CN106554625A - The preparation method and application of filling liquid, the filling liquid - Google Patents
The preparation method and application of filling liquid, the filling liquid Download PDFInfo
- Publication number
- CN106554625A CN106554625A CN201611031788.8A CN201611031788A CN106554625A CN 106554625 A CN106554625 A CN 106554625A CN 201611031788 A CN201611031788 A CN 201611031788A CN 106554625 A CN106554625 A CN 106554625A
- Authority
- CN
- China
- Prior art keywords
- silicone oil
- liquid
- filling liquid
- methyl
- safety glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to screen of intelligent device protecting film field; specifically related to a kind of filling liquid, the preparation method and application of the filling liquid; the filling liquid includes A composing types liquid and B composing type liquid; the A composing types liquid includes methyl-silicone oil and vinyl silicone oil; the methyl-silicone oil is base material, and the vinyl silicone oil is adjuvant；The B composing types liquid includes methyl-silicone oil, containing hydrogen silicone oil and platinum catalyst, and the methyl-silicone oil is base material, and the containing hydrogen silicone oil is adjuvant, and the platinum catalyst is additive.The present invention fills the gap between safety glass film and smart machine 2.5D cambered surface screens using filling liquid, " glass-film white edge " can be eliminated, safety glass film is made to be fitted with smart machine 2.5D cambered surface screens completely, the aesthetic property and display effect of smart machine are so drastically increased, experience and the satisfaction of user is greatly improved.
Description
Technical field
The present invention relates to screen of intelligent device protecting film field, and in particular to a kind of filling liquid, the preparation side of the filling liquid
Method and safety glass film is tieed up into the side that (hereinafter referred to as 2.5D) cambered surface screen is fitted completely with smart machine 2.5 using the filling liquid
Method.
Background technology
With the screen enlarging of screen of intelligent device, the use of screen protecting film is more and more.Traditional polypropylene
(Polypropylene, hereinafter referred to as PP) material, polrvinyl chloride (Polyvinyl Chloride, hereinafter referred to as PVC) material and
The adhesive cover products of polyester resin (Polyethylene terephthalate, hereinafter referred to as PET) material, it is natural because of its general character
Defect, such as Mohs' hardness it is low cannot anti-scratch flower, light transmittance it is relatively low affect display resolution, thickness too it is thin cannot protect screen from
External impacts etc., are just gradually substituted by safety glass film.Safety glass film has high Mohs' hardness, light transmittance height, Surface feel
Smooth, protectiveness is strong, it is easy to attach the advantages of.
2.5D cambered surface screens are popularized in a large number in mobile phone industry at present, so-called 2.5D cambered surfaces screen, refer to that mobile phone screen is protected
Glass edge employs the cambered surface design of 2.5D, is only that screen protection glass edge adopts cambered surface, and screen is still pure-surface, shield
The protective glass that curtain top covers is except edge part exceptionally other positions are also all pure-surface.2.5D cambered surface screens have good hand touch, prevent
The advantages of broken, easy point control, the cambered surface impact effect of 2.5D also makes Mobile phone screen more three-dimensional.
But the current poor effect of fitting of safety glass film and 2.5D cambered surface screens.Safety glass film is usually pure-surface,
When safety glass film is fitted with 2.5D cambered surface screens, in safety glass film edge, inevitably vertical direction
The discrepancy in elevation, makes gap is produced between the edge of safety glass film and 2.5D cambered surface screens, and safety glass film edge occurs
The not fit area (depending on the relative width by safety glass film with mobile phone screen) that 0.1mm-2mm is not waited, fit area is not
" bubble population " of ring-type or strip, is commonly called as " glass-film white edge ".
There are some schemes for " glass-film white edge " problem, three for being such as described below kind scheme at present：
Water padding scheme：The region do not fitted between safety glass film and 2.5D cambered surface screens is filled with water, to discharge the area
Air in domain, although so can quickly realize vision filling effect, water all will evaporate at short notice, afterwards
" glass-film white edge " can occur again.
The oily matter padding scheme such as lubricating oil or salad oil：Tempering glass is filled with oily matters such as lubricating oil or salad oils
The region do not fitted between glass film and 2.5D cambered surface screens, to discharge the air in the region, the program has following deficiency, (1) oil
Property substance diffusion it is strong, on-screen display (osd) area can be entered by mobile phone screen edge-diffusion, have a strong impact on screen light transmittance, cause light
Line is reflected, and causes screen display distortion；(2) oily matter can still volatilize after a period of time has passed, " glass-film white edge " meeting
Occur again；(3) oily matter is because of its liquid form and has certain viscosity, easily adsorbs dust, meeting shape on mobile phone screen
Circlewise dirt, has a strong impact on the display effect of the attractive in appearance and screen of mobile phone；(4) although oily matter can be filled, its nothing
Supporting role, it is impossible to solve the problems, such as that safety glass film edge is frangible.
Glass cement padding scheme：The region do not fitted between safety glass film and 2.5D cambered surface screens is filled with glass cement, but
Glass cement poor fluidity, it is impossible to realize the rapid osmotic in non-fit area, poor operability；And glass cement light transmittance pole
It is low, display effect can be had a strong impact on；Glass adhesivity is high simultaneously, safety glass film can be bonded with mobile phone screen, be caused
Safety glass film is difficult to dismantle damaged safety glass film when damaging, and unloading process is likely to damage mobile phone screen.
Currently for " glass-film white edge " problem, also using the scheme of reduction safety glass film size, i.e. safety glass
The size of film is equal with the pure-surface area size of 2.5D cambered surface screens, but because there is cambered surface tolerance, institute in the production of 2.5D cambered surfaces screen
To be still difficult to avoid that " glass-film white edge " situation, and reduction safety glass film size can have a strong impact on the attractive in appearance of mobile phone screen
And visual effect, protection zone of the safety glass film to screen can be greatly reduced, Consumer's Experience is very poor.
The content of the invention
During in order to solve safety glass film is labelled on smart machine 2.5D cambered surface screens, in the edge of safety glass film
Can there is the region do not fitted between 2.5D cambered surface screens, i.e. " glass-film white edge ", affect the attractive in appearance of smart machine and show effect
Really, protection zone of the safety glass film to screen of intelligent device is affected, causes the problem that Consumer's Experience is very poor, the invention provides
A kind of filling liquid, the preparation method of the filling liquid and will be safety glass film and smart machine 2.5D cambered surface screens complete using the filling liquid
The method of full laminating.
In a first aspect, a kind of filling liquid is embodiments provided, including A composing types liquid and B composing type liquid, institute
Stating A composing type liquid includes methyl-silicone oil and vinyl silicone oil, and the methyl-silicone oil is base material, supplemented by the vinyl silicone oil
Material；The B composing types liquid includes methyl-silicone oil, containing hydrogen silicone oil and platinum catalyst, and the methyl-silicone oil is base material, described hydrogeneous
Silicone oil is adjuvant, and the platinum catalyst is additive.
Wherein, the volume ratio of the A composing types liquid and B composing type liquid is 1:1.
Wherein, in the A composing types liquid, the volume content ratio of methyl-silicone oil is 75%-80%, the body of vinyl silicone oil
Product content ratio is 20%-25%.
Wherein, in the B composing types liquid, the volume content ratio of methyl-silicone oil is 65%-70%, the volume of containing hydrogen silicone oil
Content ratio is 20%-25%, and the volume content ratio of platinum catalyst is 5%-10%.
Second aspect, present invention also offers the preparation method of above-mentioned filling liquid, comprises the following steps：
(1) methyl-silicone oil, vinyl silicone oil are mixed to get into A composing type liquid；
(2) methyl-silicone oil, containing hydrogen silicone oil and platinum catalyst are mixed to get into B composing type liquid；
(3) A composing types liquid and B composing type liquid mixing are obtained into the filling liquid.
Wherein, in the step (1), according to the body that the volume content ratio of methyl-silicone oil is 75%-80%, vinyl silicone oil
Ratio mixed methyl silicone oil and vinyl silicone oil of the product content ratio for 20%-25%.
Wherein, in the step (2), according to the volume that the volume content ratio of methyl-silicone oil is 65%-70%, containing hydrogen silicone oil
Content ratio is 20%-25% and the volume content ratio of platinum catalyst is the ratio mixed methyl silicone oil of 5%-10%, Silicon Containing Hydrogen
Oil and platinum catalyst.
Wherein, in the step (3), it is 1 according to volume ratio:1 ratio mixing A composing types liquid and B composing type liquid.
The third aspect, present invention also offers a kind of above-mentioned filling liquid is in safety glass film and smart machine 2.5D cambered surface screens
Application in laminating, safety glass film is fitted completely with smart machine 2.5D cambered surface screens, is comprised the following steps：
S1：Safety glass film is labelled on smart machine 2.5D cambered surface screens；
S2：The filling liquid is drawn, a line edge is chosen from the four edges edge of the safety glass film, along selected
The filling liquid is extruded at edge, and is smeared back and forth, with fill the safety glass film and the smart machine 2.5D cambered surfaces screen it
Between the region do not fitted；
S3：Repeating said steps S2, to fill remaining three edges of the safety glass film and the smart machine
The region do not fitted between 2.5D cambered surface screens；
S4：3-5 hours are waited, the region to occurring residual bubble in step S2 and/or step S3 is repaired；
S5：12-48 hours are waited, the region to occurring residual bubble in step S2 and/or step S3 is carried out again
Repair.
In the present invention, filling liquid, the preparation method and application of the filling liquid have the effect that：
The filling liquid of the present invention is expressed into into " glass-film white edge " region, to fill safety glass film and smart machine 2.5D
Gap between cambered surface screen, after being extruded due to filling liquid, in longer period of time, (such as in one hour) can keep high
Mobility, and the lubricity based on containing hydrogen silicone oil, so the diffusion effect of filling liquid is substantially, are capable of achieving gap without the need for auxiliary
Filling.
After the filling liquid of the present invention is filled in " glass-film white edge " region, it is solid that 3-5 hours filling liquid is capable of achieving moderate
Change, 12-48 hour filling liquids are capable of achieving to be fully cured, after filling liquid solidification, physical aspect is stable, will not be as water and oily matter
Equally through a period of time just evaporate, so the present invention not only eliminate safety glass film edge " glass-film is white
Side ", makes safety glass film be fitted with 2.5D cambered surface screens completely, and solves " glass-film white edge " recurrent problem.By
After the filling liquid solidification of the present invention, physical aspect is stable, the gap filled and led up between safety glass film and 2.5D cambered surface screens, institute
So that tempering glass-film can be supported, make the edge of safety glass film no longer hanging, largely alleviate safety glass
The frangible problem of film edge.
The gap between the edge of safety glass film and 2.5D cambered surface screens is filled using the filling liquid of the present invention, is eliminated
" glass-film white edge ", is made safety glass film be fitted with smart machine 2.5D cambered surface screens completely, so drastically increases intelligence
The aesthetic property and display effect of equipment, greatly improves Consumer's Experience and satisfaction.And the present invention is workable, operation
Simply, it is easy to use.
The present invention filling liquid bulk composition be high transparency organosilicon material, light transmittance be usually above 90%, do not interfere with
Screen light transmittance, will not cause light to reflect, will not cause screen display distortion, improve the effect of screen display.
The filling liquid intrinsic viscosity of the present invention is very low, on the one hand solves oily matter and easily adsorbs dust, on screen
The problem of visible ring-type dirt is formed, the display effect of the aesthetic property and screen of smart machine is improve, on the other hand, works as steel
Change glass-film is damaged when needing dismounting, does not interfere with or damage the screen of smart machine.
It should be appreciated that the general description of the above and detailed description hereinafter are only exemplary and explanatory, not
The present invention can be limited.
Specific embodiment
Embodiments of the invention are described below.
The invention provides a kind of filling liquid, the filling liquid includes A composing types liquid and B composing type liquid, A composing type liquid
The volume ratio of body and B composing type liquid is 1:1.A composing type liquid includes methyl-silicone oil and vinyl silicone oil, wherein, methyl silicon
Oil is base material, and the volume content ratio of methyl-silicone oil is 75%-80%, and vinyl silicone oil is adjuvant, and the volume of vinyl silicone oil contains
Amount is than being 20%-25%.B composing type liquid includes methyl-silicone oil, containing hydrogen silicone oil and platinum catalyst, wherein, methyl-silicone oil is
Base material, the volume content ratio of methyl-silicone oil is 65%-70%, and containing hydrogen silicone oil is adjuvant, and the volume content ratio of containing hydrogen silicone oil is
20%-25%, platinum catalyst are additive, and the volume content ratio of platinum catalyst is 5%-10%.
Wherein, there is chemistry with protium in containing hydrogen silicone oil in the vinyl in vinyl silicone oil under platinum catalyst effect
Reaction, generates elastomer silicone or organic silicon resin, improves edge and the 2.5D of filling liquid filling safety glass film
The effect in the gap between cambered surface screen.
Present invention also offers the preparation method of above-mentioned filling liquid, comprises the following steps：
(1) methyl-silicone oil, vinyl silicone oil are mixed to get into A composing type liquid, wherein, the volume content ratio of methyl-silicone oil
For 75%-80%, the volume content ratio of vinyl silicone oil is 20%-25%.
(2) methyl-silicone oil, containing hydrogen silicone oil and platinum catalyst are mixed to get into B composing type liquid, wherein, methyl-silicone oil
Volume content ratio is 65%-70%, and the volume content ratio of containing hydrogen silicone oil is 20%-25%, the volume content ratio of platinum catalyst
For 5%-10%.
(3) it is 1 according to volume ratio by A composing types liquid and B composing types liquid:1 ratio is mixed to get filling liquid.
Present invention also offers application of the above-mentioned filling liquid on safety glass film is fitted with smart machine 2.5D cambered surface screens,
So that safety glass film is fitted completely with smart machine 2.5D cambered surface screens, comprise the following steps：
S1：Safety glass film is labelled on smart machine 2.5D cambered surface screens, notes keeping safety glass film and 2.5D cambered surfaces
Without obvious foreign body between screen, then, occur between the four edges edge of safety glass film and smart machine 2.5D cambered surface screens and do not paste
The region of conjunction, the non-fit area are " glass-film white edge " region, after " glass-film white edge " regional stability, after beginning preparing for
Continuous step, to use filling liquid filling " glass-film white edge " region of the present invention；
S2：Appropriate filling liquid is drawn with dropper, a line edge is chosen from the four edges edge of safety glass film and is started operation,
Filling liquid is uniformly extruded along selected edge by dropper, and is smeared back and forth, to fill safety glass film and smart machine
Gap between 2.5D cambered surface screens.After being extruded due to filling liquid, in longer period of time, (such as in one hour) can be protected
High fluidity, and the lubricity based on containing hydrogen silicone oil are held, so the diffusion effect of filling liquid substantially, is capable of achieving without the need for auxiliary
Gap filling.Wait ten minutes or so can blind more than 90%, then dry unnecessary filling liquid；If subregion goes out
Bubble is remained now, this step wouldn't be processed；
Wherein, in this step, can be by smart machine support with favored policy, to aid in filling liquid filling " glass-film white edge " area
Domain, accelerates the discharge of air in " glass-film white edge " region, to reach more preferable filling effect.Need when drying unnecessary filling liquid thorough
Wipe unnecessary filling liquid in bottom, it is to avoid the situation that erasing is difficult after filling liquid solidification occurs；
S3：Repeat step S2, to fill between remaining three edges of safety glass film and smart machine 2.5D cambered surface screens
The region do not fitted, until most " glass-film white edge " zones vanishes；If residual bubble occurs in subregion, this step is temporary
Do not process；
S4：Wait 3-5 hours, filling liquid moderate solidification, to the area for residual bubble occur in step S2 and/or step S3
Repaired in domain；
S5：12-48 hours, filling liquid is waited to be fully cured, to occurring residual bubble in step S2 and/or step S3
Repaired again in region.After filling liquid solidification, physical aspect is stable, is on the one hand filled with safety glass film and 2.5D cambered surface screens
Between gap, on the other hand eliminate " glass-film white edge ", support played a part of to safety glass film also.
On the one hand the filling liquid of the present invention and its application can make safety glass film complete with smart machine 2.5D cambered surface screens
Laminating, on the other hand, the present invention can also solve the special-shaped radian that smart machine 2.5D cambered surface screens are produced in process of production or
The problem that the safety glass film that local dent brings can not be fitted completely with 2.5D cambered surfaces screen.
After the filling liquid of the present invention is filled in the gap in " glass-film white edge " region, it is solid that 3-5 hours are capable of achieving moderate
Change, 12-48 hours are capable of achieving degree of cure, the filling liquid physical aspect after solidification is stable, will not be as water is as oily matter
Just evaporate through a period of time, so the present invention not only eliminates " the glass-film white edge " of safety glass film edge, make
Safety glass film is fitted completely with 2.5D cambered surface screens, and solves " glass-film white edge " recurrent problem.Due to this
After bright filling liquid solidification, physical aspect is stable, and the gap filled and led up between safety glass film and 2.5D cambered surface screens can support
Safety glass film, makes the edge of safety glass film no longer hanging, largely alleviates safety glass film edge frangible
Problem.
The above is only the specific embodiment of the present invention, is made skilled artisans appreciate that or realizing this
It is bright.Various modifications to these embodiments will be apparent to one skilled in the art, as defined herein
General Principle can be realized without departing from the spirit or scope of the present invention in other embodiments.Therefore it is of the invention
The embodiments shown herein is not intended to be limited to, and is to fit to and principles disclosed herein and features of novelty phase one
The most wide scope for causing.
Embodiment of the present invention above, does not constitute limiting the scope of the present invention.
Claims (10)
1. a kind of filling liquid, it is characterised in that including A composing types liquid and B composing type liquid, the A composing types liquid includes
Methyl-silicone oil and vinyl silicone oil, the methyl-silicone oil are base material, and the vinyl silicone oil is adjuvant；The B composing types liquid
Including methyl-silicone oil, containing hydrogen silicone oil and platinum catalyst, the methyl-silicone oil be base material, the containing hydrogen silicone oil be adjuvant, the platinum
Au catalyst is additive.
2. filling liquid according to claim 1, it is characterised in that the volume of the A composing types liquid and B composing type liquid
Than for 1:1.
3. filling liquid according to claim 1 and 2, it is characterised in that in the A composing types liquid, the body of methyl-silicone oil
Product content ratio is 75%-80%, and the volume content ratio of vinyl silicone oil is 20%-25%.
4. filling liquid according to claim 1 and 2, it is characterised in that in the B composing types liquid, the body of methyl-silicone oil
Product content ratio is 65%-70%, and the volume content ratio of containing hydrogen silicone oil is 20%-25%, and the volume content ratio of platinum catalyst is
5%-10%.
5. the preparation method of the filling liquid any one of a kind of claim 1-4, it is characterised in that comprise the following steps：
(1) methyl-silicone oil, vinyl silicone oil are mixed to get into A composing type liquid；
(2) methyl-silicone oil, containing hydrogen silicone oil and platinum catalyst are mixed to get into B composing type liquid；
(3) A composing types liquid and B composing type liquid mixing are obtained into the filling liquid.
6. the preparation method of filling liquid according to claim 5, it is characterised in that in the step (1), according to methyl silicon
The ratio mixed methyl silicone oil that the volume content ratio of oil is 75%-80%, the volume content ratio of vinyl silicone oil is 20%-25%
And vinyl silicone oil.
7. the preparation method of filling liquid according to claim 5, it is characterised in that in the step (2), according to methyl silicon
The volume content ratio of oil is 65%-70%, the volume content ratio of containing hydrogen silicone oil is 20%-25% and the volume of platinum catalyst contains
Amount is than the ratio mixed methyl silicone oil for 5%-10%, containing hydrogen silicone oil and platinum catalyst.
8. the preparation method of filling liquid according to claim 5, it is characterised in that in the step (3), according to volume ratio
For 1:1 ratio mixing A composing types liquid and B composing type liquid.
9. the filling liquid any one of a kind of claim 1-4 is fitted with smart machine 2.5D cambered surface screens in safety glass film
On application.
10. application of the filling liquid according to claim 9 on safety glass film is fitted with smart machine 2.5D cambered surface screens,
Characterized in that, comprising the following steps：
S1：Safety glass film is labelled on smart machine 2.5D cambered surface screens；
S2：The filling liquid is drawn, a line edge is chosen from the four edges edge of the safety glass film, along selected edge
The filling liquid is extruded, and is smeared back and forth, to fill between the safety glass film and the smart machine 2.5D cambered surface screens not
The region of laminating；
S3：Repeating said steps S2, to fill remaining three edges of the safety glass film and the smart machine 2.5D arcs
The region do not fitted between the screen of face；
S4：3-5 hours are waited, the region to occurring residual bubble in step S2 and/or step S3 is repaired；
S5：12-48 hours are waited, the region to occurring residual bubble in step S2 and/or step S3 is repaired again.