CN105038436A - Fiber glass reinforced plastic coating and preparation method and coating technique thereof - Google Patents
Fiber glass reinforced plastic coating and preparation method and coating technique thereof Download PDFInfo
- Publication number
- CN105038436A CN105038436A CN201510485377.5A CN201510485377A CN105038436A CN 105038436 A CN105038436 A CN 105038436A CN 201510485377 A CN201510485377 A CN 201510485377A CN 105038436 A CN105038436 A CN 105038436A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiberglass
- antioxidant
- defoamer
- solidifying agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses fiber glass reinforced plastic coating, which is prepared from the following raw materials in parts by weight: 90-120 parts of fluororesin, 30-50 parts of colorant, 4-6 parts of dispersant, 2-4 parts of defoamer, 2-4 parts of catalyst, 6-10 parts of curing agent, 2-4 parts of ultraviolet absorbent, and 2-4 parts of antioxidant. The invention provides the fiber glass reinforced plastic coating which is low in production cost, stable in performance, and capable of improving the yield and the service life of fiber glass reinforced plastic products, and a preparation method and a coating technique thereof, and the technique is simple and convenient to operate.
Description
Technical field
The present invention relates to field of compound material, be specifically related to a kind of fiberglass paint and preparation method thereof, coating process.
Background technology
The development of glass reinforced plastic application provides wide application prospect to process for treating surface, at present, due to the reason such as technique, technology, the surface of glass fiber reinforced plastics product is not fully up to expectations, large quantities of finished product only becomes unacceptable product because of the defect on surface, and causing unnecessary cost increases; Existing glass fiber reinforced plastics product is in order to ensure the quality of products, and higher to the requirement of matrix and sheet material, production cost is high; In order to extend the work-ing life of glass reinforced plastic, add auxiliary agent in the base, but the impact of outer bound pair finished product mostly is surface, the utilization ratio of auxiliary agent is not high.
Summary of the invention
The present invention is the weak point for avoiding existing for above-mentioned prior art, there is provided a kind of production cost low, stable performance, improve glass fiber reinforced plastics product yield rate and a kind of fiberglass paint in work-ing life and preparation method thereof, coating process, its technique is simple, easy to operate.
Object of the present invention is achieved through the following technical solutions: a kind of fiberglass paint, obtained by mass parts by following raw material: fluoro-resin 90-120 part; Tinting material 30-50 part; Dispersion agent 4-6 part; Defoamer 2-4 part; Catalyzer 2-4 part; Solidifying agent 6-10 part; UV light absorber 2-4 part; Antioxidant 2-4 part.
A preparation method for fiberglass paint, its preparation method is as follows:
In fluoro-resin, add dispersion agent, defoamer and catalyzer, stirring at low speed is even; To be mixed evenly after, add tinting material, UV light absorber and antioxidant, high speed dispersion, rotating speed is 1000-1500rpm, until its fineness reaches 30 μm; Add solidifying agent, high speed dispersion, until fineness reaches 45 μm; Sealing is preserved.
The coating process of fiberglass paint is: added by sheet material in mould, and closed press, makes product molding, until obtain minimum initial strength; Opening mold, injects product surface by fiberglass paint and reaches 0.5-0.7mm; Closed press, makes paint solidification; Open press, take out goods.
Wherein, solidifying agent is calcium carbonate.
The present invention compared with prior art has the following advantages:
The present invention can be used for glass fiber reinforced plastic surface application, the apparent mass of glass fiber reinforced plastics product can be improved, thus reduce the scrap rate of goods, avoid the surface of the glass fiber reinforced plastics product caused due to the reason such as technology, technique not fully up to expectations and make goods become unacceptable product, improve qualification rate, reduce unnecessary cost; Use the present invention, under certain conditions can low with relative valency in alkali fiber, resins for universal use replace manufacturing glass reinforced plastic finished product without alkali fiber, corrosion-resisting resin, under the prerequisite of use properties not affecting goods, the effectively raw-material cost of reduction; Related auxiliaries only need use at upper layer, thus glass fiber reinforced plastics product can not use corresponding auxiliary agent when producing, and uses at finished surface, effectively improves the utilization ratio of auxiliary agent, reduces cost; Add UV light absorber, antioxidant, add the work-ing life of glass fiber reinforced plastics product, avoid glass fiber reinforced plastics product to be formed aging by the impact of outside atmosphere; Glass reinforced plastic aging general all from surface, and main within the scope of 0.5-0.7mm, the present invention can increase the work-ing life of glass fiber reinforced plastics product, saves maintenance cost; Use calcium carbonate is solidifying agent, environmentally friendly, decreasing pollution.
embodiment:
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment of the present invention is:
Embodiment 1:
A kind of fiberglass paint, obtained by mass parts by following raw material: fluoro-resin 90-120 part; Tinting material 30-50 part; Dispersion agent 4-6 part; Defoamer 2-4 part; Catalyzer 2-4 part; Solidifying agent 6-10 part; UV light absorber 2-4 part; Antioxidant 2-4 part.
Embodiment 2:
A kind of fiberglass paint, obtained by mass parts by following raw material: fluoro-resin 90 parts; Tinting material 30 parts; Dispersion agent 4 parts; Defoamer 2 parts; Catalyzer 2 parts; 6 parts, solidifying agent; UV light absorber 2 parts; Antioxidant 2 parts.
Embodiment 3:
A kind of fiberglass paint, obtained by mass parts by following raw material: fluoro-resin 100 parts; Tinting material 40 parts; Dispersion agent 4 parts; Defoamer 2 parts; Catalyzer 2 parts; 6 parts, solidifying agent; UV light absorber 2 parts; Antioxidant 2 parts.
Embodiment 4:
A kind of fiberglass paint, obtained by mass parts by following raw material: fluoro-resin 110 parts; Tinting material 45 parts; Dispersion agent 5 parts; Defoamer 3 parts; Catalyzer 3 parts; 8 parts, solidifying agent; UV light absorber 3 parts; Antioxidant 3 parts.
Embodiment 5:
A kind of fiberglass paint, obtained by mass parts by following raw material: obtained by mass parts by following raw material: fluoro-resin 100 parts; Tinting material 40 parts; Dispersion agent 5 parts; Defoamer 3 parts; Catalyzer 3 parts; 8 parts, solidifying agent; UV light absorber 3 parts; Antioxidant 3 parts.
Embodiment 6:
A kind of fiberglass paint, obtained by mass parts by following raw material: fluoro-resin 120 parts; Tinting material 50 parts; Dispersion agent 6 parts; Defoamer 4 parts; Catalyzer 4 parts; 10 parts, solidifying agent; UV light absorber 4 parts; Antioxidant 4 parts.
In embodiment 1-embodiment 6, solidifying agent is calcium carbonate.
Present invention also offers the preparation method of above-mentioned fiberglass paint, its preparation method is as follows simultaneously:
In fluoro-resin, add dispersion agent, defoamer and catalyzer, stirring at low speed is even; To be mixed evenly after, add tinting material, UV light absorber and antioxidant, high speed dispersion, rotating speed is 1000-1500rpm, until its fineness reaches 30 μm; Add solidifying agent, high speed dispersion, until fineness reaches 45 μm; Sealing is preserved.
Present invention also offers the coating process of above-mentioned fiberglass paint: added by sheet material in mould, closed press, makes product molding, until obtain minimum initial strength simultaneously; Opening mold, injects product surface by fiberglass paint and reaches 0.5-0.7mm; Closed press, makes paint solidification; Open press, take out goods.
The present invention can be used for glass fiber reinforced plastic surface application, the apparent mass of glass fiber reinforced plastics product can be improved, thus reduce the scrap rate of goods, avoid the surface of the glass fiber reinforced plastics product caused due to the reason such as technology, technique not fully up to expectations and make goods become unacceptable product, improve qualification rate, reduce unnecessary cost; Use the present invention, under certain conditions can low with relative valency in alkali fiber, resins for universal use replace manufacturing glass reinforced plastic finished product without alkali fiber, corrosion-resisting resin, under the prerequisite of use properties not affecting goods, the effectively raw-material cost of reduction; Related auxiliaries only need use at upper layer, thus glass fiber reinforced plastics product can not use corresponding auxiliary agent when producing, and uses at finished surface, effectively improves the utilization ratio of auxiliary agent, reduces cost; Add UV light absorber, antioxidant, add the work-ing life of glass fiber reinforced plastics product, avoid glass fiber reinforced plastics product to be formed aging by the impact of outside atmosphere; Glass reinforced plastic aging general all from surface, and main within the scope of 0.5-0.7mm, the present invention can increase the work-ing life of glass fiber reinforced plastics product, saves maintenance cost; Use calcium carbonate is solidifying agent, environmentally friendly, decreasing pollution.
The foregoing is only explanation embodiments of the present invention; be not limited to the present invention, for a person skilled in the art, within the spirit and principles in the present invention all; any amendment of doing, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (5)
1. a fiberglass paint, is characterized in that: obtained by mass parts by following raw material: fluoro-resin 90-120 part; Tinting material 30-50 part; Dispersion agent 4-6 part; Defoamer 2-4 part; Catalyzer 2-4 part; Solidifying agent 6-10 part; UV light absorber 2-4 part; Antioxidant 2-4 part.
2. a kind of fiberglass paint according to claim 1, is characterized in that: obtained by mass parts by following raw material: fluoro-resin 100 parts; Tinting material 40 parts; Dispersion agent 5 parts; Defoamer 3 parts; Catalyzer 3 parts; 8 parts, solidifying agent; UV light absorber 3 parts; Antioxidant 3 parts.
3. a kind of fiberglass paint according to claim 1 and 2, is characterized in that: its preparation method is as follows:
In fluoro-resin, add dispersion agent, defoamer and catalyzer, stirring at low speed is even; To be mixed evenly after, add tinting material, UV light absorber and antioxidant, high speed dispersion, rotating speed is 1000-1500rpm, until its fineness reaches 30 μm; Add solidifying agent, high speed dispersion, until fineness reaches 45 μm; Sealing is preserved.
4. a kind of fiberglass paint according to claim 3, is characterized in that: the coating process of described fiberglass paint is: added by sheet material in mould, and closed press, makes product molding, until obtain minimum initial strength; Opening mold, injects product surface by fiberglass paint and reaches 0.5-0.7mm; Closed press, makes paint solidification; Open press, take out goods.
5. a kind of fiberglass paint according to claim 1 and 2, is characterized in that: described solidifying agent is calcium carbonate.