CN104988726A - Electronic fabric impregnating compound - Google Patents
Electronic fabric impregnating compound Download PDFInfo
- Publication number
- CN104988726A CN104988726A CN201510205062.0A CN201510205062A CN104988726A CN 104988726 A CN104988726 A CN 104988726A CN 201510205062 A CN201510205062 A CN 201510205062A CN 104988726 A CN104988726 A CN 104988726A
- Authority
- CN
- China
- Prior art keywords
- water
- sizing agent
- electronics cloth
- silane coupling
- impregnating compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an electronic fabric impregnating compound. The electronic fabric impregnating compound comprises 1-3wt% of a vinyl silane coupling agent, 5-8wt% of an epoxy silane coupling agent, 2-5wt% of water-soluble polyester, 5-8wt% of polyurethane, 3-5wt% of epoxy resin, 2-3wt% of machine oil, 1-2wt% of Vaseline, 4-8wt% of a paraffin emulsion, 1-2wt% of a special additive, and the balance of water. The use amounts of the machine oil and paraffin in the impregnating compound are reduced, and the epoxy silane coupling agent and other substances are added, so electronic fabrics using the impregnating compound have the characteristics of good textile property, and reduced content of combustibles.
Description
Technical field
The present invention relates to technical field of inorganic nonmetallic materials, particularly relate to a kind of electronics cloth sizing agent.
Background technology
At present, the emollient component in the formula of known electronics cloth paraffin sizing material does not use paraffin, vaseline, machine oil lamp oily substance.The solid content of this electronics cloth sizing agent is high, cause the electronics cloth size content of drawing more than 1%, the sizing agent on this electronics cloth surface needs high temperature smoldering to remove, a large amount of electric energy is consumed in the process of high temperature smoldering, and because electronics cloth sizing agent solid content is high, affect the processing of next process.
Summary of the invention
The object of the invention is to solve deficiency of the prior art, a kind of electronics cloth sizing agent of low-solid content is provided.
Object of the present invention can be achieved through the following technical solutions:
A kind of electronics cloth sizing agent, the chemical component weight percentage of described electronics cloth sizing agent is: vinyl silicane coupling agent 1%-3%, epoxy silane coupling 5%-8%, water-soluble polyester 2%-5%, polyurethane 5%-8%, epoxy resin 3%-5%, machine oil 2%-3%, vaseline 1%-2%, paraffin wax emulsions 4%-8%, specialist additive 1%-2%, excess water.
Preferably, the chemical component weight percentage of described electronics cloth sizing agent is: vinyl silicane coupling agent 2%, epoxy silane coupling 5%, water-soluble polyester 2%, polyurethane 5%%, epoxy resin 3%, machine oil 2%, vaseline 1%, paraffin wax emulsions 4%, specialist additive 1%, excess water.
Preferably, described specialist additive is the one in inorganic acid, Organic Acid and Base class PH conditioning agent.
Beneficial effect of the present invention: the sizing agent adopting this formula, the intensity of electronics cloth can be strengthened, the electronics cloth sizing agent of this formula is adopted to make electronics cloth combustible content low, be 0.75%-0.85% through verification experimental verification combustible content, more original paraffin class sizing agent combustible content reduces 15%-20%, reduces infiltration cost.
Detailed description of the invention
For the ease of it will be appreciated by those skilled in the art that the present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
Get the raw material of following weight percent part, vinyl silicane coupling agent 2%, epoxy silane coupling 8%, water-soluble polyester 5%, polyurethane 8%, epoxy resin 3%, machine oil 2%, vaseline 1%, paraffin wax emulsions 4%, specialist additive 1%, excess water, by vinyl silicane coupling agent, epoxy silane coupling, water-soluble polyester thin up respectively, join in paraffin, machine oil, vaseline mixed emulsion, stir; Again by after polyurethane, epoxy resin dilute with water, add respectively, added by specialist additive simultaneously, the stirring that adds water is made for 25 minutes.
Embodiment 2
Get the raw material of following weight percent part, vinyl silicane coupling agent 2%, epoxy silane coupling 5%, water-soluble polyester 2%, polyurethane 5%%, epoxy resin 3%, machine oil 2%, vaseline 1%, paraffin wax emulsions 4%, specialist additive 1%, excess water, by vinyl silicane coupling agent, epoxy silane coupling, water-soluble polyester thin up respectively, join in paraffin, machine oil, vaseline mixed emulsion, stir; Again by after polyurethane, epoxy resin dilute with water, add respectively, added by specialist additive simultaneously, the stirring that adds water is made for 30 minutes.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. an electronics cloth sizing agent, it is characterized in that, the chemical component weight percentage of described electronics cloth sizing agent is: vinyl silicane coupling agent 1%-3%, epoxy silane coupling 5%-8%, water-soluble polyester 2%-5%, polyurethane 5%-8%, epoxy resin 3%-5%, machine oil 2%-3%, vaseline 1%-2%, paraffin wax emulsions 4%-8%, specialist additive 1%-2%, excess water.
2. according to a kind of electronics cloth sizing agent described in claim 1, it is characterized in that, the chemical component weight percentage of described electronics cloth sizing agent is: vinyl silicane coupling agent 2%, epoxy silane coupling 5%, water-soluble polyester 2%, polyurethane 5%%, epoxy resin 3%, machine oil 2%, vaseline 1%, paraffin wax emulsions 4%, specialist additive 1%, excess water.
3. according to a kind of electronics cloth sizing agent described in claim 1, it is characterized in that, described specialist additive is the one in inorganic acid, Organic Acid and Base class PH conditioning agent.