CN105001770A - Naturally-drying hammer paint - Google Patents
Naturally-drying hammer paint Download PDFInfo
- Publication number
- CN105001770A CN105001770A CN201510457890.3A CN201510457890A CN105001770A CN 105001770 A CN105001770 A CN 105001770A CN 201510457890 A CN201510457890 A CN 201510457890A CN 105001770 A CN105001770 A CN 105001770A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- dry
- hammer
- alkyd resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses naturally-drying hammer paint and relates to the technical field of chemical industry. The paint is composed of 40-60 parts of dry alkyd resin, 10-20 parts of butyl acetate, 1-3 parts of hammer paint auxiliary agents, 20-40 parts of xylene, 5-8 parts of non-floating-type aluminum powder and 0.1-1 part of nanometer zinc oxide. Compared with the prior art, according to the naturally-drying hammer paint, the dry alkyd resin can get dry naturally and rapidly in air, and the drying process of the dry alkyd resin is a process of crosslinking and curing of macromolecules through the oxygen in the air; the nanometer zinc oxide is added, moisture in the air can be absorbed as a result of the super large specific surface area of the nanometer zinc oxide, the hammer paint gets further dry naturally and rapidly, meanwhile, smell emitted from the butyl acetate is absorbed by being mixed with the moisture in the air, harm of the smell to a human body is reduced, the paint is applicable to protective and decorative coating on various machinery, light and heavy equipment, machine tools, instruments, draft fans, water pumps, safe cases, metal doors and windows and the like, the defects of roughness and unevenness on the surfaces of all metal can be covered up, and the artistic decoration effect can be achieved.
Description
Technical field
The present invention relates to chemical technology field, especially a kind of from dry hammer paint.
Background technology
Hammer paint is gained the name because producing the decorative pattern of luminous reflectance behind the similar hammering metallic surface of its paint film, due to hammer paint surface irregularity and the irregular reflection to light, spraying rear surface has and forms the very strong decorative pattern of hammering shape stereoscopic sensation, thus can the defects such as cover surface is unsmooth.Hammer paint style lines is perfectly clear, color is very bright-coloured glossy, very simple and convenient when construction processing, and after spraying, metallic surface has that hardness is high, paint film is bright plentiful, bright-colored, even, photosensitive pleasing, not dust stratification, the long-pending grease surface easily advantage such as cleaning spent by hammer.Along with the development of modern application techniques, hammer paint is clear with its mallear stria, graceful unique, stereoeffect is good, be evenly distributed and obtain the extensive favor of people, becomes the decorative paint that external coating field is conventional gradually.
And traditional hammer paint adopts the matrix resin such as Synolac, acrylic resin to add non-floating type aluminium powder usually, in spraying film forming surface drying process, owing to sputtering the volatilization of construction and solvent, cause cyclotron motion and capillary change, flake aluminum sinks to being formed the mallear stria of light and shade boundary, for this traditional hammer paint, after paint film surface drying, also need just to obtain through longer dry or drying process that surface hardness is higher, the good hammer paint of patience.
Summary of the invention
Problem to be solved by this invention be to provide a kind of fast drying, without noxious odor from dry hammer paint.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is:
Include the constituent of following weight part:
Dry alkyd resin 40 parts-60 parts, N-BUTYL ACETATE 10 parts-20 parts, hammer agent 1 part-3 parts, dimethylbenzene 20 parts-40 parts, non-floating type aluminium powder 5-8 part, nano zine oxide 0.1-1 part.
In technique scheme, scheme can also be more specifically: the particle size range of described nano zine oxide is 2 ~ 10 nanometers, specific surface area be 51.5 squares of faces/gram.
Further: the weight part of constituent is:
Dry alkyd resin 40 parts, N-BUTYL ACETATE 20 parts, hammer agent 1 part, dimethylbenzene 30 parts, non-floating type aluminium powder 5 parts, nano zine oxide 1 part.
Further: the weight part of constituent is: dry alkyd resin 60 parts, N-BUTYL ACETATE 10 parts, hammer agent 3 parts, dimethylbenzene 40 parts, non-floating type aluminium powder 7 parts, nano zine oxide 0.1 part.
Further: the weight part of constituent is: dry alkyd resin 50 parts, N-BUTYL ACETATE 15 parts, hammer agent 2 parts, dimethylbenzene 20 parts, non-floating type aluminium powder 8 parts, nano zine oxide 0.5 part.
Owing to adopting technique scheme, the beneficial effect that the present invention has is: because dry alkyd resin in atmosphere can quick self-drying, its drying is that macromole is aloft through the process of oxygen crosslinking curing; In component, add nano zine oxide, the specific surface area of its super large, by the moisture absorption in air, this hammer paint quick self-drying can be made further, mix the smell that the moisture absorption N-BUTYL ACETATE in air comes out simultaneously, reduce the harm of this smell to human body.
Embodiment
Below in conjunction with specific examples, the invention will be further described:
Embodiment 1:
The raw material adopted: dry alkyd resin 40 parts, N-BUTYL ACETATE 20 parts, hammer agent 1 part, dimethylbenzene 30 parts, non-floating type aluminium powder 5 parts, nano zine oxide 1 part;
Its preparation method is: dry alkyd resin, N-BUTYL ACETATE, hammer agent, dimethylbenzene, non-floating type aluminium powder 5 parts and nano zine oxide are injected the reactor with stirrer, stirrer stirring velocity is 400-600 rev/min, until dispersed with stirring is even, this hammer paint can be obtained.
Embodiment 2:
The raw material adopted: dry alkyd resin 60 parts, N-BUTYL ACETATE 10 parts, hammer agent 3 parts, dimethylbenzene 40 parts, non-floating type aluminium powder 7 parts, nano zine oxide 0.1 part.
Its preparation method is identical with embodiment 1.
Embodiment 3:
The raw material adopted: dry alkyd resin 50 parts, N-BUTYL ACETATE 15 parts, hammer agent 2 parts, dimethylbenzene 20 parts, non-floating type aluminium powder 8 parts, nano zine oxide 0.5 part.
Its preparation method is identical with embodiment 1.
Standard detection through national building materials inspection center according to coating, prepared by the embodiment of the present invention 1,2,3 as follows from the main performance index of dry hammer paint:
Paint film appearance: decorative pattern is clear, color meets model time of drying: standard thickness single coating, 25 DEG C, surface drying≤20Min, does solid work≤18h, hardness >=0.3 gloss (60 °) >=80.
Claims (5)
1., from a dry hammer paint, it is characterized in that the constituent including following weight part:
Dry alkyd resin 40 parts-60 parts, N-BUTYL ACETATE 10 parts-20 parts, hammer agent 1 part-3 parts, dimethylbenzene 20 parts-40 parts, non-floating type aluminium powder 5-8 part, nano zine oxide 0.1-1 part.
2. according to claim 1 from dry hammer paint, it is characterized in that: the particle size range of described nano zine oxide is 2 ~ 10 nanometers, specific surface area be 51.5 squares of faces/gram.
3. according to claim 1 and 2 from dry hammer paint, it is characterized in that the weight part of constituent is:
Dry alkyd resin 40 parts, N-BUTYL ACETATE 20 parts, hammer agent 1 part, dimethylbenzene 30 parts, non-floating type aluminium powder 5 parts, nano zine oxide 1 part.
4. according to claim 1 and 2 from dry hammer paint, it is characterized in that the weight part of constituent is:
Dry alkyd resin 60 parts, N-BUTYL ACETATE 10 parts, hammer agent 3 parts, dimethylbenzene 40 parts, non-floating type aluminium powder 7 parts, nano zine oxide 0.1 part.
5. according to claim 1 and 2 from dry hammer paint, it is characterized in that the weight part of constituent is:
Dry alkyd resin 50 parts, N-BUTYL ACETATE 15 parts, hammer agent 2 parts, dimethylbenzene 20 parts, non-floating type aluminium powder 8 parts, nano zine oxide 0.5 part.