CN105032366B - A kind of konjaku glucomannan water body filter core and preparation method thereof - Google Patents
A kind of konjaku glucomannan water body filter core and preparation method thereof Download PDFInfo
- Publication number
- CN105032366B CN105032366B CN201510402509.3A CN201510402509A CN105032366B CN 105032366 B CN105032366 B CN 105032366B CN 201510402509 A CN201510402509 A CN 201510402509A CN 105032366 B CN105032366 B CN 105032366B
- Authority
- CN
- China
- Prior art keywords
- parts
- filter core
- preparation
- gel microsphere
- portuguese gansu
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of konjaku glucomannan water body filter core and preparation method thereof.The preparation method of konjaku glucomannan water body filter core, including prepared by the preparation of Rhizoma amorphophalli fiber, konjak portuguese gansu polyose gel microsphere, the preparation of the konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical and prepare filter core.The konjaku glucomannan water body filter core of the present invention, using konjaku as primary raw material, using the sustained release performance of Rhizoma amorphophalli fiber and the absorption property of konjak portuguese gansu polyose gel microsphere, and microballoon, plays a role.Rhizoma amorphophalli fiber can purify water, and konjak portuguese gansu polyose gel microsphere can filter off most of microorganism in water body, so as to need not largely use microbicide；Konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical can be such that nutriment for a long time, stably, constantly discharges, it is ensured that the absorption efficiency of human body.The composition of nutritious supplementary pharmaceutical is calcium carbonate, ferrous fumarate, zinc sulfate, sodium selenite, copper sulphate, manganese sulfate, chromium picolinate etc., can supplement trace element necessary to calcium, iron, zinc, selenium, copper, manganese, chromium of needed by human body etc..
Description
Technical field
The present invention relates to a kind of water body filter core and preparation method thereof, and in particular to a kind of konjaku glucomannan water body filter core and
Its preparation method.
Background technology
Water（H2O）, it is nontoxic, be at normal temperatures and pressures the liquid of colorless and odorless, be it is a kind of by hydrogen, oxygen element constitute it is inorganic
Thing, is the most important part of organism, the even more spring of the life of the mankind.It includes natural water（River, lake, atmospheric water,
Seawater, underground water etc.）, distilled water, purified water, ultra-pure water, deionized water etc..
At present, the present situation of water resources in china is very severe, and China is the country of a severe drought water shortage.Although fresh water is provided
Source total amount is about 28000 billion cubic meters, accounts for the 6% of global water resources, is only second to Brazil, Russia and Canada, occupies the world the
Four, but there was only about 2200 cubic metres per capita, only 1/4, the 1/5 of the U.S. of world average level ranks 121 in the world
Position, is 13, the whole world one of poorest country of water resource per capita.In addition, water resources in china is seriously polluted, count in contaminated
Water source, the utilizable water source of people is few.Therefore, in China, most cities and area are required for manually purification portion
Divide water body, such as river, lake, to provide the water source of enough human survivals.
But it is just directly to feed the water into user house just with the filtering of waterworks to purify the problem of water source is present
In, some compositions in water body are still exceeded, throughout history yearbook, the also poisoning of not fresh drinking water, or water body peracid
Or cross alkali influence human acid-base balance, and or water nutrition do not reach demand of human body etc..So, many Domestic water purifyings are set
It is standby to have come into huge numbers of families.
Nowadays, rhythm of life is fast, level is high, and people increasingly focus on the life of healthy green, there is higher pursuit and product
Taste.The need for initially common purifier can not meet people, and the purifier of main flow is adopted nothing more than on the market
With four kinds of materials：One is, PP cottons, cost is low, and technique is simple, and short life can only remove larger particle；Two are, activated carbon, can filter
Color, eliminates the unusual smell, and has preferable adsorption effect to pollutant, but invalid to bacterium, thereby increases and it is possible to can due to overstocked pollutant is used for a long time
Form secondary pollution, short life；Three are, ultrafiltration, can guarantee that big water yield, almost 100% filter out bacterium, durable, few waste water,
But it can not go to eliminate the unusual smell and ion；Four are, RO reverse osmosis membranes, can go out purified water, but need inverse concentration gradient acting, use water
Pump, it is necessary to which multipole is filtered, waste water is more, and water yield is small, short life, and unsuitable human body is drunk for a long time, easy calcium deficiency zinc-deficiency.
《Non-woven cloth》The 4th interim Liu Chao, Jin Xiangyu of volume 18 in 2010 article " novel antibacterial PP-g-NDAM water mistakes
Filter melt-blown filter ", it is main to inquire into a kind of new water filtration melt-blown filter with antibacterial functions of research and development.Polypropylene and NDAM are anti-
Resin slicer (abbreviation PP-g-NDAM) is made in the graft copolymerization in the presence of initiator of bacterium monomer, is tested by being meltblown, and inquiring into should
The melt-blown process forming property and its basic performance of melt-blowing nonwoven of raw material, and processing antibacterial water filtration melt-blown filter
Feasibility.The filter core is while filter efficiency is ensured, with the function of killing bacterium, filter water can be greatly improved drinks peace
Quan Xing.But the filter core may filter off some mineral elements of needed by human body, and the pH value in water can not be adjusted；In addition, filter core
A kind of chemical materials is used, may not be degradable after discarding, pollute environment.
A kind of patent " filter core of water filtration device " of Application No. 201420298774.2（The applying date：
2014.06.06）, describe a kind of filter core.The filter core of the patent includes upper end cover, filter core cylinder, the bottom end cover being sequentially connected, under
End cap is up axially arranged with hollow connecting rod, and bottom end cover is connected as a single entity with hollow connecting rod, is provided with suitable with hollow connecting rod in the middle of upper end cover
The opening matched somebody with somebody, hollow connecting rod pass through opening, be attached between hollow connecting rod and the opening of upper end cover by screw thread, bottom end cover with
Hollow connecting rod is connected as a single entity, and hollow connecting rod is threadedly coupled with upper end cover.Hollow connecting rod side wall is provided with some through holes, through hole height
Shift to install, carbon filter layer is provided between hollow connecting rod and filter core cylinder.But the material employed in this patent can not be very
PH value in good regulation water body, and needed by human body mineral may in the lump be filtered off.Long-term drink may be such that human body acid
Alkali disequilibrium, change osmotic pressure and subalimentation.
The patent of invention " micropore ceramic filter element with antibacterial water activating function " of Application No. 200510043703.3（Shen
Please day：2005.06.02）, describe a kind of filter core.The filter core of the patent is characterised by its dispensing, by diatomite, multifunctional key
Health ceramic material, disappearance thing, binding agent, soda ash, are made after dispensing, material mixing, molding in 600~1300 DEG C of temperature lower calcinations.
But the material employed in this invention is not degradable, and after long-term use, it is difficult to change.
The content of the invention
It is an object of the invention to provide a kind of konjaku glucomannan water body filter core and preparation method thereof.Utilize konjak portuguese gansu polyose
The absorption property of sugared gel micro-ball and Rhizoma amorphophalli fiber, and microballoon sustained release performance, make it is a kind of it is with low cost, can industrial metaplasia
Production, discarded rear konjaku glucomannan water body filter core degradable, free from environmental pollution.
The preparation method of a kind of konjaku glucomannan water body filter core of the present invention, it is characterised in that preparation process is as follows：
（1）The preparation of Rhizoma amorphophalli fiber：Component, takes 15-150 parts of konjaku glucomannan, adds 30-40 times of its weight by weight
Purified water, stirring and dissolving, gelatinization stand 1-2h obtain No. 1 standby sample；75-500 parts of the starch that purity is 75%-90% is taken, with No. 1
Standby sample is well mixed, and obtains No. 2 standby samples；90-300 parts of the dietary alkali that purity is 80%-90% is taken, 300-600 parts of food is prepared
With aqueous slkali, edible alkali solution is well mixed with No. 2 standby samples, No. 3 standby samples are obtained；No. 3 standby samples are poured into filter core mould
In, 50-70min is steamed at 80-110 DEG C, after taking-up, 20-24h is freezed in the refrigerator for placing into -40--50 DEG C, takes out and thaws,
It is 5%-20% to be dried at 50-60 DEG C to moisture content, obtains Rhizoma amorphophalli fiber；
（2）It is prepared by konjak portuguese gansu polyose gel microsphere：
A, konjaku glucomannan alkaline aqueous solution preparation：Component by weight, take 18-24 parts 0.5mol/L hydrochloric acid and
195-210 parts of deionized waters are mixed, and 45-57 parts of konjaku glucomannans are added in mixed liquor, and mechanical agitation is put into gelatin
115 DEG C of degraded 50-60min in incubator, take out and add 42-45 parts of 0.5mol/LNaOH solution, and stirring makes it all dissolve, and filters off
Impurity, is made konjaku glucomannan alkaline aqueous solution；
It is prepared by B, konjaku glucomannan emulsion：Component, takes 1000-2000 parts of mixing oil phases, will be mounted in mixer by weight
On perforated pipe insertion mixing oil phase in, step A konjaku glucomannan alkaline aqueous solution is added in perforated pipe, regulation stirring
The rotating speed of machine is 4000r/min, mixes, konjaku glucomannan emulsion is made；The mixing oil phase, it is liquid stone by weight to refer to
Wax:Petroleum ether=5:1, atoleine and petroleum ether are made into mixed liquor, emulsifying agent Span80 is added by weight for 3%-6%, matches somebody with somebody
Into mixing oil phase；The perforated pipe, refers to the general pipe that grade of steel is 10, pipe height × caliber × thickness=20cm × 3cm × 0.2cm, hole
Footpath 5000um, pitch of holes 1cm, parallel cloth hole, perforated pipe is bought by market；
It is prepared by C, konjak portuguese gansu polyose gel microsphere：Into the emulsion of step B konjaku glucomannans, 3-6 parts of crosslinkings are added
Agent epoxychloropropane（ECH）, 100r/min mechanical agitations are uniform, and 4-4.5h is solidified at 60-65 DEG C after sealing；Will be micro- after solidification
Ball is circulated 2-3 times with petroleum ether, absolute ethyl alcohol and deionized water 3000r/min centrifuge washings successively；By the microballoon 50-60 made
DEG C drying, 5%-7% is not higher than to moisture content, takes out, konjak portuguese gansu polyose gel microsphere is made；
（3）The preparation of the konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical：Take nutrient to supplement 20-50 parts of tablet to add water
100-150 parts of dissolvings, konjak portuguese gansu polyose gel microsphere is put into solution, is put into incubator, and 50-60 DEG C of steaming to moisture content is
5%-7%, takes out, and wipes crystallization outside microballoon away with hairbrush, obtains konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical；The nutrition
The composition of element supplement tablet is calcium carbonate, ferrous fumarate, zinc sulfate, sodium selenite, copper sulphate, manganese sulfate, chromium picolinate；
（4）Prepare filter core：
Component, takes 150-300 parts of Rhizoma amorphophalli fiber, 150-300 parts of activated carbon, 100-200 parts of anti-biotic material, acidity by weight
50-200 parts of conditioning agent, 50-200 parts of alkalinity regulator, 150-300 parts of konjak portuguese gansu polyose gel microsphere, containing nutritious supplementary pharmaceutical
150-300 parts of konjak portuguese gansu polyose gel microsphere, is assembled into filter core；The optimal assemble method of filter core：Filter core is divided into 7 layers, the 6th
Layer has middle interlayer, forms two interlayer rooms, acidity regulator and alkalinity regulator are loaded onto respectively；Each material puts in order from entering
The mouth of a river respectively is toward delivery port direction：Rhizoma amorphophalli fiber, activated carbon, anti-biotic material, Rhizoma amorphophalli fiber, konjak portuguese gansu polyose gel
Microballoon, acidity regulator or alkalinity regulator, konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical.
Above each component material can be filled into different size filter model.The all material of the present invention is all purchased by market
.
In use, setting a pH meter at outlet valve, according to the measured value of pH meter at water outlet, the water of filtering is selected
Or enter the interlayer room equipped with acidity regulator, or enter the interlayer room equipped with alkalinity regulator, realize the real-time controllable of pH value.
Advantages of the present invention and beneficial effect：A kind of preparation method of konjaku glucomannan water body filter core of the present invention, with
Konjaku is primary raw material, utilizes the slow release of Rhizoma amorphophalli fiber and the absorption property of konjak portuguese gansu polyose gel microsphere, and microballoon
Can, play a role：First, the chemical adsorption of Rhizoma amorphophalli fiber filters off most granule foreign and individual initial stage in water body filtration
Larger microorganism, purifies water；Second, empty konjak portuguese gansu polyose gel microsphere embodies superior by powerful tension force
Absorption property, can filter off most of microorganism in water body, so as to need not largely use microbicide；The
Three, the konjak portuguese gansu polyose gel microsphere by filling has perfect slow release effect, can make nutriment it is long-term, stably, hold
Discharge continuously, it is ensured that the absorption efficiency of human body；4th, filter fails after long-term use, after replacing, discarded old filter
It is very environmentally friendly because used material is that konjaku is made, easily degraded in atmosphere, nonhazardous effect, therefore ring is not polluted
Border；5th, the konjak portuguese gansu polyose gel microsphere in filter is filled with nutritious supplementary pharmaceutical, and composition is that calcium carbonate, fumaric acid are sub-
Iron, zinc sulfate, sodium selenite, copper sulphate, manganese sulfate, chromium picolinate, can supplement the calcium of needed by human body, iron, zinc, selenium, copper,
It is micro- necessary to manganese, chromium etc..
The reliability and security of a kind of konjaku glucomannan water body filter core of the present invention comply fully with relative national standards
It is required that, it the results are shown in Table 1 compared with water body filter core prepared by prior art：
The comparative result of table 1, the konjaku glucomannan water body filter core of the present invention and other filter cores
Embodiment
Konjaku glucomannan water body filter core for the fully open present invention and preparation method thereof, with reference to embodiment plus
With explanation.
A kind of preparation method of konjaku glucomannan water body filter core of embodiment 1
A kind of preparation method of konjaku glucomannan water body filter core, comprises the following steps：
（1）The preparation of Rhizoma amorphophalli fiber：Component, takes 30 parts of konjaku glucomannan by weight, adds the purifying of 30 times of its weight
Water, stirring and dissolving, gelatinization stands 1h, obtains No. 1 standby sample；100 parts of starch for taking purity to be 75%, is mixed with No. 1 standby sample
It is even, obtain No. 2 standby samples；90 parts of the dietary alkali that purity is 80% is taken, 300 parts of edible alkali solution is prepared, by edible alkali solution and 2
Number standby sample is well mixed, and obtains No. 3 standby samples；No. 3 standby samples are poured into filter core mould, 50min is steamed at 110 DEG C, are taken out
Afterwards, 20h is freezed in the refrigerator for placing into -40 DEG C, takes out and thaws, it is 5% to be dried at 50 DEG C to moisture content, obtains Rhizoma amorphophalli fiber；
（2）It is prepared by konjak portuguese gansu polyose gel microsphere：
A, konjaku glucomannan alkaline aqueous solution preparation：Component by weight, take 18 parts 0.5mol/L hydrochloric acid and 195 parts
Deionized water is mixed, and 45 parts of konjaku glucomannans are added in mixed liquor, and mechanical agitation is put into incubator into gelatin, 115 DEG C
Degrade 50min, takes out and adds 42 parts of 0.5mol/LNaOH solution, and stirring makes it all dissolve, and filters off impurity, Amorphophallus rivieri glucomannan is made
Glycan alkaline aqueous solution；
It is prepared by B, konjaku glucomannan emulsion：Component, takes 1000 parts of mixing oil phases, by beating on mixer by weight
In the pipe insertion mixing oil phase of hole, step A konjaku glucomannan alkaline aqueous solution is added in perforated pipe, turn of regulation mixer
Speed is 4000r/min, mixes, konjaku glucomannan emulsion is made；The mixing oil phase, it is atoleine by weight to refer to:Stone
Oily ether=5:1, atoleine and petroleum ether are made into mixed liquor, emulsifying agent Span80 is added by weight for 3%, is made into miscella
Phase；
It is prepared by C, konjak portuguese gansu polyose gel microsphere：Into the emulsion of step B konjaku glucomannans, 3 parts of crosslinking agents are added
Epoxychloropropane（ECH）, 100r/min mechanical agitations are uniform, and 4h is solidified at 60 DEG C after sealing；Microballoon after solidification is used successively
Petroleum ether, absolute ethyl alcohol and deionized water 3000r/min centrifuge washings are circulated 3 times；It is extremely aqueous by the 50 DEG C of dryings of microballoon made
Rate is not higher than 5%, and konjak portuguese gansu polyose gel microsphere is made in taking-up；
（3）The preparation of the konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical：Take nutrient to supplement 20 parts of tablet and add water 100
Part dissolving, konjak portuguese gansu polyose gel microsphere is put into solution, incubator is put into, and 50 DEG C are evaporated to moisture content and are not higher than 5%,
Take out, wipe crystallization outside microballoon away with hairbrush, obtain konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical；
（4）Prepare filter core：
Component by weight, take 150 parts of Rhizoma amorphophalli fiber, 150 parts of activated carbon, 100 parts of anti-biotic material, 50 parts of acidity regulator,
50 parts of alkalinity regulator, 150 parts of konjak portuguese gansu polyose gel microsphere, konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical 150
Part；The optimal assemble method of filter core：Filter core is divided into 7 layers, and layer 6 has middle interlayer, forms two interlayer rooms, acidity is loaded onto respectively
Conditioning agent and alkalinity regulator；Putting in order for each material respectively is from water inlet toward delivery port direction：Rhizoma amorphophalli fiber, work
Property carbon, anti-biotic material, Rhizoma amorphophalli fiber, konjak portuguese gansu polyose gel microsphere, acidity regulator or alkalinity regulator, containing nutritional supplementation
Agent konjak portuguese gansu polyose gel microsphere.
A kind of preparation method of konjaku glucomannan water body filter core of embodiment 2
A kind of preparation method of konjaku glucomannan water body filter core, including 4 steps, step（1）-（3）With embodiment 1
Step（1）-（3）It is identical；Step（4）Prepare filter core：Component, takes 200 parts of Rhizoma amorphophalli fiber, 200 parts of activated carbon, antibacterial material by weight
Material 150 parts, 100 parts of acidity regulator, 100 parts of alkalinity regulator, 200 parts of konjak portuguese gansu polyose gel microsphere, containing nutritional supplementation
200 parts of agent konjak portuguese gansu polyose gel microsphere, is assembled into filter core.
A kind of preparation method of konjaku glucomannan water body filter core of embodiment 3
A kind of preparation method of konjaku glucomannan water body filter core, including 4 steps, step（1）-（3）With embodiment 1
Step（1）-（3）It is identical；Step（4）Prepare filter core：Component, takes 250 parts of Rhizoma amorphophalli fiber, 250 parts of activated carbon, antibacterial material by weight
Material 200 parts, 150 parts of acidity regulator, 150 parts of alkalinity regulator, 250 parts of konjak portuguese gansu polyose gel microsphere, containing nutritional supplementation
250 parts of agent konjak portuguese gansu polyose gel microsphere, is assembled into filter core.
The foregoing is only presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with
Modification, should all belong to the covering scope of the present invention.
Claims (7)
1. a kind of preparation method of konjaku glucomannan water body filter core, it is characterised in that preparation process is as follows：
（1）The preparation of Rhizoma amorphophalli fiber：Component, takes 15-150 parts of konjaku glucomannan, adds the pure of 30-40 times of its weight by weight
Change water, stirring and dissolving, gelatinization stands 1-2h and obtains No. 1 standby sample；75-500 parts of the starch that purity is 75%-90% is taken, it is standby with No. 1
Sample is well mixed, and obtains No. 2 standby samples；90-300 parts of the dietary alkali that purity is 80%-90% is taken, 300-600 parts of dietary alkali is prepared
Solution, edible alkali solution is well mixed with No. 2 standby samples, obtains No. 3 standby samples；No. 3 standby samples are poured into filter core mould,
50-70min is steamed at 80-110 DEG C, after taking-up, 20-24h is freezed in the refrigerator for placing into -40--50 DEG C, takes out and thaws, 50-60
It is 5%-20% to be dried at DEG C to moisture content, obtains Rhizoma amorphophalli fiber；
（2）It is prepared by konjak portuguese gansu polyose gel microsphere：
A, konjaku glucomannan alkaline aqueous solution preparation：Component by weight, takes 18-24 parts of 0.5mol/L hydrochloric acid and 195-
210 parts of deionized waters are mixed, and 45-57 parts of konjaku glucomannans are added in mixed liquor, and mechanical agitation is put into incubator into gelatin
Interior 115 DEG C of degradeds 50-60min, takes out and adds 42-45 parts of 0.5mol/LNaOH solution, and stirring makes it all dissolve, and filters off miscellaneous
Matter, is made konjaku glucomannan alkaline aqueous solution；
It is prepared by B, konjaku glucomannan emulsion：Component, takes 1000-2000 parts of mixing oil phases, by mixer by weight
In perforated pipe insertion mixing oil phase, step A konjaku glucomannan alkaline aqueous solution is added in perforated pipe, regulation mixer
Rotating speed is 4000r/min, mixes, konjaku glucomannan emulsion is made；The mixing oil phase, it is atoleine by weight to refer to:
Petroleum ether=5:1, atoleine and petroleum ether are made into mixed liquor, emulsifying agent Span80 is added by weight for 3%-6%, is made into
Mix oil phase；The perforated pipe, refers to the general pipe that grade of steel is 10, pipe height × caliber × thickness=20cm × 3cm × 0.2cm, aperture
5000um, pitch of holes 1cm, parallel cloth hole；
It is prepared by C, konjak portuguese gansu polyose gel microsphere：Into the emulsion of step B konjaku glucomannans, 3-6 parts of crosslinking agent rings are added
Oxygen chloropropane（ECH）, 100r/min mechanical agitations are uniform, and 4-4.5h is solidified at 60-65 DEG C after sealing；By the microballoon after solidification according to
Secondary use petroleum ether, absolute ethyl alcohol and deionized water 3000r/min centrifuge washings are circulated 2-3 times；50-60 DEG C of the microballoon made is done
It is dry, 5%-7% is not higher than to moisture content, takes out, konjak portuguese gansu polyose gel microsphere is made；
（3）The preparation of the konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical：Component, takes nutrient to supplement tablet 20- by weight
50 parts of 100-150 parts of dissolvings that add water, konjak portuguese gansu polyose gel microsphere is put into solution, is put into incubator, and 50-60 DEG C is steamed extremely
Moisture content is 5%-7%, is taken out, and wipes crystallization outside microballoon away with hairbrush, obtains konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical；
The composition of the nutrient supplement tablet is calcium carbonate, ferrous fumarate, zinc sulfate, sodium selenite, copper sulphate, manganese sulfate, pyrrole
Pyridine chromic formate；
（4）Prepare filter core：
Component, takes 150-300 parts of Rhizoma amorphophalli fiber, 150-300 parts of activated carbon, 100-200 parts of anti-biotic material, acidity adjustment by weight
50-200 parts of agent, 50-200 parts of alkalinity regulator, 150-300 parts of konjak portuguese gansu polyose gel microsphere, konjaku containing nutritious supplementary pharmaceutical
150-300 parts of portuguese gansu polyose gel microsphere, is assembled into filter core.
2. a kind of preparation method of konjaku glucomannan water body filter core according to claim 1, it is characterised in that the evil spirit
The preparation of taro fiber：Component, takes 30 parts of konjaku glucomannan by weight, adds the purified water of 30 times of its weight, stirring and dissolving, paste
Change and stand 1h, obtain No. 1 standby sample；100 parts of starch for taking purity to be 75%, is well mixed with No. 1 standby sample, obtains No. 2 standby samples；
90 parts of the dietary alkali that purity is 80% is taken, 300 parts of edible alkali solution is prepared, edible alkali solution is mixed with No. 2 standby samples
It is even, obtain No. 3 standby samples；No. 3 standby samples are poured into filter core mould, 50min is steamed at 110 DEG C, after taking-up, -40 DEG C are placed into
Refrigerator in freeze 20h, take out and thaw, it is 5% to be dried at 50 DEG C to moisture content, obtains Rhizoma amorphophalli fiber.
3. a kind of preparation method of konjaku glucomannan water body filter core according to claim 1, it is characterised in that the system
Standby filter core：Component, takes 150 parts of Rhizoma amorphophalli fiber, 150 parts of activated carbon, 100 parts of anti-biotic material, 50 parts of acidity regulator, alkali by weight
50 parts of conditioning agent, 150 parts of konjak portuguese gansu polyose gel microsphere, 150 parts of konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical are spent,
It is assembled into filter core.
4. a kind of preparation method of konjaku glucomannan water body filter core according to claim 1, it is characterised in that the system
Standby filter core：Component by weight, take 200 parts of Rhizoma amorphophalli fiber, 200 parts of activated carbon, 150 parts of anti-biotic material, 100 parts of acidity regulator,
100 parts of alkalinity regulator, 200 parts of konjak portuguese gansu polyose gel microsphere, konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical 200
Part, it is assembled into filter core.
5. a kind of preparation method of konjaku glucomannan water body filter core according to claim 1, it is characterised in that the system
Standby filter core：Component by weight, take 250 parts of Rhizoma amorphophalli fiber, 250 parts of activated carbon, 200 parts of anti-biotic material, 150 parts of acidity regulator,
150 parts of alkalinity regulator, 250 parts of konjak portuguese gansu polyose gel microsphere, konjak portuguese gansu polyose gel microsphere containing nutritious supplementary pharmaceutical 250
Part, it is assembled into filter core.
6. a kind of preparation method of konjaku glucomannan water body filter core according to claim 1, it is characterised in that the filter
The assemble method of core：Filter core is divided into 7 layers, and layer 6 has middle interlayer, forms two interlayer rooms, acidity regulator and alkali are loaded onto respectively
Spend conditioning agent；Putting in order for each material respectively is from water inlet toward delivery port direction：Rhizoma amorphophalli fiber, activated carbon, antibacterial
Material, Rhizoma amorphophalli fiber, konjak portuguese gansu polyose gel microsphere, acidity regulator or alkalinity regulator, the Portugal of konjaku containing nutritious supplementary pharmaceutical
Sweet polysaccharide gel microballoon.
7. the konjaku glucomannan water body filter core prepared as the either method described in claim 1-6.