CN105001703A - Environment-friendly optical glass deinking agent - Google Patents
Environment-friendly optical glass deinking agent Download PDFInfo
- Publication number
- CN105001703A CN105001703A CN201510477047.1A CN201510477047A CN105001703A CN 105001703 A CN105001703 A CN 105001703A CN 201510477047 A CN201510477047 A CN 201510477047A CN 105001703 A CN105001703 A CN 105001703A
- Authority
- CN
- China
- Prior art keywords
- deinking agent
- ink
- water
- glass
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an environment-friendly optical glass deinking agent. The deinking agent is a water solution containing alkali compounds, inorganic auxiliary agents, organic auxiliary agents and high-flash-point organic solvents. The alkali compounds are selected from one or two of hydroxide and alkali metal salt of alcohol. The inorganic auxiliary agents are selected from one or more of carbonate, silicate and borate of metal. The organic auxiliary agents are amine compounds. The high-flash-point organic solvents are selected from one or two of alcohol ether compounds, polyhydric alcohols and derivative of the polyhydric alcohols. The glass deinking agent is mainly used for removing screen printing ink on sheet glass, touch screens and other glass; the deinking agent has very good removal effects on single-layer black ink, multi-layer white ink, light blocking printing ink, UV printing ink, shielding printing ink and the like for the printing ink to be removed.
Description
Technical field
The present invention relates to a kind of chemical technology field, relate to a kind of environment-friendly type opticglass deinking agent particularly.
Background technology
Opticglass ink for screen printing is one important procedure in glass processing, and the Logo at the edge of the glass such as handset touch panel, tablet personal computer display screen, button and decorative pattern are all by silk-screen operation, adopts the solidification measure of ink and is formed.Ink has the feature such as stable chemical nature, anti-oxidant, anticorrosive strong, high abrasion resistance by the rete that hot setting is formed, and is widely used in the fields such as electronic product, medical facilities, research equipment.
But, usually need ink to remove in following several situation: 1), ink silk screen printing is bad, in order to cost-saving, silk-screen again of need doing over again of reducing the loss; 2), in process of production, ink is for covering the part on workpiece, and non-shaded portions will carry out other operations (such as metallizing rete, etching etc.), the ink covered will be removed when completing operation; 3), through life-time service, the ink on workpiece is damaged or aging, when needing to remove again ink for screen printing.Due to the strong adhesion of ink, will remove completely at short notice and not affect ground workpiece is also difficult problem place in industrial application.
Existing de-inking method mainly contains 1), Halogen, to remove containing benzene solvent: it is long that this method removes the time, and solvent evaporates amount is large, has very large detrimentally affect to the health of environment and operator; 2), soda boiling removes: this method energy consumption is high, and higher to the requirement of equipment, eliminates gradually; 3), common deinking agent removes: this deinking agent uses more now, ubiquitous problem is inflammable, needs to be heated to 80 DEG C ~ 90 DEG C during use, effective to individual layer ink (tusche), but poor to multilayer ink effect, the requirement of present glass deinking can not be met.
Summary of the invention
The object of the invention is for overcoming existing technical problem, a kind of energy-conserving and environment-protective, use range is wide, deinking efficiency is better glass deinking agent are provided.
The technique means that the present invention adopts is:
A kind of environment-friendly type opticglass deinking agent, described deinking agent is the aqueous solution containing basic cpd, inorganic assistant agent, organic additive, high flash point organic solvent, described basic cpd be selected from an alkali metal salt of oxyhydroxide, alcohol one or both, its concentration is 20 g/L ~ 200g/L; Described inorganic assistant agent be selected from the carbonate of metal, silicate and borate one or more, its concentration is 10 g/L ~ 200g/L; Described organic additive is aminated compounds, and its concentration is 10 g/L ~ 200g/L; Described high flash point organic solvent be selected from the derivative of ether compound, polyvalent alcohol and polyvalent alcohol one or both, its concentration is 100 g/L ~ 400g/L.
Preferably, described organic additive is trolamine and/or diglycolamine.
Preferably, described high flash point organic solvent is selected from glycol ether and/or diethylene glycol ether.
Preferably, described basic cpd is alkali-metal oxyhydroxide.
Further, described basic cpd is sodium hydroxide.
Preferably, described deinking agent also containing water stablizer, described water stablizer be selected from water-soluble carboxylic acid, Water-Soluble Glucose hydrochlorate, water-soluble edetate one or more, its concentration is 5 g/L ~ 50g/L.
Preferably, described deinking agent consists of:
Sodium hydroxide 150g/L;
Water glass 10g/L;
Trolamine 80g/L;
Glycol ether 200 g/L.
Preferably, described deinking agent consists of:
Sodium hydroxide 200g/L;
Water glass 5g/L;
Trolamine 150g/L;
Glycol ether 100g/L;
Diethylene glycol ether 150 g/L;
Ethylenediamine tetraacetic acid (EDTA) 5g/L.
The using method of glass deinking agent provided by the present invention is as follows:
Use deinking agent stoste, be heated to 60-70 DEG C, put into the workpiece treating deinking, soak 3min ~ 20min, ink can remove completely, and the workpiece water having taken off ink rinses, pure water rinsing is dried.
Glass deinking agent provided by the present invention, mainly removes the ink for screen printing on the glass such as sheet glass, touch-screen, also has good effect to the depainting de-oiling ink of other alkaline-resisting materials as stainless steel, copper alloy, nickelalloy, plastics etc.; For the ink that will remove, this deinking agent to individual layer tusche, multilayer chalk, resistance ink, UV ink, cover ink etc. and have good removal effect.
Embodiment
In conjunction with example, the present invention is described further, but embodiments of the present invention are not limited thereto.
Embodiment 1
Be dissolved in 550 ml deionized water by sodium hydroxide 150g, water glass 10g, stir and dissolve completely, then glycol ether 200g, trolamine 80g are added, constant volume is 1L, stirs, for subsequent use.
Immerse in gained deinking agent completely by there being the touch-screen glass of individual layer ink and multilayer ink, soak 15min at about 65 DEG C, individual layer ink can remove completely at 5min, and multilayer ink can remove totally at 12min completely, substrate glass is tested through SEM, can see glass surface corrosion-free.
Embodiment 2
Be dissolved in 500 ml deionized water by potassium hydroxide 160g, sodium ethylene diamine tetracetate 10g, borax 10g, stir and dissolve completely, then diethylene glycol ether 240g, diglycolamine 80g are added, constant volume is 1L, stirs, for subsequent use.
Immerse in gained deinking agent completely by there being the touch-screen glass of individual layer ink and multilayer ink, soak 10min at about 65 DEG C, individual layer ink can remove completely at 3min, and multilayer ink can remove totally at 10min completely, substrate glass is tested through SEM, can see glass surface corrosion-free.
Embodiment 3
Be dissolved in 460 ml deionized water by sodium hydroxide 200g, ethylenediamine tetraacetic acid (EDTA) potassium 5g, water glass 5g, stir and dissolve completely, then glycol ether 100g, diethylene glycol ether 150g, trolamine 150g are added, constant volume is 1L, stirs, for subsequent use.
Immerse in gained deinking agent completely by there being the touch-screen glass of individual layer ink and multilayer ink, soak 15min at about 70 DEG C, individual layer ink can remove completely at 2min, and multilayer ink can remove totally at 8min completely, substrate glass is tested through SEM, can see glass surface corrosion-free.
These are only preferred embodiment of the present invention, be not limited to the present invention, all any amendments done within the spirit and principles in the present invention, equivalent to replace and improvement etc., within the protection domain that all should be included in invention.
Claims (8)
1. an environment-friendly type opticglass deinking agent, described deinking agent is the aqueous solution containing basic cpd, inorganic assistant agent, organic additive, high flash point organic solvent, it is characterized in that, described basic cpd be selected from an alkali metal salt of oxyhydroxide, alcohol one or both, its concentration is 20 g/L ~ 200g/L; Described inorganic assistant agent be selected from the carbonate of metal, silicate and borate one or more, its concentration is 10 g/L ~ 200g/L; Described organic additive is aminated compounds, and its concentration is 10 g/L ~ 200g/L; Described high flash point organic solvent be selected from the derivative of ether compound, polyvalent alcohol and polyvalent alcohol one or both, its concentration is 100 g/L ~ 400g/L.
2. deinking agent as claimed in claim 1, it is characterized in that, described organic additive is trolamine and/or diglycolamine.
3. deinking agent as claimed in claim 1, it is characterized in that, described high flash point organic solvent is selected from glycol ether and/or diethylene glycol ether.
4. deinking agent as claimed in claim 1, it is characterized in that, described basic cpd is alkali-metal oxyhydroxide.
5. deinking agent as claimed in claim 4, it is characterized in that, described basic cpd is sodium hydroxide.
6. deinking agent as claimed in claim 1, it is characterized in that, described deinking agent also containing water stablizer, described water stablizer be selected from water-soluble carboxylic acid, Water-Soluble Glucose acid alkali metal salt, water-soluble ethylenediamine tetraacetic acid (EDTA) an alkali metal salt one or more, its concentration is 5 g/L ~ 50g/L.
7. deinking agent as claimed in claim 1, it is characterized in that, described deinking agent consists of:
Sodium hydroxide 150g/L;
Water glass 10g/L;
Trolamine 80g/L;
Glycol ether 200 g/L.
8. deinking agent as claimed in claim 6, it is characterized in that, described deinking agent consists of:
Sodium hydroxide 200g/L;
Water glass 5g/L;
Trolamine 150g/L;
Glycol ether 100g/L;
Diethylene glycol ether 150 g/L;
Ethylenediamine tetraacetic acid (EDTA) potassium 5g/L.