent protective layer that mobile phone screen after smearing repairing paste is formed is done into performance test, test data see the table below:
Project |
Embodiment 1 |
Embodiment 2 |
Embodiment 3 |
Sticking film for mobile phone |
Surface tension(mN/m) |
20 |
22 |
23 |
23 |
Elongation at break |
40% |
42% |
38% |
44% |
Transparency |
It is transparent |
It is transparent |
It is transparent |
It is transparent |
It can play a protective role to mobile phone screen it can be seen that the present invention is applied to the transparent protective layer formed on mobile phone screen,
Existing mobile phone protection pad pasting can be replaced completely.