CN105034222A - Method for manufacturing glass bead polyurethane composite insulation board - Google Patents
Method for manufacturing glass bead polyurethane composite insulation board Download PDFInfo
- Publication number
- CN105034222A CN105034222A CN201510410553.9A CN201510410553A CN105034222A CN 105034222 A CN105034222 A CN 105034222A CN 201510410553 A CN201510410553 A CN 201510410553A CN 105034222 A CN105034222 A CN 105034222A
- Authority
- CN
- China
- Prior art keywords
- glass bead
- polyurethane composite
- composite heat
- polyisocyanates
- conservation board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for manufacturing a glass bead polyurethane composite insulation board and belongs to the field of building materials. According to the insulation board, on the premise that the original insulation effect is maintained, fire resistance is improved, strength is improved, water absorption performance is lowered, and production cost is reduced. The method comprises the steps that glass beads and one of polyisocyanates and premixed polyether polyols are placed in a stirrer to be evenly stirred and mixed; the material obtained after even stirring and mixing and polyisocyanates or premixed polyether polyols are sprayed into a specific mold in proportion; the specific mold is slowly vibrated and pressurized, air needs to be discharged outside gradually during vibration and pressurization of the specific mold, generation of bubbles is reduced, and then the polyisocyanates and premixed polyether polyols are fully foamed to form polyurethane and the glass beads are squeezed and bonded, so that the board is formed finally; and the product, namely the glass bead polyurethane composite insulation board is separated from the specific mold.
Description
Technical field
The invention belongs to building material field, be specifically related to a kind of glass bead polyurethane composite heat-conservation board preparation method.
Background technology
Traditional warming plate, manufacturing process is mainly by passing into high temperature and high pressure steam, and after reaching the stipulated time, water filling has cooled.This insulation material shortcoming is that production cost is high, and fire protecting performance is low, seriously polluted, and heat insulation effect is not good.Along with more and more higher to the requirement of construction material, rigid polyurethane foam heat insulation material is slowly employed, but is not suitable for actual large-scale application because of its high cost.
In prior art, in polyurethane foam material, polyisocyanates is commonly called as pearl material, and combined polyether (polyalcohol) is commonly called as ester material, and by polyalcohol, fire retardant, catalyst, other auxiliary agents such as blowing agent mix.Glass bead is commercially available.
A kind of glass bead polyurethane composite heat-conservation board preparation method of the present invention is as follows:
1) by glass bead first with polyisocyanates or combined polyether wherein one put into agitator and be uniformly mixed;
2) material after being uniformly mixed in step 1) and polyisocyanates or combined polyether are sprayed in particular mold in proportion respectively;
3) slowly vibrate particular mold and pressurize, needing to discharge air outward gradually in particular mold vibration pressure process, reduce the generation of bubble, making polyisocyanates and combined polyether fully be foamed into polyurethane and extrude bonding glass bead finally to become plate;
4) products of separated from particular mold, is glass bead polyurethane composite heat-conservation board.
In described a kind of glass bead polyurethane composite heat-conservation board preparation method, the accounting of glass bead is 10% ~ 90%.
Preferably, the accounting of described glass bead is 30%.
Preferably, the accounting of described glass bead is 50%.
Preferably, the accounting of described glass bead is 70%.
In prior art, in polyurethane foam material, polyisocyanates is commonly called as pearl material, and combined polyether (polyalcohol) is commonly called as ester material, and by polyalcohol, fire retardant, catalyst, other auxiliary agents such as blowing agent mix.Glass bead is commercially available.
Summary of the invention
For solving the problem, main purpose of the present invention is to provide a kind of glass bead polyurethane composite heat-conservation board preparation method, while the original heat insulation effect of maintenance, also improves fire line, adds intensity, reduce water imbibition, reduce production cost.
Detailed description of the invention
Embodiment 1
A kind of glass bead polyurethane composite heat-conservation board preparation method:
1) glass bead is first put into agitator with polyisocyanates to be uniformly mixed;
2) material after being uniformly mixed in step 1) and combined polyether are sprayed in particular mold in proportion respectively;
3) slowly vibrate particular mold and pressurize, needing to discharge air outward gradually in particular mold vibration pressure process, reduce the generation of bubble, making polyisocyanates and combined polyether fully be foamed into polyurethane and extrude bonding glass bead finally to become plate;
4) products of separated from particular mold, is glass bead polyurethane composite heat-conservation board.
The ratio accounting for a kind of glass bead polyurethane composite heat-conservation board preparation method of described glass bead is 30%.
Embodiment 2
A kind of glass bead polyurethane composite heat-conservation board preparation method:
1) glass bead is first put into agitator with combined polyether to be uniformly mixed;
2) material after being uniformly mixed in step 1) and polyisocyanates are sprayed in particular mold in proportion respectively;
3) slowly vibrate particular mold and pressurize, needing to discharge air outward gradually in particular mold vibration pressure process, reduce the generation of bubble, making polyisocyanates and combined polyether fully be foamed into polyurethane and extrude bonding glass bead finally to become plate;
4) products of separated from particular mold, is glass bead polyurethane composite heat-conservation board.
The ratio accounting for a kind of glass bead polyurethane composite heat-conservation board preparation method of described glass bead is 50%.
Embodiment 3
A kind of glass bead polyurethane composite heat-conservation board preparation method:
1) glass bead is first put into agitator with combined polyether to be uniformly mixed;
2) material after being uniformly mixed in step 1) and polyisocyanates are sprayed in particular mold in proportion respectively;
3) slowly vibrate particular mold and pressurize, needing to discharge air outward gradually in particular mold vibration pressure process, reduce the generation of bubble, making polyisocyanates and combined polyether fully be foamed into polyurethane and extrude bonding glass bead finally to become plate;
4) products of separated from particular mold, is glass bead polyurethane composite heat-conservation board.
The ratio that described glass bead accounts for a kind of glass bead polyurethane composite heat-conservation board preparation method is 70%.
Claims (5)
1. a glass bead polyurethane composite heat-conservation board preparation method, is characterized in that: its preparation method is
1) by glass bead first with polyisocyanates or combined polyether wherein one put into agitator and be uniformly mixed;
2) material after being uniformly mixed in step 1) and polyisocyanates or combined polyether are sprayed in particular mold in proportion respectively;
3) slowly vibrate particular mold and pressurize, needing to discharge air outward gradually in particular mold vibration pressure process, reduce the generation of bubble, making polyisocyanates and combined polyether fully be foamed into polyurethane and extrude bonding perlite finally to become plate;
4) products of separated from particular mold, is glass bead polyurethane composite heat-conservation board.
2. a kind of glass bead polyurethane composite heat-conservation board preparation method as claimed in claim 1, is characterized in that: in described a kind of glass bead polyurethane composite heat-conservation board preparation method, perlitic accounting is 10% ~ 90%.
3. a kind of glass bead polyurethane composite heat-conservation board preparation method as claimed in claim 1, is characterized in that: in described a kind of glass bead polyurethane composite heat-conservation board preparation method, perlitic accounting is 30%.
4. a kind of glass bead polyurethane composite heat-conservation board preparation method as claimed in claim 1, is characterized in that: in described a kind of glass bead polyurethane composite heat-conservation board preparation method, perlitic accounting is 50%.
5. a kind of glass bead polyurethane composite heat-conservation board preparation method as claimed in claim 1, is characterized in that: in described a kind of glass bead polyurethane composite heat-conservation board preparation method, perlitic accounting is 70%.