CN105017882B - 一种净化涂料及其制备方法 - Google Patents
一种净化涂料及其制备方法 Download PDFInfo
- Publication number
- CN105017882B CN105017882B CN201510492012.5A CN201510492012A CN105017882B CN 105017882 B CN105017882 B CN 105017882B CN 201510492012 A CN201510492012 A CN 201510492012A CN 105017882 B CN105017882 B CN 105017882B
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- minutes
- add
- follows
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种净化涂料及其制备方法,由45‑50份基料、10‑15份填料、20‑25份香料、10‑12份胶料、0.3‑0.5份荧光粉、0.02‑0.03份磷酸三丁酯组成。其加工方法包括基料的制备、填料的制备、香料制备、胶料制备,调配等过程。本发明的净化涂料,色彩可以任意调整、涂膜微簿、用量少,具有增香、耐水性强,耐洗刷,持久性好,无毒,不燃,香气自然怡人,有效去除装饰、家具的有毒异味气体,使室内优雅舒适,给人一种美的享受。
Description
技术领域
本发明涉及内墙净化涂料及其制备方法,尤其涉及一种净化涂料及其制备方法。
背景技术
家庭装修施工中,存在大量有机有害物,如甲醛、苯等致癌物,污染室内空气,使人居身体健康受损。在墙体饰面中,采用胶水石粉混合物、胶水等污染。除墙壁饰面污染外,家具、地板等也存在大量的污染。本发明一种净化增香涂料,色彩可以任意调整、涂膜微簿、用量少,具有增香、耐水性强,耐洗刷,持久性好,无毒,不燃,香气自然怡人,能效去除装饰、家具的有毒异味气体,使室内优雅舒适,给人一种美的享受。
发明内容
本发明所要解决的技术问题是提供一种具有增香、耐水性强,耐洗刷,持久性好,无毒,不燃,可有效去除装饰、家具的有毒异味气体的涂料及其制备方法。
本发明所要解决的技术问题采用以下技术方案来实现:
一种净化涂料,其特征在于,由下述的重量配比的原料制成:
包括以下步骤:
1)基料的制备:将聚乙烯醇50-60份加入加热搅拌反应釜,再加入水700-800份,开机搅拌并加热,至80℃后搅拌15分钟。然后加入30%的氢氧化钠10-15份,调节pH为7-8。自然降温至40-45℃时加入水玻璃60-65份,搅拌10分钟,再加入磷酸三丁酯适量至泡沫消失为止。最后加入盐酸适量,调节PH8.4-8.7,即为基料。
2)填料的制备:将碳酸钙600-650份、PC粉130-150份、滑石粉180-200份加入搅拌机,搅拌均匀即可。
3)香料的制备:将聚乙烯醇25-30份,溶入450-500份100℃开水中;将该溶液注入搅拌机,加入18-20份β—环状糊精,高速搅拌一小时;再加入450-500份香精,搅拌10分钟,过滤即可。
4)胶料的制备:聚乙烯100份,溶入150份80℃水中,搅拌10分钟即可。
一种天然净化内墙涂料,由下述的重量配比的原料制成:
制备一种净化涂料的方法,其制备步骤如下:按重量配比称取各个原料,将各个原料一次性投入到搅拌机中,高速搅拌30分钟,进行充分搅拌后将搅拌料用球磨机磨制一遍,再用过滤机过滤,即为成品包装入库。
具体实施方式
实施例
基料的制备,将聚乙烯醇6kg加入加热搅拌反应釜,再加入水80kg,开机搅拌并加热,至80℃后搅拌15分钟。然后加入30%的氢氧化钠1kg,调节PH为7-8。自然降温至40-45℃时加入水玻璃6kg,搅拌10分钟,再加入磷酸三丁酯适量至泡沫消失为止。最后加入盐酸适量,调节PH8.4-8.7,即为基料。填料的制备,将碳酸钙65kg、PC粉15kg、滑石粉20kg加入搅拌机,搅拌均匀即可。香料制备,将聚乙烯醇3kg,溶入50kg100℃开水中;将该溶液注入搅拌机,加入2kgβ—环状糊精,高速搅拌一小时;再加入50kgCC香精,搅拌10分钟,过滤即可。胶料制备,聚乙烯10kg,溶入15kg80℃水中,搅拌10分钟即可。一种净化涂料,由下述的重量配比的原料制成:
制备一种净化涂料的方法,其制备步骤如下:按重量配比称取各个原料,将各个原料一次性投入到搅拌机中,高速搅拌30分钟,进行充分搅拌后将搅拌料用球磨机磨制一遍,再用过滤机过滤,即为成品包装入库。
Claims (4)
1.一种天然净化涂料,其特征在于,由下述的重量配比的原料制成:
所述的基料的制备方法如下:将聚乙烯醇50-60份加入加热搅拌反应釜,再加入水700-800份,开机搅拌并加热,至80℃后搅拌15分钟;然后加入30%的氢氧化钠10-15份,调节pH为7-8;自然降温至40-45℃时加入水玻璃60-65份,搅拌10分钟,再加入磷酸三丁酯适量至泡沫消失为止,最后加入盐酸适量,调节pH8.4-8.7,即为基料。
2.根据权利要求1所述的一种净化涂料,其特征在于,所述的填料的制备方法如下:将碳酸钙600-650份、PC粉130-150份、滑石粉180-200份加入搅拌机,搅拌均匀即可;
所述的香料制备方法如下:将聚乙烯醇25-30份,溶入450-500份100℃开水中;将该溶液注入搅拌机,加入18-20份β—环状糊精,高速搅拌一小时;再加入450-500份香精,搅拌10分钟,过滤即可;
所述的胶料制备方法如下:聚乙烯100份,溶入150份80℃水中,搅拌10分钟即可。
3.根据权利要求1所述的一种净化涂料,其特征在于,由下述的重量配比的原料制成:
4.如权利要求1所述的一种净化涂料的加工方法,其特征在于,制备步骤如下:按重量配比称取各个原料,将各个原料一次性投入到搅拌机中,高速搅拌30分钟,进行充分搅拌后将搅拌料用球磨机磨制一遍,再用过滤机过滤,即为成品包装入库。