CN105001729A - Aqueous white primer for sealing wood oil and tannic acid - Google Patents
Aqueous white primer for sealing wood oil and tannic acid Download PDFInfo
- Publication number
- CN105001729A CN105001729A CN201510398203.5A CN201510398203A CN105001729A CN 105001729 A CN105001729 A CN 105001729A CN 201510398203 A CN201510398203 A CN 201510398203A CN 105001729 A CN105001729 A CN 105001729A
- Authority
- CN
- China
- Prior art keywords
- water
- tannic acid
- white primer
- based white
- acid according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses aqueous white primer for sealing wood oil and tannic acid. The aqueous white primer comprises the following components in percentage by weight: 5-10% of water, 1-2% of a dispersant, 0.5-1% of a thickener, 0.1-0.2% of a pH adjustor, 1-2% of a defoamer, 15-20% of a titanium dioxide white pigment, 3-5% of a tannic acid inhibitor, 2-3% of a film forming solution, 8-10% of talcum powder and 47.8-64.4% of an acrylic emulsion. The invention relates to aqueous white primer which can be dried at normal temperature and coated to wooden furniture or artware, so that an extremely strong adhesive force and an excellent oil and tannic acid sealing property are achieved, and the purpose of excellent decoration and protection is realized.
Description
Technical field
The present invention relates to the water-based white primer of a kind of closed timber grease and tannic acid.
Background technology
In recent years, traditional solvent-borne coating products is more and more paid attention to by people because VOC discharges too high caused atmosphere polluting problem, and the cry that aqueous product replaces solvent based product is more and more higher.But traditional solvent based coating as urethane white paint be used on pine, yellow jacket time, due to the closed performance that it is good, the grease on pine can not infiltrate into coating surface, can not affect decoration and the protected effect of coating.But aqueous product is because the Weibull in closure difference and woodwork can dissolve in water, and migrates to water-borne coatings surface white products can be caused to occur variable color, affects decorative effect.Grease in pine also can migrate to surface affects the attractive in appearance of aqueous product and decoration, thus makes coating lose defencive function.
Present conventional have two kinds of terms of settlement:
One, adopt traditional solvent-borne coating first to close once, then make aqueous white priming paint, but this kind of method still makes to contain a large amount of VOC during application discharges.
Two, waterborne cation varnish product is adopted first to close once, make aqueous white priming paint again, but this kind of method makes product of the watersoluble closed clear end and water-based white background product be positively charged ion and anionic product respectively, clean improper easy generation gel in use, all application pipelines, transferpump, coating equipment can be caused all to scrap after there is gel, cause loss up to a million sometimes, cause significant wastage, and closed performance is not good, tannic acid in time long cut wood still easily moves, also increase application number of times, cause client cost to increase.
Summary of the invention
The object of this invention is to provide the water-based white primer of a kind of closed timber grease and tannic acid, to overcome the above-mentioned defect that prior art exists.
Described closed timber grease and tannic acid water-based white background, comprise the component of following weight percent:
Water 5% ~ 10%,
Dispersion agent 1% ~ 2%,
Thickening material 0.5% ~ 1%,
PH conditioning agent 0.1% ~ 0.2%,
Defoamer 1% ~ 2%,
Titanium dioxide white pigment 15 ~ 20%,
Weibull inhibitor 3 ~ 5%,
Film forming solvent 2 ~ 3%,
Talcum powder 8 ~ 10%,
ACRYLIC EMULSION 47.8 ~ 64.4%,
The per-cent sum of said components is 100%.
Described water is common conventional tap water or distilled water
Described dispersion agent is the acrylic block copolymers solution containing pigment affinity groups, can adopt the BYK190 of German BYK company.
Described thickening material is polyurethane thickener, can adopt the ACRYSOLRM-12 of LG-DOW.
Described PH conditioning agent is 2-amino-1-methyl-propanol, can adopt the AMP-95 of Dow Chemical.
Described defoamer is polysiloxane, can adopt the BYK028 of German BYK company.
Described titanium dioxide white pigment is rutile titanium dioxide, can adopt the R-706 of du pont company.
Described Weibull inhibitor is amino zirconates, can adopt the L-44 of HALOX company of the U.S..
Described film forming solvent is dipropylene glycol monomethyl ether, can adopt the DPM of Yangzhou Hua Lun.
Described talcum powder is 1250 order talcum powder, can adopt the KB-2 of the wide company of Guangxi.
Described ACRYLIC EMULSION is that second-order transition temperature is the ACRYLIC EMULSION of 7 DEG C, can adopt the JONCRYL8227 of German BASF admittedly containing 40%, viscosity 100mPa.s.
By the said products routinely coating process (adopting spraying, roller coating or brushing after mix and blend) be coated on pine, red oak, after application after dry 7 days, cross-hatching test adhesion 1 grade, by 50 DEG C × 2 hours,-20 DEG C × 2 hours is a circulation, oozes out, oozes out without tannic acid after five circulations without grease.After sheet material after application being placed in indoor placement and outdoor exposure half a year, all oozing out without obvious grease and ooze out with tannic acid, reach good sealing effect.And closed product does not obviously occur that grease oozes out the yellow trace oozed out with tannic acid, cation blocked product also occurs that slight grease oozes out micro-yellow of oozing out with tannic acid.
Embodiment
Embodiment 1
10 kilograms, water,
Dispersion agent 1 kilogram,
Thickening material 0.5 kilogram,
PH conditioning agent 0.1 kilogram,
Defoamer 1 kilogram,
Titanium dioxide white pigment 15 kilograms,
5 kilograms, Weibull inhibitor,
Film forming solvent 2 kilograms,
Talcum powder 10 kilograms,
ACRYLIC EMULSION 55.4 kilograms,
Described water is common conventional tap water or distilled water
Described dispersion agent is the acrylic block copolymers solution containing pigment affinity groups, can adopt the BYK190 of German BYK company.
Described thickening material is polyurethane thickener, can adopt the ACRYSOLRM-12 of LG-DOW.
Described PH conditioning agent is 2-amino-1-methyl-propanol, can adopt the AMP-95 of Dow Chemical.
Described defoamer is polysiloxane, can adopt the BYK028 of German BYK company.
Described titanium dioxide white pigment is rutile titanium dioxide, can adopt the R-706 of du pont company.
Described Weibull inhibitor is amino zirconates, can adopt the L-44 of HALOX company of the U.S..
Described film forming solvent is dipropylene glycol monomethyl ether, can adopt the DPM of Yangzhou Hua Lun.
Described talcum powder is 1250 order talcum powder, can adopt the KB-2 of the wide company of Guangxi.
Described ACRYLIC EMULSION is that second-order transition temperature is the ACRYLIC EMULSION of 7 DEG C, can adopt the JONCRYL8227 of German BASF admittedly containing 40%, viscosity 100mPa.s.
By the said products routinely coating process (adopting spraying, roller coating or brushing after mix and blend) be coated on pine, red oak, detect correlated performance after dry 7 days after application:
Embodiment 2
Described water is common conventional tap water or distilled water
Described dispersion agent is the acrylic block copolymers solution containing pigment affinity groups, can adopt the BYK190 of German BYK company.
Described thickening material is polyurethane thickener, can adopt the ACRYSOLRM-12 of LG-DOW.
Described PH conditioning agent is 2-amino-1-methyl-propanol, can adopt the AMP-95 of Dow Chemical.
Described defoamer is polysiloxane, can adopt the BYK028 of German BYK company.
Described titanium dioxide white pigment is rutile titanium dioxide, can adopt the R-706 of du pont company.
Described Weibull inhibitor is amino zirconates, can adopt the L-44 of HALOX company of the U.S..
Described film forming solvent is dipropylene glycol monomethyl ether, can adopt the DPM of Yangzhou Hua Lun.
Described talcum powder is 1250 order talcum powder, can adopt the KB-2 of the wide company of Guangxi.
Described ACRYLIC EMULSION is that second-order transition temperature is the ACRYLIC EMULSION of 7 DEG C, can adopt the JONCRYL8227 of German BASF admittedly containing 40%, viscosity 100mPa.s.
By the said products routinely coating process (adopting spraying, roller coating or brushing after mix and blend) be coated on pine, red oak, detect correlated performance after dry 7 days after application:
Embodiment 3
Described water is common conventional tap water or distilled water
Described dispersion agent is the acrylic block copolymers solution containing pigment affinity groups, can adopt the BYK190 of German BYK company.
Described thickening material is polyurethane thickener, can adopt the ACRYSOLRM-12 of LG-DOW.
Described PH conditioning agent is 2-amino-1-methyl-propanol, can adopt the AMP-95 of Dow Chemical.
Described defoamer is polysiloxane, can adopt the BYK028 of German BYK company.
Described titanium dioxide white pigment is rutile titanium dioxide, can adopt the R-706 of du pont company.
Described Weibull inhibitor is amino zirconates, can adopt the L-44 of HALOX company of the U.S..
Described film forming solvent is dipropylene glycol monomethyl ether, can adopt the DPM of Yangzhou Hua Lun.
Described talcum powder is 1250 order talcum powder, can adopt the KB-2 of the wide company of Guangxi.
Described ACRYLIC EMULSION is that second-order transition temperature is the ACRYLIC EMULSION of 7 DEG C, can adopt the JONCRYL8227 of German BASF admittedly containing 40%, viscosity 100mPa.s.
By the said products routinely coating process (adopting spraying, roller coating or brushing after mix and blend) be coated on pine, red oak, detect correlated performance after dry 7 days after application:
Claims (12)
1. for the water-based white primer of closed timber grease and tannic acid, it is characterized in that, according to weight percent, its formula comprises as follows:
Water 5% ~ 10%,
Dispersion agent 1% ~ 2%,
Thickening material 0.5% ~ 1%,
PH conditioning agent 0.1% ~ 0.2%,
Defoamer 1% ~ 2%,
Titanium dioxide white pigment 15 ~ 20%,
Weibull inhibitor 3 ~ 5%,
Film forming solvent 2 ~ 3%,
Talcum powder 8 ~ 10%,
ACRYLIC EMULSION 47.8 ~ 64.4%,
The per-cent sum of said components is 100%.
2. the water-based white primer for closed timber grease and tannic acid according to claim 1, it is characterized in that, described water is common conventional tap water or distilled water.
3. the water-based white primer for closed timber grease and tannic acid according to claim 1, is characterized in that, described dispersion agent is the acrylic block copolymers solution containing pigment affinity groups.
4. the water-based white primer for closed timber grease and tannic acid according to claim 1, it is characterized in that, described thickening material is polyurethane thickener.
5. the water-based white primer for closed timber grease and tannic acid according to claim 1, it is characterized in that, described PH conditioning agent is 2-amino-1-methyl-propanol.
6., according to the water-based white primer for closed timber grease and tannic acid described in claim 1, it is characterized in that, described defoamer is polysiloxane.
7. the water-based white primer for closed timber grease and tannic acid according to claim 1, it is characterized in that, described titanium dioxide white pigment is rutile titanium dioxide.
8. the water-based white primer for closed timber grease and tannic acid according to claim 1, it is characterized in that, described Weibull inhibitor is amino zirconates.
9. the water-based white primer for closed timber grease and tannic acid according to claim 1, it is characterized in that, described film forming solvent is dipropylene glycol monomethyl ether.
10. the water-based white primer for closed timber grease and tannic acid according to claim 1, it is characterized in that, described talcum powder is 1250 order talcum powder.
11. water-based white primers for closed timber grease and tannic acid according to claim 1, is characterized in that, described ACRYLIC EMULSION is that second-order transition temperature is the ACRYLIC EMULSION of 7 DEG C admittedly containing 40%, viscosity 100mPa.s.
The application of 12. water-based white primers for closed timber grease and tannic acid according to any one of claim 1 ~ 11, is characterized in that, be applied on wood furniture or artwork.