CN105002506A - Rust-proof corrosion inhibitor and preparing method thereof - Google Patents
Rust-proof corrosion inhibitor and preparing method thereof Download PDFInfo
- Publication number
- CN105002506A CN105002506A CN201510478647.XA CN201510478647A CN105002506A CN 105002506 A CN105002506 A CN 105002506A CN 201510478647 A CN201510478647 A CN 201510478647A CN 105002506 A CN105002506 A CN 105002506A
- Authority
- CN
- China
- Prior art keywords
- parts
- mercaptobenzothiazole
- rust
- sodium
- hexamethylenetetramine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a rust-proof corrosion inhibitor and the preparing method thereof. The rust-proof corrosion inhibitor comprises sodium silicate, sodium polyacrylate, mercaptobenzothiazole, benzotriazole, sodium tripolyphosphate, hexamethylenetetramine, imidazoline, mercaptobenzothiazole, alkane amido alcohol, furfural, polyphosphates, ethanol amine, sodium borate and ethyl alcohol. The preparing method comprises the steps of heating sodium silicate, sodium polyacrylate, mercaptobenzothiazole, benzotriazole, sodium tripolyphosphate, hexamethylenetetramine, imidazoline, mercaptobenzothiazole, alkane amido alcohol, furfural, ethanol amine and ethyl alcohol mixed liquor to 50-60 DEG C firstly, then adding polyphosphates and sodium borate, continuing to heating to 85-90 DEG C, conducting heat preservation for 2-3 h, and then obtaining the rust-proof corrosion inhibitor after cooling. The rust-proof corrosion inhibitor can be well compatible with variable materials, rust-proof time is long and can be as long as 4-6 months, adaptability to the copper material and the aluminum material is high, and rust-proof time is prolonged due to the fact that a film can be formed on the surface of metal while corrosion inhibition and rust resistance are realized.
Description
Technical field
The invention belongs to technical field of metal anti-corrosion, be specifically related to a kind of rust inhibitor and preparation method thereof.
Background technology
Inhibiter is a kind of when being present in environment with suitable concentration and form, can prevent or slow down the chemical substance of corrosion or the mixture of several chemical substance.At present, the inhibiter used has mineral compound inhibiter and organic compound inhibiter.The most function singleness of known inhibiter, is merely able to the corrosion for preventing or slow down single metal, namely only for iron, steel, copper etc. wherein a kind of metal play a major role, purposes is single, is only applicable to a kind of medium; In addition, except delaying corrosion of metal, can not use as lubricant, tenderizer, wetting Agent for Printing Inks, frostproofer or thermal conducting agent; Inhibiter dissolves in various organic solvent more, and what have is toxic, and use can cause certain harm to environment.Up till now, there is not yet and can be applicable to medium, various metals has been played to the inhibiter of corrosion inhibition simultaneously.Certainly, also have and adopt the sustained release dosage of several chemical substance used in combination, but its function and purposes can not include various metal or medium, and other auxiliary agents be used as except inhibiter use.
Summary of the invention
The object of this invention is to provide a kind of rust inhibitor and preparation method thereof.
A kind of rust inhibitor, comprises with parts by weight: water glass 5 ~ 9 parts, sodium polyacrylate 2 ~ 7 parts, mercaptobenzothiazole 1 ~ 5 part, benzotriazole 0.8 ~ 4.5 part, tripoly phosphate sodium STPP 0.2 ~ 2.5 part, hexamethylenetetramine 0.1 ~ 1.5 part, tetrahydroglyoxaline 0.5 ~ 2 part, mercaptobenzothiazole 1 ~ 4 part, alkylamino radical alcohol 0.5 ~ 4.2 part, 0.3 ~ 1.2 part, furfural, poly-phosphate 2 ~ 5 parts, thanomin 1.2 ~ 4.5 parts, Sodium Tetraborate 1.8 ~ 5 parts, ethanol 10 ~ 15 parts.
As the further improvement of foregoing invention, above-mentioned rust inhibitor, comprises with parts by weight: water glass 7 parts, sodium polyacrylate 6 parts, mercaptobenzothiazole 2 parts, benzotriazole 2.3 parts, tripoly phosphate sodium STPP 1.6 parts, hexamethylenetetramine 0.9 part, tetrahydroglyoxaline 1.4 parts, mercaptobenzothiazole 2 parts, alkylamino radical alcohol 3.3 parts, 0.7 part, furfural, poly-phosphate 3 parts, thanomin 2.8 parts, Sodium Tetraborate 3.5 parts, ethanol 13 parts.
The preparation method of above-mentioned rust inhibitor, concrete steps are: first water glass, sodium polyacrylate, mercaptobenzothiazole, benzotriazole, tripoly phosphate sodium STPP, hexamethylenetetramine, tetrahydroglyoxaline, mercaptobenzothiazole, alkylamino radical alcohol, furfural, thanomin and alcohol mixeding liquid are heated to 50 ~ 60 DEG C, add polyphosphoric acid Asia and Sodium Tetraborate again, continue to be heated to 85 ~ 90 DEG C, and after being incubated 2 ~ 3 hours, letting cool and get final product.
The consistency of rust inhibitor of the present invention and each material is good, and antirust time is long, can reach 4-6 month, and have good adaptability to copper, aluminum, the present invention can slowly-releasing antirust while in metallic surface film forming, thus extend antirust time.
Embodiment
Embodiment 1
A kind of rust inhibitor, comprises with parts by weight: water glass 5 parts, sodium polyacrylate 2 parts, mercaptobenzothiazole 1 part, benzotriazole 0.8 part, tripoly phosphate sodium STPP 0.2 part, hexamethylenetetramine 0.1 part, tetrahydroglyoxaline 0.5 part, mercaptobenzothiazole 1 part, alkylamino radical alcohol 0.5 part, 0.3 part, furfural, poly-phosphate 2 parts, thanomin 1.2 parts, Sodium Tetraborate 1.8 parts, ethanol 10 parts.
First water glass, sodium polyacrylate, mercaptobenzothiazole, benzotriazole, tripoly phosphate sodium STPP, hexamethylenetetramine, tetrahydroglyoxaline, mercaptobenzothiazole, alkylamino radical alcohol, furfural, thanomin and alcohol mixeding liquid are heated to 50 ~ 60 DEG C, add polyphosphoric acid Asia and Sodium Tetraborate again, continue to be heated to 85 ~ 90 DEG C, and after being incubated 2 ~ 3 hours, letting cool and get final product.
Embodiment 2
A kind of rust inhibitor, comprises with parts by weight: water glass 6 parts, sodium polyacrylate 5 parts, mercaptobenzothiazole 3 parts, benzotriazole 3.2 parts, tripoly phosphate sodium STPP 2.1 parts, hexamethylenetetramine 1.2 parts, tetrahydroglyoxaline 0.9 part, mercaptobenzothiazole 3 parts, alkylamino radical alcohol 2.8 parts, 0.6 part, furfural, poly-phosphate 4 parts, thanomin 3.5 parts, Sodium Tetraborate 4.2 parts, ethanol 14 parts.
First water glass, sodium polyacrylate, mercaptobenzothiazole, benzotriazole, tripoly phosphate sodium STPP, hexamethylenetetramine, tetrahydroglyoxaline, mercaptobenzothiazole, alkylamino radical alcohol, furfural, thanomin and alcohol mixeding liquid are heated to 50 ~ 60 DEG C, add polyphosphoric acid Asia and Sodium Tetraborate again, continue to be heated to 85 ~ 90 DEG C, and after being incubated 2 ~ 3 hours, letting cool and get final product.
Embodiment 3
A kind of rust inhibitor, comprises with parts by weight: water glass 7 parts, sodium polyacrylate 6 parts, mercaptobenzothiazole 2 parts, benzotriazole 2.3 parts, tripoly phosphate sodium STPP 1.6 parts, hexamethylenetetramine 0.9 part, tetrahydroglyoxaline 1.4 parts, mercaptobenzothiazole 2 parts, alkylamino radical alcohol 3.3 parts, 0.7 part, furfural, poly-phosphate 3 parts, thanomin 2.8 parts, Sodium Tetraborate 3.5 parts, ethanol 13 parts.
First water glass, sodium polyacrylate, mercaptobenzothiazole, benzotriazole, tripoly phosphate sodium STPP, hexamethylenetetramine, tetrahydroglyoxaline, mercaptobenzothiazole, alkylamino radical alcohol, furfural, thanomin and alcohol mixeding liquid are heated to 50 ~ 60 DEG C, add polyphosphoric acid Asia and Sodium Tetraborate again, continue to be heated to 85 ~ 90 DEG C, and after being incubated 2 ~ 3 hours, letting cool and get final product.
Embodiment 4
A kind of rust inhibitor, comprises with parts by weight: water glass 9 parts, sodium polyacrylate 7 parts, mercaptobenzothiazole 5 parts, benzotriazole 4.5 parts, tripoly phosphate sodium STPP 2.5 parts, hexamethylenetetramine 1.5 parts, tetrahydroglyoxaline 2 parts, mercaptobenzothiazole 4 parts, alkylamino radical alcohol 4.2 parts, 1.2 parts, furfural, poly-phosphate 5 parts, thanomin 4.5 parts, Sodium Tetraborate 5 parts, ethanol 15 parts.
First water glass, sodium polyacrylate, mercaptobenzothiazole, benzotriazole, tripoly phosphate sodium STPP, hexamethylenetetramine, tetrahydroglyoxaline, mercaptobenzothiazole, alkylamino radical alcohol, furfural, thanomin and alcohol mixeding liquid are heated to 50 ~ 60 DEG C, add polyphosphoric acid Asia and Sodium Tetraborate again, continue to be heated to 85 ~ 90 DEG C, and after being incubated 2 ~ 3 hours, letting cool and get final product.
Above-described embodiment gained sample and commercial rust inhibitors are carried out simultaneous test, and result is as follows:
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Commercial samples | |
Sample concentration % | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 |
Dilute solution pH value | 8.5 | 8.3 | 8.2 | 8 | 8.7 |
High/low temperature stability | Stable | Stable | Stable | Stable | Stable |
Damp and hot antirust (my god) | 15 | 18 | 16 | 17 | 8 |
Corrodibility H 62Copper 2h | 0 grade | 0 grade | 0 grade | 0 grade | 0 grade |
Corrodibility LY 12Aluminium alloy 2h | 0 grade | 0 grade | 0 grade | 0 grade | 0 grade |
Indoor lacing film (moon) | 5 | 5 | 6 | 6 | 2 |
Seal up for safekeeping antirust (moon) | 9 | 10 | 12 | 11 | 7 |
Residual % | 39 | 37 | 36 | 35 | 38 |
The consistency of rust inhibitor of the present invention and each material is good, and antirust time is long, can reach 4-6 month, and have good adaptability to copper, aluminum, the present invention can slowly-releasing antirust while in metallic surface film forming, thus extend antirust time.
Claims (3)
1. a rust inhibitor, is characterized in that, comprises with parts by weight: water glass 5 ~ 9 parts, sodium polyacrylate 2 ~ 7 parts, mercaptobenzothiazole 1 ~ 5 part, benzotriazole 0.8 ~ 4.5 part, tripoly phosphate sodium STPP 0.2 ~ 2.5 part, hexamethylenetetramine 0.1 ~ 1.5 part, tetrahydroglyoxaline 0.5 ~ 2 part, mercaptobenzothiazole 1 ~ 4 part, alkylamino radical alcohol 0.5 ~ 4.2 part, 0.3 ~ 1.2 part, furfural, poly-phosphate 2 ~ 5 parts, thanomin 1.2 ~ 4.5 parts, Sodium Tetraborate 1.8 ~ 5 parts, ethanol 10 ~ 15 parts.
2. rust inhibitor according to claim 1, is characterized in that, comprises with parts by weight: water glass 7 parts, sodium polyacrylate 6 parts, mercaptobenzothiazole 2 parts, benzotriazole 2.3 parts, tripoly phosphate sodium STPP 1.6 parts, hexamethylenetetramine 0.9 part, tetrahydroglyoxaline 1.4 parts, mercaptobenzothiazole 2 parts, alkylamino radical alcohol 3.3 parts, 0.7 part, furfural, poly-phosphate 3 parts, thanomin 2.8 parts, Sodium Tetraborate 3.5 parts, ethanol 13 parts.
3. the preparation method of the rust inhibitor described in claim 1 or 2, it is characterized in that, first water glass, sodium polyacrylate, mercaptobenzothiazole, benzotriazole, tripoly phosphate sodium STPP, hexamethylenetetramine, tetrahydroglyoxaline, mercaptobenzothiazole, alkylamino radical alcohol, furfural, thanomin and alcohol mixeding liquid are heated to 50 ~ 60 DEG C, add polyphosphoric acid Asia and Sodium Tetraborate again, continue to be heated to 85 ~ 90 DEG C, and after being incubated 2 ~ 3 hours, letting cool and get final product.