CN105015076B - A kind of wet manufacturing process of water proof nonwoven cloth roof liner - Google Patents
A kind of wet manufacturing process of water proof nonwoven cloth roof liner Download PDFInfo
- Publication number
- CN105015076B CN105015076B CN201510444991.7A CN201510444991A CN105015076B CN 105015076 B CN105015076 B CN 105015076B CN 201510444991 A CN201510444991 A CN 201510444991A CN 105015076 B CN105015076 B CN 105015076B
- Authority
- CN
- China
- Prior art keywords
- glue
- semi
- water
- finished product
- roof liner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The wet manufacturing process of the present invention a kind of water proof nonwoven cloth roof liner, belongs to technical field of automotive upholstery.It comprises the steps: PU plastic roll, spray soften water, combination of materials, base material is hot-forming, base material semi-finished product cooling and shaping, base material glue spraying are dried, fabric laminating, cooling and shaping, high pressure waterjet and adnexa group are vertical.The automobile roof liner that the present invention produces greatly reduces roof liner weight; meet the requirement of automotive light weight technology design; product rigidity is good; the product of nearly 3 meters will not fracture, sagging; whole production process does not has harmful substance to produce; client can be met well and use requirement, meet the requirement of Hyundai Motor lightweight, environmental protection.
Description
Technical field
The wet manufacturing process of the present invention a kind of water proof nonwoven cloth roof liner, specifically one is for automobile top, plays the production technology of the low VOC wet method automobile roof liner of heat insulation, sound insulation and beautification function, belongs to technical field of automotive upholstery.
Background technology
Automobile roof liner is installed on automobile top, has decoration, sound insulation, the feature such as heat insulation, is increasingly pursuing high-performance, environment-friendly type, lightweight, the energy-saving epoch, automotive trim becomes people as car conour and selects a key factor of car, and therefore the requirement to automotive upholstery is more and more higher.In the prior art, the performance indications such as the high sound-absorbing of roof liner, low grammes per square metre, high intensity, low VOC become bottleneck, govern development originally.Existing roof liner generally uses compound PU sheet material straight forming.This kind of moulding process is primarily present problems with: 1, sound-absorbing index does not reaches requirement；2, product rigidity is poor, the most sagging, easy to break；3, product weight is big, is unfavorable for car load lightweight, energy-conservation；4, VOC (VOC) is defective cannot meet main engine plants' technology requirement.The present invention utilizes new wet processing to produce automobile roof liner, preferably resolves the problems referred to above.
Summary of the invention
It is an object of the invention to overcome above-mentioned weak point, it is provided that a kind of sound absorption qualities is good, rigidity is big, be difficult to sagging jackknifing; light weight, the manufacturing process of automobile roof liner of low VOC; this process non-volatility organic compound produces, recyclable, meets the requirement of Hyundai Motor environmental protection.
The technical scheme provided according to the present invention, the wet manufacturing process of a kind of water proof nonwoven cloth roof liner, step is as follows:
(1) plastic roll: take PU sheet material feeding glue spreader and carry out plastic roll, heating, obtain PU sheet material；Rolling motor frequency is 20-40Hz, glue spreader up-down roller gap 5.0-5.5mm, glue spreader bowl temperature 40-50 DEG C, and PU base material upper and lower surface each one side plastic roll amount is at 35-45 g/m2；
(2) softening water is sprayed: the PU sheet material spray purified water machine that step (1) has been rolled glue uniformly sprays pure water；Electric machine frequency: 40-60Hz, the amount of purified water of sprinkling is 25-35g/m2；
(3) material-paving: by transfer matic lay material, the superiors' table cloth is water proof nonwoven cloth, and the second layer is Chopped Strand Mat, and third layer is that step (2) is sprayed and softened the PU sheet material of gained after water, and the 4th layer is Chopped Strand Mat, bottom lay non-woven fabrics；
(4) hot-forming: it is compressing that mould sent into by material step (3) completed, press-moulding die temperature: 120-130 DEG C, briquetting pressure 8-10MPa, molding time: 40-50s obtains molding semi product；
(5) cooling and shaping: step (4) gained molding semi product is carried out vac sorb cooling and shaping, cool time is 40-50s, and vacuum is 0.5-0.8MPa；
(6) base material glue spraying is dried: being placed by step (5) gained base material on glue spraying tool and position, pallet carries out glue spraying operation in being sent to glue spraying room, obtains spraying semi-finished product, glue spraying air pressure 0.2-0.4MPa；Spraying semi-finished product are hung to drying shed hook, carries out dried, obtain glue spraying and be dried semi-finished product；Baking temperature is 70-80 DEG C, and transmission frequency is F1.90-F2.0；
(7) fabric laminating: step (6) gained glue spraying is dried semi-finished product and is placed in mould well with fabric lay and fits, mold temperature 65-75 DEG C during laminating, laminate pressure 8-10MPa, laminating time 45-55s；
(8) cooling and shaping: the semi-finished product that step (7) posts fabric are cooled to room temperature sizing；
(9) high pressure waterjet: the semi-finished product after step (8) cooling and shaping are carried out high pressure waterjet, cutting hydraulic pressure is 40000-50000psi, and cutting air pressure is 0.6-0.8MPa；
(10) adnexa group is stood: semi-finished product good for step (9) gained Water Cutting are installed adnexa, and get product water proof nonwoven cloth roof liner, vanning warehouse-in after inspection.
Described in step (3), water proof nonwoven cloth density is 50-80g/m2；Chopped Strand Mat density is 120-150g/m2。
Step (1) described plastic roll glue is polyurethane glue.
The glue that step (6) described glue spraying uses is environment-friendly water-based glue.
The fabric that step (7) is fitted is that two layers of warp knit composite material, i.e. warp knit monomer fabric are combined one layer of soft bubble of PU.
Beneficial effects of the present invention: compared with the prior art the present invention has the advantage that the automobile roof liner that the present invention produces greatly reduces roof liner weight; meet the requirement of automotive light weight technology design; product rigidity is good; the product of nearly 3 meters will not fracture, sagging; whole production process does not has harmful substance to produce; client can be met well and use requirement, meet the requirement of Hyundai Motor lightweight, environmental protection.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further detailed.
In following example, PU sheet material is purchased from lucky emerging wooden bridge, and plastic roll is with glue purchased from BASF, and glue spraying is with glue purchased from Fuller, and two layers of warp knit composite material are purchased from Wal, Ruian.
Embodiment 1
(1) plastic roll: take PU sheet material feeding glue spreader and carry out plastic roll, heating；Rolling motor frequency 20Hz, glue spreader up-down roller gap 5.0mm, glue spreader bowl temperature 40 DEG C, PU sheet material upper and lower surface each one side plastic roll amount is at 35 g/m2, the rigidity effect of roof liner is played by PU gluing；
(2) spray softening water: the PU sheet material of glue will have been rolled, uniformly spray pure water with spray purified water machine；Electric machine frequency: 40Hz, the amount of purified water of sprinkling is 25g/m2；
(3) material-paving: by transfer matic lay material, the superiors' table cloth is water proof nonwoven cloth, and the second layer is Chopped Strand Mat, and third layer is PU sheet material, and the 4th layer is Chopped Strand Mat, bottom lay common non-woven fabric；
(4) hot-forming: material good for above-mentioned lay to be sent into mould compressing, press-moulding die temperature: 120 DEG C, briquetting pressure 8MPa, molding time: 40s, the compressing semi-finished product of system；Make the substrate forming of roof liner after compacting by heating mould, after fully being reacted by glue, meet the requirement of automotive trim abnormal smells from the patient simultaneously；
(5) cooling and shaping: the semi-finished product after compressing for step (4) are carried out vac sorb cooling and shaping, cool time 40s, vacuum: 0.5MPa；
(6) base material glue spraying is dried: being placed by base material and position on glue spraying tool, pallet carries out glue spraying operation, glue spraying air pressure 0.2MPa in being sent to glue spraying room；Spraying semi-finished product are hung to drying shed hook, carries out dried, baking temperature: 70 DEG C, transmission frequency: F1.90；
(7) fabric laminating: glue spraying is dried the combination of semi-finished product and fabric and is placed in mould and fits, mold temperature 65 DEG C during laminating, laminate pressure 8MPa, laminating time 45s；
(8) cooling and shaping: the semi-finished product posting fabric are cooled to room temperature so that it is sizing, sizing is considered the assembling of car load, is met the matching requirements of roof liner size by cooling and shaping, and part is unlikely to deform.
(9) high pressure waterjet: will carry out high pressure waterjet through step semi-finished product (8), cutting hydraulic pressure control controls at 0.6MPa at 40000psi, cutting air pressure；
(10) adnexa group is stood: the semi-finished product that Water Cutting is good are installed adnexa and is finished product, vanning warehouse-in after inspection.
In described step (6) glue spraying glue be water-base cement, i.e. solvent be water, by with air reaction evaporation of solvent water, fully meet abnormal smells from the patient and VOC requirement, unharmful substance.
In described step (6), the readily permeable common non-woven fabric of water-base cement characteristic, is sprayed on water proof nonwoven cloth and will not form suction glue, with fabric firm pasting.
Embodiment 2
(1) plastic roll: take PU feeding glue spreader and carry out plastic roll, heating；Rolling motor frequency 30Hz, glue spreader up-down roller gap 5.25mm, glue spreader bowl temperature 45 DEG C, PU base material upper and lower surface each one side plastic roll amount is at 40 g/m2, the rigidity effect of roof liner is played by PU gluing；
(2) spray softening water: the PU foam of glue will have been rolled, uniformly spray pure water with spray purified water machine；Electric machine frequency: 50Hz, the amount of purified water of sprinkling is 30g/m2；
(3) material-paving: by transfer matic lay material, the superiors' table cloth is water proof nonwoven cloth, and the second layer is Chopped Strand Mat, and third layer is PU base material, and the 4th layer is Chopped Strand Mat, bottom lay common non-woven fabric；
(4) hot-forming: material good for above-mentioned lay to be sent into mould compressing, press-moulding die temperature: 125 DEG C, briquetting pressure 9MPa, molding time: 45s, the compressing semi-finished product of system；Make the substrate forming of roof liner after compacting by heating mould, after fully being reacted by glue, meet the requirement of automotive trim abnormal smells from the patient simultaneously；
(5) cooling and shaping: the semi-finished product after compressing are carried out vac sorb cooling and shaping, cool time 45s, vacuum: 0.5MPa；
(6) base material glue spraying is dried: being placed by base material and position on glue spraying tool, pallet carries out glue spraying operation, glue spraying air pressure 0.3MPa in being sent to glue spraying room；Spraying semi-finished product are hung to drying shed hook, carries out dried, baking temperature: 75 DEG C, transmission frequency: F1.95；
(7) fabric laminating: glue spraying is dried the combination of semi-finished product and fabric and is placed in mould and fits, mold temperature 70 DEG C during laminating, laminate pressure 9MPa, laminating time 50s；
(8) cooling and shaping: the semi-finished product posting fabric are cooled to room temperature so that it is sizing, sizing is considered the assembling of car load, is met the matching requirements of roof liner size by cooling and shaping, and part is unlikely to deform.
(9) high pressure waterjet: will carry out high pressure waterjet through step semi-finished product (8), cutting hydraulic pressure control controls at 0.7MPa at 45000psi, cutting air pressure；
(10) adnexa group is stood: the semi-finished product that Water Cutting is good are installed adnexa and is finished product, vanning warehouse-in after inspection.
In described step (6) glue spraying glue be water-base cement, i.e. solvent be water, by with air reaction evaporation of solvent water, fully meet abnormal smells from the patient and VOC requirement, unharmful substance.In described step (6), the readily permeable common non-woven fabric of water-base cement characteristic, is sprayed on water proof nonwoven cloth and will not form suction glue, with fabric firm pasting.
Embodiment 3
(1) plastic roll: take PU feeding glue spreader and carry out plastic roll, heating；Rolling motor frequency 40Hz, glue spreader up-down roller gap 5.5mm, glue spreader bowl temperature 50 DEG C, PU base material upper and lower surface each one side plastic roll amount is at 45g/m2, the rigidity effect of roof liner is played by PU gluing；
(2) spray softening water: the PU foam of glue will have been rolled, uniformly spray pure water with spray purified water machine；Electric machine frequency: 60Hz, the amount of purified water of sprinkling is 35g/m2；
(3) material-paving: by transfer matic lay material, the superiors' table cloth is water proof nonwoven cloth, and the second layer is Chopped Strand Mat, and third layer is PU base material, and the 4th layer is Chopped Strand Mat, bottom lay common non-woven fabric；
(4) hot-forming: material good for above-mentioned lay to be sent into mould compressing, press-moulding die temperature: 130 DEG C, briquetting pressure: 10MPa, molding time: 50s, the compressing semi-finished product of system；Make the substrate forming of roof liner after compacting by heating mould, after fully being reacted by glue, meet the requirement of automotive trim abnormal smells from the patient simultaneously；
(5) cooling and shaping: the semi-finished product after compressing are carried out vac sorb cooling and shaping, cool time 50s, vacuum: 0.5MPa；
(6) base material glue spraying is dried: being placed by step (5) gained base material on glue spraying tool and position, pallet carries out glue spraying operation, glue spraying air pressure 0.4MPa in being sent to glue spraying room；Spraying semi-finished product are hung to drying shed hook, carries out dried, baking temperature: 80 DEG C, transmission frequency: F2.0；
(7) fabric laminating: glue spraying is dried the combination of semi-finished product and fabric and is placed in mould and fits, mold temperature 75 DEG C during laminating, laminate pressure 10MPa, laminating time 55s；
(8) cooling and shaping: the semi-finished product posting fabric are cooled to room temperature so that it is sizing, sizing is considered the assembling of car load, is met the matching requirements of roof liner size by cooling and shaping, and part is unlikely to deform.
(9) high pressure waterjet: will carry out high pressure waterjet through step semi-finished product (8), cutting hydraulic pressure control controls at 0.8MPa at 50000psi, cutting air pressure；
(10) adnexa group is stood: the semi-finished product that Water Cutting is good are installed adnexa and is finished product, vanning warehouse-in after inspection.
In described step (6) glue spraying glue be water-base cement, i.e. solvent be water, by with air reaction evaporation of solvent water, fully meet abnormal smells from the patient and VOC requirement, unharmful substance.In described step (6), the readily permeable common non-woven fabric of water-base cement characteristic, is sprayed on water proof nonwoven cloth and will not form suction glue, with fabric firm pasting.
Claims (2)
1. a wet manufacturing process for water proof nonwoven cloth roof liner, is characterized in that step is as follows:
(1) plastic roll: take PU sheet material feeding glue spreader and carry out plastic roll, heating, obtain PU sheet material；Rolling motor frequency is 20-40Hz, glue spreader up-down roller gap 5.0-5.5mm, glue spreader bowl temperature 40-50 DEG C, and PU base material upper and lower surface each one side plastic roll amount is at 35-45 g/m2；
(2) softening water is sprayed: the PU sheet material spray purified water machine that step (1) has been rolled glue uniformly sprays pure water；Electric machine frequency: 40-60Hz, the amount of purified water of sprinkling is 25-35g/m2；
(3) material-paving: by transfer matic lay material, the superiors' table cloth is water proof nonwoven cloth, and the second layer is Chopped Strand Mat, and third layer is that step (2) is sprayed and softened the PU sheet material of gained after water, and the 4th layer is Chopped Strand Mat, bottom lay non-woven fabrics；
(4) hot-forming: it is compressing that mould sent into by material step (3) completed, press-moulding die temperature: 120-130 DEG C, briquetting pressure 8-10MPa, molding time: 40-50s obtains molding semi product；
(5) cooling and shaping: step (4) gained molding semi product is carried out vac sorb cooling and shaping, cool time is 40-50s, and vacuum is 0.5-0.8MPa；
(6) base material glue spraying is dried: being placed by step (5) gained base material on glue spraying tool and position, pallet carries out glue spraying operation in being sent to glue spraying room, obtains spraying semi-finished product, glue spraying air pressure 0.2-0.4MPa；Spraying semi-finished product are hung to drying shed hook, carries out dried, obtain glue spraying and be dried semi-finished product；Baking temperature is 70-80 DEG C, and transmission frequency is F1.90-F2.0；
(7) fabric laminating: step (6) gained glue spraying is dried semi-finished product and is placed in mould well with fabric lay and fits, mold temperature 65-75 DEG C during laminating, laminate pressure 8-10MPa, laminating time 45-55s；
(8) cooling and shaping: the semi-finished product that step (7) posts fabric are cooled to room temperature sizing；
(9) high pressure waterjet: the semi-finished product after step (8) cooling and shaping are carried out high pressure waterjet, cutting hydraulic pressure is 40000-50000psi, and cutting air pressure is 0.6-0.8MPa；
(10) adnexa group is stood: semi-finished product good for step (9) gained Water Cutting are installed adnexa, and get product water proof nonwoven cloth roof liner, vanning warehouse-in after inspection；
Step (1) described plastic roll glue is polyurethane glue；
The glue that step (6) described glue spraying uses is environment-friendly water-based glue；
The fabric that step (7) is fitted is that two layers of warp knit composite material, i.e. warp knit monomer fabric are combined one layer of soft bubble of PU.
2. the wet manufacturing process of water proof nonwoven cloth roof liner as claimed in claim 1, is characterized in that: described in step (3), water proof nonwoven cloth density is 50-80g/m2；Chopped Strand Mat density is 120-150g/m2。